CN112646460A - Roller coating hand-feeling gloss oil - Google Patents
Roller coating hand-feeling gloss oil Download PDFInfo
- Publication number
- CN112646460A CN112646460A CN202011513526.1A CN202011513526A CN112646460A CN 112646460 A CN112646460 A CN 112646460A CN 202011513526 A CN202011513526 A CN 202011513526A CN 112646460 A CN112646460 A CN 112646460A
- Authority
- CN
- China
- Prior art keywords
- parts
- gloss oil
- resin
- weight
- roller coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to roller coating hand feeling gloss oil which comprises the following components in parts by weight: 45-70 parts of resin, 2-10 parts of auxiliary agent, 6-20 parts of filler and 12-30 parts of thinner. Compared with the prior art, the roller-coating hand-feeling gloss oil can be continuously produced by roller coating, has excellent stability, high efficiency, labor cost saving and fluffy touch.
Description
Technical Field
The invention belongs to the technical field of gloss oil, and particularly relates to roll-coating hand-feeling gloss oil.
Background
The gloss oil is coated on the surface of an object, a solid layer which is firm in adhesion, has certain strength and is continuous is formed after drying, the gloss oil is shiny after film forming, the original pattern of the object surface can be displayed, the performances such as hardness and wear resistance are superior, the protective effect can be well played, and the gloss oil is widely applied to coating of furniture, doors and windows, automobiles and the like.
The hand feeling gloss oil is developed by adopting various special functional materials, and after the hand feeling gloss oil is coated on the surface of an object, the coated object has the oily hand feeling of cotton smoothness, silk, moisture, velvet and the like, the product grade is greatly improved, and the user experience feeling is good. With the improvement of cultural living standard and appreciation level of people, people are pursuing products with good touch feeling. At present, the hand-feeling gloss oil on the market is mainly used for coating the surface of an object in a spraying mode, and the operation mode has low efficiency and low utilization rate. The hand-feeling gloss oil is mainly developed, can be continuously roll-coated on a coiled material for production, and has soft and fluffy hand feeling.
Disclosure of Invention
In order to achieve the purpose, the invention provides the roller coating gloss oil which not only can achieve good texture and has fluffy touch, but also can be continuously coated, thereby improving the production efficiency and saving the labor cost.
The invention is realized by the following technical scheme:
a roller coating gloss oil comprises the following components in parts by weight:
45-70 parts of resin, 2-10 parts of auxiliary agent, 6-20 parts of filler and 12-30 parts of thinner.
Wherein, the resin comprises 14 to 30 parts by weight of 3873 polyester resin, 20 to 48 parts by weight of RP7552 resin and 2 to 10 parts by weight of 303 to 98 resin.
Further, the auxiliary agent comprises, by weight, 0.5-1.5 parts of ADT-1 adhesion promoter, 0.5-1.5 parts of BCR 9807 promoter, 0.1-0.5 part of constant AC300 defoaming agent, 0.1-0.5 part of DD0825 catalyst, 1-2 parts of BYK ATP dilution auxiliary agent and 1-3 parts of Tech-2080 organic silicon leveling agent. And adjusting the content of the ATP dilution auxiliary agent of BYK and the content of the Tech-2080 organosilicon leveling agent to adjust the hand feeling of the paint film.
Further, the filler is M7 organic matting powder, and the addition of M7 organic matting powder can make the paint film achieve a fluffy touch.
Furthermore, the roller coating hand gloss oil comprises the following components in parts by weight:
3873 parts of polyester resin 22.38 parts;
34.09 parts of RP7552 resin;
303-98 parts of resin 5.76;
1.04 parts of ADT-1 adhesion promoter;
1.04 parts of a BCR 9807 accelerator;
0.31 part of constant AC300 defoaming agent;
0.31 part of DD0825 catalyst;
1.25 parts of ATP (adenosine triphosphate) dilution auxiliary agent of BYK;
1.56 parts of Tech-2080 organosilicon leveling agent;
13.53 parts of M7 organic matting powder;
and 18.73 parts of thinner.
Compared with the prior art, the invention has the following beneficial effects:
the roller coating hand feeling gloss oil can enable a paint film to meet the performance requirement of continuous coating through the mutual matching of the resin, the accelerator, the defoamer and the DD0825 catalyst, can be used for continuous roller coating production, has excellent stability, improves the production efficiency and saves the labor cost. The ATP dilution auxiliary agent of BYK and the Tech-2080 organic silicon flatting agent provide the hand feeling of a paint film, and the M7 organic matting powder can enable the paint film to achieve a fluffy touch feeling.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention clearer and clearer, the present invention is further described in detail by referring to the following embodiments. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention.
Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs, and the terms used herein in the specification of the present invention are for the purpose of describing particular embodiments only and are not intended to limit the present invention.
The roll-coating gloss oil provided by the embodiment of the invention can be used for continuous roll coating of a coiled material, is good in stability and can realize fluffy touch.
Example 1
A roll-coating hand gloss oil comprises the following components in parts by weight:
3873 parts of polyester resin;
40.32 parts of RP7552 resin;
303-98 parts of resin 3.5;
0.56 part of ADT-1 adhesion promoter;
0.56 part of BCR 9807 promoter;
0.1 part of constant AC300 defoaming agent;
0.1 part of DD0825 catalyst;
1 part of ATP (adenosine triphosphate) dilution auxiliary agent of BYK;
1.16 parts of Tech-2080 organosilicon leveling agent;
7 parts of M7 organic matting powder;
and 12 parts of a thinner.
Example 2
A roller coating gloss oil comprises the following components in parts by weight:
3873 parts of polyester resin 22.38 parts;
34.09 parts of RP7552 resin;
303-98 parts of resin 5.76;
1.04 parts of ADT-1 adhesion promoter;
1.04 parts of a BCR 9807 accelerator;
0.31 part of constant AC300 defoaming agent;
0.31 part of DD0825 catalyst;
1.25 parts of ATP (adenosine triphosphate) dilution auxiliary agent of BYK;
1.56 parts of Tech-2080 organosilicon leveling agent;
13.53 parts of M7 organic matting powder;
and 18.73 parts of thinner.
Example 3
A roller coating gloss oil comprises the following components in parts by weight:
3873 parts of polyester resin;
46 parts of RP7552 resin;
8.26 parts of 303-98 parts of resin;
1.44 parts of ADT-1 adhesion promoter;
1.04 parts of a BCR 9807 accelerator;
0.5 part of constant AC300 defoaming agent;
0.45 part of DD0825 catalyst;
1.8 parts of an ATP (adenosine triphosphate) dilution auxiliary agent of BYK;
2.06 parts of Tech-2080 organosilicon leveling agent;
18.53 parts of M7 organic matting powder;
and 25 parts of a thinner.
The roller-coating hand gloss oil obtained in the above examples was tested for adhesion, hardness, MEK rub resistance, impact resistance, T-bend resistance, etc., and the results were MEK: greater than 100 cycles; t bending: less than 1T; hardness: the nail has no obvious mark; boiling in water: 2 hours, no abnormity exists; adhesion force: level 0; impact: 5J is qualified, meets the production requirements, and particularly has the best hand feeling gloss oil performance and hand feeling in the embodiment 2.
The roller-coating hand-feeling gloss oil provided by the invention solves the problems of low efficiency, high energy consumption, high cost and the like of the traditional spraying, and has better touch feeling and fluffy touch feeling compared with the traditional gloss oil.
It is to be understood that the invention is not limited to the examples described above, but that modifications and variations may be effected thereto by those of ordinary skill in the art in light of the foregoing description, and that all such modifications and variations are intended to be within the scope of the invention as defined by the appended claims.
Claims (5)
1. The roll-coating gloss oil is characterized by comprising the following components in parts by weight:
45-70 parts of resin, 2-10 parts of auxiliary agent, 6-20 parts of filler and 12-30 parts of thinner.
2. The roller coating hand varnish according to claim 1, wherein the resin comprises 14-30 parts by weight of 3873 polyester resin, 20-48 parts by weight of RP7552 resin and 2-10 parts by weight of 303-98 resin.
3. The roller coating hand gloss oil as defined in claim 1, wherein the auxiliary agent comprises, by weight, 0.5-1.5 parts of ADT-1 adhesion promoter, 0.5-1.5 parts of BCR 9807 promoter, 0.1-0.5 parts of constant AC300 defoamer, 0.1-0.5 parts of DD0825 catalyst, 1-2 parts of BYK ATP dilution auxiliary agent, and 1-3 parts of Tech-2080 organosilicon leveling agent.
4. The roller-coating hand gloss oil as claimed in claim 1, wherein the filler is M7 organic matting powder, and the addition of M7 organic matting powder can make the paint film achieve a fluffy touch.
5. The roller coating gloss oil according to claim 1, which is characterized by comprising the following components in parts by weight:
3873 parts of polyester resin 22.38 parts;
34.09 parts of RP7552 resin;
303-98 parts of resin 5.76;
1.04 parts of ADT-1 adhesion promoter;
1.04 parts of a BCR 9807 accelerator;
0.31 part of constant AC300 defoaming agent;
0.31 part of DD0825 catalyst;
1.25 parts of ATP (adenosine triphosphate) dilution auxiliary agent of BYK;
1.56 parts of Tech-2080 organosilicon leveling agent;
13.53 parts of M7 organic matting powder;
and 18.73 parts of thinner.