CN112813457A - 一种催化剂负载合金钢电极板的制备方法 - Google Patents
一种催化剂负载合金钢电极板的制备方法 Download PDFInfo
- Publication number
- CN112813457A CN112813457A CN202011607910.8A CN202011607910A CN112813457A CN 112813457 A CN112813457 A CN 112813457A CN 202011607910 A CN202011607910 A CN 202011607910A CN 112813457 A CN112813457 A CN 112813457A
- Authority
- CN
- China
- Prior art keywords
- alloy steel
- catalyst
- powder
- electrode plate
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (10)