CN112826298A - Manufacturing method of titanium liner three-layer composite vacuum cup - Google Patents
Manufacturing method of titanium liner three-layer composite vacuum cup Download PDFInfo
- Publication number
- CN112826298A CN112826298A CN202110296734.9A CN202110296734A CN112826298A CN 112826298 A CN112826298 A CN 112826298A CN 202110296734 A CN202110296734 A CN 202110296734A CN 112826298 A CN112826298 A CN 112826298A
- Authority
- CN
- China
- Prior art keywords
- liner
- layer
- titanium
- stainless steel
- semi
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for manufacturing a titanium liner three-layer composite vacuum cup, which comprises the following steps: s1: forming a semi-finished product liner; s2: forming a titanium inner container; s3: crystallizing the titanium liner; s4: forming a semi-finished product middle-layer liner; s5: a gap is left between the mouth of the semi-finished product middle-layer liner and the mouth of the titanium liner to form a stainless steel middle-layer liner; s6: forming a semi-finished shell; s7: forming a lower weld; s8: forming a stainless steel shell and forming a vacuum layer; s9: forming a heat-insulating layer and forming an upper welding seam; s10: grinding the lower welding line and the upper welding line, and treating the surface of the stainless steel shell. Through the design, the invention can realize the consistent air pressure between the inside and the outside in the vacuum-pumping process, and avoid the deformation and the scrapping of the titanium liner and the stainless steel middle-layer liner caused by the expansion of the air between the titanium liner and the stainless steel middle-layer liner in the vacuum-pumping process, thereby improving the production quality of the vacuum cup.
Description
Technical Field
The invention relates to the technical field of vacuum cups, in particular to a manufacturing method of a titanium liner three-layer composite vacuum cup.
Background
At present, in the manufacturing process of the three-layer composite vacuum cup, the middle layer and the inner layer are welded firstly, then the outer layer and the middle layer are welded, and finally the outer layer bottom sheet is welded and vacuumized. However, air is left between the middle layer and the inner layer by such operation, and the inner and outer air pressure difference is formed when the outer layer bottom sheet is vacuumized, thereby affecting the quality of the vacuum cup. Improvements are needed.
Disclosure of Invention
The invention provides a novel method for manufacturing a titanium inner container three-layer composite vacuum cup, aiming at the defects of the prior art that the inner and outer air pressure difference is formed when the outer bottom sheet is vacuumized.
In order to solve the technical problems, the invention is realized by the following technical scheme:
a manufacturing method of a titanium liner three-layer composite vacuum cup comprises the following steps:
s1: taking a titanium raw material pipe, performing water expansion molding, and then sequentially performing cup separation, opening flattening, necking, roll sealing of water ribs, edge curling, flattening, thinning and opening flattening to form a semi-finished product liner;
s2: taking a titanium liner bottom sheet, and welding the titanium liner bottom sheet to the bottom of the semi-finished liner to form the titanium liner;
s3: crystallizing the titanium inner container by using a vacuum furnace;
s4: taking a stainless steel raw material pipe A, performing water expansion molding, and then sequentially performing cup separation, flat bottom, necking, curling, flattening, spinning and flat bottom to form a semi-finished product middle-layer liner;
s5: sleeving the semi-finished product middle-layer liner on the outer side of the titanium liner for port matching, wherein the position of the port of the semi-finished product middle-layer liner is lower than that of the port of the titanium liner, so that a gap is reserved between the port of the semi-finished product middle-layer liner and the port of the titanium liner, then taking a stainless steel middle-layer bottom sheet, and welding the stainless steel middle-layer bottom sheet to the bottom of the semi-finished product middle-layer liner to form the stainless steel middle-layer liner;
s6: taking a stainless steel raw material pipe B, performing water expansion molding, and then sequentially performing cup separation, flat bottom, necking and flat bottom to form a semi-finished shell;
s7: sleeving the semi-finished shell on the outer side of the stainless steel middle-layer liner, wherein the position of an opening of the semi-finished shell is lower than that of the opening of the stainless steel middle-layer liner, and then welding the opening of the semi-finished shell on the stainless steel middle-layer liner to form a lower welding seam;
s8: taking a stainless steel shell bottom plate with a vacuumizing hole, welding the stainless steel shell bottom plate on the bottom of the semi-finished shell to form a stainless steel shell, and vacuumizing to form a vacuum layer;
s9: using a gas injector to inject inert gas between the stainless steel middle-layer liner and the titanium liner, so as to discharge air between the stainless steel middle-layer liner and the titanium liner to form a heat insulation layer, and then welding the stainless steel middle-layer liner on the titanium liner to form an upper welding seam;
s10: and grinding the lower welding line and the upper welding line, and performing surface treatment on the stainless steel shell to finish the manufacture of the titanium liner three-layer composite vacuum cup.
In the step S1, the separately formed semi-finished inner container has lower processing difficulty, thereby improving the processing efficiency and the yield and reducing the production cost. In step S2, after the titanium liner bottom sheet is welded to the semi-finished liner, a complete sealed cavity is formed, so that the liquid contacting part in the vacuum cup is made of titanium, and the liquid is prevented from being polluted. In step S3, the surface crystallization treatment is performed on the titanium liner, so that the characteristics of the titanium material can be more prominent, and the characteristics of the titanium material can be better. In step S4, the separately formed intermediate layer liner of the semi-finished product is finally wrapped in the stainless steel shell, so that the requirement of the intermediate layer liner of the semi-finished product on the surface smoothness is not high, thereby greatly reducing the processing difficulty, improving the processing efficiency and the yield, and reducing the production cost. In the step S5, the gap is reserved so that air between the two layers can be pumped away in the vacuumizing process, the air pressure inside and outside is consistent, deformation and scrapping of the titanium inner container and the stainless steel middle-layer inner container caused by expansion of the air between the two layers in the vacuumizing process are avoided, the production quality of the vacuum cup is improved, and an air filling opening is reserved for the subsequent step of filling inert gas between the two layers. In the step S6, the separately formed semi-finished shell has lower processing difficulty, thereby improving the processing efficiency and the yield and reducing the production cost. In the step S7, the lower welding seam and the upper welding seam are staggered, so that the air tightness of the two welding seams is ensured, and the subsequent vacuumizing step caused by air leakage of the welding seams due to the fact that the same positions are welded twice is avoided. In step S8, the stainless steel shell and the stainless steel middle layer liner form a complete sealed cavity, and a vacuum environment is formed after vacuum pumping, so that the heat preservation efficiency of the vacuum cup is improved. In step S9, the inert gas can reduce the thermal convection of the insulation layer, thereby improving the insulation efficiency by 5% to 10% compared with the case where the insulation layer is filled with air. In step S10, the ground may remove the welding trace of the lower weld and the upper weld, making the surfaces of the lower weld and the upper weld smoother, and making the user experience more comfortable when using the device.
Through the design, the invention can realize the consistent air pressure between the inside and the outside in the vacuum-pumping process, and avoid the deformation and the scrapping of the titanium liner and the stainless steel middle-layer liner caused by the expansion of the air between the titanium liner and the stainless steel middle-layer liner in the vacuum-pumping process, thereby improving the production quality of the vacuum cup.
Preferably, in the above method for manufacturing a titanium liner three-layer composite vacuum cup, in step S5, the step of sleeving the intermediate layer liner on the outer side of the titanium liner for matching comprises: pre-inverting the mouth part of the titanium inner container, sleeving the semi-finished product middle layer inner container on the outer side of the titanium inner container, and inverting the mouth part of the titanium inner container to form an arc-shaped mouth part with the width of 1.5-3 mm.
The arc-shaped mouth part with the width of 1.5 mm-3 mm can be formed through the design, and a larger lip contact area is provided in the drinking process of a user, so that the use experience of the invention is improved.
Preferably, in the above method for manufacturing a titanium liner three-layer composite vacuum cup, in step S5, the position of the mouth of the intermediate layer liner of the semi-finished product is 1mm to 5mm lower than the position of the mouth of the titanium liner.
Through the design, a gap can be reserved between the middle-layer inner container opening part of the semi-finished product and the titanium inner container opening part, and the gap cannot be too small or too large, so that a sufficient exhaust space is provided for subsequent vacuumizing, the subsequent welding efficiency is guaranteed, and deformation of the vacuum cup caused by the formation of inside and outside air pressure is avoided.
Preferably, in the above method for manufacturing a titanium inner container three-layer composite vacuum cup, in step S7, the position of the mouth of the semi-finished shell is 1mm to 5mm lower than the position of the mouth of the stainless steel middle layer inner container.
The mouth of the semi-finished shell is staggered with the mouth of the stainless steel middle-layer liner, so that the complete air tightness of the lower welding line and the upper welding line is ensured, and the phenomenon that the air leakage and the vacuum degree are lost due to the welding of the same position is avoided. The distance between the two welding lines is kept between 1mm and 5mm, so that the two welding lines are not influenced mutually, and the yield of the vacuum cup is improved.
Preferably, in the above manufacturing method of the titanium inner container three-layer composite vacuum cup, in step S7, the welding between the mouth of the semi-finished shell and the stainless steel middle layer inner container is laser welding or brazing.
The invention can be widely compatible with laser welding equipment in the current market by adopting laser welding, for example, the welding device disclosed in the patent of CN201811167317.9 'argon gas protection welding device for titanium cup' can be adopted, so that the production cost is reduced, the welding quality can be ensured, and the vacuum effect and the yield are ensured. The brazing of the mouth of the semi-finished shell and the stainless steel middle-layer liner and the brazing of the bottom of the semi-finished shell and the stainless steel middle-layer bottom sheet can be simultaneously carried out in production by adopting brazing, so that the working procedure times are reduced, and the production efficiency is improved.
Preferably, in the above method for manufacturing a titanium liner three-layer composite vacuum cup, the welding the stainless steel middle layer liner to the titanium liner in step S9 includes: and tightly matching the mouth position of the stainless steel middle-layer liner with the mouth position of the titanium liner in a flush manner, and welding the stainless steel middle-layer liner on the titanium liner.
The invention adopts the close-fitting design of the mouth part, so that the invention can adopt simplified welding equipment, for example, the welding device disclosed in the patent of CN201811167317.9 'argon gas protection welding device for titanium cup', thereby reducing the production cost and ensuring the welding quality.
Preferably, in the above method for manufacturing a titanium liner three-layer composite vacuum cup, the welding the stainless steel middle layer liner to the titanium liner in step S9 includes: and pressing the mouth part of the titanium inner container to the mouth part of the stainless steel middle-layer inner container, and welding the stainless steel middle-layer inner container on the titanium inner container.
Through the design, the mouth structures with different shapes can be produced, the welding quality is improved, and the welding device disclosed in the patent of CN201811167317.9 'argon protection welding device for titanium cups' can be adopted.
Preferably, in the manufacturing method of the titanium liner three-layer composite vacuum cup, in step S9, the thickness of the heat insulation layer is 0.05 mm-2 mm, the stainless steel middle layer liner protrudes inwards or the titanium liner protrudes outwards, and the stainless steel middle layer liner and the titanium liner are tightly matched through the protruding part.
Through the design, the air in the heat insulation layer can be pumped away in the vacuumizing process, the production quality of the vacuum cup is improved, enough inert gas can be filled, and the heat insulation efficiency of the vacuum cup is further improved. On the other hand, stainless steel middle level inner bag passes through the bulge position tight fit with the titanium inner bag, further plays the effect of supporting the titanium inner bag, avoids the thermos cup accident to fall and leads to the titanium inner bag to warp, has improved the life of thermos cup.
Preferably, in the manufacturing method of the titanium liner three-layer composite vacuum cup, in step S9, the thickness of the heat insulation layer is 0.01mm to 0.05mm, and the stainless steel middle layer liner protrudes outwards or the titanium liner protrudes inwards to form the air guide groove.
Through the design, the stainless steel middle layer inner container is basically tightly matched with the titanium inner container, the effect of supporting the titanium inner container is further achieved, the phenomenon that the titanium inner container is deformed due to the fact that the vacuum cup falls accidentally is avoided, and the service life of the vacuum cup is prolonged. The air guide groove plays a role in guiding air, so that the production efficiency of the vacuum cup is higher, and the flushing effect of inert gas is also ensured.
Preferably, in the above method for manufacturing a titanium liner three-layer composite vacuum cup, in step S9, the inert gas is injected for 5S to 100S, and the inert gas is argon or xenon.
Through the design, not only can the heat preservation be guaranteed to be flushed with enough inert gas, but also the flushing time is limited, so that the production cost is reduced, and the production efficiency is improved. The inert gas is argon or xenon, so that the production cost can be controlled, and a good heat insulation effect can be provided.
Drawings
FIG. 1 is a schematic structural diagram of the present invention after being processed by steps S1, S2, S3, S4 and S5;
FIG. 2 is a schematic view of the structure of the titanium inner container with the mouth portion thereof reversed;
FIG. 3 is a schematic structural view of the mouth and the back of the titanium inner container;
FIG. 4 is a schematic structural diagram of the present invention after being processed by steps S6, S7, S8;
FIG. 5 is a schematic structural view of the flush welding of the mouth of the stainless steel middle layer inner container and the mouth of the titanium inner container;
FIG. 6 is a schematic structural view of the mouth of the stainless steel middle layer inner container welded to the mouth of the titanium inner container in a reversed manner;
FIG. 7 is a schematic view of the inward protrusion of the stainless steel middle liner of the present invention;
FIG. 8 is a schematic view of the outward convex structure of the titanium liner of the present invention;
FIG. 9 is a schematic view of the outward convex structure of the stainless steel middle layer inner container of the present invention;
FIG. 10 is a schematic view of the inward protrusion of the titanium liner of the present invention.
Detailed Description
The invention will be described in further detail below with reference to the accompanying figures 1-10 and the detailed description, but they are not intended to limit the invention:
example 1
A manufacturing method of a titanium liner three-layer composite vacuum cup comprises the following steps:
s1: taking a titanium raw material pipe, performing water expansion molding, and then sequentially performing cup separation, opening flattening, necking, roll sealing of water ribs, edge curling, flattening, thinning and opening flattening to form a semi-finished product liner;
s2: taking a titanium liner bottom sheet, and welding the titanium liner bottom sheet to the bottom of the semi-finished liner to form a titanium liner 1;
s3: crystallizing the titanium liner 1 by using a vacuum furnace;
s4: taking a stainless steel raw material pipe A, performing water expansion molding, and then sequentially performing cup separation, flat bottom, necking, curling, flattening, spinning and flat bottom to form a semi-finished product middle-layer liner;
s5: sleeving the semi-finished product middle-layer liner on the outer side of the titanium liner 1 for matching, wherein the position of the mouth of the semi-finished product middle-layer liner is lower than that of the titanium liner 1, so that a gap is reserved between the mouth of the semi-finished product middle-layer liner and the mouth of the titanium liner 1, then taking a stainless steel middle-layer bottom sheet, and welding the stainless steel middle-layer bottom sheet to the bottom of the semi-finished product middle-layer liner to form a stainless steel middle-layer liner 2;
s6: taking a stainless steel raw material pipe B, performing water expansion molding, and then sequentially performing cup separation, flat bottom, necking and flat bottom to form a semi-finished shell;
s7: sleeving the semi-finished shell on the outer side of the stainless steel middle-layer liner 2, wherein the position of the opening of the semi-finished shell is lower than that of the opening of the stainless steel middle-layer liner 2, and then welding the opening of the semi-finished shell on the stainless steel middle-layer liner 2 to form a lower welding seam 4;
s8: taking a stainless steel shell bottom plate with a vacuumizing hole, welding the stainless steel shell bottom plate on the bottom of the semi-finished shell to form a stainless steel shell 3, and vacuumizing to form a vacuum layer;
s9: using a gas injector to flush inert gas between the stainless steel middle-layer liner 2 and the titanium liner 1, so as to discharge air between the stainless steel middle-layer liner 2 and the titanium liner 1 to form a heat insulation layer, and then welding the stainless steel middle-layer liner 2 on the titanium liner 1 to form an upper welding seam 5;
s10: and grinding the lower welding line 4 and the upper welding line 5, and performing surface treatment on the stainless steel shell 3 to finish the manufacture of the titanium liner three-layer composite vacuum cup.
Preferably, in step S5, the position of the mouth of the intermediate layer liner is 1mm lower than the position of the mouth of the titanium liner 1.
Preferably, in step S7, the mouth position of the semi-finished casing is 1mm lower than the mouth position of the stainless steel middle liner 2.
Preferably, in step S7, the welding between the mouth of the semi-finished shell and the stainless steel middle layer inner container 2 is laser welding or brazing.
Preferably, in step S9, the inert gas is flushed for 5 seconds, and the inert gas is argon or xenon.
Example 2
A manufacturing method of a titanium liner three-layer composite vacuum cup comprises the following steps:
s1: taking a titanium raw material pipe, performing water expansion molding, and then sequentially performing cup separation, opening flattening, necking, roll sealing of water ribs, edge curling, flattening, thinning and opening flattening to form a semi-finished product liner;
s2: taking a titanium liner bottom sheet, and welding the titanium liner bottom sheet to the bottom of the semi-finished liner to form a titanium liner 1;
s3: crystallizing the titanium liner 1 by using a vacuum furnace;
s4: taking a stainless steel raw material pipe A, performing water expansion molding, and then sequentially performing cup separation, flat bottom, necking, curling, flattening, spinning and flat bottom to form a semi-finished product middle-layer liner;
s5: sleeving the semi-finished product middle-layer liner on the outer side of the titanium liner 1 for matching, wherein the position of the mouth of the semi-finished product middle-layer liner is lower than that of the titanium liner 1, so that a gap is reserved between the mouth of the semi-finished product middle-layer liner and the mouth of the titanium liner 1, then taking a stainless steel middle-layer bottom sheet, and welding the stainless steel middle-layer bottom sheet to the bottom of the semi-finished product middle-layer liner to form a stainless steel middle-layer liner 2;
s6: taking a stainless steel raw material pipe B, performing water expansion molding, and then sequentially performing cup separation, flat bottom, necking and flat bottom to form a semi-finished shell;
s7: sleeving the semi-finished shell on the outer side of the stainless steel middle-layer liner 2, wherein the position of the opening of the semi-finished shell is lower than that of the opening of the stainless steel middle-layer liner 2, and then welding the opening of the semi-finished shell on the stainless steel middle-layer liner 2 to form a lower welding seam 4;
s8: taking a stainless steel shell bottom plate with a vacuumizing hole, welding the stainless steel shell bottom plate on the bottom of the semi-finished shell to form a stainless steel shell 3, and vacuumizing to form a vacuum layer;
s9: using a gas injector to flush inert gas between the stainless steel middle-layer liner 2 and the titanium liner 1, so as to discharge air between the stainless steel middle-layer liner 2 and the titanium liner 1 to form a heat insulation layer, and then welding the stainless steel middle-layer liner 2 on the titanium liner 1 to form an upper welding seam 5;
s10: and grinding the lower welding line 4 and the upper welding line 5, and performing surface treatment on the stainless steel shell 3 to finish the manufacture of the titanium liner three-layer composite vacuum cup.
Preferably, in step S5, the mouth of the intermediate inner container is 5mm lower than the mouth of the titanium inner container 1.
Preferably, in step S7, the position of the mouth of the semi-finished casing is 5mm lower than the position of the mouth of the stainless steel middle liner 2.
Preferably, in step S7, the welding between the mouth of the semi-finished shell and the stainless steel middle layer inner container 2 is laser welding or brazing.
Preferably, in step S9, the inert gas is flushed for 100 seconds, and the inert gas is argon or xenon.
Example 3
A manufacturing method of a titanium liner three-layer composite vacuum cup comprises the following steps:
s1: taking a titanium raw material pipe, performing water expansion molding, and then sequentially performing cup separation, opening flattening, necking, roll sealing of water ribs, edge curling, flattening, thinning and opening flattening to form a semi-finished product liner;
s2: taking a titanium liner bottom sheet, and welding the titanium liner bottom sheet to the bottom of the semi-finished liner to form a titanium liner 1;
s3: crystallizing the titanium liner 1 by using a vacuum furnace;
s4: taking a stainless steel raw material pipe A, performing water expansion molding, and then sequentially performing cup separation, flat bottom, necking, curling, flattening, spinning and flat bottom to form a semi-finished product middle-layer liner;
s5: sleeving the semi-finished product middle-layer liner on the outer side of the titanium liner 1 for matching, wherein the position of the mouth of the semi-finished product middle-layer liner is lower than that of the titanium liner 1, so that a gap is reserved between the mouth of the semi-finished product middle-layer liner and the mouth of the titanium liner 1, then taking a stainless steel middle-layer bottom sheet, and welding the stainless steel middle-layer bottom sheet to the bottom of the semi-finished product middle-layer liner to form a stainless steel middle-layer liner 2;
s6: taking a stainless steel raw material pipe B, performing water expansion molding, and then sequentially performing cup separation, flat bottom, necking and flat bottom to form a semi-finished shell;
s7: sleeving the semi-finished shell on the outer side of the stainless steel middle-layer liner 2, wherein the position of the opening of the semi-finished shell is lower than that of the opening of the stainless steel middle-layer liner 2, and then welding the opening of the semi-finished shell on the stainless steel middle-layer liner 2 to form a lower welding seam 4;
s8: taking a stainless steel shell bottom plate with a vacuumizing hole, welding the stainless steel shell bottom plate on the bottom of the semi-finished shell to form a stainless steel shell 3, and vacuumizing to form a vacuum layer;
s9: using a gas injector to flush inert gas between the stainless steel middle-layer liner 2 and the titanium liner 1, so as to discharge air between the stainless steel middle-layer liner 2 and the titanium liner 1 to form a heat insulation layer, and then welding the stainless steel middle-layer liner 2 on the titanium liner 1 to form an upper welding seam 5;
s10: and grinding the lower welding line 4 and the upper welding line 5, and performing surface treatment on the stainless steel shell 3 to finish the manufacture of the titanium liner three-layer composite vacuum cup.
Preferably, in step S5, the mouth of the intermediate inner container is 3mm lower than the mouth of the titanium inner container 1.
Preferably, in step S7, the position of the mouth of the semi-finished casing is 3mm lower than the position of the mouth of the stainless steel middle liner 2.
Preferably, in step S7, the welding between the mouth of the semi-finished shell and the stainless steel middle layer inner container 2 is laser welding or brazing.
Preferably, in step S9, the inert gas is flushed for 52.5S, and the inert gas is argon or xenon.
Example 4
Preferably, the welding of the stainless steel inner liner 2 to the titanium inner liner 1 in step S9 includes: and (3) tightly matching the mouth position of the stainless steel middle-layer liner 2 with the mouth position of the titanium liner 1 in a flush manner, and welding the stainless steel middle-layer liner 2 on the titanium liner 1.
Other embodiments are the same as examples 1 to 3.
Example 5
Preferably, the step S5 of sleeving the intermediate-layer liner on the outer side of the titanium liner 1 for matching includes: pre-turning the mouth of the titanium liner 1, sleeving the intermediate layer liner of the semi-finished product on the outer side of the titanium liner 1, and turning the mouth of the titanium liner 1 to form an arc mouth with the width of 1.5 mm.
Preferably, the welding of the stainless steel inner liner 2 to the titanium inner liner 1 in step S9 includes: and pressing the mouth part of the titanium inner container 1 against the mouth part of the stainless steel middle-layer inner container 2, and welding the stainless steel middle-layer inner container 2 on the titanium inner container 1.
Other embodiments are the same as examples 1 to 3.
Example 6
Preferably, the step S5 of sleeving the intermediate-layer liner on the outer side of the titanium liner 1 for matching includes: pre-inverting the mouth of the titanium liner 1, sleeving the intermediate-layer liner of the semi-finished product on the outer side of the titanium liner 1, and inverting the mouth of the titanium liner 1 to form an arc mouth with the width of 3 mm.
Preferably, the welding of the stainless steel inner liner 2 to the titanium inner liner 1 in step S9 includes: and pressing the mouth part of the titanium inner container 1 against the mouth part of the stainless steel middle-layer inner container 2, and welding the stainless steel middle-layer inner container 2 on the titanium inner container 1.
Other embodiments are the same as examples 1 to 3.
Example 7
Preferably, the step S5 of sleeving the intermediate-layer liner on the outer side of the titanium liner 1 for matching includes: pre-turning the mouth of the titanium liner 1, sleeving the intermediate layer liner of the semi-finished product on the outer side of the titanium liner 1, and turning the mouth of the titanium liner 1 to form an arc mouth with the width of 2.25 mm.
Preferably, the welding of the stainless steel inner liner 2 to the titanium inner liner 1 in step S9 includes: and pressing the mouth part of the titanium inner container 1 against the mouth part of the stainless steel middle-layer inner container 2, and welding the stainless steel middle-layer inner container 2 on the titanium inner container 1.
Other embodiments are the same as examples 1 to 3.
Example 8
Preferably, in step S9, the thickness of the heat insulating layer is 0.05mm, the stainless steel middle layer inner container 2 protrudes inward or the titanium inner container 1 protrudes outward, and the stainless steel middle layer inner container 2 and the titanium inner container 1 are tightly fitted through the protruding portion.
Other embodiments are the same as examples 1 to 7.
Example 9
Preferably, in step S9, the thickness of the heat insulating layer is 2mm, the stainless steel middle layer inner container 2 protrudes inward or the titanium inner container 1 protrudes outward, and the stainless steel middle layer inner container 2 and the titanium inner container 1 are tightly fitted through the protruding portion.
Other embodiments are the same as examples 1 to 7.
Example 10
Preferably, in step S9, the thickness of the insulating layer is 1.025mm, the stainless steel middle layer inner container 2 protrudes inward or the titanium inner container 1 protrudes outward, and the stainless steel middle layer inner container 2 and the titanium inner container 1 are tightly fitted through the protruding portion.
Other embodiments are the same as examples 1 to 7.
Example 11
Preferably, in step S9, the thickness of the insulating layer is 0.01mm, and the stainless steel middle layer inner container 2 protrudes outward or the titanium inner container 1 protrudes inward to form an air guide groove.
Other embodiments are the same as examples 1 to 7.
Example 12
Preferably, in step S9, the thickness of the insulating layer is 0.05mm, and the stainless steel middle layer inner container 2 protrudes outward or the titanium inner container 1 protrudes inward to form an air guide groove.
Other embodiments are the same as examples 1 to 7.
Example 13
Preferably, in step S9, the thickness of the insulating layer is 0.03mm, and the stainless steel middle liner 2 protrudes outward or the titanium liner 1 protrudes inward to form an air guide groove.
Other embodiments are the same as examples 1 to 7.
In summary, the above-mentioned embodiments are only preferred embodiments of the present invention, and all equivalent changes and modifications made within the scope of the claims of the present invention should be covered by the present invention.
Claims (10)
1. A manufacturing method of a titanium liner three-layer composite vacuum cup is characterized by comprising the following steps:
s1: taking a titanium raw material pipe, performing water expansion molding, and then sequentially performing cup separation, opening flattening, necking, roll sealing of water ribs, edge curling, flattening, thinning and opening flattening to form a semi-finished product liner;
s2: taking a titanium liner bottom sheet, and welding the titanium liner bottom sheet to the bottom of the semi-finished liner to form a titanium liner (1);
s3: crystallizing the titanium inner container (1) by using a vacuum furnace;
s4: taking a stainless steel raw material pipe A, performing water expansion molding, and then sequentially performing cup separation, flat bottom, necking, curling, flattening, spinning and flat bottom to form a semi-finished product middle-layer liner;
s5: sleeving the semi-finished product middle-layer liner on the outer side of the titanium liner (1) for port matching, wherein the position of the port of the semi-finished product middle-layer liner is lower than the position of the port of the titanium liner (1), so that a gap is reserved between the port of the semi-finished product middle-layer liner and the port of the titanium liner (1), then taking a stainless steel middle-layer bottom sheet, and welding the stainless steel middle-layer bottom sheet to the bottom of the semi-finished product middle-layer liner to form a stainless steel middle-layer liner (2);
s6: taking a stainless steel raw material pipe B, performing water expansion molding, and then sequentially performing cup separation, flat bottom, necking and flat bottom to form a semi-finished shell;
s7: sleeving the semi-finished shell on the outer side of the stainless steel middle-layer liner (2), wherein the position of the opening of the semi-finished shell is lower than that of the opening of the stainless steel middle-layer liner (2), and then welding the opening of the semi-finished shell on the stainless steel middle-layer liner (2) to form a lower welding seam (4);
s8: taking a stainless steel shell bottom plate with a vacuumizing hole, welding the stainless steel shell bottom plate on the bottom of the semi-finished shell to form a stainless steel shell (3), and vacuumizing to form a vacuum layer;
s9: injecting inert gas between the stainless steel middle layer liner (2) and the titanium liner (1) by using a gas injector, so as to discharge air between the stainless steel middle layer liner (2) and the titanium liner (1) to form a heat insulation layer, and then welding the stainless steel middle layer liner (2) on the titanium liner (1) to form an upper welding seam (5);
s10: and (3) grinding the lower welding seam (4) and the upper welding seam (5), and performing surface treatment on the stainless steel shell (3) to finish the manufacture of the titanium liner three-layer composite vacuum cup.
2. The manufacturing method of a titanium liner three-layer composite vacuum cup as claimed in claim 1, wherein the step of sleeving the semi-finished product middle layer liner on the outer side of the titanium liner (1) in step S5 for matching comprises the following steps: pre-inverting the mouth of the titanium inner container (1), sleeving the semi-finished product middle-layer inner container on the outer side of the titanium inner container (1), and inverting the mouth of the titanium inner container (1) to form an arc-shaped mouth with the width of 1.5-3 mm.
3. The manufacturing method of the titanium liner three-layer composite vacuum cup as claimed in claim 1, wherein: in step S5, the position of the mouth of the intermediate layer inner container of the semi-finished product is 1 mm-5 mm lower than the position of the mouth of the titanium inner container (1).
4. The manufacturing method of the titanium liner three-layer composite vacuum cup as claimed in claim 1, wherein: in step S7, the position of the mouth of the semi-finished shell is 1 mm-5 mm lower than the position of the mouth of the stainless steel middle layer liner (2).
5. The manufacturing method of the titanium liner three-layer composite vacuum cup as claimed in claim 1, wherein: in step S7, the welding between the mouth of the semi-finished shell and the stainless steel middle layer inner container (2) is laser welding or brazing.
6. The method for manufacturing a titanium liner three-layer composite thermos cup according to the claim 1, wherein the step S9 of welding the stainless steel middle layer liner (2) on the titanium liner (1) comprises: and (3) tightly matching the mouth position of the stainless steel middle-layer liner (2) with the mouth position of the titanium liner (1) in a flush manner, and welding the stainless steel middle-layer liner (2) on the titanium liner (1).
7. The method for manufacturing a titanium liner three-layer composite thermos cup according to the claim 2, wherein the step S9 of welding the stainless steel middle layer liner (2) on the titanium liner (1) comprises: and pressing the mouth part of the titanium inner container (1) to the mouth part of the stainless steel middle-layer inner container (2), and welding the stainless steel middle-layer inner container (2) on the titanium inner container (1).
8. The manufacturing method of the titanium liner three-layer composite vacuum cup as claimed in claim 1, wherein: in the step S9, the thickness of the heat-insulating layer is 0.05 mm-2 mm, the stainless steel middle layer liner (2) protrudes inwards or the titanium liner (1) protrudes outwards, and the stainless steel middle layer liner (2) and the titanium liner (1) are tightly matched through the protruding part.
9. The manufacturing method of the titanium liner three-layer composite vacuum cup as claimed in claim 1, wherein: in step S9, the thickness of the insulating layer is 0.01mm to 0.05mm, and the stainless steel middle layer inner container (2) protrudes outward or the titanium inner container (1) protrudes inward to form an air guide groove.
10. The manufacturing method of the titanium liner three-layer composite vacuum cup as claimed in claim 1, wherein: in step S9, the inert gas is flushed for 5S to 100S, and the inert gas is argon or xenon.