CN112358773A - 一种防腐防水环保新涂料及其制备方法 - Google Patents
一种防腐防水环保新涂料及其制备方法 Download PDFInfo
- Publication number
- CN112358773A CN112358773A CN202011141130.9A CN202011141130A CN112358773A CN 112358773 A CN112358773 A CN 112358773A CN 202011141130 A CN202011141130 A CN 202011141130A CN 112358773 A CN112358773 A CN 112358773A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- resistance
- emulsion
- mica powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明涉及防水涂料加工技术领域，具体涉及一种防腐防水环保新涂料及其制备方法，这种防腐防水涂料，其特征在于，包含以下组份，乳液、环氧树脂、云母粉、分散剂、成膜剂、消泡剂、水性环氧固化剂、邻苯二甲酯二丁酯、石墨粉等组成，按其重量份数为：乳液40‑60、环氧树脂分散剂20‑30、云母粉10‑15份、分散剂1‑2份、水性环氧固化剂5‑8份、成膜剂0.6‑1、消泡剂2‑4、邻苯二甲酯二丁酯10‑12、石墨粉1‑6份，本发明有优良的防霉性、耐油性、耐水性、抗渗、耐化学腐蚀等性能；具有优良的机械性能，硬度高、耐冲击、耐磨及良好的附着力；防腐层性能稳定，使用寿命长；具有良好的润湿性，提高涂料的粘结强度，增强与基材的粘结效果，提高涂膜的稳定性和抗剥离强度，抗老化性强，施工方便；无毒无异味，绿色环保，安全无毒副作用。
Description
技术领域
本发明涉及防水涂料加工技术领域，具体涉及一种防腐防水环保新涂料及其制备方法。
背景技术
近年来，随着海洋工程、交通运输、能源工业的飞速发展，使得防腐市场越来越广阔，防腐涂料作为防腐材料领域的生力军，有着更加广泛的应用前景。环保法规发展中新的标准和要求不断更新，目前上防腐型防水涂料满足不了防腐市场的新需求，我国生产防水涂料的企业很多，涂料品种繁多，但均属普通产品，现有的防水涂料，反应型因价格太贵，限制了使用范围，溶剂型与水乳型防水涂料，固含量不高，一次性涂刷成膜薄，影响施工进度，远不能适应我国建设工程的防水要求，此外我国的防腐防水材料还处于起步阶段，因此，开发一种防腐防水涂料产品其意义非比寻常，迫在眉睫。
发明内容
为了解决上述问题，本发明提出一种防腐防水涂料及其制备方法。
这种防腐防水涂料，其特征在于，包含以下组份，乳液、环氧树脂、云母粉、分散剂、成膜剂、消泡剂、水性环氧固化剂、邻苯二甲酯二丁酯、石墨粉等组成。
按其重量份数为 ：乳液 40-60 、环氧树脂分散剂 20-30、云母粉10-15份、分散剂1-2份、水性环氧固化剂5-8份、成膜剂 0.6-1 、消泡剂 2- 4、邻苯二甲酯二丁酯 10 -12、石墨粉1-6份。
消泡剂为有机硅消泡剂 。
分散剂为 BYK306。
所述乳液为VAE乳液、纯丙乳液、苯丙乳液、丁苯胶乳和氯丁胶乳的任意一种或多种混合物。
所述水性环氧固化剂为多元胺改性产物，多元胺的改性方法是由多元胺与单脂肪酸反应制得酰胺化的多胺，改性后的多胺固化剂具有两亲性结构，以改善与树脂的相容性。
所述云母粉含有多种成分，二氧化硅和 三氧化二铝，所述二氧化硅的含量为30-40％，所述三氧化二铝的含量为40-52％；所述云母粉具有良好的弹性、韧性、绝缘性、耐高温、耐酸碱、耐腐蚀、附着力强等特性，是涂料优良的添加剂。
其制备方法为步骤一是将计量的云母粉、石墨粉放入研磨机进行研磨，然后放入到搅拌桶内在 1000r/min的转速下进行搅拌20分钟，让粉剂充分混合，制得混合物；
步骤二：将计量的乳液、环氧树脂、适量的水、水性环氧固化剂、邻苯二甲酯二丁酯投入到反应釜中升温到190摄氏度，在1500r/min的转速下进行搅拌20分钟后，让产品冷却，PH调节至7-8，然后再按计量依次加入云母粉和石墨粉的混合物，升温到120摄氏度，在800r/min的转速下进行搅拌10分钟；
步骤三：把反应釜升温到170摄氏度，按计量依次向反应釜中加入分散剂、成膜剂、消泡剂、PH调节剂，并在1300r/min的转速下搅拌20分钟后；出料然后过滤。
本发明有优良的防霉性、耐油性、耐水性、抗渗、耐化学腐蚀等性能；具有优良的机械性能，硬度高、耐冲击、耐磨及良好的附着力；防腐层性能稳定，使用寿命长；具有良好的润湿性，提高涂料的 粘结强度，增强与基材的粘结效果，提高涂膜的稳定性和抗剥离强度，抗老化性强，施工方便；无毒无异味，绿色环保，安全无毒副作用。
具体实施方式
实施例一
这种防腐防水涂料，其特征在于，包含以下组份，乳液、环氧树脂、云母粉、分散剂、成膜剂、消泡剂、水性环氧固化剂、邻苯二甲酯二丁酯、石墨粉等组成。
按其重量份数为 ：乳液40 、环氧树脂分散剂 20、云母粉10份、分散剂1份、水性环氧固化剂5份、成膜剂 0.6、消泡剂 2、邻苯二甲酯二丁酯 10、石墨粉1份。
消泡剂为有机硅消泡剂 。
分散剂为 BYK306。
所述乳液为VAE乳液、纯丙乳液、苯丙乳液、丁苯胶乳和氯丁胶乳的任意一种或多种混合物。
所述水性环氧固化剂为多元胺改性产物，多元胺的改性方法是由多元胺与单脂肪酸反应制得酰胺化的多胺，改性后的多胺固化剂具有两亲性结构，以改善与树脂的相容性。
所述云母粉含有多种成分，二氧化硅和 三氧化二铝，所述二氧化硅的含量为30-40％，所述三氧化二铝的含量为40-52％；所述云母粉具有良好的弹性、韧性、绝缘性、耐高温、耐酸碱、耐腐蚀、附着力强等特性，是涂料优良的添加剂。
其制备方法为步骤一是将计量的云母粉、石墨粉放入研磨机进行研磨，然后放入到搅拌桶内在 1000r/min的转速下进行搅拌20分钟，让粉剂充分混合，制得混合物。
其制备方法为步骤一是将计量的云母粉、石墨粉放入研磨机进行研磨，然后放入到搅拌桶内在 1000r/min的转速下进行搅拌20分钟，让粉剂充分混合，制得混合物；
步骤二：将计量的乳液、环氧树脂、适量的水、水性环氧固化剂、邻苯二甲酯二丁酯投入到反应釜中升温到190摄氏度，在1500r/min的转速下进行搅拌20分钟后，让产品冷却，PH调节至7-8，然后再按计量依次加入云母粉和石墨粉的混合物，升温到120摄氏度，在800r/min的转速下进行搅拌10分钟； 步骤三：把反应釜升温到170摄氏度，按计量依次向反应釜中加入分散剂、成膜剂、消泡剂、PH调节剂，并在1300r/min的转速下搅拌20分钟后；出料然后过滤。
实施例二
这种防腐防水涂料，其特征在于，包含以下组份，乳液、环氧树脂、云母粉、分散剂、成膜剂、消泡剂、水性环氧固化剂、邻苯二甲酯二丁酯、石墨粉等组成。
按其重量份数为 ：乳液 50 、环氧树脂分散剂 24、云母粉12份、分散剂1份、水性环氧固化剂6份、成膜剂 0.8、消泡剂3、邻苯二甲酯二丁酯 11、石墨粉3份。
消泡剂为有机硅消泡剂 。
分散剂为 BYK306。
所述乳液为VAE乳液、纯丙乳液、苯丙乳液、丁苯胶乳和氯丁胶乳的任意一种或多种混合物。
所述水性环氧固化剂为多元胺改性产物，多元胺的改性方法是由多元胺与单脂肪酸反应制得酰胺化的多胺，改性后的多胺固化剂具有两亲性结构，以改善与树脂的相容性。
所述云母粉含有多种成分，二氧化硅和 三氧化二铝，所述二氧化硅的含量为30-40％，所述三氧化二铝的含量为40-52％；所述云母粉具有良好的弹性、韧性、绝缘性、耐高温、耐酸碱、耐腐蚀、附着力强等特性，是涂料优良的添加剂。
其制备方法为步骤一是将计量的云母粉、石墨粉放入研磨机进行研磨，然后放入到搅拌桶内在 1000r/min的转速下进行搅拌20分钟，让粉剂充分混合，制得混合物；
步骤二：将计量的乳液、环氧树脂、适量的水、水性环氧固化剂、邻苯二甲酯二丁酯投入到反应釜中升温到190摄氏度，在1500r/min的转速下进行搅拌20分钟后，让产品冷却，PH调节至7-8，然后再按计量依次加入云母粉和石墨粉的混合物，升温到120摄氏度，在800r/min的转速下进行搅拌10分钟； 步骤三：把反应釜升温到170摄氏度，按计量依次向反应釜中加入分散剂、成膜剂、消泡剂、PH调节剂，并在1300r/min的转速下搅拌20分钟后；出料然后过滤。
实施例三
这种防腐防水涂料，其特征在于，包含以下组份，乳液、环氧树脂、云母粉、分散剂、成膜剂、消泡剂、水性环氧固化剂、邻苯二甲酯二丁酯、石墨粉等组成。
按其重量份数为 ：乳液 60 、环氧树脂分散剂 30、云母粉15份、分散剂1-2份、水性环氧固化剂8份、成膜剂 1 、消泡剂 4、邻苯二甲酯二丁酯12、石墨粉6份。
消泡剂为有机硅消泡剂 。
分散剂为 BYK306。
所述乳液为VAE乳液、纯丙乳液、苯丙乳液、丁苯胶乳和氯丁胶乳的任意一种或多种混合物。
所述水性环氧固化剂为多元胺改性产物，多元胺的改性方法是由多元胺与单脂肪酸反应制得酰胺化的多胺，改性后的多胺固化剂具有两亲性结构，以改善与树脂的相容性。
所述云母粉含有多种成分，二氧化硅和 三氧化二铝，所述二氧化硅的含量为30-40％，所述三氧化二铝的含量为40-52％；所述云母粉具有良好的弹性、韧性、绝缘性、耐高温、耐酸碱、耐腐蚀、附着力强等特性，是涂料优良的添加剂。
其制备方法为步骤一是将计量的云母粉、石墨粉放入研磨机进行研磨，然后放入到搅拌桶内在 1000r/min的转速下进行搅拌20分钟，让粉剂充分混合，制得混合物；
步骤二：将计量的乳液、环氧树脂、适量的水、水性环氧固化剂、邻苯二甲酯二丁酯投入到反应釜中升温到190摄氏度，在1500r/min的转速下进行搅拌20分钟后，让产品冷却，PH调节至7-8，然后再按计量依次加入云母粉和石墨粉的混合物，升温到120摄氏度，在800r/min的转速下进行搅拌10分钟； 步骤三：把反应釜升温到170摄氏度，按计量依次向反应釜中加入分散剂、成膜剂、消泡剂、PH调节剂，并在1300r/min的转速下搅拌20分钟后；出料然后过滤。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (8)
1.一种防腐防水涂料，其特征在于，包含以下组份，乳液、环氧树脂、云母粉、分散剂、成膜剂、消泡剂、水性环氧固化剂、邻苯二甲酯二丁酯、石墨粉等组成。
2. 按其重量份数为 ：乳液 40-60 、环氧树脂分散剂 20-30、云母粉10-15份、分散剂1-2份、水性环氧固化剂5-8份、成膜剂 0.6-1 、消泡剂 2- 4、邻苯二甲酯二丁酯 10 -12、石墨粉1-6份。
3. 根据权利要求1所述的一种防腐防水涂料，其特征在于，消泡剂为有机硅消泡剂 。
4.根据权利要求1所述的一种防腐防水涂料，其特征在于，分散剂为 BYK306。
5.根据权利要求1所述的一种防腐防水涂料，其特征在于，所述乳液为VAE乳液、纯丙乳液、苯丙乳液、丁苯胶乳和氯丁胶乳的任意一种或多种混合物。
6.根据权利要求1所述的一种防腐防水涂料，其特征在于，所述水性环氧固化剂为多元胺改性产物，多元胺的改性方法是由多元胺与单脂肪酸反应制得酰胺化的多胺，改性后的多胺固化剂具有两亲性结构，以改善与树脂的相容性。
7.根据权利要求1所述的一种防腐防水涂料，其特征在于，所述云母粉含有多种成分，二氧化硅和 三氧化二铝，所述二氧化硅的含量为30-40％，所述三氧化二铝的含量为40-52％；所述云母粉具有良好的弹性、韧性、绝缘性、耐高温、耐酸碱、耐腐蚀、附着力强等特性，是涂料优良的添加剂。
8.一种防腐防水涂料的制备方法，其特征在于，步骤一是将计量的云母粉、石墨粉放入研磨机进行研磨，然后放入到搅拌桶内在1000r/min的转速下进行搅拌20分钟，让粉剂充分混合，制得混合物；
步骤二：将计量的乳液、环氧树脂、适量的水、水性环氧固化剂、邻苯二甲酯二丁酯投入到反应釜中升温到190摄氏度，在1500r/min的转速下进行搅拌20分钟后，让产品冷却，PH调节至7-8，然后再按计量依次加入云母粉和石墨粉的混合物，升温到120摄氏度，在800r/min的转速下进行搅拌10分钟；
步骤三：把反应釜升温到170摄氏度，按计量依次向反应釜中加入分散剂、成膜剂、消泡剂、PH调节剂，并在1300r/min的转速下搅拌20分钟后；出料然后过滤。