CN112796019A - Garment fabric for gymnastics training and preparation process - Google Patents

Garment fabric for gymnastics training and preparation process Download PDF

Info

Publication number
CN112796019A
CN112796019A CN202011570235.6A CN202011570235A CN112796019A CN 112796019 A CN112796019 A CN 112796019A CN 202011570235 A CN202011570235 A CN 202011570235A CN 112796019 A CN112796019 A CN 112796019A
Authority
CN
China
Prior art keywords
fiber
fibers
fabric
polyester
solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202011570235.6A
Other languages
Chinese (zh)
Inventor
黄荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaanxi University of Technology
Original Assignee
Shaanxi University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shaanxi University of Technology filed Critical Shaanxi University of Technology
Priority to CN202011570235.6A priority Critical patent/CN112796019A/en
Publication of CN112796019A publication Critical patent/CN112796019A/en
Pending legal-status Critical Current

Abstract

The invention discloses a garment fabric for gymnastics training and a preparation process thereof. Compared with the prior art, the gymnastics training special-purpose garment fabric is prepared by adopting scientific proportioning raw materials and a scientific process, not only is sweat-absorbent and breathable, but also the activated carbon powder is well fused with the fabric, and the gymnastics training garment prepared by adopting the fabric is sweat-absorbent and breathable, the activated carbon is beneficial to body health, the comfort level can be improved, and the gymnastics training special-purpose garment fabric has popularization and application values.

Description

Garment fabric for gymnastics training and preparation process
Technical Field
The invention relates to a garment fabric, in particular to a garment fabric for gymnastics training and a preparation process thereof.
Background
The gymnastics is a general term of all gymnastics projects, including athletics projects such as competitive gymnastics, artistic gymnastics and trampolines, and non-Olympic games projects such as competitive aerobics and skill sports. The competitive gymnastics are a branch of gymnastics, and are exercises for completing complex and coordinated actions on a specified instrument and giving scores according to scores of the actions or difficulty, arrangement and completion conditions and the like of the actions. In the prior art, most of training clothes for gymnastics training only have elasticity, but have insufficient sweat absorption and air permeability and poor comfort, so that an improvement space exists.
Disclosure of Invention
The invention aims to solve the problems and provide a garment material for gymnastics training and a preparation process thereof.
The invention realizes the purpose through the following technical scheme:
the invention relates to a garment fabric for gymnastics training, which consists of cotton fibers, polyester fibers, polyamide fibers, modal fibers, tencel fibers, chemical fiber filaments, chloromethyl methyl ether solution, methyl isothioketone solution, organic silicon quaternary ammonium salt emulsion, activated carbon powder, polyester fibers and spandex fibers.
Preferably, the fabric comprises, by weight, 35% of the cotton fiber, 15% of the polyester fiber, 15% of the polyamide fiber, 8% of the modal fiber, 4% of the tencel fiber, 6% of the chemical fiber filament, 2% of the chloromethyl methyl ether solution, 1% of the methyl isothioketone solution, 1% of the organic silicon quaternary ammonium salt emulsion, 3% of the activated carbon powder, 5% of the polyester fiber and 5% of the spandex fiber.
The invention relates to a preparation process of a garment fabric for gymnastics training, which comprises the following steps:
spinning cotton fibers and polyester fibers into silk threads serving as warp threads of the garment material;
soaking the warps in chloromethyl solution for 1-2 min;
thirdly, polyester fiber, nylon fiber, modal fiber, tencel fiber and chemical fiber filament are blended into silk threads which are used as weft threads of the garment material;
soaking the weft in the methyl isothiazolinone solution for 1-2 min;
fifthly, preparing the polyester fiber and the spandex fiber into silk threads, and respectively weaving the silk threads and the warps and the wefts into cloth;
sixthly, fully mixing the organosilicon quaternary ammonium salt emulsion and the activated carbon powder;
seventhly, putting the woven cloth into the emulsion obtained in the step sixteenth to soak for 24 hours;
and eighthly, airing the soaked cloth to prepare the clothing fabric for gymnastics training.
The invention has the beneficial effects that:
the invention is a gymnastics training uses the facing material and preparation method, compared with prior art, the invention adopts scientific matching raw materials and scientific craft to make the specialized facing material of gymnastics training, not merely absorb sweat and ventilate, and fuse activated carbon powder well with cloth, the gymnastics training clothes made of facing material of the invention absorb sweat and ventilate, activated carbon is favorable to the health, and can improve the comfort level, have value popularized and applied.
Detailed Description
The invention is further illustrated below:
the invention relates to a garment fabric for gymnastics training, which consists of cotton fibers, polyester fibers, polyamide fibers, modal fibers, tencel fibers, chemical fiber filaments, chloromethyl methyl ether solution, methyl isothioketone solution, organic silicon quaternary ammonium salt emulsion, activated carbon powder, polyester fibers and spandex fibers.
Preferably, the fabric comprises, by weight, 35% of the cotton fiber, 15% of the polyester fiber, 15% of the polyamide fiber, 8% of the modal fiber, 4% of the tencel fiber, 6% of the chemical fiber filament, 2% of the chloromethyl methyl ether solution, 1% of the methyl isothioketone solution, 1% of the organic silicon quaternary ammonium salt emulsion, 3% of the activated carbon powder, 5% of the polyester fiber and 5% of the spandex fiber.
The invention relates to a preparation process of a garment fabric for gymnastics training, which comprises the following steps:
spinning cotton fibers and polyester fibers into silk threads serving as warp threads of the garment material;
soaking the warps in chloromethyl solution for 1-2 min;
thirdly, polyester fiber, nylon fiber, modal fiber, tencel fiber and chemical fiber filament are blended into silk threads which are used as weft threads of the garment material;
soaking the weft in the methyl isothiazolinone solution for 1-2 min;
fifthly, preparing the polyester fiber and the spandex fiber into silk threads, and respectively weaving the silk threads and the warps and the wefts into cloth;
sixthly, fully mixing the organosilicon quaternary ammonium salt emulsion and the activated carbon powder;
seventhly, putting the woven cloth into the emulsion obtained in the step sixteenth to soak for 24 hours;
and eighthly, airing the soaked cloth to prepare the clothing fabric for gymnastics training.
The foregoing shows and describes the general principles and features of the present invention, together with the advantages thereof. It will be understood by those skilled in the art that the present invention is not limited to the embodiments described above, which are described in the specification and illustrated only to illustrate the principle of the present invention, but that various changes and modifications may be made therein without departing from the spirit and scope of the present invention, which fall within the scope of the invention as claimed. The scope of the invention is defined by the appended claims and equivalents thereof.

Claims (3)

1. A clothing fabric for gymnastics training is characterized in that: the fabric is composed of cotton fibers, polyester fibers, polyamide fibers, modal fibers, tencel fibers, chemical fiber filaments, chloromethyl solution, methyl isothioketone solution, organic silicon quaternary ammonium salt emulsion, activated carbon powder, polyester fibers and spandex fibers.
2. The clothing fabric for gymnastic training as claimed in claim 1, wherein: according to the weight ratio, the fabric comprises 35% of the cotton fiber, 15% of the polyester fiber, 15% of the polyamide fiber, 8% of the modal fiber, 4% of the tencel fiber, 6% of the chemical fiber filament, 2% of the chloromethyl methyl ether solution, 1% of the methyl isothioketone solution, 1% of the organic silicon quaternary ammonium salt emulsion, 3% of the activated carbon powder, 5% of the polyester fiber and 5% of the spandex fiber.
3. A preparation process of a garment fabric for gymnastics training is characterized by comprising the following steps:
spinning cotton fibers and polyester fibers into silk threads serving as warp threads of the garment material;
soaking the warps in chloromethyl solution for 1-2 min;
thirdly, polyester fiber, nylon fiber, modal fiber, tencel fiber and chemical fiber filament are blended into silk threads which are used as weft threads of the garment material;
soaking the weft in the methyl isothiazolinone solution for 1-2 min;
fifthly, preparing the polyester fiber and the spandex fiber into silk threads, and respectively weaving the silk threads and the warps and the wefts into cloth;
sixthly, fully mixing the organosilicon quaternary ammonium salt emulsion and the activated carbon powder;
seventhly, putting the woven cloth into the emulsion obtained in the step sixteenth to soak for 24 hours;
and eighthly, airing the soaked cloth to prepare the clothing fabric for gymnastics training.
CN202011570235.6A 2020-12-26 2020-12-26 Garment fabric for gymnastics training and preparation process Pending CN112796019A (en)