CN112646404A - Antibacterial pigment and preparation method thereof - Google Patents
Antibacterial pigment and preparation method thereof Download PDFInfo
- Publication number
- CN112646404A CN112646404A CN202011588405.3A CN202011588405A CN112646404A CN 112646404 A CN112646404 A CN 112646404A CN 202011588405 A CN202011588405 A CN 202011588405A CN 112646404 A CN112646404 A CN 112646404A
- Authority
- CN
- China
- Prior art keywords
- parts
- toner
- pigment
- bacteriostatic
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antibacterial pigment which is prepared from the following raw materials: refined sunflower seed oil, tea saponin, toner, starch ether, silicone oil, aluminum stearate, monoglyceride, carrageenan, barium sulfate, titanium zinc white, chitosan modified talcum powder, potassium sorbate, propylene glycol, sodium dodecyl benzene sulfonate, tetradecanol oleate and isothiazolinone; the cost is low, the alkali resistance is good, and the sterilization and bacteriostasis are realized, and the bacteriostasis rate to staphylococcus aureus, escherichia coli and the like is 96% according to GB1741-79 (89) detection; the paint is non-toxic, harmless, excellent in wear resistance, not easy to yellow, not easy to crack and easy to clean, and the water resistance is detected to be 4-5 grade according to GB/T5211.5-85; the paint is simple, safe and environment-friendly, has no harm to human body, and has good dispersibility, film forming property, heat resistance, steam resistance and weather resistance, and fine quality; the color is bright, the coating can be widely used in various extreme environments, is resistant to light, is dried for 5min and is dried for 2h, and the coating can be widely produced and continuously replaces the existing materials.
Description
Technical Field
The invention relates to the technical field of pigments, in particular to an antibacterial pigment and a preparation method thereof.
Background
Pigment means a substance that can color an object. Pigments are distinguished by being soluble and insoluble, inorganic and organic. Inorganic pigments are generally mineral substances, and it has long been known to use inorganic pigments to draw and paint the body on the rock wall by using colored soils and ores. The organic pigment is generally extracted from plants and marine animals, such as alizarin, gamboge and ancient Rome, to obtain purple color from shellfish.
The pigment is divided into an inorganic pigment and an organic pigment, the organic pigment is prepared by extracting pigment from plants, does not contain elements harmful to human bodies, belongs to an environment-friendly pigment, and is mainly applied to the industries of paint, printing ink, printing and dyeing, plastic products, papermaking, rubber products, ceramics and the like.
Pigments (pigments) are used for coloring powdery substances. The natural pigment is insoluble in media such as refined sunflower seed oil, grease, resin, organic solvent and the like, but can be uniformly dispersed in the media, can color the media and has certain covering power. The art pigment basically requires that the finer the particles, the brighter the color, and the longer the color, the better the color will not change (the better the stability). Refined sunflower seed oil color pigment is almost transparent except for white. Thus, the requirement of color-cover dyeing of refined sunflower seed oil can be met.
The oil painting (a painting in oils) is a kind of painting made on canvas linen, cardboard or wood board by blending pigments with quick-drying vegetable oil (linseed oil, poppy oil, walnut oil, etc.). The diluent used in drawing is volatile turpentine oil, dry linseed oil, etc. The paint attached to the picture has strong hardness, and can keep luster for a long time after the picture is dried. The painting object is fully expressed by virtue of the covering power and the transparency of the pigment, and the painting object is rich in color and strong in three-dimensional texture. The oil painting is one of the main painting types of western painting.
Disclosure of Invention
The invention provides an antibacterial pigment with alkali resistance, easy cleaning, good film-forming property, water resistance, dispersibility, heat resistance and weather resistance and a preparation method thereof, and solves the technical problems of poor hiding power, poor gloss and the like of the existing pigment.
The invention adopts the following technical scheme: the antibacterial pigment comprises the following raw materials in parts by weight: 100 parts of refined sunflower seed oil, 1-3 parts of tea saponin, 6-10 parts of toner, 10-20 parts of starch ether, 4-8 parts of silicone oil, 0.4-0.8 part of aluminum stearate, 1-3 parts of monoglyceride, 6-10 parts of carrageenan, 0.2-1 part of isothiazolinone, 4-8 parts of barium sulfate, 0.5-4.5 parts of titanium zinc white, 10-20 parts of chitosan modified talcum powder, 1-5 parts of potassium sorbate, 1-2 parts of propylene glycol, 5-15 parts of sodium dodecyl benzene sulfonate and 6-10 parts of tetradecanol oleate.
As a preferred technical scheme of the invention: the toner is inorganic toner and/or organic toner.
As a preferred technical scheme of the invention: the inorganic toner is iron oxide yellow and/or iron oxide red.
As a preferred technical scheme of the invention: the organic toner is one or more of phthalocyanine green, phthalocyanine blue, ultramarine and sun-proof yellow G.
As a preferred technical scheme of the invention: the antibacterial pigment comprises the following raw materials in parts by weight: 100 parts of refined sunflower seed oil, 1 part of tea saponin, 6 parts of toner, 10 parts of starch ether, 4 parts of silicone oil, 0.4 part of aluminum stearate, 1 part of monoglyceride, 6 parts of carrageenan, 0.2 part of isothiazolinone, 4 parts of barium sulfate, 0.5 part of titanium zinc white, 10 parts of chitosan modified talcum powder, 1 part of potassium sorbate, 1 part of propylene glycol, 5 parts of sodium dodecyl benzene sulfonate and 6 parts of tetradecanol oleate.
As a preferred technical scheme of the invention: the antibacterial pigment comprises the following raw materials in parts by weight: 100 parts of refined sunflower seed oil, 3 parts of tea saponin, 10 parts of toner, 20 parts of starch ether, 8 parts of silicone oil, 0.8 part of aluminum stearate, 3 parts of monoglyceride, 10 parts of carrageenan, 1 part of isothiazolinone, 8 parts of barium sulfate, 4.5 parts of titanium zinc white, 20 parts of chitosan modified talcum powder, 5 parts of potassium sorbate, 2 parts of propylene glycol, 15 parts of sodium dodecyl benzene sulfonate and 10 parts of tetradecanol oleate.
As a preferred technical scheme of the invention: the antibacterial pigment comprises the following raw materials in parts by weight: 100 parts of refined sunflower seed oil, 2 parts of tea saponin, 8 parts of toner, 15 parts of starch ether, 6 parts of silicone oil, 0.6 part of aluminum stearate, 2 parts of monoglyceride, 8 parts of carrageenan, 0.6 part of isothiazolinone, 6 parts of barium sulfate, 2.5 parts of titanium zinc white, 15 parts of chitosan modified talcum powder, 3 parts of potassium sorbate, 1.5 parts of propylene glycol, 10 parts of sodium dodecyl benzene sulfonate and 8 parts of tetradecanol oleate.
A method for preparing the antibacterial pigment comprises the following steps:
the first step is as follows: weighing refined sunflower seed oil, tea saponin, toner, starch ether, silicone oil, aluminum stearate, monoglyceride, carrageenan, barium sulfate, titanium zinc white, chitosan modified talcum powder, potassium sorbate, propylene glycol, sodium dodecyl benzene sulfonate, tetradecanol oleate and isothiazolinone according to the mass part ratio;
the second step is that: putting aluminum stearate, barium sulfate, titanium zinc white and chitosan modified talcum powder into a grinding machine, grinding for 3-5min at the grinding speed of 1000r/min, adding the rest raw materials, mixing for 40-60min in a mixer at the mixing temperature of 60-80 ℃, and uniformly mixing;
the third step: and (3) adjusting the pH of the uniformly mixed raw materials to 6.5-7.5, grinding to 30 mu m, press-filtering, drying and packaging to obtain the antibacterial pigment.
Advantageous effects
Compared with the prior art, the antibacterial pigment and the preparation method thereof have the following technical effects: 1. the cost is low, the alkali resistance is good, and the sterilization and bacteriostasis are realized, and the bacteriostasis rate to staphylococcus aureus, escherichia coli and the like is 92-96% according to GB1741-79 (89) detection; 2. the paint is non-toxic, harmless, excellent in wear resistance, not easy to yellow, not easy to crack and easy to clean, and the water resistance is detected to be 4-5 grade according to GB/T5211.5-85; 3. the paint is simple, safe and environment-friendly, has no harm to human body, and has good dispersibility, film forming property, heat resistance, steam resistance and weather resistance, and fine quality; 4. the color is bright, the coating can be widely used in various extreme environments, is resistant to illumination, is surface-dried for 5-10min and is dried for 2-6h, and the coating can be widely produced and continuously replaces the existing materials.
Detailed Description
The present invention is further described with reference to the following examples, which are intended to be illustrative only and not to be limiting of the scope of the claims, and other alternatives which may occur to those skilled in the art are within the scope of the claims.
Example 1:
the preparation method of the bacteriostatic pigment comprises the following steps:
the first step is as follows: weighing 100 parts of refined sunflower seed oil, 1 part of tea saponin, 6 parts of fast yellow G, 10 parts of starch ether, 4 parts of silicone oil, 0.4 part of aluminum stearate, 1 part of monoglyceride, 6 parts of carrageenan, 0.2 part of isothiazolinone, 4 parts of barium sulfate, 0.5 part of titanium zinc white, 10 parts of chitosan modified talcum powder, 1 part of potassium sorbate, 1 part of propylene glycol, 5 parts of sodium dodecyl benzene sulfonate and 6 parts of tetradecanol oleate according to the mass part ratio.
The second step is that: putting aluminum stearate, barium sulfate, titanium zinc white and chitosan modified talcum powder into a grinding machine, grinding for 3-5min at the grinding speed of 1000r/min, adding the rest raw materials, mixing for 40-60min in a mixer at the mixing temperature of 60-80 ℃, and uniformly mixing;
the third step: and (3) adjusting the pH of the uniformly mixed raw materials to 6.5-7.5, grinding to 30 mu m, press-filtering, drying and packaging to obtain the antibacterial pigment.
Example 2:
the preparation method of the bacteriostatic pigment comprises the following steps:
the first step is as follows: weighing 100 parts of refined sunflower seed oil, 3 parts of tea saponin, 10 parts of phthalocyanine blue, 20 parts of starch ether, 8 parts of silicone oil, 0.8 part of aluminum stearate, 3 parts of monoglyceride, 10 parts of carrageenan, 1 part of isothiazolinone, 8 parts of barium sulfate, 4.5 parts of titanium zinc white, 20 parts of chitosan modified talcum powder, 5 parts of potassium sorbate, 2 parts of propylene glycol, 15 parts of sodium dodecyl benzene sulfonate and 10 parts of tetradecanol oleate according to the mass part ratio.
The second step is that: putting aluminum stearate, barium sulfate, titanium zinc white and chitosan modified talcum powder into a grinding machine, grinding for 3-5min at the grinding speed of 1000r/min, adding the rest raw materials, mixing for 40-60min in a mixer at the mixing temperature of 60-80 ℃, and uniformly mixing;
the third step: and (3) adjusting the pH of the uniformly mixed raw materials to 6.5-7.5, grinding to 30 mu m, press-filtering, drying and packaging to obtain the antibacterial pigment.
Example 3:
the preparation method of the bacteriostatic pigment comprises the following steps:
the first step is as follows: weighing 100 parts of refined sunflower seed oil, 2 parts of tea saponin, 8 parts of iron oxide yellow, 15 parts of starch ether, 6 parts of silicone oil, 0.6 part of aluminum stearate, 2 parts of monoglyceride, 8 parts of carrageenan, 0.6 part of isothiazolinone, 6 parts of barium sulfate, 2.5 parts of titanium zinc white, 15 parts of chitosan modified talcum powder, 3 parts of potassium sorbate, 1.5 parts of propylene glycol, 10 parts of sodium dodecyl benzene sulfonate and 8 parts of tetradecanol oleate according to the mass part ratio.
The second step is that: putting aluminum stearate, barium sulfate, titanium zinc white and chitosan modified talcum powder into a grinding machine, grinding for 3-5min at the grinding speed of 1000r/min, adding the rest raw materials, mixing for 40-60min in a mixer at the mixing temperature of 60-80 ℃, and uniformly mixing;
the third step: and (3) adjusting the pH of the uniformly mixed raw materials to 6.5-7.5, grinding to 30 mu m, press-filtering, drying and packaging to obtain the antibacterial pigment.
The cost is low, the alkali resistance is good, and the sterilization and bacteriostasis are realized, and the bacteriostasis rate to staphylococcus aureus, escherichia coli and the like is 96% according to GB1741-79 (89) detection; the paint is non-toxic, harmless, excellent in wear resistance, not easy to yellow, not easy to crack and easy to clean, and the water resistance is detected to be 4-5 grade according to GB/T5211.5-85; the paint is simple, safe and environment-friendly, has no harm to human body, and has good dispersibility, film forming property, heat resistance, steam resistance and weather resistance, and fine quality; the color is bright, the coating can be widely used in various extreme environments, is resistant to light, is dried for 5min and is dried for 2h, and the coating can be widely produced and continuously replaces the existing materials.
Claims (8)
1. The bacteriostatic pigment is characterized by comprising the following raw materials in parts by mass: 100 parts of refined sunflower seed oil, 1-3 parts of tea saponin, 6-10 parts of toner, 10-20 parts of starch ether, 4-8 parts of silicone oil, 0.4-0.8 part of aluminum stearate, 1-3 parts of monoglyceride, 6-10 parts of carrageenan, 0.2-1 part of isothiazolinone, 4-8 parts of barium sulfate, 0.5-4.5 parts of titanium zinc white, 10-20 parts of chitosan modified talcum powder, 1-5 parts of potassium sorbate, 1-2 parts of propylene glycol, 5-15 parts of sodium dodecyl benzene sulfonate and 6-10 parts of tetradecanol oleate.
2. A bacteriostatic pigment according to claim 1, characterized in that: the toner is inorganic toner and/or organic toner.
3. A bacteriostatic pigment according to claim 2, characterized in that: the inorganic toner is iron oxide yellow and/or iron oxide red.
4. A bacteriostatic pigment according to claim 2, characterized in that: the organic toner is one or more of phthalocyanine green, phthalocyanine blue, ultramarine and sun-proof yellow G.
5. A bacteriostatic pigment according to claim 1, characterized in that: the antibacterial pigment comprises the following raw materials in parts by weight: 100 parts of refined sunflower seed oil, 1 part of tea saponin, 6 parts of toner, 10 parts of starch ether, 4 parts of silicone oil, 0.4 part of aluminum stearate, 1 part of monoglyceride, 6 parts of carrageenan, 0.2 part of isothiazolinone, 4 parts of barium sulfate, 0.5 part of titanium zinc white, 10 parts of chitosan modified talcum powder, 1 part of potassium sorbate, 1 part of propylene glycol, 5 parts of sodium dodecyl benzene sulfonate and 6 parts of tetradecanol oleate.
6. A bacteriostatic pigment according to claim 1, characterized in that: the antibacterial pigment comprises the following raw materials in parts by weight: 100 parts of refined sunflower seed oil, 3 parts of tea saponin, 10 parts of toner, 20 parts of starch ether, 8 parts of silicone oil, 0.8 part of aluminum stearate, 3 parts of monoglyceride, 10 parts of carrageenan, 1 part of isothiazolinone, 8 parts of barium sulfate, 4.5 parts of titanium zinc white, 20 parts of chitosan modified talcum powder, 5 parts of potassium sorbate, 2 parts of propylene glycol, 15 parts of sodium dodecyl benzene sulfonate and 10 parts of tetradecanol oleate.
7. A bacteriostatic pigment according to claim 1, characterized in that: the antibacterial pigment comprises the following raw materials in parts by weight: 100 parts of refined sunflower seed oil, 2 parts of tea saponin, 8 parts of toner, 15 parts of starch ether, 6 parts of silicone oil, 0.6 part of aluminum stearate, 2 parts of monoglyceride, 8 parts of carrageenan, 0.6 part of isothiazolinone, 6 parts of barium sulfate, 2.5 parts of titanium zinc white, 15 parts of chitosan modified talcum powder, 3 parts of potassium sorbate, 1.5 parts of propylene glycol, 10 parts of sodium dodecyl benzene sulfonate and 8 parts of tetradecanol oleate.
8. A method of preparing a bacteriostatic pigment according to claim 1, comprising the steps of:
the first step is as follows: weighing refined sunflower seed oil, tea saponin, toner, starch ether, silicone oil, aluminum stearate, monoglyceride, carrageenan, barium sulfate, titanium zinc white, chitosan modified talcum powder, potassium sorbate, propylene glycol, sodium dodecyl benzene sulfonate, tetradecanol oleate and isothiazolinone according to the mass part ratio;
the second step is that: putting aluminum stearate, barium sulfate, titanium zinc white and chitosan modified talcum powder into a grinding machine, grinding for 3-5min at the grinding speed of 1000r/min, adding the rest raw materials, mixing for 40-60min in a mixer at the mixing temperature of 60-80 ℃, and uniformly mixing;
the third step: and (3) adjusting the pH of the uniformly mixed raw materials to 6.5-7.5, grinding to 30 mu m, press-filtering, drying and packaging to obtain the antibacterial pigment.