CN112142384A - Modified concrete interface agent for veneering type inner and outer wall surfaces and preparation method thereof - Google Patents
Modified concrete interface agent for veneering type inner and outer wall surfaces and preparation method thereof Download PDFInfo
- Publication number
- CN112142384A CN112142384A CN202011061305.5A CN202011061305A CN112142384A CN 112142384 A CN112142384 A CN 112142384A CN 202011061305 A CN202011061305 A CN 202011061305A CN 112142384 A CN112142384 A CN 112142384A
- Authority
- CN
- China
- Prior art keywords
- component
- parts
- veneering
- interface agent
- modified concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of building engineering, and particularly relates to a modified concrete interface agent for veneering inner and outer wall surfaces. The invention relates to a modified concrete interface agent for veneering inner and outer wall surfaces, which comprises a component A and a component B, wherein the mass ratio of the component A to the component B is 1: 1-3 parts of an A component, 1-5 parts of an interfacial agent, 1-5 parts of quartz sand and 1-5 parts of lime slurry according to parts by weight, and a B component is cement. The invention mixes the interface agent, quartz sand, lime slurry and cement in market, which enhances the concentration of the mortar and improves the caking property and water absorption rate, thus leading the tile of the outer wall to be easy to operate and enhancing the caking property between the tile and the original outer wall surface.
Description
Technical Field
The invention belongs to the field of building engineering, and particularly relates to a waterproof interface agent for a wall surface of a veneering type outer wall and a preparation method thereof.
Background
The interfacial agent is used for treating the surface of an object so as to improve or completely change the physical and technical properties and surface chemical characteristics of the surface of the material. The interface agent has the following characteristics: bidirectional infiltration bonding, which generates radioactive chain type anchoring effect to permanently and firmly bond the bidirectional materials together; the high-flexibility high-toughness air-permeable floor mat has high softness, high toughness, good air permeability, freeze-thaw resistance, water resistance, aging resistance, no toxicity, no odor and no pollution; acid and alkali resistance and weather resistance, and good adaptability and affinity with acid and alkali materials; can be constructed and hardened in a humid environment.
The existing interface agent is troublesome to operate, labor-consuming and time-consuming, and has low operation efficiency and is not practical in actual construction engineering.
Disclosure of Invention
The invention aims to provide a modified concrete interface agent for veneering inner and outer wall surfaces.
The invention also aims to provide a preparation method of the modified concrete interface agent.
According to the specific embodiment of the invention, the modified concrete interface agent for veneering inner and outer wall surfaces comprises a component A and a component B, wherein the mass ratio of the component A to the component B is 1: 1-3 parts of an A component, 1-5 parts of an interfacial agent, 1-5 parts of quartz sand and 1-5 parts of lime slurry according to parts by weight, and a B component is cement.
The commercially available concrete interface agent is purchased from Kunshanxinda building materials Co., Ltd.
According to the modified concrete interface agent for veneering inner and outer wall surfaces, which is disclosed by the specific embodiment of the invention, the lime slurry is dissolved by adding water according to the metering of 10-20%.
According to the specific embodiment of the invention, the modified concrete interface agent for veneering inner and outer wall surfaces comprises a component A and a component B, wherein the mass ratio of the component A to the component B is 1: 1, the component A comprises 1-5 parts of an interfacial agent, 1-5 parts of quartz sand and 1-5 parts of lime slurry according to parts by weight, and the component B is cement.
According to the specific embodiment of the invention, the modified concrete interface agent for veneering inner and outer wall surfaces comprises a component A and a component B, wherein the mass ratio of the component A to the component B is 1: 2, the component A comprises 1-5 parts of an interfacial agent, 1-5 parts of quartz sand and 1-5 parts of lime slurry according to parts by weight, and the component B is cement.
According to the specific embodiment of the invention, the modified concrete interface agent for veneering inner and outer wall surfaces comprises a component A and a component B, wherein the mass ratio of the component A to the component B is 1: 3, the component A comprises 1-5 parts of an interfacial agent, 1-5 parts of quartz sand and 1-5 parts of lime slurry according to parts by weight, and the component B is cement.
The preparation method of the modified concrete interface agent for veneering inner and outer wall surfaces according to the specific embodiment of the invention comprises the following steps:
(1) dissolving lime slurry in water, and then uniformly mixing an interfacial agent, quartz sand and the lime slurry to obtain a component A;
(2) mixing the component A and the component B according to the mass ratio of 1: 1-3, and adding water to prepare paste.
According to the preparation method of the modified concrete interface agent for veneering inner and outer wall surfaces, which is provided by the specific embodiment of the invention, in the step (1), the lime slurry is dissolved by adding water according to the metering of 10-20%.
According to the preparation method of the modified concrete interface agent for veneering inner and outer wall surfaces, which is disclosed by the specific embodiment of the invention, in the step (2), the component A and the component B are mixed according to the mass ratio of 1: 1, mixing uniformly.
According to the preparation method of the modified concrete interface agent for veneering inner and outer wall surfaces, which is disclosed by the specific embodiment of the invention, in the step (2), the component A and the component B are mixed according to the mass ratio of 1: 2, mixing uniformly.
According to the preparation method of the modified concrete interface agent for veneering inner and outer wall surfaces, which is disclosed by the specific embodiment of the invention, in the step (2), the component A and the component B are mixed according to the mass ratio of 1: 3, mixing uniformly.
The invention has the beneficial effects that:
the invention mixes the interface agent, quartz sand, lime slurry and cement in market, which enhances the concentration of the mortar and improves the caking property and water absorption rate, thus leading the tile of the outer wall to be easy to operate and enhancing the caking property between the tile and the original outer wall surface.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, the technical solutions of the present invention will be described in detail below. It is to be understood that the described embodiments are merely exemplary of the invention, and not restrictive of the full scope of the invention. All other embodiments, which can be derived by a person skilled in the art from the examples given herein without any inventive step, are within the scope of the present invention.
Example 1
1.1 the invention relates to a veneering type interior and exterior wall surface modified concrete interface agent, which comprises a component A and a component B, wherein the mass ratio of the component A to the component B is 1: 1,
the component A comprises 1 part of interfacial agent, 1 part of quartz sand and 1 part of lime slurry according to parts by weight;
the component B is cement.
The invention relates to a veneering type interior and exterior wall surface modified concrete interface agent, which comprises a component A and a component B, wherein the mass ratio of the component A to the component B is 1: 2,
the component A comprises 2 parts of interfacial agent, 3 parts of quartz sand and 4 parts of lime slurry according to parts by weight;
the component B is cement.
The invention relates to a veneering type interior and exterior wall surface modified concrete interface agent, which comprises a component A and a component B, wherein the mass ratio of the component A to the component B is 1: 3,
the component A comprises 5 parts of interfacial agent, 4 parts of quartz sand and 5 parts of lime slurry according to parts by weight,
the component B is cement.
Example 2
2.1 the modified concrete interface agent for veneering type inner and outer wall surfaces is prepared according to the following method:
(1) adding 10-20% of lime slurry into water for dissolving, and uniformly mixing 1 part of interfacial agent, 1 part of quartz sand and 1 part of lime slurry to obtain a component A;
(2) mixing the component A and the component B according to the mass ratio of 1: 1, mixing uniformly, adding water and blending into paste to obtain the product.
2.2 the modified concrete interface agent for veneering type inner and outer wall surfaces is prepared according to the following method:
(1) adding 10-20% of lime slurry into water for dissolving, and uniformly mixing 2 parts of interfacial agent, 3 parts of quartz sand and 4 parts of lime slurry to obtain a component A;
(2) mixing the component A and the component B according to the mass ratio of 1: 2, mixing uniformly, adding water to prepare paste, and thus obtaining the Chinese medicinal composition.
2.3 the modified concrete interface agent for veneering type inner and outer wall surfaces is prepared according to the following method:
(1) adding 10-20% of lime slurry into water for dissolving, and uniformly mixing 5 parts of interfacial agent, 4 parts of quartz sand and 5 parts of lime slurry to obtain a component A;
(2) mixing the component A and the component B according to the mass ratio of 1: 3, mixing uniformly, adding water and blending into paste to obtain the product.
During construction, the modified concrete interface agent is coated until the grass decoration project is almost white and dry, and fine cracks on the wall appear, so that the modified concrete interface agent is most suitable for rolling brushing. If the wall is too dry, the wall can be wetted with water and smeared after the dust is washed away.
The modified concrete interface agent is coated on the grass veneer of the outer wall, so that the sand holes of the wall surface and the water seepage slit which is not easy to see can be thoroughly eliminated, and the water seepage problem of the outer wall veneer caused by the wall body plastering problem is greatly reduced.
The modified concrete interface agent can be directly coated on an outer wall surface, plays a role in water prevention, makes up the problems caused by construction defects, has strong weather resistance, and can be an effective guarantee for outer wall painting.
The modified concrete interface agent disclosed by the invention is proved to have super strong weather resistance, strong bonding rate, good water absorption and easiness in tiling and wall mounting by being smeared in the open air for 3 years, and the quality problems that the water absorption of a wall body is poor and the wall brick is easy to move down and the like due to the existing waterproof engineering of workers are solved.
The above description is only for the specific embodiments of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art can easily conceive of the changes or substitutions within the technical scope of the present invention, and all the changes or substitutions should be covered within the scope of the present invention. Therefore, the protection scope of the present invention shall be subject to the protection scope of the appended claims.
Claims (10)
1. The modified concrete interface agent for veneering inner and outer wall surfaces is characterized by comprising a component A and a component B, wherein the mass ratio of the component A to the component B is 1: 1-3 parts of an A component, 1-5 parts of an interfacial agent, 1-5 parts of quartz sand and 1-5 parts of lime slurry according to parts by weight, and a B component is cement.
2. The modified concrete interface agent for veneering type interior and exterior wall surfaces according to claim 1, wherein the lime slurry is dissolved by adding water according to the metering of 10-20%.
3. The modified concrete interface agent for veneering inner and outer wall surfaces according to claim 1, which comprises a component A and a component B, wherein the mass ratio of the component A to the component B is 1: 1, the component A comprises 1-5 parts of an interfacial agent, 1-5 parts of quartz sand and 1-5 parts of lime slurry according to parts by weight, and the component B is cement.
4. The modified concrete interface agent for veneering inner and outer wall surfaces according to claim 1, which comprises a component A and a component B, wherein the mass ratio of the component A to the component B is 1: 2, the component A comprises 1-5 parts of an interfacial agent, 1-5 parts of quartz sand and 1-5 parts of lime slurry according to parts by weight, and the component B is cement.
5. The modified concrete interface agent for veneering inner and outer wall surfaces according to claim 1, which comprises a component A and a component B, wherein the mass ratio of the component A to the component B is 1: 3, the component A comprises 1-5 parts of an interfacial agent, 1-5 parts of quartz sand and 1-5 parts of lime slurry according to parts by weight, and the component B is cement.
6. The method for preparing the modified concrete interface agent for veneering similar inner and outer wall surfaces of claim 1, which is characterized by comprising the following steps:
(1) dissolving lime slurry in water, and then uniformly mixing an interfacial agent, quartz sand and the lime slurry to obtain a component A;
(2) mixing the component A and the component B according to the mass ratio of 1: 1-3, and adding water to prepare paste.
7. The preparation method of the modified concrete interface agent for veneering inner and outer wall surfaces according to claim 6, wherein in the step (1), the lime slurry is dissolved by adding water according to the metering of 10-20%.
8. The preparation method of the modified concrete interface agent for veneering inner and outer walls according to claim 6, wherein in the step (2), the component A and the component B are mixed according to a mass ratio of 1: 1, mixing uniformly.
9. The preparation method of the modified concrete interface agent for veneering inner and outer walls according to claim 6, wherein in the step (2), the component A and the component B are mixed according to a mass ratio of 1: 2, mixing uniformly.
10. The preparation method of the modified concrete interface agent for veneering inner and outer walls according to claim 6, wherein in the step (2), the component A and the component B are mixed according to a mass ratio of 1: 3, mixing uniformly.