CN112624218A - Mineral hydrogen-rich activation water purification filter element - Google Patents
Mineral hydrogen-rich activation water purification filter element Download PDFInfo
- Publication number
- CN112624218A CN112624218A CN202011359066.1A CN202011359066A CN112624218A CN 112624218 A CN112624218 A CN 112624218A CN 202011359066 A CN202011359066 A CN 202011359066A CN 112624218 A CN112624218 A CN 112624218A
- Authority
- CN
- China
- Prior art keywords
- percent
- water
- balls
- rich
- hydrogen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of water purification equipment, and discloses a mineral hydrogen-rich activation water purification filter element which comprises a filter bin, wherein the side wall of the filter bin is provided with a plurality of through grooves for water to pass through, filter material particles for activating water are contained in the filter material bin, and the filter material particles comprise negative potential balls, alkaline mineralized balls, bacteriostatic mineralized balls, titanium energy balls, far infrared negative ion balls, magnetic energy balls and microcrystal energy balls. The water purifying filter element provided by the invention can change purified water into mineral hydrogen-rich activated water without electricity, the water quality is alkalescent, has no substances harmful to human bodies, is rich in mineral substances and trace elements required by human bodies, has small molecular groups, is negative potential, is hydrogen-rich, has energy and has an activation function; the water purified by the filter material particles contains hydrogen ions, which have strong antioxidation, cell activating function and cell activity enhancing function.
Description
Technical Field
The invention relates to the technical field of water purification equipment, in particular to a mineral hydrogen-rich activated water purification filter element.
Background
At present, with the development of society, the pollution of water resources is becoming serious. In the traditional water treatment, I perform reverse osmosis technology treatment on water to prepare the water into pure water, but the pure water is only safe water and is not healthy water; the purified water does not contain substances harmful to human bodies, but lacks minerals, rare elements and the like beneficial to the human bodies, and the water is acidic, so that the purified water is not beneficial to the health of the human bodies after being drunk for a long time.
In recent years, various functional water treatment technologies have been developed, and the corresponding functional water includes electrolyzed water, magnetized water, mineralized water, activated water, and the like, and the functional water is simply filtered by PPF, activated carbon, and the like, and then is subjected to functional treatment, and therefore, the safety of the functional water is not high.
With the improvement of human cognition and the development of medicine. The 2007 Japanese scientists published a paper on Nature media, which proves that hydrogen molecules have selective antioxidation function and can effectively neutralize harmful hydroxyl free radicals and nitrite anions in human bodies, so that the medical research of the hydrogen molecules is rapidly developed, and the efficacy of the hydrogen molecules is more and more clinically verified. In order to make hydrogen an element to enter the health care field, the prior art is to make hydrogen directly for human use, but the cost of the method is too high.
In recent years, many patents have been issued for the production of hydrogen water and other patents relating to hydrogen water have been issued. These patents have disadvantages: some of the water is only hydrogen-rich water, other minerals are few, some of the water is insufficient and can only be drunk by a small number of people, and the comprehensive performance of the healthy water is not perfect. Wherein, the water quality performance is reduced when the variety of trace elements needed by human body is small, the water quality performance is unstable and the continuous water discharge amount is large.
Disclosure of Invention
The invention aims to provide a mineral hydrogen-rich activated water purification filter element which has the advantage of changing purified water into mineral hydrogen-rich activated water.
In order to achieve the above purpose, the basic scheme of the invention is as follows: the utility model provides a rich hydrogen activation water purification filter core of mineral substance, includes the filter bin, a plurality of logical grooves that make the water pass through are seted up to the lateral wall of filter bin, it has the filter material granule that is used for the activated water to hold in the filter bin, the filter material granule includes negative potential ball, alkaline mineralize ball, antibacterial mineralize ball, titanium energy ball, far infrared anion ball, magnetic energy ball and micrite energy ball.
Further, the weight proportion of the negative potential balls is 28-57%, the weight proportion of the alkaline mineralized balls is 8-25%, the weight proportion of the bacteriostatic mineralized balls is 2-10%, the weight proportion of the titanium energy balls is 2-8%, the weight proportion of the far infrared negative ion balls is 6-20%, the weight proportion of the magnetic energy balls is 6-34%, and the weight proportion of the microcrystal energy balls is 6-20%.
By adopting the technical scheme, the substances with the mass percentage are preferably selected as filtering material particles for purifying water, and purified water subjected to the purification treatment of the filtering material particles can be changed into mineral hydrogen-enriched activated water;
wherein, the water treated by the negative potential ball is in low potential or negative potential, which can balance the oxidative free radicals generated in the metabolism process of human body, improve the activity of SOD and eliminate degradation product Malonaldehyde (MDA) of lipid peroxide, so that the cells are full of activity;
the alkaline mineralized spheres are alkaline, and the treated water is beneficial to balancing lactic acid generated by internal fatigue and neutralizing acidic substances in the body;
the antibacterial mineralized spheres have high solubility and strong permeability, and ensure that the water contains more calcium ions; meanwhile, the water treated by the emulsifier has certain emulsifying capacity on grease, and is beneficial to relieving symptoms such as hyperlipidemia, hypercholesterolemia, high blood viscosity and the like caused by high-protein and high-calorie diet;
the water treated by the titanium energy ball is rich in mineral substances and trace elements required by human bodies, and has energy and activation functions;
the far infrared anion ball has a positive electrode and a negative electrode, and can instantly release current after being fused with water, and the current is 0.06mA current which is most suitable for a human body, so that hydrogen ions and hydroxide ions in water molecules around the far infrared anion ball are separated; the hydrogen ions and the electrons are combined into hydrogen gas, and the hydroxide ions and the surrounding water molecules are combined into interface active substances and can generate more than 300 times of negative ions;
the magnetic energy ball can magnetize and sterilize the water body and decompose large molecular groups in the water into weakly alkaline small molecular groups, so that the water body has the direct drinking effect;
the microcrystalline energy ball can make the raw water rich in minerals and trace elements required by human body, and has energy and activation functions.
Further, the negative potential ball is composed of the following components in percentage by weight: 10-50% of alpha-aluminum oxide, 5-60% of magnesium powder, 5-10% of binder, 1-5% of mineral powder and 1-10% of auxiliary material.
By adopting the technical scheme, the negative potential ball is used in the water purifier, so that the negative potential alkalescent water can be generated, oxygen free radicals in a human body can be eliminated, and the acidic constitution of the human body can be improved; in addition, the raw materials for forming the negative potential ball are NSF authentication materials, and the negative potential ball has the advantages of low manufacturing cost and good effects of generating negative potential and alkalescence.
Further, the alkaline mineralized spheres are composed of the following components in percentage by weight: 20-40% of medical stone powder, 5-30% of zeolite, 20-30% of coconut shell activated carbon powder and 10-40% of ultra-high molecular polyethylene powder.
By adopting the technical scheme, the water body treated by the alkaline mineralized spheres is alkalescent, and the alkalescent water is beneficial to balancing lactic acid generated by internal fatigue and neutralizing acidic substances in the body; the medical stone powder can dissolve out a large amount of trace elements when contacting with water, which is beneficial to the health of human body; the zeolite can be used for resisting aging and removing heavy metals accumulated in the body; the coconut shell activated carbon powder adsorbs large-particle impurities in water, and plays a role in water body purification; the ultra-high molecular polyethylene powder can be used as a filter medium for filtering impurity particles in water.
Further, the bacteriostatic mineralization ball comprises the following components in percentage by weight: 1-5 percent of antibacterial agent, 10-15 percent of tourmaline powder, 30-40 percent of medical stone powder, 2-10 percent of bamboo carbon powder and 20-28 percent of pottery clay.
By adopting the technical scheme, the antibacterial mineralized spheres have high solubility and strong permeability; the antibacterial agent can play a role in sterilization; the tourmaline powder can enhance the activity of the drinking water and effectively improve the activity of the drinking water; the medical stone powder can dissolve out a large amount of trace elements when contacting with water, which is beneficial to the health of human body; the bamboo carbon powder can adsorb large-particle impurities in water, and plays a role in purifying water; the pottery clay has excellent alkali corrosion resistance.
Further, the titanium energy ball comprises the following components in percentage by weight: 20-30% of zirconium silicate, 10-24% of titanium dioxide, 3-8% of rare earth, 3-8% of cobalt oxide, 1-10% of fullerene and 10-20% of tourmaline.
By adopting the technical scheme, the water treated by the titanium energy ball is rich in minerals and trace elements required by human bodies and has the functions of energy and activation; the zirconium silicate has high chemical stability and is a high-quality and low-cost opacifier; the titanium dioxide has strong adhesive force and can adsorb impurities in water; the rare earth is rich in a large amount of trace elements required by a human body, can be dissolved in water, and is beneficial to the health of the human body after being drunk by the human body; fullerene can adsorb harmful elements such as benzene and naphthalene in water body, and has water body purifying effect; the tourmaline can enhance the activity of drinking water and effectively improve the activity of the drinking water.
Further, the far infrared anion ball comprises the following components in percentage by weight: 6 to 20 percent of far infrared ball, 3 to 10 percent of negative ion ball, 20 to 50 percent of tourmaline powder and 1 to 10 percent of auxiliary material.
By adopting the technical scheme, the far infrared ball has a positive pole, the negative ion ball has a negative pole, and water contacts the far infrared ball and the negative ion to instantly release current which is 0.06mA current most suitable for a human body, so that hydrogen ions and hydroxide ions in water molecules around the far infrared ball are separated; the hydrogen ions and the electrons are combined into hydrogen, and the hydroxide ions and the surrounding water molecules are combined into interface active substances and can generate more than 300 times of negative ions; meanwhile, the hydrogen ions have stronger antioxidation, have the function of activating cells and enhance the activity of the cells; the tourmaline powder can enhance the activity of drinking water and effectively improve the activity of the drinking water.
Further, the magnetic energy ball is composed of the following components in percentage by weight: 3% -10% of igneous rock, 6% -20% of tourmaline, 10% -25% of magnetized stone, 30% -50% of hydrogen-rich balls and 2% -20% of nano silver powder.
By adopting the technical scheme, the substances with the mass percentage are preferably selected as the raw materials of the magnetic energy ball, the magnetic energy ball can carry out magnetization sterilization on the water body and decompose large molecular groups in the water into weakly alkaline small molecular groups, so that the water body has the direct drinking effect; wherein, the igneous rock mainly comprises 12 elements of oxygen, silicon, aluminum, iron, calcium, sodium, potassium, magnesium, titanium, manganese, hydrogen, phosphorus and the like, and also contains a plurality of microelements, such As Au, Ag, As, B, Ba, Be, Cu, Pb, Zn, F, Cl, S, Ce, Li and the like, and the microelements can Be dissolved in water, and are beneficial to the health of human bodies after being drunk by the human bodies; the tourmaline can enhance the activity of the drinking water and effectively improve the activity of the drinking water; the magnetized stone can magnetize and sterilize the water body, and decompose large molecular groups in the water into weakly alkaline small molecular groups, so that the water body has the direct drinking effect; the hydrogen-rich spheres can separate hydrogen ions and hydroxide ions in water molecules around the hydrogen-rich spheres, and the hydrogen ions have strong antioxidation, have the function of activating cells and enhance the activity of the cells; the nano silver powder can play a role in sterilization and disinfection, thereby ensuring the safety of water.
Further, the microcrystalline energy ball is composed of the following components in percentage by weight: 10 to 25 percent of calcium sulfite, 10 to 30 percent of medical stone, 2 to 10 percent of tourmaline and 30 to 50 percent of nano fiber active carbon.
By adopting the technical scheme, the microcrystalline energy ball can ensure that the raw water is rich in minerals and trace elements required by a human body and has the functions of energy and activation; the substances with the mass percentage are preferably used as raw materials of the microcrystalline energy ball, wherein calcium sulfite can be freely passed by water molecules, has high adsorption force, can purify a water body deeply and in a large area, kills various pathogenic bacteria in water, inhibits the growth and reproduction of bacterial microorganisms, and has extremely strong adsorption effect on toxic and harmful metal ions and bacterial viruses; the medical stone can dissolve out a large amount of trace elements when contacting with water, which is beneficial to the health of human body; the tourmaline can enhance the activity of the drinking water and effectively improve the activity of the drinking water; the nano-fiber activated carbon can adsorb large particle impurities in water, and plays a role in water purification.
To sum up, compare this scheme's beneficial effect with prior art and be:
1. the water purification filter element provided by the invention can change purified water into mineral hydrogen-rich activated water without electricity, and the water quality can reach all the performances of healthy water: the product is alkalescent, contains no substances harmful to human body, is rich in minerals and trace elements required by human body, has small molecular groups, is negative potential, is rich in hydrogen, has energy and has an activation function; the water passing through the water purifying filter element has stronger penetrability and dissolving power, can quickly permeate into cells of a human body, brings mineral substances and trace elements in the water into the cells, can effectively remove waste in the cells and promotes metabolism of the human body; the water purified by the filter material particles contains hydrogen ions, which have strong antioxidation, cell activating function and cell activity enhancing function.
Detailed Description
The invention will be described in more detail by means of specific embodiments and with reference to the following description:
the utility model provides a rich hydrogen activation water purification filter core of mineral substance, includes the filter storehouse, holds the filter material granule that is used for the activated water body in the filter storehouse, and the filter material granule includes following mass percent material:
28 to 57 percent of negative potential ball,
8 to 25 percent of alkaline mineralized balls,
2 to 10 percent of bacteriostatic mineralization ball,
2 to 8 percent of titanium energy balls,
6 to 20 percent of far infrared negative ion balls,
6 to 34 percent of magnetic energy ball,
6 to 20 percent of microcrystalline energy ball.
The invention is further illustrated by the following examples,
filter media particles of examples 1 to 5 were made according to the formulation in Table 1
Table 1:
filter media particles of comparative examples 1 to 4 were made according to the formulation of Table 2
Table 2:
test example I Water pH and mineral content test
The quality of purified water and the quality of purified water purified by the filter material particles of the embodiments 1 to 5 are detected according to GB/T5750.6-2006 and GB8538-2016, and the detection method comprises the following steps: pouring purified water into a water cup with the filter material particles of the embodiments 1 to 5 inside, shaking the water cup for 1 minute, taking out the water sample purified by the filter material particles of the embodiments 1 to 5, detecting, and comparing with the purified water; the results are shown in Table 3:
table 3:
the quality of purified water and the quality of purified water purified by the filter material particles of the comparative examples 1 to 4 are detected according to GB/T5750.6-2006 and GB8538-2016 standards, and the detection method comprises the following steps: pouring purified water into a water cup with the filter material particles of the comparative examples 1 to 4 inside, shaking the water cup for 1 minute, taking out the water sample purified by the filter material particles of the comparative examples 1 to 4, detecting, and comparing with the purified water; the results are shown in Table 3:
table 4:
as can be seen from the comparison results in tables 3 and 4, the pH of the water samples of comparative examples 1, 3, and 4 and examples 1 to 5 is more weakly alkaline than that of the water samples of comparative examples 1 to 4 and examples 1 to 5, and the water samples of comparative examples 1, 3, and 4 and examples 1 to 5 contain mineral elements and trace elements necessary for human body at higher levels.
The alkaline mineralization balls are added into the filter material particles of comparative examples 1, 3 and 4 and examples 1 to 5, and as can be seen from tables 3 and 4, the alkaline mineralization balls are alkaline, the treated water is alkalescent, and the alkalescent water is beneficial to balancing lactic acid generated by internal fatigue and neutralizing acidic substances in the body; because the contents of mineral elements and trace elements in the purified water and the water sample purified by the filter material particles in the comparative example 2 are less, and compared with the filter material particles in the comparative examples 1, 3 and 4 and the examples 1 to 5, the filter material particles in the comparative example 2 lack the alkaline mineralized spheres, the alkaline mineralized spheres can provide mineral elements and trace elements besides the alkaline water body, and the composition of the alkaline mineralized spheres can show that a large amount of trace elements can be dissolved out when the medical stone powder in the alkaline mineralized spheres is contacted with the water body.
Test example two, examination of Water molecules of Small molecular groups
The detection method comprises the following steps: pouring purified water into water cups in which the filter material particles of the examples 1 to 5 and the comparative examples 1 to 4 are arranged respectively, shaking the water cups for 1 minute, taking out water samples purified by the filter material particles of the examples 1 to 5 and the comparative examples 1 to 4 in equal amount, brewing the tea leaves, observing the color of the tea water, and comparing the water samples with the purified water; the results are shown in Table 5:
table 5:
group of | Color of tea water |
Pure water (Cold water) | Colorless and colorless |
Water sample of example 1 (Cold Water) | Light yellow |
Water sample of example 2 (Cold Water) | Light yellow |
Water sample of example 3 (Cold Water) | Light yellow |
Water sample (Cold water) of example 4 | Light yellow |
Water sample (Cold water) of example 5 | Light yellow |
Water sample (Cold Water) of comparative example 1 | Colorless and colorless |
Water sample (Cold Water) of comparative example 2 | Light yellow |
Water sample (Cold Water) of comparative example 3 | Light yellow |
Water sample (Cold Water) of comparative example 4 | Light yellow |
It can be known from the comparison results in table 5 that, compared with the water samples of comparative examples 1 to 4 and examples 1 to 5, the water samples of the tea brewed by the water samples of comparative examples 2 to 4 and examples 1 to 5 are light yellow, because the magnetic energy balls are added in the filter material particles of comparative examples 2 to 4 and examples 1 to 5, the magnetic energy balls can magnetize and sterilize the water body, and decompose the macromolecular groups in the water into weakly alkaline small molecular groups, so that the water permeability of the small molecular groups is stronger, and the tea can be better dissolved.
Test example III test for Oxidation resistance
The detection method comprises the following steps: pouring purified water into water cups in which the filter material particles of examples 1 to 5 and comparative examples 1 to 4 are arranged respectively, shaking the water cups for 1 minute, taking out water samples purified by the filter material particles of examples 1 to 5 and comparative examples 1 to 4 in equal amount, adding iodine tincture in equal amount into different water samples respectively, and comparing the iodine tincture with the purified water; the results are shown in Table 6:
TABLE 6
Group of | Color change of water sample |
Purified water | Colorless → yellow |
Sample of example 1 | Colorless → yellow → colorless |
Sample of example 2 | Colorless → yellow → colorless |
Sample of example 3 | Colorless → yellow →Colorless and colorless |
Sample of example 4 | Colorless → yellow → colorless |
Sample of example 5 | Colorless → yellow → colorless |
Sample of comparative example 1 | Colorless → yellow → colorless |
Sample of comparative example 2 | Colorless → yellow → colorless |
Sample of comparative example 3 | Colorless → yellow → colorless |
Sample of comparative example 4 | Colorless → yellow |
As can be seen from the comparison results in table 6, in comparison with the water samples of comparative examples 1 to 4 and examples 1 to 5, the water samples of comparative examples 1 to 3 and examples 1 to 5 changed from colorless to yellow and then changed back to colorless again under the action of iodine tincture, and the pure water and the water sample of comparative example 4 still changed from colorless to yellow and then became yellow, the difference is that far infrared anion spheres are added to the filter material particles of comparative examples 1 to 3 and examples 1 to 5, and have a positive electrode and a negative electrode, and instantly release current through fusion with water, wherein the current is 0.06mA current most suitable for human body, so that hydrogen ions and hydroxide ions in water molecules around the spheres are separated; the hydrogen ions have strong antioxidation, have the functions of activating cells and enhancing the vitality of the cells, and can reduce the iodine tincture so that the water sample returns to a colorless state again.
Test example four, detection of Oxidation-reduction potential
The detection method comprises the following steps: pouring the purified water into water cups with the filter material particles of the examples 1 to 5 and the comparative examples 1 to 4 respectively, shaking the water cups for 1 minute, taking out water samples purified by the filter material particles of the examples 1 to 5 and the comparative examples 1 to 4 in equal amount, and testing the potential values of the purified water and different water samples by using an ORP measuring instrument; the results are shown in Table 7:
TABLE 7
Group of | Potential value MV |
Purified water | -0.5 |
Sample of example 1 | -55 |
Sample of example 2 | -98 |
Sample of example 3 | -125 |
Sample of example 4 | -155 |
Sample of example 5 | -182 |
Sample of comparative example 1 | -58 |
Sample of comparative example 2 | -62 |
Sample of comparative example 3 | -0.8 |
Sample of comparative example 4 | -65 |
It can be seen from the comparison results in table 7 that, compared with the water samples of comparative examples 1 to 4 and examples 1 to 5, the purified water has a lower potential value than the water sample of comparative example 3, and the water samples of comparative examples 1, 2, 4 and examples 1 to 5 have a higher potential value, and the difference is that the filter material particles of comparative examples 1, 2, 4 and examples 1 to 5 are added with negative potential spheres, and the water treated by the negative potential spheres has a low potential or a negative potential, so that the oxidation free radicals generated in the metabolism process of a human body can be balanced, the activity of SOD can be improved, and Malondialdehyde (MDA), which is a degradation product of lipid peroxide, can be eliminated, so that the cells can be full of activity.
Test example five detection of Floating chlorine concentration
The detection method comprises the following steps: pouring purified water into water cups containing the filter material particles of examples 1 to 5 and comparative examples 1 to 4 respectively, shaking the water cups for 1 minute, taking out water samples purified by the filter material particles of examples 1 to 5 and comparative examples 1 to 4 in equal amount, and detecting the water samples by using an EMH-100 dissolved chlorine measuring instrument, wherein the measured results are shown in Table 8:
TABLE 8
Group of | Content of dissolved chlorine ppm |
Purified water | 100 |
Sample of example 1 | 102 |
Sample of example 2 | 101 |
Sample of example 3 | 105 |
Sample of example 4 | 102 |
Sample of example 5 | 102 |
Sample of comparative example 1 | 101 |
Sample of comparative example 2 | 103 |
Sample of comparative example 3 | 101 |
Sample of comparative example 4 | 105 |
From the comparison results in table 8, it can be seen that the filter material particles of comparative examples 1 to 4 and examples 1 to 5 can sterilize and disinfect water bodies in purified water compared with the water samples of comparative examples 1 to 4 and examples 1 to 5.
Test example six, detection of activation Performance
The detection method comprises the following steps: pouring purified water into water cups with the filter material particles of examples 1 to 5 and comparative examples 1 to 4 respectively, shaking the water cups for 1 minute, taking out water samples purified by the filter material particles of examples 1 to 5 and comparative examples 1 to 4 in equal amount, and detecting the purified water and the water samples by using an ecological activated water detection reagent, wherein the measured results are shown in table 9:
TABLE 9
Group of | Color of water sample |
Purified water | Colorless and colorless |
Sample of example 1 | Light red |
Sample of example 2 | Light red |
Sample of example 3 | Light red |
Sample of example 4 | Light red |
Sample of example 5 | Light red |
Sample of comparative example 1 | Light red |
Sample of comparative example 2 | Light red |
Sample of comparative example 3 | Light red |
Sample of comparative example 4 | Light red |
From the comparison results in table 9, it can be seen that, compared with the water samples of comparative examples 1 to 4 and examples 1 to 5, the water samples of comparative examples 1 to 4 and examples 1 to 5 react with the ecological activated water detection reagent to make the water samples light red, which indicates that the water samples have activity, and the purified water is colorless, which indicates that the purified water has no activity; the filter material particles of comparative examples 1 to 4 and examples 1 to 5 are added with titanium energy balls and microcrystalline energy balls, and water treated by the titanium energy balls is rich in minerals and trace elements required by a human body and has energy and activation functions; the microcrystal energy ball can make the raw water rich in mineral substances and trace elements required by human body, and has energy and activation functions, and tourmaline is added in both the titanium energy ball and the microcrystal energy ball, and can enhance the activity of drinking water and effectively improve the activity of the drinking water.
The foregoing is merely an example of the present invention and common general knowledge of known specific structures and features of the embodiments is not described herein in any greater detail. It should be noted that, for those skilled in the art, without departing from the structure of the present invention, several changes and modifications can be made, which should also be regarded as the protection scope of the present invention, and these will not affect the effect of the implementation of the present invention and the practicability of the patent. The scope of the claims of the present application shall be defined by the claims and the description of the embodiments and the like in the specification shall be used to explain the contents of the claims.
Claims (9)
1. The utility model provides a rich hydrogen activation water purification filter core of mineral substance which characterized in that: the filter material comprises a filter bin, wherein the side wall of the filter bin is provided with a plurality of through grooves for enabling a water body to pass through, filter material particles for activating the water body are contained in the filter bin, and the filter material particles comprise negative potential balls, alkaline mineralized balls, bacteriostatic mineralized balls, titanium energy balls, far infrared negative ion balls, magnetic energy balls and microcrystal energy balls.
2. The mineral hydrogen-rich activated water purification cartridge of claim 1, wherein: the weight proportion of the negative potential ball is 28-57 percent,
the weight proportion of the alkaline mineralized balls is 8-25%,
the weight proportion of the bacteriostatic mineralization ball is 2-10 percent,
the weight proportion of the titanium energy ball is 2-8%,
the weight proportion of the far infrared anion ball is 6-20%,
the weight proportion of the magnetic energy ball is 6-34 percent,
the weight proportion of the microcrystalline energy ball is 6-20%.
3. The mineral hydrogen-rich activated water purification cartridge of claim 1, wherein: the negative potential ball comprises the following components in percentage by weight:
10 to 50 percent of alpha-aluminum oxide,
5 to 60 percent of magnesium powder,
5 to 10 percent of adhesive,
1 to 5 percent of ore powder,
1 to 10 percent of auxiliary material.
4. The mineral hydrogen-rich activated water purification cartridge of claim 1, wherein: the alkaline mineralized balls are composed of the following components in percentage by weight:
20 to 40 percent of medical stone powder,
5 to 30 percent of zeolite,
20 to 30 percent of coconut shell activated carbon powder,
10-40% of ultra-high molecular polyethylene powder.
5. The mineral hydrogen-rich activated water purification cartridge of claim 1, wherein: the bacteriostatic mineralized ball comprises the following components in percentage by weight:
1 to 5 percent of antibacterial agent,
10 to 15 percent of tourmaline powder,
30 to 40 percent of medical stone powder,
2 to 10 percent of bamboo carbon powder,
20 to 28 percent of argil.
6. The mineral hydrogen-rich activated water purification cartridge of claim 1, wherein: the titanium energy ball comprises the following components in percentage by weight:
20 to 30 percent of zirconium silicate,
10 to 24 percent of titanium dioxide,
3 to 8 percent of rare earth,
3 to 8 percent of cobalt oxide,
1 to 10 percent of fullerene,
10 to 20 percent of tourmaline.
7. The mineral hydrogen-rich activated water purification cartridge of claim 1, wherein: the far infrared anion ball comprises the following components in percentage by weight:
6 to 20 percent of far infrared ball,
3 to 10 percent of negative ion ball,
20 to 50 percent of tourmaline powder,
1 to 10 percent of auxiliary material.
8. The mineral hydrogen-rich activated water purification cartridge of claim 1, wherein: the magnetic energy ball comprises the following components in percentage by weight:
3 to 10 percent of igneous rock,
6 to 20 percent of tourmaline,
10 to 25 percent of magnetized stone,
30 to 50 percent of hydrogen-rich balls,
2 to 20 percent of nano silver powder.
9. The mineral hydrogen-rich activated water purification cartridge of claim 1, wherein: the microcrystalline energy ball comprises the following components in percentage by weight:
10 to 25 percent of calcium sulfite,
10 to 30 percent of medical stone,
2 to 10 percent of tourmaline,
30-50% of nano-fiber activated carbon.