CN1127774A - 保护通讯电缆接头的灌充密封物 - Google Patents
保护通讯电缆接头的灌充密封物 Download PDFInfo
- Publication number
- CN1127774A CN1127774A CN 95101222 CN95101222A CN1127774A CN 1127774 A CN1127774 A CN 1127774A CN 95101222 CN95101222 CN 95101222 CN 95101222 A CN95101222 A CN 95101222A CN 1127774 A CN1127774 A CN 1127774A
- Authority
- CN
- China
- Prior art keywords
- sealing material
- component
- cable joint
- communication cable
- filled sealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种保护通讯电缆接头的灌充密封物。它是选用异氰酸酯3-40%,邻苯二甲酸二辛酯5-60%,植物油5-60%组成A组分,选用聚丙醚二醇0-50%,蓖麻油5-50%,邻苯二甲酸二辛酯5-60%,催化剂0.1-5%组成B组分,然后把A组分与B组分按1∶1-3混合均匀而成。本品除能满足保护通讯电缆接头的各种必须要求外,更重要的是成本低廉、施工简便、原材料国产化、对人体无毒害作用。
Description
本发明涉及的是一种保护通讯电缆接头的灌充密封物,特别涉及一种用于保护电话充油电缆接头的灌充密封物。
众所周知,为了使电话线路正常工作,必须对电话电缆接头的裸露部分进行防水、防潮、防震及防有害物质侵蚀的保护处理。具体地说,就是用一种灌封物质包裹在电缆接头的外部,将其保护起来,以达上述目的。用于上述接头密封的材料应满足下述要求,(1)良好的电绝缘性能;(2)在工作环境温度下有稳定的化学性能;(3)有良好的柔韧性;(4)具有透明性;(5)无毒性、无刺激性嗅味,不污染环境。传统的灌封物是用沥青、石蜡等材料,这些材料的缺点是施工麻烦;不透明,维修时无从下手,只能全部拆掉,重新处理;化学性能不稳定。近几年来,国内外研制成功多种反应型双组分高分子弹性体灌封材料,例如美国3M公司公开的一种用聚丁二烯及酯和矿物油等制成的反应型双组分高分子弹性体灌封材料,但其成本太高,有些原材料国内没有生产,不适于国内大量采用。国内亦有专利论及用端羟基聚丁二烯及异晴酸酯体系反应型双组分高分子弹性体灌封材料,其效果据介绍同3M公司的相近,但由于端羟基聚丁二烯极其昂贵,而且具有强烈的刺激性,对人体不利,因此亦未能大量广泛应用。
本发明目的在于改进现有技术之缺点而提供一种成本低廉,施工简便、原材料国产化、对人体无毒害作用,同时又能满足保护通讯电缆接头的上述各种性能要求的灌充密封物。
本发明目的是这样实现的,选用下列成分及其重量百分比分别制成A组分和B组分:
A组分:
异氰酸酯 3-40%
邻苯二甲酸二辛酯 5-60%
植物油 5-60%
B组分:
聚丙醚二醇 0-50%
蓖麻油 5-50%
邻苯二甲酸二辛酯 5-60%
催化剂 0.1-5%
其中异氰酯酯可以是甲苯二异氰酸酯、液态的4、4`-二苯基甲烷二异氰酸酯或者萘二异氰酸酯,聚丙醚二醇的分子量为1000-3000,植物油可选用花生油、豆油或菜籽油等。催化剂可以选用有机锡催化剂,如二月桂酸二丁基锡、辛酸亚锡或者乙酰丙酮二丁基锡,也可以选用有机胺类催化剂,如三亚乙基二胺、N、N`-二甲基环已胺或者三乙基胺等,当然也可以是有机锡催化剂和有机胺催化剂的混合物。
其制备与使用方法为,将A组分、B组分中各成分分别在常温下混配均匀,分别密封保存,使用时把两组分按A∶B=1∶1-3混合,搅拌均匀,倒入充油电讯电缆接头的透明封闭套管中,固化后,即完成操作工作。
本发明灌充密封物为反应型双组分高分子弹性体灌封材料,具有优良的电绝缘性能,在工作环境下有稳定手化学性能,高度的透明性,良好的柔韧性,能有效地防止水、潮气及各种有害物质对线路的侵蚀,对人无毒、无害、无刺激性,更重要的是成本低廉、原材料国产化,施工简便。
下面引用实用例叙述如下,
实施例1
选用下列成分及其重量百分比分别制成A组分和B组分:
A组分:
甲苯二异氰酸酯 35%
邻苯二甲酸二辛酯 60%
花生油 5%
B组分:
聚丙醚二醇(分子量2000) 0%
蓖麻油 39.9%
邻苯二甲酸二辛酯 60%
二月桂酸二丁基锡 0.1%
其制备与使用方法为,将A组分、B组分中各成分分别在常温下混配均匀,分别密封保存,使用时把两组分按A∶B=1∶1混合,搅拌均匀,倒入充油电讯电缆接头的透明封闭套管中,固化后,即完成操作工作。
实施例2
选用下列成分及其重量百分比分别制成A组分和B组分:
A组分:
4、4`-二苯基甲烷二异氰酸酯 3%
邻苯二甲酸二辛酯 37%
豆油 60%
B组分:
聚丙醚二醇(分子量1000) 43%
蓖麻油 50%
邻苯二甲酸二辛酯 5%
辛酸亚锡 2%
其制备与使用方法为,将A组分、B组分中各成分分别在常温下混配均匀,分别密封保存,使用时把两组分按A∶B=1∶2混合,搅拌均匀,倒入充油电讯电缆接头的透明封闭套管中,固化后,即完成操作工作。
实施例3
选用下列成分及其重量百分比分别制成A组分和B组分:
A组分:
萘二异氰酸酯 40%
邻苯二甲酸二辛酯 5%
菜籽油 55%
B组分:
聚丙醚二醇(分子量3000) 50%
蓖麻油 5%
邻苯二甲酸二辛酯 40%
N、N`-二甲基环乙胺 5%
其制备与使用方法为,将A组分、B组分中各成分分别在常温下混配均匀,分别密封保存,使用时把两组分按A∶B=1∶3混合,搅拌均匀,倒入充油电讯电缆接头的透明封闭套管中,固化后,即完成操作工作。
Claims (7)
1、一种保护通讯电缆接头的灌充密封物,其特征在于它是选用下列成分及其重量百分比分别制成A组分和B组分。
A组分:
异氰酸酯 3-40%
邻苯二甲酸二辛酯 5-60%
植物油 5-60%
B组分:
聚丙醚二醇 0-50%
蓖麻油 5-50%
邻苯二甲酸二辛酯 5-60%
催化剂 0.1-5%
然后把A组分与B组分按1∶1-3混合。
2、如权利要求1所述的一种保护通讯电缆接头的灌充密封物,其特征在于异氰酸酯可以是甲苯二异氰酸酯、液态的4、4`二苯基甲烷二异氰酸酯或者萘二异氰酸酯。
3、如权利要求1所述的一种保护通讯电缆接头的灌充密封物,其特征在于植物油可选用花生油、豆油或菜籽油。
4、如权利要求1所述的一种保护通讯电缆接头的灌充密封物,其特征在于催化剂可以选用有机锡催化剂,也可以选用有机胺类催化剂。
5、如权利要求4所述的一种保护通讯电缆接头的灌充密封物,其特征在于有机锡催化剂可以是二月桂酸二丁基锡、辛酸亚锡或者丁氧二丁基锡。
6、如权利要求4所述的一种保护通讯电缆接头的灌充密封物,其特征在于有机胺类催化剂可以是三亚乙基二胺、N、N-二甲基环已胺或者三乙基胺。
7、如权利要求1所述的一种保护通讯电缆接头的灌充密封物,其特征在于催化剂是有机锡催化剂和有机胺催化剂的混合物。