CN112663343A - Pearl graphene fiber and production method thereof - Google Patents
Pearl graphene fiber and production method thereof Download PDFInfo
- Publication number
- CN112663343A CN112663343A CN202011585458.XA CN202011585458A CN112663343A CN 112663343 A CN112663343 A CN 112663343A CN 202011585458 A CN202011585458 A CN 202011585458A CN 112663343 A CN112663343 A CN 112663343A
- Authority
- CN
- China
- Prior art keywords
- polyester fiber
- fiber fabric
- pearl
- acrylic resin
- graphene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a pearl graphene fiber and a production method thereof, which are characterized by comprising the following steps: s1: the polyester fiber fabric is woven into the polyester fiber fabric by spinning the polyester fiber fabric, the polyester fiber fabric is soaked, the cleaning agent is added into the soaking water, and then the polyester fiber fabric is fully stirred and mixed, so that the fabric is fully soaked by the liquid material added with the cleaning agent. The acrylic resin with the advantages of good light and color retention, water and chemical resistance, fast drying, convenient construction and the like can stably fix the pearl layered graphene microchip on the surface of the polyester fiber fabric, so that the polyester fiber fabric has the excellent characteristics of the pearl layered graphene microchip such as mechanical strength, electric conduction, heat conduction performance, good lubrication, high temperature resistance and corrosion resistance, the effect of conveniently meeting diversified market demands is achieved, and the advantages of use are more diversified.
Description
Technical Field
The invention relates to the technical field of graphene, in particular to a pearl graphene fiber and a production method thereof.
Background
Graphene is a two-dimensional carbon nanomaterial which is formed into a hexagonal honeycomb lattice by sp hybridized orbits through carbon atoms, has excellent optical, electrical and mechanical properties, has important application prospects in the aspects of materials science, micro-nano processing, energy, biomedicine, drug delivery and the like, and is considered to be a future revolutionary material; the pearl graphene is a graphene microchip with a pearl layered structure, the original planar carbon six-membered ring conjugated crystal structure of graphite is maintained, the pearl graphene microchip has excellent mechanical strength, electric conduction and heat conduction properties and good lubricating, high temperature resistant and corrosion resistant properties, and compared with common graphite, the thickness of the graphene microchip is in a nanoscale range, but the radial width of the graphene microchip can reach several to tens of microns, and the graphene microchip has an oversized shape ratio.
The graphene fiber fabric in the current market is difficult to fix the pearl-layered graphene microchip on the surface of the fiber fabric, so that the surface of the graphene fiber fabric is difficult to have the advantages of excellent mechanical strength, electric conductivity, heat conductivity, good lubricating, high temperature resistant and corrosion resistant properties and the like of the pearl-layered graphene microchip, and the application of the pearl-layered graphene fiber fabric is difficult to meet the market demand which is gradually promoted.
Disclosure of Invention
The invention aims to solve the defects in the prior art and provides a pearl graphene fiber and a production method thereof.
A pearl graphene fiber and a production method thereof comprise the following steps:
s1: the method comprises the steps of spinning polyester fibers into polyester fiber fabrics by spinning the polyester fibers, soaking the polyester fiber fabrics, adding a cleaning agent into soaking water, and fully stirring and mixing the polyester fiber fabrics to fully soak the fabrics by adding liquid materials of the cleaning agent;
s2: taking out the polyester fiber fabric soaked in the step S1, washing the polyester fiber fabric soaked in the cleaning agent liquid material, and washing the polyester fiber fabric by washing equipment;
s3: taking out the polyester fiber fabric cleaned by the washing equipment in the step S2, drying the wet polyester fiber fabric, and drying the polyester fiber fabric by using drying equipment;
s4: putting the pearl-layered graphene microchip into melted acrylic resin, continuously heating the acrylic resin, sensing the temperature of the acrylic resin through a temperature sensor, transmitting an electric signal to a processor unit, processing and calculating the electric signal through the processor, controlling a heating device according to the temperature to maintain the temperature of the acrylic resin in a melted state, stirring the acrylic resin through a stirring device, and uniformly stirring the pearl-layered graphene microchip put into the stirring device;
s5, paving the polyester fiber fabric dried in the step S3 on a clean working table, and spraying the acrylic resin stirred into the pearl-layered graphene micro-sheets through spraying equipment, so that the acrylic resin added with the pearl-layered graphene micro-sheets is uniformly sprayed on the surface of the polyester fiber fabric.
Preferably, in the step S1, the soaking of the polyester fiber fabric requires that all the polyester fiber fabric be soaked in the liquid material added with the cleaning agent, so that all the polyester fiber fabric is fully soaked.
Preferably, in step S3, the polyester fiber fabric is dried and then placed in a dust-free storage device or a dust-free workshop for pre-storage, and the storage space needs to be subjected to moisture-proof drying treatment to ensure cleanness and dryness of the polyester fiber fabric after drying and before spraying.
The invention provides a pearl graphene fiber and a production method thereof, which comprises the steps of putting pearl-layered graphene micro-sheets into melted acrylic resin, stirring the mixture by stirring equipment, fully and uniformly mixing the pearl-layered graphene micro-sheets into the melted acrylic resin, spraying the acrylic resin melted into the pearl-layered graphene micro-sheets on the surface of a polyester fiber fabric after cleaning and drying by spraying equipment, so that the pearl-layered graphene micro-sheets can be stably fixed on the surface of the polyester fiber fabric by the acrylic resin with the advantages of good light and color retention, water and chemical resistance, fast drying, convenient construction and the like, and the polyester fiber fabric has the excellent characteristics of the pearl-layered graphene micro-sheets such as mechanical strength, electric conduction, heat conduction performance, good lubrication, high temperature resistance, corrosion resistance and the like, the effect of being convenient for satisfy diversified market demand has been reached, and the advantage of using is more various.
Detailed Description
The present invention will be further illustrated with reference to the following specific examples.
The invention provides a pearl graphene fiber and a production method thereof, and the pearl graphene fiber comprises the following steps:
s1: the method comprises the steps of spinning polyester fibers into polyester fiber fabrics by spinning the polyester fibers, soaking the polyester fiber fabrics, adding a cleaning agent into soaking water, and fully stirring and mixing the polyester fiber fabrics to fully soak the fabrics by adding liquid materials of the cleaning agent;
s2: taking out the polyester fiber fabric soaked in the step S1, washing the polyester fiber fabric soaked in the cleaning agent liquid material, and washing the polyester fiber fabric by washing equipment;
s3: taking out the polyester fiber fabric cleaned by the washing equipment in the step S2, drying the wet polyester fiber fabric, and drying the polyester fiber fabric by using drying equipment;
s4: putting the pearl-layered graphene microchip into melted acrylic resin, continuously heating the acrylic resin, sensing the temperature of the acrylic resin through a temperature sensor, transmitting an electric signal to a processor unit, processing and calculating the electric signal through the processor, controlling a heating device according to the temperature to maintain the temperature of the acrylic resin in a melted state, stirring the acrylic resin through a stirring device, and uniformly stirring the pearl-layered graphene microchip put into the stirring device;
s5, paving the polyester fiber fabric dried in the step S3 on a clean working table, and spraying the acrylic resin stirred into the pearl-layered graphene micro-sheets through spraying equipment, so that the acrylic resin added with the pearl-layered graphene micro-sheets is uniformly sprayed on the surface of the polyester fiber fabric.
In the step S1, the soaking of the polyester fiber fabric requires that all the polyester fiber fabric be soaked in the liquid material added with the cleaning agent, so that all the polyester fiber fabric is fully soaked.
In step S3, the polyester fiber fabric is dried and then placed in a dust-free storage device or a dust-free workshop for pre-storage, and the storage space needs to be subjected to moisture-proof drying treatment to ensure cleanness and dryness of the polyester fiber fabric after drying and before spraying.
The invention provides a pearl graphene fiber and a production method thereof, which comprises the steps of putting pearl-layered graphene micro-sheets into melted acrylic resin, stirring the mixture by stirring equipment, fully and uniformly mixing the pearl-layered graphene micro-sheets into the melted acrylic resin, spraying the acrylic resin melted into the pearl-layered graphene micro-sheets on the surface of a polyester fiber fabric after cleaning and drying by spraying equipment, so that the pearl-layered graphene micro-sheets can be stably fixed on the surface of the polyester fiber fabric by the acrylic resin with the advantages of good light and color retention, water and chemical resistance, fast drying, convenient construction and the like, and the polyester fiber fabric has the excellent characteristics of the pearl-layered graphene micro-sheets such as mechanical strength, electric conduction, heat conduction performance, good lubrication, high temperature resistance, corrosion resistance and the like, the effect of being convenient for satisfy diversified market demand has been reached, and the advantage of using is more various.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.
Claims (3)
1. The pearl graphene fiber and the production method thereof are characterized by comprising the following steps:
s1: the method comprises the steps of spinning polyester fibers into polyester fiber fabrics by spinning the polyester fibers, soaking the polyester fiber fabrics, adding a cleaning agent into soaking water, and fully stirring and mixing the polyester fiber fabrics to fully soak the fabrics by adding liquid materials of the cleaning agent;
s2: taking out the polyester fiber fabric soaked in the step S1, washing the polyester fiber fabric soaked in the cleaning agent liquid material, and washing the polyester fiber fabric by washing equipment;
s3: taking out the polyester fiber fabric cleaned by the washing equipment in the step S2, drying the wet polyester fiber fabric, and drying the polyester fiber fabric by using drying equipment;
s4: putting the pearl-layered graphene microchip into melted acrylic resin, continuously heating the acrylic resin, sensing the temperature of the acrylic resin through a temperature sensor, transmitting an electric signal to a processor unit, processing and calculating the electric signal through the processor, controlling a heating device according to the temperature to maintain the temperature of the acrylic resin in a melted state, stirring the acrylic resin through a stirring device, and uniformly stirring the pearl-layered graphene microchip put into the stirring device;
s5, paving the polyester fiber fabric dried in the step S3 on a clean working table, and spraying the acrylic resin stirred into the pearl-layered graphene micro-sheets through spraying equipment, so that the acrylic resin added with the pearl-layered graphene micro-sheets is uniformly sprayed on the surface of the polyester fiber fabric.
2. The pearl graphene fiber and the production method thereof according to claim 1, wherein the soaking of the polyester fiber fabric in the step S1 requires that all the polyester fiber fabric is soaked in the liquid material added with the cleaning agent, so that all the polyester fiber fabric is fully soaked.
3. The pearl graphene fiber and the production method thereof according to claim 1, wherein the polyester fiber fabric is dried in step S3 and then is stored in a dust-free storage device or a dust-free workshop for pre-storage, and the storage space is subjected to moisture-proof drying treatment to ensure cleanliness and dryness of the polyester fiber fabric after drying and before spraying.