CN111961391A - Orange peel powder coating and preparation method thereof - Google Patents

Orange peel powder coating and preparation method thereof Download PDF

Info

Publication number
CN111961391A
CN111961391A CN202010932952.2A CN202010932952A CN111961391A CN 111961391 A CN111961391 A CN 111961391A CN 202010932952 A CN202010932952 A CN 202010932952A CN 111961391 A CN111961391 A CN 111961391A
Authority
CN
China
Prior art keywords
powder coating
crushing
tabletting
epoxy resin
polyester resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN202010932952.2A
Other languages
Chinese (zh)
Inventor
夏连心
方志望
朱满子
李时雨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hunan Lianxin Technology Co Ltd
Original Assignee
Hunan Lianxin Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hunan Lianxin Technology Co Ltd filed Critical Hunan Lianxin Technology Co Ltd
Priority to CN202010932952.2A priority Critical patent/CN111961391A/en
Publication of CN111961391A publication Critical patent/CN111961391A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses an orange peel powder coating and a preparation method thereof, wherein the orange peel powder coating comprises the following raw materials in parts by weight: 80-90 parts of polyester resin, 80-90 parts of epoxy resin, 3-6 parts of triglycidyl isocyanurate, 2.5-4.5 parts of brightening agent, 2.5-4.5 parts of flatting agent, 0.8-1.6 parts of benzoin and 55-65 parts of barium sulfate powder, wherein the polyester resin is saturated polyester resin, the acid value is 68-72mgKOH/g, and the viscosity is 27-31P/200 ℃. The coating formed by the powder coating has excellent orange grain lines; and after the coating is applied to a plate to form a coating, the adhesion and impact resistance of the coating are excellent, and the comprehensive performance is good.

Description

Orange peel powder coating and preparation method thereof
Technical Field
The invention relates to the technical field of powder coatings, and particularly relates to an orange peel powder coating and a preparation method thereof.
Background
Powder coatings represent a rapidly growing area in the overall coating technology. Because the VOC emission is almost zero, the rapid development of the VOC is driven by the environmental protection requirement. The requirements of global and Chinese environmental protection laws and regulations are more and more strict, and the development of the environmental protection powder coating industry is effectively promoted.
Powder coatings have several advantages over paint coatings, but also have disadvantages, such as: the coating effect is poor, the pattern is less, and the effect is too single.
Disclosure of Invention
In view of the above, the invention provides an orange-peel powder coating and a preparation method thereof, and a coating formed by the powder coating has an orange-peel structure and is beautiful.
An orange peel powder coating comprises the following raw materials in parts by weight:
Figure BDA0002670905710000011
the polyester resin is saturated polyester resin, the acid value is 68-72mgKOH/g, and the viscosity is 27-31P/200 ℃.
Preferably, the raw materials comprise the following components in parts by weight:
Figure BDA0002670905710000012
Figure BDA0002670905710000021
preferably, the epoxy resin is one of glycidyl amine epoxy resin, linear aliphatic epoxy resin and alicyclic epoxy resin.
Preferably, the benzoin particle size is 20-50 um.
Preferably, the particle size of the barium sulfate powder is 0.08-0.2 um.
A preparation method of orange peel powder coating comprises the following steps:
premixing: placing polyester resin, epoxy resin, triglycidyl isocyanurate, benzoin and barium sulfate powder in a mixer, and mixing for 5-15min at the rotating speed of 250-450r/min to obtain a mixed material;
melt extrusion: adding the mixed material into a double-screw extruder, wherein the temperature of a machine cavity is 90-110 ℃, the temperature of a machine head is 105-;
tabletting and cooling: adding the extrudate into a tabletting machine, and naturally cooling after tabletting;
crushing: and crushing the crushed tablets by a grinder, crushing to 400 meshes by 200 meshes, and sieving to obtain the powder coating.
Preferably, the method is as follows:
premixing: placing polyester resin, epoxy resin, triglycidyl isocyanurate, benzoin and barium sulfate powder in a mixer, and mixing for 6-12min at the rotating speed of 300-420r/min to obtain a mixed material;
melt extrusion: adding the mixed material into a double-screw extruder, wherein the temperature of a cavity of the extruder is 95-106 ℃, the temperature of a head of the extruder is 108-;
tabletting and cooling: adding the extrudate into a tabletting machine, and naturally cooling after tabletting;
crushing: and crushing the crushed tablets by a grinder, crushing to 240 meshes and 360 meshes, and sieving to obtain the powder coating.
Preferably, the method is as follows:
premixing: putting polyester resin, epoxy resin, triglycidyl isocyanurate, benzoin and barium sulfate powder into a mixer, and mixing for 8min at the rotating speed of 380r/min to obtain a mixed material;
melt extrusion: adding the mixed materials into a double-screw extruder, wherein the temperature of a machine cavity is 102 ℃, the temperature of a machine head is 106 ℃, and performing melt extrusion to obtain an extrudate;
tabletting and cooling: adding the extrudate into a tabletting machine, and naturally cooling after tabletting;
crushing: and crushing the crushed tablets by a grinder, crushing to 280 meshes, and sieving to obtain the powder coating.
The invention provides orange-peel powder coating and a preparation method thereof, and a coating formed by the powder coating has excellent orange-peel grains; and after the coating is applied to a plate to form a coating, the adhesion and impact resistance of the coating are excellent, and the comprehensive performance is good.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are some, but not all, embodiments of the present invention. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
It will be understood that the terms "comprises" and/or "comprising," when used in this specification and the appended claims, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.
It should be further understood that the term "and/or" as used in this specification and the appended claims refers to and includes any and all possible combinations of one or more of the associated listed items.
An orange peel powder coating comprises the following raw materials in parts by weight:
Figure BDA0002670905710000041
the polyester resin is saturated polyester resin, the acid value is 68-72mgKOH/g, and the viscosity is 27-31P/200 ℃.
Wherein the epoxy resin is one of glycidyl amine epoxy resin, linear aliphatic epoxy resin and alicyclic epoxy resin; the grain diameter of benzoin is 20-50 um; the particle size of the barium sulfate powder is 0.08-0.2 um.
A preparation method of orange peel powder coating comprises the following steps:
premixing: placing polyester resin, epoxy resin, triglycidyl isocyanurate, benzoin and barium sulfate powder in a mixer, and mixing for 5-15min at the rotating speed of 250-450r/min to obtain a mixed material;
melt extrusion: adding the mixed material into a double-screw extruder, wherein the temperature of a machine cavity is 90-110 ℃, the temperature of a machine head is 105-;
tabletting and cooling: adding the extrudate into a tabletting machine, and naturally cooling after tabletting;
crushing: and crushing the crushed tablets by a grinder, crushing to 400 meshes by 200 meshes, and sieving to obtain the powder coating.
Example 1
An orange peel powder coating comprises the following raw materials in parts by weight:
Figure BDA0002670905710000051
the polyester resin is saturated polyester resin, the acid value is 68mgKOH/g, and the viscosity is 27P/200 ℃; wherein the epoxy resin is glycidyl amine epoxy resin; the grain diameter of benzoin is 20-40 um; the particle size of the barium sulfate powder is 0.1-0.18 um.
A preparation method of orange peel powder coating comprises the following steps:
premixing: putting polyester resin, epoxy resin, triglycidyl isocyanurate, benzoin and barium sulfate powder into a mixer, and mixing for 15min at the rotating speed of 250r/min to obtain a mixed material;
melt extrusion: adding the mixed materials into a double-screw extruder, wherein the temperature of a machine cavity is 90 ℃, the temperature of a machine head is 105 ℃, and performing melt extrusion to obtain an extruded material;
tabletting and cooling: adding the extrudate into a tabletting machine, and naturally cooling after tabletting;
crushing: and crushing the crushed tablets by a grinder, crushing the crushed tablets to 400 meshes, and sieving the crushed tablets to obtain the powder coating.
Example 2
An orange peel powder coating comprises the following raw materials in parts by weight:
Figure BDA0002670905710000052
Figure BDA0002670905710000061
the polyester resin is saturated polyester resin, the acid value is 69mgKOH/g, and the viscosity is 30P/200 ℃.
Wherein the epoxy resin is linear aliphatic epoxy resin; the grain diameter of benzoin is 25-45 um; the particle size of the barium sulfate powder is 0.09-0.16 um.
A preparation method of orange peel powder coating comprises the following steps:
premixing: putting polyester resin, epoxy resin, triglycidyl isocyanurate, benzoin and barium sulfate powder into a mixer, and mixing for 6min at the rotating speed of 420r/min to obtain a mixed material;
melt extrusion: adding the mixed materials into a double-screw extruder, wherein the temperature of a machine cavity is 106 ℃, the temperature of a machine head is 112 ℃, and performing melt extrusion to obtain an extrudate;
tabletting and cooling: adding the extrudate into a tabletting machine, and naturally cooling after tabletting;
crushing: and crushing the crushed tablets by a grinder, crushing the crushed tablets to 240 meshes, and sieving the crushed tablets to obtain the powder coating.
Example 3
An orange peel powder coating comprises the following raw materials in parts by weight:
Figure BDA0002670905710000062
the polyester resin is saturated polyester resin, the acid value is 72mgKOH/g, and the viscosity is 31P/200 ℃.
Wherein the epoxy resin is linear aliphatic epoxy resin; the particle size of the barium sulfate powder is 0.08-0.15 um.
A preparation method of orange peel powder coating comprises the following steps:
premixing: putting polyester resin, epoxy resin, triglycidyl isocyanurate, benzoin and barium sulfate powder into a mixer, and mixing for 5min at the rotating speed of 450r/min to obtain a mixed material;
melt extrusion: adding the mixed materials into a double-screw extruder, wherein the temperature of a machine cavity is 110 ℃, the temperature of a machine head is 115 ℃, and performing melt extrusion to obtain an extrudate;
tabletting and cooling: adding the extrudate into a tabletting machine, and naturally cooling after tabletting;
crushing: and crushing the crushed tablets by a grinder, crushing the crushed tablets to 200 meshes, and sieving the crushed tablets to obtain the powder coating.
Example 4
An orange peel powder coating comprises the following raw materials in parts by weight:
Figure BDA0002670905710000071
the polyester resin is saturated polyester resin, the acid value is 71mgKOH/g, and the viscosity is 29P/200 ℃.
Wherein the epoxy resin is alicyclic epoxy resin; the grain diameter of benzoin is 20-40 um; the particle size of the barium sulfate powder is 0.1-0.18 um.
A preparation method of orange peel powder coating comprises the following steps:
premixing: putting polyester resin, epoxy resin, triglycidyl isocyanurate, benzoin and barium sulfate powder into a mixer, and mixing for 12min at the rotating speed of 300r/min to obtain a mixed material;
melt extrusion: adding the mixed materials into a double-screw extruder, wherein the temperature of a machine cavity is 95 ℃, the temperature of a machine head is 108 ℃, and performing melt extrusion to obtain an extrudate;
tabletting and cooling: adding the extrudate into a tabletting machine, and naturally cooling after tabletting;
crushing: and crushing the crushed tablets by a grinder, crushing the crushed tablets into 360 meshes, and sieving the crushed tablets to obtain the powder coating.
Example 5
An orange peel powder coating comprises the following raw materials in parts by weight:
Figure BDA0002670905710000081
the polyester resin is saturated polyester resin, the acid value is 70mgKOH/g, and the viscosity is 30P/200 ℃.
Wherein the epoxy resin is glycidyl amine epoxy resin; the grain diameter of benzoin is 30-45 um; the particle size of the barium sulfate powder is 0.12-0.18 um.
A preparation method of orange peel powder coating comprises the following steps:
premixing: putting polyester resin, epoxy resin, triglycidyl isocyanurate, benzoin and barium sulfate powder into a mixer, and mixing for 9min at the rotating speed of 350r/min to obtain a mixed material;
melt extrusion: adding the mixed materials into a double-screw extruder, wherein the temperature of a machine cavity is 100 ℃, the temperature of a machine head is 110 ℃, and performing melt extrusion to obtain an extrudate;
tabletting and cooling: adding the extrudate into a tabletting machine, and naturally cooling after tabletting;
crushing: and crushing the crushed tablets by a grinder, crushing the crushed tablets to 300 meshes, and sieving the crushed tablets to obtain the powder coating.
The powder coatings of examples 1-5 were compared with commercially available powder coatings in terms of coating effect, and the powder coatings of examples 1-5 and commercially available powder coatings were applied to panels respectively to test adhesion, impact strength and bending properties; the test method comprises the following steps: adhesion (ISO2409-2007), impact strength (GB/T1732-93) and bending (GB/T6742-1986) tests, the test results are as follows:
Figure BDA0002670905710000091
as can be seen from the above table: the powder coatings of specific examples 1-5 have certain advantages in adhesion, impact strength and flexural strength properties compared to comparative example 1, and examples 1-5 have a very large advantage in appearance texture compared to comparative example 1, with clear orange-peel texture.
The steps in the method of the embodiment of the invention can be sequentially adjusted, combined and deleted according to actual needs.
The present invention has been described in detail, and the principle and embodiments of the present invention are explained by applying specific examples, which are only used to help understanding the method and the core idea of the present invention; meanwhile, for a person skilled in the art, according to the idea of the present invention, there may be variations in the specific embodiments and the application scope, and in summary, the content of the present specification should not be construed as a limitation to the present invention.
It is clear to those skilled in the art that, for convenience and brevity of description, the specific working processes of the above-described systems and units may refer to the corresponding processes in the foregoing method embodiments, and are not described herein again.

Claims (8)

1. The orange peel powder coating is characterized by comprising the following raw materials in parts by weight:
Figure FDA0002670905700000011
the polyester resin is saturated polyester resin, the acid value is 68-72mgKOH/g, and the viscosity is 27-31P/200 ℃.
2. The powder coating of claim 1, wherein the raw materials comprise, by weight:
Figure FDA0002670905700000012
3. the powder coating according to any one of claims 1-2, wherein the epoxy resin is one of a glycidyl amine based epoxy resin, a linear aliphatic epoxy resin, and an alicyclic epoxy resin.
4. The powder coating according to any of claims 1-2, wherein the benzoin particles have a size of 20-50 um.
5. The powder coating of any one of claims 1-2, wherein the barium sulfate powder has a particle size of 0.08-0.2 um.
6. A preparation method of orange peel powder coating is characterized by comprising the following steps:
premixing: placing polyester resin, epoxy resin, triglycidyl isocyanurate, benzoin and barium sulfate powder in a mixer, and mixing for 5-15min at the rotating speed of 250-450r/min to obtain a mixed material;
melt extrusion: adding the mixed material into a double-screw extruder, wherein the temperature of a machine cavity is 90-110 ℃, the temperature of a machine head is 105-;
tabletting and cooling: adding the extrudate into a tabletting machine, and naturally cooling after tabletting;
crushing: and crushing the crushed tablets by a grinder, crushing to 400 meshes by 200 meshes, and sieving to obtain the powder coating.
7. The method for preparing the compound of claim 6, wherein the method comprises the following steps:
premixing: placing polyester resin, epoxy resin, triglycidyl isocyanurate, benzoin and barium sulfate powder in a mixer, and mixing for 6-12min at the rotating speed of 300-420r/min to obtain a mixed material;
melt extrusion: adding the mixed material into a double-screw extruder, wherein the temperature of a cavity of the extruder is 95-106 ℃, the temperature of a head of the extruder is 108-;
tabletting and cooling: adding the extrudate into a tabletting machine, and naturally cooling after tabletting;
crushing: and crushing the crushed tablets by a grinder, crushing to 240 meshes and 360 meshes, and sieving to obtain the powder coating.
8. The method for preparing the compound of claim 7, wherein the method comprises the following steps:
premixing: putting polyester resin, epoxy resin, triglycidyl isocyanurate, benzoin and barium sulfate powder into a mixer, and mixing for 8min at the rotating speed of 380r/min to obtain a mixed material;
melt extrusion: adding the mixed materials into a double-screw extruder, wherein the temperature of a machine cavity is 102 ℃, the temperature of a machine head is 106 ℃, and performing melt extrusion to obtain an extrudate;
tabletting and cooling: adding the extrudate into a tabletting machine, and naturally cooling after tabletting;
crushing: and crushing the crushed tablets by a grinder, crushing to 280 meshes, and sieving to obtain the powder coating.
CN202010932952.2A 2020-09-08 2020-09-08 Orange peel powder coating and preparation method thereof Withdrawn CN111961391A (en)