CN1122650C - Boron clay brick or tile and manufacture method thereof - Google Patents
Boron clay brick or tile and manufacture method thereof Download PDFInfo
- Publication number
- CN1122650C CN1122650C CN01106155A CN01106155A CN1122650C CN 1122650 C CN1122650 C CN 1122650C CN 01106155 A CN01106155 A CN 01106155A CN 01106155 A CN01106155 A CN 01106155A CN 1122650 C CN1122650 C CN 1122650C
- Authority
- CN
- China
- Prior art keywords
- tile
- boron
- pigment
- brick
- clay brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a method for making bricks and tiles from boric sludge (waste slag), which comprises: adhesive, pigment, etc. are added to powdery boric sludge formed by drying; after being evenly mixed, the boric sludge, the adhesive, the pigment, etc. are formed on a brick making apparatus and a tile making machine, and cured to obtain the bricks and the tiles for construction. The method has the advantages of simpleness and practicality. The method not only can thoroughly solve the problem of environmental pollution resulting from boric sludge, but also can reduce the waste degree of calcined bricks and tiles to the land sources. In addition, after the formed products are tested, all indexes achieve or exceed the standard specified in China.
Description
The present invention announces be a kind of waste boric sludge manufacture of building brick of producing with borax, watt and manufacture method.
At present, the waste residue that produces after the suitability for industrialized production for borax, just said boron mud.How handling is a very troubling thing.Because also contain the borax of 11 grams in the per kilogram waste residue, the air storage meeting is because rain drop erosion polluted river water and groundwater resource.In addition, air storage then because surface drying causes airborne dust with the wind, pollutes again the ambient atmosphere environment.Environmental administration does not allow because preventing polluted underground water to bury.Therefore can't handle basically now, have only air storage.Up to the present, also do not have what good treatment process, also of no use its made the method for material of construction.
The purpose of this invention is to provide a kind of boron mud that utilizes and make brick and tile for building and manufacture method thereof for main raw material, the one, solve of the pollution problem of boron mud to environment.In addition, also can alleviate the problem of present firing brick-and tile waste land resources.
Technical scheme of the present invention is as follows:
One, technical formula (weight percent)
Dry boron mud 60～90
Resol 8～20
Pigment 0.5～4
Paraffin 0.4～3
Water is an amount of
Two, manufacturing process
Earlier boron mud is carried out drying treatment, remove moisture content wherein, can adopt the method for seasoning or oven dry.Dry back is powdered.Then pigment is added in the boron mud, make the pigment uniform distribution through fully mixing.Again paraffin is ground into powder and adds in the batching.Add the phenolic aldehyde latex then.Through fully stirring, make each starting material uniform mixing again, can add a certain amount of water as required, make raw material can reach the making state better.Deliver to then on brick, the tile forming machines tool and carry out the moulding manufacturing.Can adopt general brickmaking, watt equipment to get final product.After compression moulding, the demoulding, be placed on air drying again.When reaching the slaking requirement, it is delivered to carry out maturation process in the kiln.Treatment temp requires at 120～240 ℃.Curing time required at 15～30 minutes.Promptly make product.
Technical solution of the present invention is simple, practicality.Not only can solve boron mud waste residue and handle, protect problem of environment, may alleviate the problem of present burned brick, watt waste land resources again.In addition
The material of construction that utilizes present method to make on an index such as resistance to compression, anti-folding, freeze thawing, infiltration, accords with or surpasses the national standard index through check fully.It is a kind of very ideal boron mud comprehensive utilization method.
The present invention does not have figure
Claims (2)
1, boron clay brick or tile is characterized in that its technical formula is: (weight percent)
Dry boron mud 60～90
Resol 8～20
Pigment 0.5～4
Paraffin 0.4～3
Water is an amount of
2, the manufacture method of boron clay brick or tile, the manufacturing process that it is characterized in that it is: with boron mud drying treatment, remove moisture content, then pigment is mixed with boron mud in proportion, batch mixing more in proportion is ground into powder paraffin, through fully stirring, make its uniform mixing, add resol then in proportion, add an amount of water again, fully stirring mixes it, deliver to moulding on brick, watt molding device then, treat depanning after seasoning is delivered to then and carried out the thermalization processing in the kiln, curing temperature is 120～240 ℃, and the curing time is 15～30 minutes.