CN112563880B - Green light source based on multifunctional fluorescent ceramic - Google Patents
Green light source based on multifunctional fluorescent ceramic Download PDFInfo
- Publication number
- CN112563880B CN112563880B CN202011561206.3A CN202011561206A CN112563880B CN 112563880 B CN112563880 B CN 112563880B CN 202011561206 A CN202011561206 A CN 202011561206A CN 112563880 B CN112563880 B CN 112563880B
- Authority
- CN
- China
- Prior art keywords
- fluorescent ceramic
- ceramic
- lens
- green light
- fluorescent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a green light source based on multifunctional fluorescent ceramic, which comprises a laser, a heat dissipation substrate, a lens, an optical fiber, fluorescent ceramic and a shell. Blue light emitted by the laser enters the optical fiber through the lens in a coupling mode, the blue light is transmitted to the surface of the fluorescent ceramic through the optical fiber, the fluorescent ceramic is excited to become green light, and then the green light source with high brightness is output through shaping of the fluorescent ceramic. The fluorescent ceramic is in a plano-convex lens shape, integrates light emitting and shaping, saves lighting elements and has higher brightness.
Description
Technical Field
The invention relates to the field of laser illumination, in particular to a green light source based on a multifunctional fluorescent ceramic material.
Background
Green light has wide applications in biology, industry, printing, medical treatment, storage, display, military and the like. To obtain a high brightness green light source, there are generally two schemes: the laser device adopts a green light semiconductor laser or combines the green light semiconductor laser and adopts a blue light laser excitation light conversion material. Both relate to the field of laser lighting.
In the first technical scheme, excellent laser spectrum and beam characteristics can be obtained, and high-energy green light output can be obtained. However, green lasers require a higher indium fraction than blue lasers; the main physical changes are induced, so that the lattice constant changes and the band gap is shortened, the light output power is reduced, and the price is high. If the optical output power is improved by adopting the scheme of combining optical fibers, the price and the cost are also improved, and the cost performance is not high. Meanwhile, the green light is laser, can only be used for laser medical treatment or laser projection after expanding the beam, and is not suitable for being applied to the general illumination field.
The second solution has significant advantages. The cost is low, and the process is simple; on the premise of keeping the stable luminescence of the light conversion material, the higher brightness can be obtained only by increasing the power of the blue laser. In recent years, domestic scholars develop blue-light semiconductor lasers following world trends, mass production is achieved at present, and cost is further reduced; meanwhile, the research on the light conversion materials in China is continuously expanded, and the mass production can be realized from fluorescent powder to fluorescent glass and then to fluorescent ceramic.
One of the fluorescence conversion schemes is to focus blue light with a lens for transmission to the surface of the fluorescent ceramic and then excite the fluorescent ceramic; the other is that the optical fiber conducts the blue laser light to the surface of the fluorescent ceramic, and then excites the fluorescent ceramic. Compared with the former, the scheme of conducting laser blue light by the optical fiber can separate two heat sources, namely an excitation source and an emission source, and carry out heat dissipation treatment independently; the relative position of the two can be adjusted at will, and the design flexibility is high. Meanwhile, the optical fiber directly guides out the blue light, and compared with a mode of focusing the blue light on the surface of the ceramic by adopting a lens, the system stability is better. However, the two schemes for fluorescence conversion have the following problems: 1) the optical system is still relatively complex; 2) aiming at the fluorescent ceramic, secondary optical design elements are also needed to be adopted to induce luminescence, and related heat dissipation devices are designed to stabilize the operation of devices. Therefore, the fluorescence conversion green light source needs to be further designed and extended to obtain a high-brightness green light source.
Disclosure of Invention
Aiming at the problems in the prior art, the invention provides a green light source for laser illumination based on multifunctional fluorescent ceramics, and the composition of a laser illumination light source system is simplified.
In order to achieve the purpose, the invention adopts the following technical scheme:
a green light source based on multifunctional fluorescent ceramic comprises a laser, a heat dissipation substrate, a lens, an optical fiber, fluorescent ceramic and a shell.
The fluorescent ceramic is in a plano-convex lens shape and integrates light emitting and shaping into a whole; the blue light emitted by the laser enters the optical fiber through the lens in a coupling mode, the blue light is transmitted to the surface of the fluorescent ceramic through the optical fiber, the fluorescent ceramic is excited to become green light, and the generated green light is shaped by the fluorescent ceramic to become parallel light beams.
Preferably, the wavelength emitted by the laser is 450-465 nm;
preferably, the heat dissipation substrate is made of red copper or aluminum;
preferably, the lens is one of a spherical lens and a graded index lens;
preferably, the fluorescent ceramic is Ce: LuAG fluorescent ceramic; the doping concentration of Ce is 0.05-1.0 at%.
Preferably, the manufacturing method of the plano-convex lens type fluorescent ceramic is gel casting molding and vacuum sintering; namely the optical design is combined with the preparation process. The specific manufacturing steps are as follows:
proportioning according to the stoichiometric ratio of LuAG fluorescent ceramic with Ce doping concentration of 0.05-1.0 at%, and weighing Al 2 O 3 、Lu 2 O 3 、CeO 2 Adding absolute ethyl alcohol, an Isobam104 solution, ammonium citrate and a Polyethyleneimine (PEI) solution for ball milling; the ball milling medium is Al 2 O 3 And (3) performing ball milling for 2 hours at a ball milling rotation speed of 160-200 r/min to obtain mixed slurry. Wherein the absolute ethyl alcohol accounts for 1-1.5 times of the total mass of the raw material powder; the Isobam104 solution is 0.025-0.06 time of the total mass of the raw material powder; the ammonium citrate is 0.02-0.05 time of the total mass of the raw material powder.
And (5) gel injection molding. Pouring the slurry into a mold to obtain a ceramic biscuit; the mold is in the shape of a plano-convex lens.
And (3) drying: the temperature is 25-50 ℃, and the heat preservation time is 30 min.
Pre-burning: the temperature is 750-800 ℃, and the heat preservation time is 8 h.
And (3) vacuum sintering: the temperature is 1800-1820 ℃, and the heat preservation time is 8 h.
Annealing: the temperature is 1400-1450 ℃, and the heat preservation time is 12 h.
Polishing: the surface roughness Ra is 0.05-0.10.
The diameter phi of the finally obtained multifunctional fluorescent ceramic is 20-50 mm; the focal length f = 30-50 mm.
Preferably, the transmittance of the fluorescent ceramic at 555 nm is 80.0-84.8%.
Preferably, the shell is made of metal.
Compared with the prior art, the invention has the following beneficial effects:
1. by combining optical design with material preparation process, the ceramic material is designed into a device integrating multiple functions of fluorescence conversion, lens and beam shaping. The innovation is a combination process of the preparation process of the ceramic and the back-end application, and is a combination process of materials science and optics. In addition, the design greatly simplifies the structure of the laser illumination light source system; after the optical fiber emits light, laser is excited by a point, and the generated green fluorescence can be directly used for illumination, so that the loss caused by the use of an optical device is greatly reduced.
2. Under the excitation of the blue light with small light spots, the high-transmittance fluorescent ceramic device has higher transmittance than a translucent or opaque fluorescent conversion device, and the scattering effect is correspondingly weakened, so that the light-emitting area of a light source is smaller, a light source with higher brightness is generated, and the shaping is easy.
3. The fluorescent ceramic has higher heat conductivity, and the surrounding ceramic can be used as a heat dissipation element for conducting heat generated by the luminous point, so that the metal heat sink design of the ceramic is omitted.
Drawings
FIGS. 1-2 are schematic diagrams of a green light source based on multifunctional fluorescent ceramics;
in the figure: 1 laser, 2 heat dissipation substrate, 3 lens, 4 optical fiber, 5 fluorescent ceramic and 6 shell.
Detailed Description
Example 1:
a laser display green light source based on multifunctional fluorescent ceramic is shown in figures 1 and 2 and comprises a laser 1, a heat dissipation substrate 2, a lens 3, an optical fiber 4, fluorescent ceramic 5 and a shell 6.
The wavelength emitted by the laser 1 is 450 nm; the heat dissipation substrate 2 is made of red copper; the lens 3 is a spherical lens; the fluorescent ceramic 5 is Ce-LuAG fluorescent ceramic, and the doping concentration of Ce is 0.05 at%; the housing 6 is a metal housing.
The fluorescent ceramic is in a plano-convex lens shape, and the manufacturing method is 'gel casting molding + vacuum sintering'; the preparation method comprises the following specific steps:
(1) proportioning according to the stoichiometric ratio of LuAG fluorescent ceramic with Ce doping concentration of 0.05 at%, and weighing Al 2 O 3 、Lu 2 O 3 、CeO 2 Adding absolute ethyl alcohol, an Isobam104 solution, ammonium citrate and a Polyethyleneimine (PEI) solution for ball milling; the ball milling medium is Al 2 O 3 And (4) performing ball milling for 2 hours at the ball milling rotating speed of 160 r/min to obtain mixed slurry. Wherein the absolute ethyl alcohol accounts for 1 time of the total mass of the raw material powder; the Isobam104 solution is 0.025 times of the total mass of the raw material powder; the ammonium citrate is 0.02 times of the total mass of the raw material powder.
(2) Gel casting: pouring the slurry into a mold to obtain a ceramic biscuit; the mold is in the shape of a plano-convex lens.
(3) And (3) drying: the temperature is 25 ℃, and the heat preservation time is 30 min.
(4) Pre-burning: the temperature is 750 ℃, and the heat preservation time is 8 h.
(5) And (4) vacuum sintering. The temperature is 1800 ℃ and the heat preservation time is 8 h.
(6) Annealing: the temperature is 1400 ℃, and the heat preservation time is 12 h.
(7) Polishing: the surface roughness Ra was 0.05.
The diameter phi of the finally obtained lens type fluorescent ceramic is 20 mm; focal length f =30 mm; the transmittance at 555 nm is 80.0 percent, and the product meets the requirement of a lens type fluorescent ceramic device. Blue light emitted by the laser 1 is coupled into the optical fiber 4 through the lens 3, the blue light is transmitted to the surface of the fluorescent ceramic 5 through the optical fiber 4, the fluorescent ceramic 5 is excited to become green light, and the generated green light forms a high-brightness light spot at a position of 30 mm through the shaping of the fluorescent ceramic 5.
Example 2:
a laser display green light source based on multifunctional fluorescent ceramic comprises a laser, a heat dissipation substrate, a lens, an optical fiber, fluorescent ceramic and a shell.
The wavelength emitted by the laser is 465 nm; the heat dissipation substrate is made of aluminum; the lens is a graded index lens; the fluorescent ceramic is Ce: LuAG fluorescent ceramic; the doping concentration of Ce is 1.0 at%; the shell is a metal shell.
The fluorescent ceramic is in a plano-convex lens shape, and the manufacturing method is 'gel casting molding + vacuum sintering'; the preparation method comprises the following specific steps:
(1) proportioning according to the stoichiometric ratio of LuAG fluorescent ceramics with the Ce doping concentration of 1.0at percent, and weighing Al 2 O 3 、Lu 2 O 3 、CeO 2 Adding absolute ethyl alcohol, an Isobam104 solution, ammonium citrate and a Polyethyleneimine (PEI) solution for ball milling; the ball milling medium is Al 2 O 3 And (4) performing ball milling for 2 hours at the ball milling rotating speed of 200r/min to obtain mixed slurry. Wherein the absolute ethyl alcohol accounts for 1.5 times of the total mass of the raw material powder; the Isobam104 solution is 0.06 time of the total mass of the raw material powder; the ammonium citrate is 0.05 time of the total mass of the raw material powder.
(2) And (4) gel injection molding. Pouring the slurry into a mold to obtain a ceramic biscuit; the mold is in the shape of a plano-convex lens.
(3) And (3) drying: the temperature is 50 ℃, and the heat preservation time is 30 min.
(4) Pre-burning: the temperature is 800 ℃, and the heat preservation time is 8 h.
(4) And (3) vacuum sintering: the temperature is 1820 ℃, and the holding time is 8 h.
(6) Annealing: the temperature is 1450 ℃, and the heat preservation time is 12 h.
(6) Polishing: the surface roughness Ra was 0.10.
The diameter phi of the finally obtained multifunctional fluorescent ceramic is 50 mm; focal length f =50 mm; a transmittance at 555 nm of 84.8%; satisfies the requirement of a lens type fluorescent ceramic device. Blue light emitted by the laser enters the optical fiber through the lens in a coupling mode, the blue light is transmitted to the surface of the fluorescent ceramic through the optical fiber, the fluorescent ceramic is excited to become green light, and the generated green light forms high-brightness light spots at the position of 50 mm through the shaping of the fluorescent ceramic.
Example 3:
a laser display green light source based on multifunctional fluorescent ceramic comprises a laser, a heat dissipation substrate, a lens, an optical fiber, fluorescent ceramic and a shell.
The wavelength emitted by the laser is 460 nm; the heat dissipation substrate is made of aluminum; the lens is a spherical lens; the fluorescent ceramic is Ce: LuAG fluorescent ceramic; the doping concentration of Ce is 0.1 at%; the shell is a metal shell.
The fluorescent ceramic is in a plano-convex lens shape, and the manufacturing method is 'gel casting molding + vacuum sintering'; the preparation method comprises the following specific steps:
(1) proportioning according to the stoichiometric ratio of LuAG fluorescent ceramics with Ce doping concentration of 0.1 at%, and weighing Al 2 O 3 、Lu 2 O 3 、CeO 2 Adding absolute ethyl alcohol, an Isobam104 solution, ammonium citrate and a Polyethyleneimine (PEI) solution for ball milling; the ball milling medium is Al 2 O 3 And (4) performing ball milling for 2 hours at the ball milling rotating speed of 180 r/min to obtain mixed slurry. Wherein the absolute ethyl alcohol accounts for 1.2 times of the total mass of the raw material powder; the Isobam104 solution is 0.01 time of the total mass of the raw material powder; the ammonium citrate is 0.01 time of the total mass of the raw material powder.
(2) And (5) gel injection molding. Pouring the slurry into a mold to obtain a ceramic biscuit; the mold is in the shape of a plano-convex lens.
(3) And (3) drying: the temperature is 40 ℃, and the heat preservation time is 30 min.
(4) Pre-burning: the temperature is 780 ℃ and the heat preservation time is 8 h.
(4) And (3) vacuum sintering: the temperature is 1810 ℃ and the heat preservation time is 8 h.
(6) Annealing: the temperature is 1425 ℃, and the holding time is 12 h.
(6) Polishing: the surface roughness Ra was 0.07.
The diameter phi of the finally obtained multifunctional fluorescent ceramic is 40 mm; focal length f =40 mm; a transmittance at 555 nm of 84.8%; satisfies the requirement of a lens type fluorescent ceramic device. Blue light emitted by the laser enters the optical fiber through the lens in a coupling mode, the blue light is transmitted to the surface of the fluorescent ceramic through the optical fiber, the fluorescent ceramic is excited to become green light, and the generated green light forms high-brightness light spots at the position of 40 mm through shaping of the fluorescent ceramic.
Example 4:
a laser display green light source based on multifunctional fluorescent ceramic comprises a laser, a heat dissipation substrate, a lens, an optical fiber, fluorescent ceramic and a shell.
The wavelength emitted by the laser is 450 nm; the heat dissipation substrate is made of aluminum; the lens is a graded index lens; the fluorescent ceramic is Ce: LuAG fluorescent ceramic; the doping concentration of Ce is 1.0 at%; the shell is a metal shell.
The fluorescent ceramic is in a plano-convex lens shape, and the manufacturing method is 'gel casting molding + vacuum sintering'; the preparation method comprises the following specific steps:
(1) proportioning according to the stoichiometric ratio of LuAG fluorescent ceramic with the Ce doping concentration of 1.0at%, and weighing Al 2 O 3 、Lu 2 O 3 、CeO 2 Adding absolute ethyl alcohol, an Isobam104 solution, ammonium citrate and a Polyethyleneimine (PEI) solution for ball milling; the ball milling medium is Al 2 O 3 And (4) performing ball milling for 2 hours at the ball milling rotating speed of 200r/min to obtain mixed slurry. Wherein the absolute ethyl alcohol accounts for 1.5 times of the total mass of the raw material powder; the Isobam104 solution is 0.01 time of the total mass of the raw material powder; the ammonium citrate is 0.06 time of the total mass of the raw material powder.
(2) Gel casting: pouring the slurry into a mold to obtain a ceramic biscuit; the mold is in the shape of a plano-convex lens.
(3) And (3) drying: the temperature is 50 ℃, and the heat preservation time is 30 min.
(4) Pre-burning: the temperature is 800 ℃, and the heat preservation time is 8 h.
(4) And (3) vacuum sintering: the temperature is 1790 ℃, and the heat preservation time is 8 h.
(6) Annealing: the temperature is 1450 ℃, and the heat preservation time is 12 h.
(6) And (6) polishing. The surface roughness Ra was 0.10.
The diameter phi of the finally obtained multifunctional fluorescent ceramic is 50 mm; focal length f =50 mm; the transmittance at 555 nm is 60%, which does not satisfy the requirement of a lens type fluorescent ceramic device. The main reason is that the content of ammonium citrate as a dispersant is too high, the activity of the powder is very strong, but the sintering temperature is too low, so that the optical quality of the ceramic is not high, and the lens type fluorescent ceramic device cannot be successfully prepared.
Blue light emitted by the laser enters the optical fiber through the lens in a coupling mode, the blue light is transmitted to the surface of the fluorescent ceramic through the optical fiber to excite the fluorescent ceramic to become green light, the generated green light is diffused at a position of 50 mm through the shaping of the fluorescent ceramic, the convergence function is not achieved, and high-brightness light spots cannot be obtained.
Claims (1)
1. A green light source based on multifunctional fluorescent ceramic is characterized by comprising a laser (1), a heat dissipation substrate (2), a lens (3), an optical fiber (4), fluorescent ceramic (5) and a shell (6);
the fluorescent ceramic (5) is in a plano-convex lens shape and integrates light emitting and shaping into a whole; the wavelength emitted by the laser (1) is 465 nm, the blue light emitted by the laser (1) is coupled into the optical fiber (4) through the lens (3), the blue light is transmitted to the surface of the fluorescent ceramic (5) through the optical fiber (4), the fluorescent ceramic (5) is excited to become green light, and then the green light source with high brightness is obtained through the shaping of the fluorescent ceramic (5); the heat dissipation substrate (2) is made of aluminum; the lens (3) is a graded index lens; the shell (6) is a metal shell;
the fluorescent ceramic (5) is Ce: LuAG fluorescent ceramic, the doping concentration of Ce is 1.0at%, and the preparation steps of the fluorescent ceramic (5) are as follows:
(1) proportioning according to the stoichiometric ratio of LuAG fluorescent ceramics with the Ce doping concentration of 1.0at percent, and weighing Al 2 O 3 、Lu 2 O 3 、CeO 2 Adding absolute ethyl alcohol, an Isobam104 solution, ammonium citrate and a polyethyleneimine solution for ball milling; the ball milling medium isAl 2 O 3 Ball milling is carried out for 2 hours at the ball milling rotation speed of 200r/min to obtain mixed slurry; wherein the absolute ethyl alcohol accounts for 1.5 times of the total mass of the raw material powder; the Isobam104 solution is 0.06 time of the total mass of the raw material powder; ammonium citrate is 0.05 time of the total mass of the raw material powder;
(2) gel casting: pouring the slurry into a mold to obtain a ceramic biscuit; the mould is in a plano-convex lens shape;
(3) and (3) drying: keeping the temperature at 50 ℃ for 30 min;
(4) pre-burning: the temperature is 800 ℃, and the heat preservation time is 8 hours;
(4) vacuum sintering: the temperature is 1820 ℃, and the heat preservation time is 8 h;
(6) annealing: the temperature is 1450 ℃, and the heat preservation time is 12 h;
(7) polishing: the surface roughness Ra is 0.10;
the diameter phi of the obtained fluorescent ceramic (5) is 50 mm, the focal length f is 50 mm, and the transmittance of the fluorescent ceramic (5) at 555 nm is 84.8%; blue light emitted by the laser enters the optical fiber through the lens in a coupling mode, the blue light is transmitted to the surface of the fluorescent ceramic through the optical fiber, the fluorescent ceramic is excited to become green light, and the generated green light forms high-brightness light spots at the position of 50 mm through the shaping of the fluorescent ceramic.