CN112409949A - Preparation formula of adhesion promoter - Google Patents
Preparation formula of adhesion promoter Download PDFInfo
- Publication number
- CN112409949A CN112409949A CN202011407836.5A CN202011407836A CN112409949A CN 112409949 A CN112409949 A CN 112409949A CN 202011407836 A CN202011407836 A CN 202011407836A CN 112409949 A CN112409949 A CN 112409949A
- Authority
- CN
- China
- Prior art keywords
- adhesion promoter
- isopropanol
- acetic acid
- white vinegar
- formulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation formula of an adhesion promoter, which comprises the following components in percentage by weight: 80-95% of isopropanol, 8-10% of water, 0-3% of acetic acid and 0.1-0.3% of 4-aminopropyltriethoxysilane, wherein the acetic acid can be white vinegar or glacial acetic acid, the purity of the isopropanol and the white vinegar is high, the isopropanol and the white vinegar do not contain other additive components, the adhesion promoter is stored in a heat source isolation area and an open fire prevention area, the adhesion promoter is recommended to be stored in a plastic or glass closed container, the preparation is required to be placed for 24 hours for use, and the storage life is 4 months. The adhesion promoter prepared by the method can greatly improve the adhesive strength of the adhesive and ensure the adhesive force between the SGP film and the glass air surface, and the use effect of the adhesion promoter can be ensured only by adding a small amount of 4-aminopropyltriethoxysilane in the formula, so that the adhesive force between the SGP film and the glass air surface can be ensured, and the overall quality of float glass is ensured.
Description
Technical Field
The invention relates to the technical field of adhesion promoters, in particular to a preparation formula of an adhesion promoter.
Background
Two surfaces of float glass are divided into an air surface and a tin surface, SGP laminated glass requires that an SGP film must be laminated with the tin surface of the glass, the SGP film has adhesive force, if the SGP film is laminated with the air surface of the glass, the adhesive force is greatly reduced, but when three layers of glass are laminated in the SGP laminating process of a factory, the condition that the air surface of the glass and the SGP film are laminated is certainly generated in the middle glass, and an adhesion promoter is required to be used, so the adhesion promoter with high adhesive strength is provided.
Disclosure of Invention
The invention aims to provide a preparation formula of an adhesion promoter, which has the advantage of high service performance and solves the problem that the existing adhesion promoter is not ideal in adhesion effect.
In order to achieve the purpose, the invention provides the following technical scheme: the adhesive promoter comprises the following components in percentage by weight:
80-95% of isopropanol,
8-10% of water,
0-3 percent of acetic acid,
0.1 to 0.3 percent of 4-aminopropyl triethoxysilane.
Preferably, the preferable component ratio is as follows: 92% of isopropanol, 7.90% of water, 0.01% of acetic acid and 0.09% of 4-aminopropyltriethoxysilane.
Preferably, the acetic acid may be either white vinegar or glacial acetic acid.
Preferably, the preferable component ratio is as follows: 89.92% of isopropanol, 8.47% of water, 1.50% of white vinegar and 0.11% of 4-aminopropyltriethoxysilane.
Preferably, the preferable volume ratio is as follows: 91.91% of isopropanol, 6.80% of water, 1.19% of white vinegar and 0.90% of 4-aminopropyltriethoxysilane.
Preferably, the isopropyl alcohol and the white vinegar have high purity, and do not contain other additive components.
Preferably, the adhesion promoter should be preserved in areas that are insulated from heat sources and avoid open flames.
Preferably, the adhesion promoter is recommended to be stored in a plastic or glass closed container, and is set to be used after 24 hours after the preparation is completed, and the storage life is 4 months.
Compared with the prior art, the invention has the following beneficial effects:
the adhesion promoter prepared by the method can greatly improve the adhesive strength of the adhesive and ensure the adhesive force between the SGP film and the glass air surface, and the use effect of the adhesion promoter can be ensured only by adding a small amount of 4-aminopropyltriethoxysilane in the formula, so that the adhesive force between the SGP film and the glass air surface can be ensured, and the overall quality of float glass is ensured.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The invention provides a technical scheme that:
the adhesive promoter comprises the following components in percentage by weight:
80-95% of isopropanol,
8-10% of water,
0-3 percent of acetic acid,
0.1 to 0.3 percent of 4-aminopropyl triethoxysilane.
The first embodiment is as follows:
the adopted component ratio is as follows: 92% of isopropanol, 7.90% of water, 0.01% of acetic acid and 0.09% of 4-aminopropyltriethoxysilane;
in this embodiment, the acetic acid may be white vinegar or glacial acetic acid, the adhesion promoter should be stored in a sealed container made of plastic or glass to isolate heat source and avoid open fire, and the adhesion promoter should be stored in a sealed container made of plastic or glass for 24 hours before use, and the storage life is 4 months.
Example two:
the adopted component ratio is as follows: 89.92% of isopropanol, 8.47% of water, 1.50% of white vinegar and 0.11% of 4-aminopropyltriethoxysilane;
in this example, the purity of the isopropyl alcohol and the white vinegar is high, and they contain no other additive components, the adhesion promoter should be stored in a heat-insulating and open-fire-preventing area, the adhesion promoter is recommended to be stored in a plastic or glass closed container, and the container should be left for 24 hours after the preparation, and the storage life is 4 months.
Example three:
the volume ratio is as follows: 91.91% of isopropanol, 6.80% of water, 1.19% of white vinegar and 0.90% of 4-aminopropyltriethoxysilane;
in this example, the purity of the isopropyl alcohol and the white vinegar is high, and they contain no other additive components, the adhesion promoter should be stored in a heat-insulating and open-fire-preventing area, the adhesion promoter is recommended to be stored in a plastic or glass closed container, and the container should be left for 24 hours after the preparation, and the storage life is 4 months.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (8)
1. The preparation formula of the adhesion promoter is characterized in that: the components by weight percentage are as follows:
80-95% of isopropanol,
8-10% of water,
0-3 percent of acetic acid,
0.1 to 0.3 percent of 4-aminopropyl triethoxysilane.
2. The formulation for preparing an adhesion promoter as claimed in claim 1, wherein: the preferable component proportion is as follows: 92% of isopropanol, 7.90% of water, 0.01% of acetic acid and 0.09% of 4-aminopropyltriethoxysilane.
3. The formulation for preparing an adhesion promoter as claimed in claim 1, wherein: the acetic acid can be white vinegar or glacial acetic acid.
4. The formulation of an adhesion promoter as claimed in claim 3, wherein: the preferable component proportion is as follows: 89.92% of isopropanol, 8.47% of water, 1.50% of white vinegar and 0.11% of 4-aminopropyltriethoxysilane.
5. The formulation of an adhesion promoter as claimed in claim 4, wherein: the preferable volume ratio is as follows: 91.91% of isopropanol, 6.80% of water, 1.19% of white vinegar and 0.90% of 4-aminopropyltriethoxysilane.
6. The formulation of an adhesion promoter as claimed in claim 3, wherein: the isopropyl alcohol and the white vinegar have high purity, and they do not contain other additive components.
7. The formulation for preparing an adhesion promoter as claimed in claim 1, wherein: the adhesion promoter should be preserved in areas that are insulated from heat sources and avoid open fires.
8. The formulation for preparing an adhesion promoter as claimed in claim 1, wherein: the adhesion promoter is recommended to be stored in a plastic or glass closed container, and is set to be used after 24 hours after the preparation is completed, and the storage life is 4 months.