CN112644097A - Anti-ultraviolet, easy-drying and antibacterial environment-friendly lining cloth and production process thereof - Google Patents
Anti-ultraviolet, easy-drying and antibacterial environment-friendly lining cloth and production process thereof Download PDFInfo
- Publication number
- CN112644097A CN112644097A CN202011001415.2A CN202011001415A CN112644097A CN 112644097 A CN112644097 A CN 112644097A CN 202011001415 A CN202011001415 A CN 202011001415A CN 112644097 A CN112644097 A CN 112644097A
- Authority
- CN
- China
- Prior art keywords
- layer
- woven
- lining cloth
- ultraviolet
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-ultraviolet, easy-drying and antibacterial environment-friendly lining cloth and a production process thereof, wherein the lining cloth comprises an upper layer, a middle layer and a lower layer structure, the upper layer is a woven cloth layer, the middle layer is an adhesive layer, the lower layer is a non-woven hot-melt adhesive lining cloth layer, the woven cloth layer comprises warp yarns and weft yarns, the woven cloth layer is subjected to fabric ultraviolet-proof finishing, the adhesive layer uses TPU (thermoplastic polyurethane) glue, PU (polyurethane) glue or acrylic acid) glue as main materials, and the non-woven hot-melt adhesive lining cloth layer is a melt-blown non-woven cloth layer of PP (polypropylene) and/or ES (ethylene styrene) fibers. According to the invention, the benzotriazole ultraviolet-proof finishing agent, the dye and the ice vinegar are bathed together at room temperature to treat the woven fabric layer in the lining cloth, so that the ultraviolet resistance and the washing fastness of the clothes are effectively improved, the clothes can keep long-term ultraviolet resistance, and the skin of a human body is protected.
Description
Technical Field
The invention relates to the technical field of lining cloth, in particular to an anti-ultraviolet, easy-drying and antibacterial environment-friendly lining cloth and a production process thereof.
Background
If the house is built, reinforced cement is needed to be used as a framework; the lining cloth is used as a framework for making clothes. The clothes can form beautiful styles of shapes and colors by the modeling, reinforcing and shape-preserving functions of the lining cloth. The lining cloth is a special clothing accessory which is used for the inner layer of clothing to play the roles of reinforcement, stiffness, smoothness and the like and is bonded (or not bonded) with the fabric, wherein woven fabrics, knitted fabrics and non-woven fabrics are used as base cloth, a thermoplastic high molecular compound is (or is not) adopted, and special finishing processing is carried out by special machinery. In short, the lining cloth is actually the outer fabric and the inner lining of a piece of clothes, and the lining cloth is arranged in the middle, so the lining cloth cannot be directly seen in general conditions, but the lining cloth is covered at the position where the lining cloth needs to be formed to be stiff, full in hand feeling, smooth in transition and reinforced. The materials of the garment need to be considered aesthetically pleasing, durable, and for other functions, such as uv resistance, antimicrobial, quick drying, the addition of these functions greatly enhances the comfort of the garment, increasing the durability of the garment in use.
Therefore, the invention provides the anti-ultraviolet easy-drying antibacterial environment-friendly lining cloth and the production process thereof.
Disclosure of Invention
The invention aims to: in order to solve the problems, the anti-ultraviolet easy-drying antibacterial environment-friendly lining cloth and the production process thereof are provided.
In order to achieve the purpose, the invention adopts the following technical scheme:
the utility model provides an antibiotic environmental protection lining cloth is easily done to ultraviolet resistance and production technology thereof, includes, the lining cloth includes upper strata, middle level and understructure, the upper strata is woven the cloth layer, the middle level is the adhesive linkage, non-woven hot melt bonding lining cloth layer of lower floor, woven the cloth layer including warp and woof, woven the cloth layer through the fabric ultraviolet protection arrangement, TPU glue, PU glue or acrylic acid colloid are used to the adhesive linkage main material, non-woven hot melt bonding lining cloth layer is the fibrous melt-blown non-woven fabrics layer of PP and/or ES, non-woven hot melt bonding lining cloth layer two sides has the line of rectangle or rhombus, the line is the shallow slot that the hot pressing formed, and the inside of shallow slot has nanometer silver ion antibiotic master batch and active carbon particle, nanometer silver ion antibiotic master batch surface has the rubber coating protective layer.
As a further description of the above technical solution:
the active carbon particles are positioned between the non-woven hot-melt adhesive lining layer and the bonding layer, and the nano silver ion antibacterial master batch is positioned between the non-woven hot-melt adhesive lining layer and the clothing fabric layer.
As a further description of the above technical solution:
the glue coating protective layer can be coated on a shallow groove in a glue dispensing mode or coated on a non-woven hot-melt adhesive lining layer in a full coating mode.
As a further description of the above technical solution:
the warp yarns of the woven fabric layer are subjected to water repellent finishing, and the weft yarns of the woven fabric layer are subjected to hydrophilic finishing.
As a further description of the above technical solution:
the woven fabric layer is treated by fabric ultraviolet-proof finishing and is subjected to dyeing bath, and the woven fabric layer is treated by the fabric ultraviolet-proof finishing steps:
s1; when dyeing is started, carrying out one-bath on the benzotriazole ultraviolet-proof finishing agent, the dye and the glacial vinegar at room temperature, adding the base cloth, heating to 80 ℃ at the speed of 1 ℃/min, then heating to 120 ℃ at the speed of 1.5 ℃/min, dyeing, keeping the temperature for 65min, and then cooling to 80 ℃ at the speed of 1 ℃/min;
s2: drying at 130 ℃;
s3: acid reduction cleaning and saponification are adopted;
s4; performing centrifugal dehydration in a physical mode to spin dry the cloth;
s5: and (3) tentering and shaping, namely tentering and shaping in a shaping machine at the temperature of 110-140 ℃.
As a further description of the above technical solution:
the water repellent finishing steps of the warp are as follows: the water-repellent auxiliary agent accounting for 10-15% of the weight of the warp and the water-repellent synergist accounting for 1-4% of the weight of the warp are adopted to treat the warp at 80-100 ℃ for 30-60 minutes, and the bath ratio is 1: 5-1: 30, dehydrating to the liquid carrying rate of 100-150% after treatment, and then baking for 60-90 minutes at the temperature of 100-.
As a further description of the above technical solution:
the weft yarn is treated by hydrophilic auxiliary agent accounting for 5-10% of the weight of the weft yarn for 30-60 minutes at 50-100 ℃, and the bath ratio is 1: 5-1: 30, dehydrating the mixture after treatment until the liquid carrying rate is 100-150 percent, and then baking the mixture for 60-90 minutes at the temperature of 100-150 ℃.
As a further description of the above technical solution:
the water repellent synergist comprises one or more of methylol melamine derivatives, organic silicon compounds and organic fluorine compounds, and the water repellent synergist comprises one or more of polyurethane and polyether compounds.
As a further description of the above technical solution:
the hydrophilic auxiliary agent is polyether modified polysiloxane.
In summary, due to the adoption of the technical scheme, the invention has the beneficial effects that:
1. according to the invention, the benzotriazole ultraviolet-proof finishing agent, the dye and the ice vinegar are bathed together at room temperature to treat the woven fabric layer in the lining cloth, so that the ultraviolet resistance and the washing fastness of the clothes are effectively improved, the clothes can keep long-term ultraviolet resistance, and the skin of a human body is protected.
2. In the invention, the warp yarns of the woven fabric layer are subjected to water repellent finishing, the weft yarns of the woven fabric layer are subjected to hydrophilic finishing, and the water repellent auxiliary agent, the hydrophilic auxiliary agent and the water repellent synergist are used, so that the woven fabric layer has a quick drying function, and the non-woven hot-melt adhesive lining cloth layer has good waterproof and filtering functions and good oil absorption.
3. According to the invention, the nano silver ion antibacterial master batch and the active carbon particles are arranged, so that the lining cloth has excellent antibacterial performance and adsorption performance, the lining cloth is excellent in performance, practical and durable, odor generated in the using process is effectively adsorbed, the breeding of bacteria is inhibited, the nano silver ions are slowly released and protected by the arrangement of the gluing protective layer, the sterilization action time is longer, and the active carbon particles are arranged between the non-woven hot-melt adhesive lining cloth layers and the adhesive layers, so that the active carbon particles cannot run off due to multi-washing and water-washing.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example 1
The anti-ultraviolet easy-drying antibacterial environment-friendly lining cloth comprises an upper layer, a middle layer and a lower layer structure, wherein the upper layer is a woven cloth layer, the middle layer is an adhesive layer, the lower layer is a non-woven hot-melt adhesive lining cloth layer, the woven cloth layer comprises warp yarns and weft yarns, the woven cloth layer is subjected to fabric ultraviolet-proof finishing, the adhesive layer is mainly made of TPU (thermoplastic polyurethane) glue, PU (polyurethane) glue or acrylic acid colloid, the non-woven hot-melt adhesive lining cloth layer is a melt-blown non-woven cloth layer made of PP (polypropylene) and/or ES (ethylene styrene) fibers, rectangular or rhombic grains are arranged on two sides of the non-woven hot-melt adhesive lining cloth layer, the grains are shallow grooves formed by hot pressing, nano silver ion antibacterial master batches and active carbon particles are arranged inside the shallow grooves, and a gluing protective layer is.
The active carbon particles are positioned between the non-woven hot-melt adhesive lining cloth layer and the bonding layer, and the nano silver ion antibacterial master batch is positioned between the non-woven hot-melt adhesive lining cloth layer and the clothing fabric layer.
The glue coating protective layer can be coated on the shallow groove in a glue dispensing mode or coated on the non-woven hot melt adhesive lining layer in a full coating mode.
The warp yarns of the woven fabric layer are subjected to water repellent finishing, and the weft yarns of the woven fabric layer are subjected to hydrophilic finishing.
The woven fabric layer is treated by fabric ultraviolet-proof finishing and dyeing of the woven fabric layer in one bath, and the woven fabric layer is treated by the fabric ultraviolet-proof finishing steps:
s1; when dyeing is started, carrying out one-bath on the benzotriazole ultraviolet-proof finishing agent, the dye and the glacial vinegar at room temperature, adding the base cloth, heating to 80 ℃ at the speed of 1 ℃/min, then heating to 120 ℃ at the speed of 1.5 ℃/min, dyeing, keeping the temperature for 65min, and then cooling to 80 ℃ at the speed of 1 ℃/min;
s2: drying at 130 ℃;
s3: acid reduction cleaning and saponification are adopted;
s4; performing centrifugal dehydration in a physical mode to spin dry the cloth;
s5: and (3) tentering and shaping, namely tentering and shaping in a shaping machine at the temperature of 110-140 ℃.
The water repellent finishing steps of the warp are as follows: the water-repellent auxiliary agent accounting for 10-15% of the weight of the warp and the water-repellent synergist accounting for 1-4% of the weight of the warp are adopted to treat the warp at 80-100 ℃ for 30-60 minutes, and the bath ratio is 1: 5-1: 30, dehydrating to the liquid carrying rate of 100-150% after treatment, and then baking for 60-90 minutes at the temperature of 100-.
Hydrophilic auxiliary agent which accounts for 5-10% of the weight of the weft is adopted to carry out treatment on the weft for 30-60 minutes at 50-100 ℃, and the bath ratio is 1: 5-1: 30, dehydrating the mixture after treatment until the liquid carrying rate is 100-150 percent, and then baking the mixture for 60-90 minutes at the temperature of 100-150 ℃.
The water repellent auxiliary agent comprises one or a combination of more of hydroxymethyl melamine derivatives, organic silicon compounds and organic fluorine compounds, and the water repellent synergist comprises one or a combination of more of polyurethane and polyether compounds.
The hydrophilic auxiliary agent is polyether modified polysiloxane.
Example 2
The anti-ultraviolet easy-drying antibacterial environment-friendly lining cloth comprises an upper layer, a middle layer and a lower layer structure, wherein the upper layer is a woven cloth layer, the middle layer is an adhesive layer, the lower layer is a non-woven hot-melt adhesive lining cloth layer, the woven cloth layer comprises warp yarns and weft yarns, the woven cloth layer is subjected to fabric ultraviolet-proof finishing, the adhesive layer is mainly made of TPU (thermoplastic polyurethane) glue, PU (polyurethane) glue or acrylic acid colloid, the non-woven hot-melt adhesive lining cloth layer is a melt-blown non-woven cloth layer made of PP (polypropylene) and/or ES (ethylene styrene) fibers, rectangular or rhombic grains are arranged on two sides of the non-woven hot-melt adhesive lining cloth layer, the grains are shallow grooves formed by hot pressing, nano silver ion antibacterial master batches and active carbon particles are arranged inside the shallow grooves, and a gluing protective layer is.
The active carbon particles are positioned between the non-woven hot-melt adhesive lining cloth layer and the bonding layer, and the nano silver ion antibacterial master batch is positioned between the non-woven hot-melt adhesive lining cloth layer and the clothing fabric layer.
The glue coating protective layer can be coated on the shallow groove in a glue dispensing mode or coated on the non-woven hot melt adhesive lining layer in a full coating mode.
The woven fabric layer is treated by fabric ultraviolet-proof finishing and dyeing of the woven fabric layer in one bath, and the woven fabric layer is treated by the fabric ultraviolet-proof finishing steps:
s1; when dyeing is started, carrying out one-bath on the benzotriazole ultraviolet-proof finishing agent, the dye and the glacial vinegar at room temperature, adding the base cloth, heating to 80 ℃ at the speed of 1 ℃/min, then heating to 120 ℃ at the speed of 1.5 ℃/min, dyeing, keeping the temperature for 65min, and then cooling to 80 ℃ at the speed of 1 ℃/min;
s2: drying at 130 ℃;
s3: acid reduction cleaning and saponification are adopted;
s4; performing centrifugal dehydration in a physical mode to spin dry the cloth;
s5: and (3) tentering and shaping, namely tentering and shaping in a shaping machine at the temperature of 110-140 ℃.
Example 3
The anti-ultraviolet easy-drying antibacterial environment-friendly lining cloth comprises an upper layer, a middle layer and a lower layer structure, wherein the upper layer is a woven cloth layer, the middle layer is an adhesive layer, the lower layer is a non-woven hot-melt adhesive lining cloth layer, the woven cloth layer comprises warp yarns and weft yarns, the adhesive layer uses TPU (thermoplastic polyurethane) glue, PU (polyurethane) glue or acrylic acid colloid as main materials, the non-woven hot-melt adhesive lining cloth layer is a melt-blown non-woven cloth layer of PP (polypropylene) and/or ES (ethylene styrene-ethylene) fibers, rectangular or rhombic grains are arranged on two sides of the non-woven hot-melt adhesive lining cloth layer, the grains are shallow grooves formed by hot pressing, nano silver ion antibacterial master batches and active carbon particles are arranged inside the shallow grooves, and a gluing protective layer is arranged on the.
The active carbon particles are positioned between the non-woven hot-melt adhesive lining cloth layer and the bonding layer, and the nano silver ion antibacterial master batch is positioned between the non-woven hot-melt adhesive lining cloth layer and the clothing fabric layer.
The glue coating protective layer can be coated on the shallow groove in a glue dispensing mode or coated on the non-woven hot melt adhesive lining layer in a full coating mode.
The warp yarns of the woven fabric layer are subjected to water repellent finishing, and the weft yarns of the woven fabric layer are subjected to hydrophilic finishing.
The water repellent finishing steps of the warp are as follows: the water-repellent auxiliary agent accounting for 10-15% of the weight of the warp and the water-repellent synergist accounting for 1-4% of the weight of the warp are adopted to treat the warp at 80-100 ℃ for 30-60 minutes, and the bath ratio is 1: 5-1: 30, dehydrating to the liquid carrying rate of 100-150% after treatment, and then baking for 60-90 minutes at the temperature of 100-.
Hydrophilic auxiliary agent which accounts for 5-10% of the weight of the weft is adopted to carry out treatment on the weft for 30-60 minutes at 50-100 ℃, and the bath ratio is 1: 5-1: 30, dehydrating the mixture after treatment until the liquid carrying rate is 100-150 percent, and then baking the mixture for 60-90 minutes at the temperature of 100-150 ℃.
The water repellent auxiliary agent comprises one or a combination of more of hydroxymethyl melamine derivatives, organic silicon compounds and organic fluorine compounds, and the water repellent synergist comprises one or a combination of more of polyurethane and polyether compounds.
The hydrophilic auxiliary agent is polyether modified polysiloxane.
Example 4
The anti-ultraviolet easy-drying antibacterial environment-friendly lining cloth comprises an upper layer, a middle layer and a lower layer structure, wherein the upper layer is a woven cloth layer, the middle layer is an adhesive layer, the lower layer is a non-woven hot-melt adhesive lining cloth layer, the woven cloth layer comprises warp yarns and weft yarns, the woven cloth layer is subjected to fabric ultraviolet-proof finishing, the adhesive layer uses TPU (thermoplastic polyurethane) glue, PU (polyurethane) glue or acrylic acid) glue as main materials, and the non-woven hot-melt adhesive lining cloth layer is a melt-blown non-woven cloth layer of PP (polypropylene) and/or ES (ethylene styrene) fibers.
The warp yarns of the woven fabric layer are subjected to water repellent finishing, and the weft yarns of the woven fabric layer are subjected to hydrophilic finishing.
The woven fabric layer is treated by fabric ultraviolet-proof finishing and dyeing of the woven fabric layer in one bath, and the woven fabric layer is treated by the fabric ultraviolet-proof finishing steps:
s1; when dyeing is started, carrying out one-bath on the benzotriazole ultraviolet-proof finishing agent, the dye and the glacial vinegar at room temperature, adding the base cloth, heating to 80 ℃ at the speed of 1 ℃/min, then heating to 120 ℃ at the speed of 1.5 ℃/min, dyeing, keeping the temperature for 65min, and then cooling to 80 ℃ at the speed of 1 ℃/min;
s2: drying at 130 ℃;
s3: acid reduction cleaning and saponification are adopted;
s4; performing centrifugal dehydration in a physical mode to spin dry the cloth;
s5: and (3) tentering and shaping, namely tentering and shaping in a shaping machine at the temperature of 110-140 ℃.
The water repellent finishing steps of the warp are as follows: the water-repellent auxiliary agent accounting for 10-15% of the weight of the warp and the water-repellent synergist accounting for 1-4% of the weight of the warp are adopted to treat the warp at 80-100 ℃ for 30-60 minutes, and the bath ratio is 1: 5-1: 30, dehydrating to the liquid carrying rate of 100-150% after treatment, and then baking for 60-90 minutes at the temperature of 100-.
Hydrophilic auxiliary agent which accounts for 5-10% of the weight of the weft is adopted to carry out treatment on the weft for 30-60 minutes at 50-100 ℃, and the bath ratio is 1: 5-1: 30, dehydrating the mixture after treatment until the liquid carrying rate is 100-150 percent, and then baking the mixture for 60-90 minutes at the temperature of 100-150 ℃.
The water repellent auxiliary agent comprises one or a combination of more of hydroxymethyl melamine derivatives, organic silicon compounds and organic fluorine compounds, and the water repellent synergist comprises one or a combination of more of polyurethane and polyether compounds.
The hydrophilic auxiliary agent is polyether modified polysiloxane.
The interlining fabrics of examples 1-4 were subjected to washing and natural drying tests to obtain the test results shown in table 1:
example 1 | Example 2 | Example 3 | Example 4 | |
Water content condition | 30% | 30% | 30% | 30% |
Hang dry time | 1 hour 15 minutes | 2 hours 45 minutes | 1 hour and 12 minutes | 1 hour and 5 minutes |
UPF refers to the ratio of the average effect of ultraviolet radiation calculated without protection of the skin to the average effect of ultraviolet radiation calculated with protection of the skin with fabric, according to the definition in the national standard. The interlinings of examples 1 to 4 were subjected to ultraviolet irradiation and measurement tests, and the measured UPF values are shown in table 2:
example 1 | Example 2 | Example 3 | Example 4 | |
UPF | 58 | 56 | 42 | 52 |
In example 4, the nano silver ion antibacterial master batch and the activated carbon particles are not used, and the lining cloth in example 4 is stored and used in an environment simulation experiment, so that the lining cloth in example 4 is easy to mildew, has a large colony amount and cannot effectively adsorb odor.
The lining cloth in the embodiment 1 has good antibacterial performance and good ultraviolet resistance, and due to the arrangement of the quick drying process, the natural drying time of the lining cloth is shortened, the drying speed is high, the lining cloth is excellent in performance, practical and durable, odor generated in the using process is effectively adsorbed, and the breeding of bacteria is inhibited.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.
Claims (9)
1. The utility model provides an antibiotic environmental protection lining cloth is easily done to ultraviolet resistance and production technology thereof, includes, its characterized in that, the lining cloth includes upper strata, middle level and understructure, the upper strata is woven the cloth layer for the machine, the middle level is the adhesive linkage, non-woven hot melt bonding lining cloth layer of lower floor, the woven cloth layer includes warp and woof, the woven cloth layer is through fabric ultraviolet protection arrangement, TPU glue, PU glue or acrylic acid colloid are used to the adhesive linkage main material, non-woven hot melt bonding lining cloth layer is PP and/or the fibrous melt-blown non-woven fabrics layer of ES, non-woven hot melt bonding lining cloth layer two sides has the line of rectangle or rhombus, the line is the shallow slot that hot pressing formed, and the inside of shallow slot has antibiotic master batch of nanometer silver ion and active carbon particle, the antibiotic master batch surface of nanometer silver ion has the rubber coating protective layer.
2. The anti-ultraviolet, easy-drying and antibacterial environmentally-friendly lining cloth and the production process thereof according to claim 1, wherein the activated carbon particles are positioned between the non-woven hot-melt adhesive lining cloth layer and the adhesive layer, and the nano silver ion antibacterial master batch is positioned between the non-woven hot-melt adhesive lining cloth layer and the clothing fabric layer.
3. The lining cloth of claim 1, wherein the glue protective layer is a polypropylene glue layer, and the glue protective layer can be coated on the shallow groove in a glue dispensing manner or coated on the non-woven hot-melt adhesive lining cloth layer in a full coating manner.
4. The ultraviolet-resistant, easily-dried and antibacterial environmentally-friendly lining cloth and the production process thereof as claimed in claim 1, wherein warp yarns of the woven cloth layer are warp yarns subjected to water repellent finishing, and weft yarns of the woven cloth layer are weft yarns subjected to hydrophilic finishing.
5. The anti-ultraviolet, easy-drying and antibacterial environmentally-friendly lining cloth and the production process thereof as claimed in claim 1, wherein the woven cloth layer is treated by fabric anti-ultraviolet finishing and dyeing of the woven cloth layer in one bath, and the woven cloth layer is treated by the fabric anti-ultraviolet finishing steps of:
s1; when dyeing is started, carrying out one-bath on the benzotriazole ultraviolet-proof finishing agent, the dye and the glacial vinegar at room temperature, adding the base cloth, heating to 80 ℃ at the speed of 1 ℃/min, then heating to 120 ℃ at the speed of 1.5 ℃/min, dyeing, keeping the temperature for 65min, and then cooling to 80 ℃ at the speed of 1 ℃/min;
s2: drying at 130 ℃;
s3: acid reduction cleaning and saponification are adopted;
s4; performing centrifugal dehydration in a physical mode to spin dry the cloth;
s5: and (3) tentering and shaping, namely tentering and shaping in a shaping machine at the temperature of 110-140 ℃.
6. The ultraviolet-resistant, easily-dried and antibacterial environmentally-friendly lining cloth and the production process thereof according to claim 4 are characterized in that the water-repellent finishing step of the warp yarns is as follows: the water-repellent auxiliary agent accounting for 10-15% of the weight of the warp and the water-repellent synergist accounting for 1-4% of the weight of the warp are adopted to treat the warp at 80-100 ℃ for 30-60 minutes, and the bath ratio is 1: 5-1: 30, dehydrating to the liquid carrying rate of 100-150% after treatment, and then baking for 60-90 minutes at the temperature of 100-.
7. The ultraviolet-resistant, easily-dried and antibacterial environmentally-friendly lining cloth and the production process thereof as claimed in claim 4, wherein the weft yarns are treated by hydrophilic auxiliary agents accounting for 5-10% of the weight of the weft yarns at 50-100 ℃ for 30-60 minutes, and the bath ratio is 1: 5-1: 30, dehydrating the mixture after treatment until the liquid carrying rate is 100-150 percent, and then baking the mixture for 60-90 minutes at the temperature of 100-150 ℃.
8. The ultraviolet-resistant, easily-dried and antibacterial environmentally-friendly lining cloth and the production process thereof as claimed in claim 6, wherein the water-repellent auxiliary comprises one or a combination of several of methylol melamine derivatives, organic silicon compounds and organic fluorine compounds, and the water-repellent synergist comprises one or a combination of several of polyurethane and polyether compounds.
9. The ultraviolet-resistant, easy-drying and antibacterial environmentally-friendly lining cloth and the production process thereof as claimed in claim 7, wherein the hydrophilic auxiliary agent is polyether modified polysiloxane.