CN112795287A - Low-viscosity high-solid environment-friendly coating - Google Patents
Low-viscosity high-solid environment-friendly coating Download PDFInfo
- Publication number
- CN112795287A CN112795287A CN202011615792.5A CN202011615792A CN112795287A CN 112795287 A CN112795287 A CN 112795287A CN 202011615792 A CN202011615792 A CN 202011615792A CN 112795287 A CN112795287 A CN 112795287A
- Authority
- CN
- China
- Prior art keywords
- low
- coating
- viscosity high
- viscosity
- friendly coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a low-viscosity high-solid environment-friendly coating which comprises the following components: low-viscosity high-sterol acid resin, 996 titanium dioxide, phthalocyanine blue BGS, precipitated barium sulfate, JF-38 bentonite, D40 solvent oil, a rare earth dry material and a cobalt dry material. The low-viscosity high-solid environment-friendly coating provided by the invention has the characteristics of excellent covering power performance, good drying performance, no tendency and sagging of a coating layer, thick coating and the like, is mainly used for coating various substrates such as steel structural members, industrial machinery, buildings and the like, and has the characteristics of low production cost, convenience in construction, small environmental influence and the like.
Description
Technical Field
The invention belongs to the field of coatings, and particularly relates to a low-viscosity high-solid environment-friendly coating.
Background
High solids coatings, coatings with relatively low molecular mass and high solids content. Such as low solvent polyester coatings, and the like. Characterized in that the amount of volatile solvent and the construction number can be reduced. Is an energy-saving coating. It can be used for brushing products in the aspects of light industry, handwork, spinning, electromechanics, instruments and the like.
CN101280055B discloses an environment-friendly alkyd resin with high solid content and low viscosity, which has low organic solvent content and high solid content, and a preparation method thereof. The acid value of the high-solid low-viscosity environment-friendly alkyd resin is less than or equal to 10mg KOH/g, the non-volatile matter is 63-67%, and the viscosity is 50-110 s/25 ℃; the alkyd resin is prepared by the following steps: under the catalysis of an organic tin catalyst, gradually heating terephthalic acid, oleic acid with the iodine value of more than 120, rosin and glycerol in a reflux solvent to carry out esterification reaction, cooling after the reaction is finished, and adjusting the non-volatile components and the viscosity to obtain a final product; the weight ratio of the terephthalic acid, the oleic acid, the rosin, the glycerol, the organic tin catalyst and the reflux solvent is 10-20: 20-30: 12-18: 10-15: 0.10-0.20: 1.0-5.0.
CN102993925A discloses a self-drying alkyd resin coating with high solid content and a preparation method thereof. The air-drying alkyd resin coating with high solid content is characterized by mainly comprising the following components in parts by weight: high-solid alkyd resin (1), titanium white, calcium carbonate, rosin water, glass beads, high-solid alkyd resin (2), cobalt naphthenate, lead naphthenate, methyl ethyl ketoxime and the like. The high-solid alkyd resin coating generally refers to a coating with a solid content of more than 70% and an organic solvent of less than 20% abroad, the conventional alkyd resin process cannot ensure that the solid content of the coating reaches the standard, and because the conventional alkyd resin has long molecular chain, high molecular weight and viscosity which is increased along with the increase of the molecular weight, a large amount of solvent is added for dilution during paint preparation or construction, so that the requirement can be met.
Disclosure of Invention
The invention aims to overcome the defects of the prior art and provide the low-viscosity high-solid environment-friendly coating with excellent covering power performance and good drying performance.
In order to achieve the purpose, the invention is realized according to the following steps:
the environment-friendly coating with low viscosity and high solid comprises the following components:
moreover, the solid content of the alkyd resin is high and can reach 75-78%, the viscosity is 28S, the Grignard pipe and the short oil length resin are less than 2# iron-cobalt number, generally 0-1 # (when the vegetable oil is less than 6 #), and the medium and long oil length resin are less than 6 #.
Compared with the prior art, the invention has the beneficial effects that:
the low-viscosity high-solid environment-friendly coating provided by the invention has the characteristics of excellent covering power performance, good drying performance, no tendency and sagging of a coating layer, thick coating and the like, is mainly used for coating various substrates such as steel structural members, industrial machinery, buildings and the like, and has the characteristics of low production cost, convenience in construction, small environmental influence and the like.
Detailed description of the invention
The following examples are intended to further illustrate the invention, but not to limit the scope of the invention. Any changes made in the art upon reading this disclosure are to be considered equivalents thereof.
Example 1
The low-viscosity high-solid environment-friendly coating comprises the following components in parts by weight:
the solid content of the alkyd resin is high and can reach 75-78%, the viscosity is 28S, the Grignard reaction tube is adopted, the short oil length resin is less than 2# iron-cobalt number, generally, the number is 0-1 # (when the vegetable oil is less than 6 #), and the medium and long oil length resin is less than 6 #.
The low-viscosity high-solid environment-friendly coating provided by the invention comprises the following steps:
adding titanium dioxide, phthalocyanine blue BGS, precipitated barium sulfate and JF-38 bentonite into a mixing disperser according to the formula, fully mixing and dispersing to 15-25 mu m, adding low-viscosity high-sterol acid resin, D40 solvent oil, rare earth dry material and cobalt dry material, uniformly mixing, and filtering to obtain the coating.
Example 2
The hyperbranched epoxy primer comprises the following components in parts by weight:
the preparation method is the same as that of example 1
The technical scheme described in the two embodiments of the invention has the following detection data:
item | Results |
Paint color and appearance | Uniform, particle-free, pinhole-free bubbles |
Time to surface dry | 4-5min |
Actual drying time/h | 2 |
Hardness of pencil | 3H |
Cross-cut adhesion/grade | 0 |
Impact resistance (kg. cm) | 100 |
Flexibility (cylindrical shaft bending) | 0.8 |
Gasoline resistance (10h) | By passing |
Engine oil resistant | By passing |
Gasoline resistant | By passing |
Diesel resistant oil | By passing |
Artificially accelerated aging | Qualified |
Claims (3)
2. the low viscosity high solid environment-friendly coating according to claim 1, characterized in that: the solid content of the low-viscosity high-sterol acid resin is 75%.
3. The low viscosity high solid environment-friendly coating according to claim 1, characterized in that: the solid content of the low-viscosity high-sterol alkyd resin is high and can reach 75-78%, the viscosity is 28S, the short oil length resin is less than 2# Fe-Co number, generally 0-1 # and the medium and long oil length resin is less than 6 #.