CN1125710C - Non-woven fibrous plate and its making process - Google Patents
Non-woven fibrous plate and its making process Download PDFInfo
- Publication number
- CN1125710C CN1125710C CN01127814A CN01127814A CN1125710C CN 1125710 C CN1125710 C CN 1125710C CN 01127814 A CN01127814 A CN 01127814A CN 01127814 A CN01127814 A CN 01127814A CN 1125710 C CN1125710 C CN 1125710C
- Authority
- CN
- China
- Prior art keywords
- fibrous plate
- fibre
- fibers
- sheet material
- base fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention belongs to a sheet material with fibers made by a nonweaving method and a manufacture method of the sheet material. The sheet material is mainly used as a special material for mid-soles of shoes, and is formed by the mixture of various kinds of different short fibers through needling forming and heating shaping. The present invention is characterized in that the mixed short fiber is formed by the mixture of the following fibers (by weight ratio): 50% to 60% of polyester fibers., 20% to 30% of polyacrylonitrile fibers and, 15% to 25% of polypropylene fibers. The manufacture method is characterized in that a fiber net is made through the opening and the carding of the short fibers, the fiber net is made into a base fabric through tight-needle stabbing weaving on a needle machine in a disposable way, the base fabric is heated until the polyacrylonitrile fibers are melted, and the surface of the base fabric is leveled in the mode of pressing so that the thickness of the base fabric is corrected to the product thickness; after the base fabric is shaped, the base fabric becomes a finished product. The fiber sheet material of the present invention is a truly pollution-free environmental protection product and has the advantages of tastelessness, mildew resistance, peracid and concentrated alkali resistance, good breathability and sweat removal performance, excellent joggling resistance performance of the fiber sheet material, simple manufacture process and high production efficiency; the excellent joggling resistance performance is the most outstanding advantage.
Description
Technical field: the invention belongs to sheet material and manufacture method thereof that a kind of fiber is made by nonwoven processes.Sheet material of the present invention is mainly as the special-purpose material at the end in the footwear, also can be used as with similar characteristics requirement other and uses material, as the material that substitutes of the timber on furniture, stationery, suitcase, the building materials, leather and so on.
Background technology: at present existing non-woven fiber board and the manufacture method that can be used for the end in the footwear and similar applications, " fiberboard and manufacture method thereof " just like No. the 98116989.9th, Chinese patent application, be to constitute non-weaving cloth by piling up with needling process by spray filament length fiber, with its impregnation, be hot pressed into fiberboard then again.The shortcoming of the manufacture method that this two procedures process: the one, the sewage dirt that the impregnation production process is discharged can cause environmental pollution; The 2nd, this sheet material that is cured by chemical resin can produce chemical reaction and produce harmful material with the sweat acid of pin during as the footwear material; The 3rd, gum dipping process must adopt packing material, wait space between fill fiber as Paris white, and the hardness that consequently makes fiberboard increases and toughness is very poor, not folding song.With respect to this gum dipping process, " novel material used to make inner sole of shoe and the production technology thereof " that No. the 98112183.7th, Chinese patent application, propose to adopt scrap fabric and waste polypropylene woven bags silk, mix shredding to fibrous fully, make non-weaving cloth through needling process, be cut into standby, on request thickness do multilayer laminated, the hot repressing moulding.Wherein polypropylene is as hot melt adhesive material, and its content is up to 50%~80%, and cloth content then accounts for 20%~50%, and hot-press equipment is 200 tons of 4 layers of hot presses, and heating-up temperature is 210 ℃.Obviously there is following defective in this technical scheme: the one, because the power of filling the span of a man's arms that fabric fibre interweaves mutually is weak, pulling force is poor, so need solidify the coarse sclerosis of feel of back product like this by the hot melt adhesive material of high-load, pliability is relatively poor; The 2nd, the water imbibition of fabric fibre is strong, perspire is poor; The 3rd, hot melt adhesive material content height can make the gas permeability variation; The 4th, adopt waste and scrap must pass through cleaning and wait arranging process, the releaser that waste water that cleans and waste and scrap are stacked process all can pollute environment, and raw material are irregular, difficult quality is grasped, and its product must belong to the low gear time product of materials recycling; The 5th, production technology more complicated and backwardness, production efficiency is low.
Summary of the invention: the problem to be solved in the present invention provides a kind of improved non-woven fiber board and manufacture method thereof, as the special-purpose material in the end in the footwear, can reach free of contamination environmental requirement and water-fast requirement and the folding song is high especially, gas permeability and perspire is good, the flexible and cortex feel in surface, pliability is strong especially, technology is simple and science, production efficiency height, can overcome the defective of prior art products.The present invention realizes by the following technical solutions.
A kind of non-woven fibrous plate, be by multiple different staple fibre mix, through the needling process moulding and through the sheet material of heating process typing, it is characterized in that described mixing staple fibre is to be mixed by the polyester fiber of weight ratio 50%~60%, 20%~30% polyacrylonitrile fibre, 15%~25% polypropylene fibre to constitute.
A kind of manufacture method of non-woven fibrous plate, the short fiber material shredding that it is characterized in that to mix, make fiber web after dividing comb processing, fiber web is knitted through close acupuncture on needing machine, make base cloth with required thickness, base cloth is heated to the polypropylene fibre fusing, through hot pressing, making the base cloth surfacing and make the correction of base cloth thickness to product thickness then, just is the fibrous plate finished product after the typing to be cooled.
The fibre-bearing amount of above-mentioned fibrous plate is preferably every square metre of 500~1200 gram; The thickness of fibrous plate generally can be at 1.0~5.0 millimeters; Above-mentioned different staple fibre mixes can be even admixture, also can be non-homogeneous admixture, non-homogeneous admixture is just like keeping under the constant situation of the total occupancy volume of polypropylene fibre, low and the polypropylene fibre ratio height of fibrous plate internal layer of the polypropylene fibre ratio on fibrous plate top layer is in order to the softness characteristics that improves the fibrous plate top layer and tough elasticity of internal layer or the like; The pin density that above-mentioned close acupuncture is knitted can be on every square centimeter on 700~1300 pins; Heating-up temperature is preferably in 170 ℃~190 ℃, and preferably be no less than 1.5 minutes heat time heating time.
The mixing staple fibre of technique scheme adopts 50%~60% polyester fiber, 20%~30% polyacrylonitrile fibre, 15%~25% polypropylene fibre mixes formation, because the cohesive force that interweaves mutually of polyester fiber is quite strong and have a good stiffness, and in mixing staple fibre, occupy higher proportion, become the thickness of base cloth all can be thicker with acupuncture so can be made into fibroreticulate thickness, on needing machine, just can disposable processing generate all thickness that the end requires in the footwear like this, and superpose without multilayer, need not be through gum dipping process, so not only can make work simplification, and the production efficiency height; Owing to have enough toughness and stiffness,, help improving the ventilative and perspire of product so simultaneously so just can reduce as the polypropylene fibre content of hot melt adhesive material; Because polyacrylonitrile fibre has softness characteristics and wool characteristic, can make fibrous plate can not give the people hard cold sensation, product surface has the cortex feel, the product specification height, the while also can strengthen the toughness of product.Just because of distinctive materials of the present invention and proportioning, thereby making the preparation method of fibrous plate become quite simplifies, once just can sting the base cloth that weaves required thickness on needing machine, this production for the end in the various footwear with different-thickness requirement just seems convenient especially and makes product neat and artistic; Whole manufacturing process is not a bit all used the major-minor material of chemical resin adhesive as product, and is hundred-percent fibrous structure, so fibrous plate of the present invention is real free of contamination environment-friendly products, it has the advantage of the tasteless mildew-resistant concentrated base of anti-the peracid; The gas permeability of product and perspire are also good especially, and the same equal time humidity volatile quantity under the uniform temperature can reach 92%; Needing ben be that the folding Qu Xingneng of the fibrous plate that generated by manufacture method of the present invention is good especially, measures through machinery, and the bent number of times of folding can reach more than ten times of general like product.As seen fibrous plate of the present invention is the special-purpose material in the end in a kind of desirable footwear, its good operating characteristic be prior art can not compare.
Below in conjunction with the specific embodiment the present invention is done to describe more specifically.The specific embodiment is a kind of giving an example of the present invention.
The specific embodiment: a kind of being used in bottom fiber sheet material in the footwear of high 30 millimeters women village footwear, its thickness is 1.25 millimeters, and the mixing staple fibre that constitutes fibrous plate is characterized in that being made up of the hollow polyester fibre of weight ratio 50%, 30% polyacrylonitrile fibre, 20% the two property polypropylene fibres of low melting point.The manufacture method of fibrous plate is characterized in that described mixing staple fibre is through shredding, make fiber web after dividing comb processing, then on needing machine with the needling density of every square centimeter on 800 pins, disposable thorn is made into and meets 1.25 millimeters desired base cloths of product thickness, base cloth fully heats with the hot blast of 175 ℃ of temperature in heating cabinet, approximately need 1.5 minutes heat time heating time, at this moment as the skin fusing of the two property polypropylene fibres of the low melting point of hot melt adhesive, with other fiber adhesion, base cloth is again through a pair of roll extrusion with cylinder of setting the gap, its surface becomes more smooth, its thickness also is compressed and is modified to product thickness, just can be the fibrous plate finished product after the typing to be cooled.In addition, keeping under the constant situation of the total occupancy volume of polypropylene fibre 20%, the polypropylene fibre ratio on fibrous plate top layer can be reduced to about 7%, and corresponding the uprising of polypropylene fibre ratio of fibrous plate internal layer can obviously be improved the softness characteristics on fibrous plate top layer and the elasticity and the toughness of internal layer.
Polyester fiber in this specific embodiment adopts hollow material, and the one, can alleviate panel weight, the 2nd, can improve softening of sheet material and endure elasticity; Polypropylene fibre adopts the two property materials of low melting point, be because the two property materials of low melting point have the characteristic that outer fusing point is low, the inside fusing point is high, in above-mentioned heat pressing process process, the top layer fusing of fiber is to reach the purpose of condensing with other fiber adhesion, the inside is not melted and can be kept former form of fiber and position, can improve the overall characteristic of fibrous plate like this.
Claims (10)
1, a kind of non-woven fibrous plate, be by multiple different staple fibre mix, through the needling process moulding and through the sheet material of heating process typing, it is characterized in that described mixing staple fibre is to be mixed by the polyester fiber of weight ratio 50%~60%, 20%~30% polyacrylonitrile fibre, 15%~25% polypropylene fibre to constitute.
2,, it is characterized in that described polypropylene fibre is two property polypropylene fibres by the described fibrous plate of claim 1.
3, by the described fibrous plate of claim 1, the fibre-bearing amount that it is characterized in that described fibrous plate is every square metre of 500~1200 gram.
4, by claim 1 or 3 described fibrous plates, the thickness that it is characterized in that described fibrous plate is 1.0~5.0 millimeters.
5, by the described fibrous plate of claim 1, it is characterized in that it is to be even admixture or non-homogeneous admixture that described multiple different staple fibre mixes.
6,, it is characterized in that the low and polypropylene fibre ratio height of fibrous plate internal layer of polypropylene fibre ratio that described non-homogeneous admixture is the fibrous plate top layer by the described fibrous plate of claim 5.
7, a kind of manufacture method of non-woven fibrous plate, the short fiber material shredding that it is characterized in that to mix, make fiber web after dividing comb processing, fiber web is knitted through close acupuncture on needing machine, make base cloth with required thickness, base cloth is heated to the polypropylene fibre fusing, through hot pressing, making the base cloth surfacing and make the correction of base cloth thickness to product thickness then, just is the fibrous plate finished product after the typing to be cooled.
8, by the described manufacture method of claim 7, it is characterized in that the pin density that described close acupuncture is knitted can be on every square centimeter on 700~1300 pins.
9, by the described manufacture method of claim 8, it is characterized in that described heating-up temperature is 170 ℃~190 ℃, is no less than 1.5 minutes heat time heating time.
10, by claim 7,8 or 9 described manufacture methods, it is characterized in that described heating is to heat with hot blast in heating cabinet.