CN112476072B - Preparation method of optical glass with high light transmittance and high stability - Google Patents
Preparation method of optical glass with high light transmittance and high stability Download PDFInfo
- Publication number
- CN112476072B CN112476072B CN202011466943.5A CN202011466943A CN112476072B CN 112476072 B CN112476072 B CN 112476072B CN 202011466943 A CN202011466943 A CN 202011466943A CN 112476072 B CN112476072 B CN 112476072B
- Authority
- CN
- China
- Prior art keywords
- optical glass
- polishing
- machine
- putting
- cerium oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a preparation method of optical glass with high light transmittance and high stability. According to the invention, the polishing process and the components of the polishing agent in the traditional optical glass preparation process are improved, the lithium oxide with a proper amount is added on the basis of the conventional cerium oxide, and the secondary polishing process is adopted, so that the light transmittance and the stability of the finished optical glass are obviously improved, and the preparation process is simple, low in production cost and suitable for industrial large-scale production.
Description
Technical Field
The invention belongs to the technical field of optics, and particularly relates to a preparation method of optical glass with high light transmittance and high stability.
Background
Optical glass refers to glass that can change the direction of light propagation and can change the relative spectral distribution of ultraviolet, visible, or infrared light. Optical glass in a narrow sense means colorless optical glass; the optical glass in a broad sense also includes colored optical glass, laser glass, quartz optical glass, radiation-resistant glass, ultraviolet infrared optical glass, fiber optical glass, acousto-optic glass, magneto-optic glass and photochromic glass. The optical glass can be used for manufacturing lenses, prisms, reflectors, windows and the like in optical instruments. Components made of optical glass are critical elements in optical instruments.
Optical glass is a fundamental and important component of the photovoltaic technology industry. Particularly, after the 90 s of the 20 th century, along with the continuous fusion of optics, electronic information science and new material science, the application of optical glass as a photoelectronic base material in three fields of optical transmission, optical storage and photoelectric display is more rapid and rapid, and the optical glass becomes one of the basic conditions for the development of social informatization, particularly photoelectric information technology. The optical glass is prepared by mainly using high-quality quartz sand as a main material and properly adding auxiliary materials.
With the development of science and technology, optical glass is used more and more widely, for example, in the manufacture of optical instruments such as cameras, video cameras, telescopes, etc., and daily optical articles such as myopia glasses, presbyopic glasses, etc., and the applications in these fields usually have higher requirements on refractive index, dispersion ratio, precision, light transmittance, chemical stability, etc. of the optical glass. However, in the actual production and application process, the quality of the prepared optical glass finished product is often uneven due to the difference of the polishing agent and the polishing process, and the problems of low light transmittance, poor stability, easy aging and yellowing and the like occur, so that the application of the optical glass finished product in some high-precision fields is greatly limited.
Disclosure of Invention
The invention aims to solve the problems of low precision, poor weather resistance and the like in the preparation process of the optical glass in the prior art, and improves the type of a polishing agent and the polishing process in the polishing process of the optical glass, so that the light transmittance of the finished optical glass is obviously improved, the stability of the finished optical glass is improved, and meanwhile, the preparation process is simple, the production cost is low, and the method is suitable for industrial large-scale production.
In order to achieve the purpose, the invention is realized by the following means:
the invention provides a preparation method of optical glass with high light transmittance and high stability, which comprises the following steps:
(1) cutting the optical glass into a preset size required by a drawing through a cutting machine, and then chamfering on a sand wheel of the cutting machine;
(2) finely grinding the cut optical glass;
(3) placing the finely ground optical glass into a polishing machine, and performing pre-polishing on the optical glass by using a polishing agent;
(4) putting the polished optical glass into an ultrasonic cleaner for cleaning;
(5) putting the cleaned optical glass into a polishing machine again, and further polishing the optical glass by using a polishing agent to remove impurities and bubbles with uneven surfaces on the optical glass; carrying out QC (quality control) inspection on the pre-polished optical glass, and removing defective products;
(6) putting the optical glass qualified after secondary polishing into an ultrasonic cleaning machine for cleaning;
(7) putting the optical glass cleaned in the step (6) on an engraving and milling machine to be manufactured into a shape required by a drawing;
(8) tempering the optical glass in a tempering pot to increase the surface hardness of the optical glass;
(9) finished product warehousing procedure: and (5) detecting the finished optical glass, and warehousing qualified products.
Preferably, step (2) is performed by using corundum.
Preferably, the polishing agent in step (3) comprises cerium oxide and a solvent.
Preferably, the concentration of cerium oxide in step (3) is 1.08-1.12%.
Preferably, the solvent in step (3) is selected from water.
Preferably, the washing time in step (4) is 5 to 10 minutes.
Preferably, the polishing agent in step (5) comprises cerium oxide, lithium oxide and a solvent.
Preferably, in the step (5), the concentration of the cerium oxide is 1.08 to 1.12%, and the concentration of the lithium oxide is 0.05 to 0.08%.
Preferably, the solvent in step (5) is selected from water.
Preferably, the washing time in step (6) is 10 to 30 minutes.
Preferably, the step (8) uses potassium nitrate to perform the toughening operation, the toughening temperature is 415-450 ℃, and the toughening time can be adjusted according to the requirement on the hardness of the optical glass.
Optionally, after the optical glass is tempered in the step (8), an ink screen printing operation can be further performed, wherein the ink screen printing operation is performed by a semi-automatic or manual screen printing machine.
Optionally, after the optical glass is subjected to the ink screen printing operation, a gluing operation may be further performed, specifically: gluing a plurality of optical glasses into a shape required by a drawing by using glue, and then baking the optical glasses in a UV lamp curing oven to accelerate the curing speed of the glue; the illumination intensity of the UV lamp and the baking temperature and time are determined according to the selection of the glue and the stability of the optical glass.
Compared with the prior art, the invention has the following beneficial effects:
according to the invention, the polishing process and the components of the polishing agent in the traditional optical glass preparation process are improved, the lithium oxide with a proper amount is added on the basis of the conventional cerium oxide, and the secondary polishing process is adopted, so that the light transmittance and the stability of the finished optical glass are obviously improved, and the preparation process is simple, low in production cost and suitable for industrial large-scale production.
Detailed Description
In order to make the objects, technical solutions and effects of the present invention clearer and clearer, the present invention is further described in detail below with reference to examples. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention.
Example 1
A preparation method of optical glass with high light transmittance and high stability comprises the following steps:
(1) cutting the optical glass into a preset size required by a drawing through a cutting machine, and then chamfering on a sand wheel of the cutting machine;
(2) finely grinding the cut optical glass by adopting carborundum;
(3) putting the finely ground optical glass into a polishing machine, and performing pre-polishing on the optical glass by using a polishing agent; the polishing agent comprises 1.08% by mass of cerium oxide and the balance of water;
(4) putting the polished optical glass into an ultrasonic cleaning machine for cleaning for 5 minutes;
(5) putting the cleaned optical glass into a polishing machine again, and further polishing the optical glass by using a polishing agent to remove impurities and bubbles with uneven surfaces on the optical glass; carrying out QC (quality control) inspection on the optical glass after pre-polishing, and removing defective products; the polishing agent comprises 1.08% of cerium oxide and 0.05% of lithium oxide by mass percentage, and the balance of water;
(6) putting the optical glass qualified after secondary polishing into an ultrasonic cleaning machine for cleaning for 10 minutes;
(7) putting the optical glass cleaned in the step (6) on an engraving and milling machine to be manufactured into a shape required by a drawing;
(8) tempering the optical glass in a tempering pot by using potassium nitrate at the tempering temperature of 415 ℃ so as to increase the surface hardness of the optical glass;
(9) finished product warehousing procedure: and (5) detecting the finished optical glass, and warehousing qualified products.
Example 2
A preparation method of optical glass with high light transmittance and high stability comprises the following steps:
(1) cutting the optical glass into a preset size required by a drawing through a cutting machine, and then chamfering on a sand wheel of the cutting machine;
(2) finely grinding the cut optical glass by using carborundum;
(3) placing the finely ground optical glass into a polishing machine, and performing pre-polishing on the optical glass by using a polishing agent; the polishing agent comprises 1.1% by mass of cerium oxide, and the balance of water;
(4) putting the polished optical glass into an ultrasonic cleaning machine for cleaning for 8 minutes;
(5) putting the cleaned optical glass into a polishing machine again, and further polishing the optical glass by using a polishing agent to remove impurities and bubbles with uneven surfaces on the optical glass; carrying out QC (quality control) inspection on the optical glass after pre-polishing, and removing defective products; the polishing agent comprises 1.10% of cerium oxide and 0.06% of lithium oxide by mass percent, and the balance of water;
(6) putting the optical glass qualified after the secondary polishing into an ultrasonic cleaning machine for cleaning for 20 minutes;
(7) placing the optical glass cleaned in the step (6) on an engraving and milling machine to perform engraving and milling to form the shape required by the drawing;
(8) tempering the optical glass in a tempering pot by using potassium nitrate at the tempering temperature of 430 ℃ so as to increase the surface hardness of the optical glass;
(9) finished product warehousing procedure: and (5) detecting the finished optical glass, and warehousing qualified products.
Example 3
A preparation method of optical glass with high light transmittance and high stability comprises the following steps:
(1) cutting the optical glass into a preset size required by a drawing through a cutting machine, and then chamfering on a sand wheel of the cutting machine;
(2) finely grinding the cut optical glass by adopting carborundum;
(3) placing the finely ground optical glass into a polishing machine, and performing pre-polishing on the optical glass by using a polishing agent; the polishing agent comprises 1.12% by mass of cerium oxide, and the balance of water;
(4) putting the polished optical glass into an ultrasonic cleaning machine for cleaning for 10 minutes;
(5) putting the cleaned optical glass into a polishing machine again, and further polishing the optical glass by using a polishing agent to remove impurities and bubbles with uneven surfaces on the optical glass; carrying out QC (quality control) inspection on the optical glass after pre-polishing, and removing defective products; the polishing agent comprises 1.10% of cerium oxide and 0.08% of lithium oxide by mass percent, and the balance of water;
(6) putting the optical glass qualified after secondary polishing into an ultrasonic cleaning machine for cleaning for 30 minutes;
(7) putting the optical glass cleaned in the step (6) on an engraving and milling machine to be manufactured into a shape required by a drawing;
(8) tempering the optical glass in a tempering pot by using potassium nitrate at the tempering temperature of 450 ℃ so as to increase the surface hardness of the optical glass;
(9) finished product warehousing procedure: and (5) detecting the finished optical glass, and warehousing qualified products.
Comparative example 1
A method for preparing optical glass comprises the following steps:
(1) cutting the optical glass into a preset size required by a drawing through a cutting machine, and then chamfering on a sand wheel of the cutting machine;
(2) finely grinding the cut optical glass by using carborundum;
(3) putting the finely ground optical glass into a polishing machine, and polishing the optical glass by using a polishing agent; removing impurities and bubbles on the surface of the optical glass, wherein the impurities and the bubbles are uneven; carrying out QC (quality control) inspection on the optical glass after pre-polishing, and removing defective products; the polishing agent comprises 1.08% by mass of cerium oxide and the balance of water;
(4) putting the polished optical glass into an ultrasonic cleaning machine for cleaning for 5 minutes;
(5) putting the optical glass cleaned in the step (4) on an engraving and milling machine to be manufactured into a shape required by a drawing;
(6) tempering the optical glass in a tempering pot by using potassium nitrate at the tempering temperature of 415 ℃ so as to increase the surface hardness of the optical glass;
(7) finished product warehousing procedure: and (5) detecting the finished optical glass, and warehousing qualified products.
Comparative example 2
A method for preparing optical glass comprises the following steps:
(1) cutting the optical glass into a preset size required by a drawing through a cutting machine, and then chamfering on a sand wheel of the cutting machine;
(2) finely grinding the cut optical glass by using carborundum;
(3) putting the finely ground optical glass into a polishing machine, polishing the optical glass by using a polishing agent, and removing impurities and bubbles with uneven surfaces on the optical glass; carrying out QC (quality control) inspection on the optical glass after pre-polishing, and removing defective products; the polishing agent comprises 1.08% of cerium oxide and 0.05% of lithium oxide by mass percentage, and the balance of water;
(4) putting the polished optical glass into an ultrasonic cleaning machine for cleaning for 5 minutes;
(5) placing the optical glass cleaned in the step (4) on an engraving and milling machine to be engraved into a shape required by a drawing;
(6) tempering the optical glass in a tempering pot by using potassium nitrate at the tempering temperature of 415 ℃ so as to increase the surface hardness of the optical glass;
(7) finished product warehousing procedure: and (5) detecting the finished optical glass, and warehousing qualified products.
Comparative example 3
A method for preparing optical glass comprises the following steps:
(1) cutting the optical glass into a preset size required by a drawing through a cutting machine, and then chamfering on a sand wheel of the cutting machine;
(2) finely grinding the cut optical glass by using carborundum;
(3) putting the finely ground optical glass into a polishing machine, and performing pre-polishing on the optical glass by using a polishing agent; the polishing agent comprises 1.08% by mass of cerium oxide and the balance of water;
(4) putting the polished optical glass into an ultrasonic cleaning machine for cleaning for 5 minutes;
(5) putting the cleaned optical glass into a polishing machine again, and further polishing the optical glass by using a polishing agent to remove impurities and bubbles with uneven surfaces on the optical glass; carrying out QC (quality control) inspection on the pre-polished optical glass, and removing defective products; the polishing agent comprises 1.08% by mass of cerium oxide, and the balance of water;
(6) putting the optical glass qualified after secondary polishing into an ultrasonic cleaning machine for cleaning for 10 minutes;
(7) placing the optical glass cleaned in the step (6) on an engraving and milling machine to perform engraving and milling to form the shape required by the drawing;
(8) tempering the optical glass in a tempering pot by using potassium nitrate at the tempering temperature of 415 ℃ so as to increase the surface hardness of the optical glass;
(9) finished product warehousing procedure: and (5) detecting the finished optical glass, and warehousing qualified products.
Verification example 1
The optical glasses prepared in examples 1 to 3 and comparative examples 1 to 3 were respectively subjected to a performance test, and the test results are shown in table 1 below.
TABLE 1 results of testing the Properties of optical glasses of examples 1 to 3 and comparative examples 1 to 3
| Surface roughness Rz (. mu.m) | Visible light transmittance (%) | Coefficient of dispersion | Yellowing of the color of the product after 12 months of ultraviolet irradiation | |
| Example 1 | 0.011 | 99.0 | 42.9 | Without change |
| Example 2 | 0.009 | 98.8 | 40.7 | Without change |
| Example 3 | 0.013 | 99.1 | 43.1 | Without change |
| Comparative example 1 | 0.036 | 89.4 | 25.7 | Yellowing of |
| Comparative example 2 | 0.028 | 91.2 | 26.1 | Yellowing of |
| Comparative example 3 | 0.027 | 92.5 | 30.8 | Yellowing of |
The results show that the optical glasses prepared according to examples 1 to 3 of the present invention are significantly superior to those of comparative examples 1 to 3 in terms of surface roughness, visible light transmittance, dispersion coefficient and yellowing resistance. The reason is that comparative example 1 only adopts a single polishing process, and the polishing agent only uses cerium oxide, and comparative example 2 has an unsatisfactory effect despite the addition of lithium oxide to the polishing agent; comparative example 3, although the secondary polishing process was used, only cerium oxide was used as a polishing agent, and thus there was a significant gap in the properties and stability of the optical glass prepared in comparison with the present invention. Therefore, the optical glass obtained by the preparation process disclosed by the invention has the advantages that the light transmittance and stability of the finished optical glass are remarkably improved due to the improvement of the polishing process and the components of the polishing agent, and meanwhile, the preparation process is simple, the production cost is low, and the preparation process is suitable for industrial large-scale production.
The above detailed description section specifically describes the analysis method according to the present invention. It should be noted that the above description is only for the purpose of helping those skilled in the art better understand the method and idea of the present invention, and not for the limitation of the related contents. The present invention can be appropriately adjusted or modified by those skilled in the art without departing from the principle of the present invention, and the adjustment and modification should also fall within the protection scope of the present invention.
Claims (5)
1. A preparation method of optical glass with high light transmittance and high stability comprises the following steps:
(1) cutting the optical glass into a preset size required by a drawing through a cutting machine, and then chamfering on a grinding wheel of the cutting machine;
(2) finely grinding the cut optical glass;
(3) placing the finely ground optical glass into a polishing machine, and performing pre-polishing on the optical glass by using a polishing agent; the polishing agent comprises cerium oxide and water, wherein the concentration of the cerium oxide is 1.08-1.12%;
(4) putting the polished optical glass into an ultrasonic cleaning machine for cleaning;
(5) putting the cleaned optical glass into a polishing machine again, and further polishing the optical glass by using a polishing agent to remove the uneven impurities and bubbles on the surface of the optical glass; carrying out QC (quality control) inspection on the optical glass after pre-polishing, and removing defective products; the polishing agent comprises cerium oxide, lithium oxide and water, wherein the concentration of the cerium oxide is 1.08-1.12%, and the concentration of the lithium oxide is 0.05-0.08%;
(6) putting the optical glass qualified after secondary polishing into an ultrasonic cleaning machine for cleaning;
(7) placing the optical glass cleaned in the step (6) on an engraving and milling machine to perform engraving and milling to form the shape required by the drawing;
(8) tempering the optical glass by using potassium nitrate in a tempering pot, increasing the surface hardness of the optical glass, wherein the tempering temperature is 415-450 ℃;
(9) finished product warehousing procedure: and (5) detecting the finished optical glass, and warehousing qualified products.
2. The production method according to claim 1, wherein the fine grinding operation is performed using corundum in step (2).
3. The production method according to claim 1, wherein the washing time in the step (4) is 5 to 10 minutes.
4. A method for preparing according to any one of claims 1 to 3, wherein optionally, after tempering the optical glass in step (8), an ink screen printing operation is further performed by a semi-automatic or manual screen printing machine.
5. A method for preparing a glass according to any one of claims 1 to 3, wherein, optionally, after the step of screen printing the optical glass, a gluing step is further carried out, in particular: and gluing the optical glass into the shape required by the drawing by using glue, and then baking in a UV lamp curing oven to accelerate the curing speed of the glue.