CN111793977A - 一种保暖纤维面料的制备方法 - Google Patents
一种保暖纤维面料的制备方法 Download PDFInfo
- Publication number
- CN111793977A CN111793977A CN202010670669.7A CN202010670669A CN111793977A CN 111793977 A CN111793977 A CN 111793977A CN 202010670669 A CN202010670669 A CN 202010670669A CN 111793977 A CN111793977 A CN 111793977A
- Authority
- CN
- China
- Prior art keywords
- parts
- sodium
- fumaric acid
- preparing
- blocked polyisocyanate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种保暖纤维面料的制备方法,包括如下步骤:1)配制处理液;2)在现有的纺丝设备上,采用聚酯切片作为原料,利用步骤1)所配制的处理液代替纺丝油剂并采用FDY纺丝工艺制备FDY纤维,且所用喷丝孔为环形,对应制备出纤维具有贯通纤维轴向的管状空腔。本发明制备的纤维具有中空保暖的功能,且具有较好的抗菌、防霉、阻燃、耐磨性能。
Description
技术领域
本发明涉及一种保暖纤维面料的制备方法。
背景技术
纤维(美:Fiber;英:Fibre)是指由连续或不连续的细丝组成的物质。纤维的种类和应用很多,其中纺织纤维是用来纺织布的纤维,是纺织领域必备的原材料。纤维是纺织纤维中的一种,且纤维是絮片常用的原材料,纤维具有贯通纤维轴向的管状空腔。
但现有纤维的功能相对单一,不能满足市场多样化的需求。
发明内容
本发明的目的在于提供一种保暖纤维面料的制备方法,其制备的纤维具有中空保暖的功能,且具有较好的抗菌、防霉、阻燃、耐磨性能。
为实现上述目的,本发明的技术方案是设计一种保暖纤维面料的制备方法,包括如下步骤:
1)配制处理液;
2)在现有的纺丝设备上,采用聚酯切片作为原料,利用步骤1)所配制的处理液代替纺丝油剂并采用FDY纺丝工艺制备FDY纤维,且所用喷丝孔为环形,对应制备出纤维具有贯通纤维轴向的管状空腔;
其中,
按重量份计,所述处理液由以下组分组成:
20~25份常规聚酯纺丝油剂,
2~4份封闭多异氰酸酯,
2.1份乙二醛,
1.6份月桂酰氨乙基硫酸钠,
1.7份油酰氨基酸钠,
2.2份脂肪醇聚氧乙烯醚,
1.8份烷基苯磺酸钠,
2.3份羧甲基纤维素,
1.4份六偏磷酸钠,
0.7份黄柏提取液,
1.2份十二烷基二甲基苄基氯化铵,
2.2份反丁烯二酸,
1.6份对苯二胺,
2.5份磷酸二氢铵,
60份水。
优选的,按重量份计,所述处理液由以下组分组成:
20份常规聚酯纺丝油剂,
2份封闭多异氰酸酯,
2.1份乙二醛,
1.6份月桂酰氨乙基硫酸钠,
1.7份油酰氨基酸钠,
2.2份脂肪醇聚氧乙烯醚,
1.8份烷基苯磺酸钠,
2.3份羧甲基纤维素,
1.4份六偏磷酸钠,
0.7份黄柏提取液,
1.2份十二烷基二甲基苄基氯化铵,
2.2份反丁烯二酸,
1.6份对苯二胺,
2.5份磷酸二氢铵,
60份水。
优选的,按重量份计,所述处理液由以下组分组成:
25份常规聚酯纺丝油剂,
4份封闭多异氰酸酯,
2.1份乙二醛,
1.6份月桂酰氨乙基硫酸钠,
1.7份油酰氨基酸钠,
2.2份脂肪醇聚氧乙烯醚,
1.8份烷基苯磺酸钠,
2.3份羧甲基纤维素,
1.4份六偏磷酸钠,
0.7份黄柏提取液,
1.2份十二烷基二甲基苄基氯化铵,
2.2份反丁烯二酸,
1.6份对苯二胺,
2.5份磷酸二氢铵,
60份水。
优选的,按重量份计,所述处理液由以下组分组成:
21份常规聚酯纺丝油剂,
2.4份封闭多异氰酸酯,
2.1份乙二醛,
1.6份月桂酰氨乙基硫酸钠,
1.7份油酰氨基酸钠,
2.2份脂肪醇聚氧乙烯醚,
1.8份烷基苯磺酸钠,
2.3份羧甲基纤维素,
1.4份六偏磷酸钠,
0.7份黄柏提取液,
1.2份十二烷基二甲基苄基氯化铵,
2.2份反丁烯二酸,
1.6份对苯二胺,
2.5份磷酸二氢铵,
60份水。
本发明的优点和有益效果在于:提供一种保暖纤维面料的制备方法,其制备的纤维具有中空保暖的功能,且具有较好的抗菌、防霉、阻燃、耐磨性能。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
一种保暖纤维面料的制备方法,包括如下步骤:
1)配制处理液;
2)在现有的纺丝设备上,采用聚酯切片作为原料,利用步骤1)所配制的处理液代替纺丝油剂并采用FDY纺丝工艺制备FDY纤维,且所用喷丝孔为环形,对应制备出纤维具有贯通纤维轴向的管状空腔;
其中,
按重量份计,所述处理液由以下组分组成:
20份常规聚酯纺丝油剂,
2份封闭多异氰酸酯,
2.1份乙二醛,
1.6份月桂酰氨乙基硫酸钠,
1.7份油酰氨基酸钠,
2.2份脂肪醇聚氧乙烯醚,
1.8份烷基苯磺酸钠,
2.3份羧甲基纤维素,
1.4份六偏磷酸钠,
0.7份黄柏提取液,
1.2份十二烷基二甲基苄基氯化铵,
2.2份反丁烯二酸,
1.6份对苯二胺,
2.5份磷酸二氢铵,
60份水。
实施例2
一种保暖纤维面料的制备方法,包括如下步骤:
1)配制处理液;
2)在现有的纺丝设备上,采用聚酯切片作为原料,利用步骤1)所配制的处理液代替纺丝油剂并采用FDY纺丝工艺制备FDY纤维,且所用喷丝孔为环形,对应制备出纤维具有贯通纤维轴向的管状空腔;
其中,
按重量份计,所述处理液由以下组分组成:
25份常规聚酯纺丝油剂,
4份封闭多异氰酸酯,
2.1份乙二醛,
1.6份月桂酰氨乙基硫酸钠,
1.7份油酰氨基酸钠,
2.2份脂肪醇聚氧乙烯醚,
1.8份烷基苯磺酸钠,
2.3份羧甲基纤维素,
1.4份六偏磷酸钠,
0.7份黄柏提取液,
1.2份十二烷基二甲基苄基氯化铵,
2.2份反丁烯二酸,
1.6份对苯二胺,
2.5份磷酸二氢铵,
60份水。
实施例3
一种保暖纤维面料的制备方法,包括如下步骤:
1)配制处理液;
2)在现有的纺丝设备上,采用聚酯切片作为原料,利用步骤1)所配制的处理液代替纺丝油剂并采用FDY纺丝工艺制备FDY纤维,且所用喷丝孔为环形,对应制备出纤维具有贯通纤维轴向的管状空腔;
其中,
按重量份计,所述处理液由以下组分组成:
21份常规聚酯纺丝油剂,
2.4份封闭多异氰酸酯,
2.1份乙二醛,
1.6份月桂酰氨乙基硫酸钠,
1.7份油酰氨基酸钠,
2.2份脂肪醇聚氧乙烯醚,
1.8份烷基苯磺酸钠,
2.3份羧甲基纤维素,
1.4份六偏磷酸钠,
0.7份黄柏提取液,
1.2份十二烷基二甲基苄基氯化铵,
2.2份反丁烯二酸,
1.6份对苯二胺,
2.5份磷酸二氢铵,
60份水。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (4)
1.一种保暖纤维面料的制备方法,其特征在于,包括如下步骤:
1)配制处理液;
2)在现有的纺丝设备上,采用聚酯切片作为原料,利用步骤1)所配制的处理液代替纺丝油剂并采用FDY纺丝工艺制备FDY纤维,且所用喷丝孔为环形,对应制备出纤维具有贯通纤维轴向的管状空腔;
其中,
按重量份计,所述处理液由以下组分组成:
20~25份常规聚酯纺丝油剂,
2~4份封闭多异氰酸酯,
2.1份乙二醛,
1.6份月桂酰氨乙基硫酸钠,
1.7份油酰氨基酸钠,
2.2份脂肪醇聚氧乙烯醚,
1.8份烷基苯磺酸钠,
2.3份羧甲基纤维素,
1.4份六偏磷酸钠,
0.7份黄柏提取液,
1.2份十二烷基二甲基苄基氯化铵,
2.2份反丁烯二酸,
1.6份对苯二胺,
2.5份磷酸二氢铵,
60份水。
2.根据权利要求1所述的中空保暖纤维的制备方法,其特征在于,按重量份计,所述处理液由以下组分组成:
20份常规聚酯纺丝油剂,
2份封闭多异氰酸酯,
2.1份乙二醛,
1.6份月桂酰氨乙基硫酸钠,
1.7份油酰氨基酸钠,
2.2份脂肪醇聚氧乙烯醚,
1.8份烷基苯磺酸钠,
2.3份羧甲基纤维素,
1.4份六偏磷酸钠,
0.7份黄柏提取液,
1.2份十二烷基二甲基苄基氯化铵,
2.2份反丁烯二酸,
1.6份对苯二胺,
2.5份磷酸二氢铵,
60份水。
3.根据权利要求1所述的一种保暖纤维的制备方法,其特征在于,按重量份计,所述处理液由以下组分组成:
25份常规聚酯纺丝油剂,
4份封闭多异氰酸酯,
2.1份乙二醛,
1.6份月桂酰氨乙基硫酸钠,
1.7份油酰氨基酸钠,
2.2份脂肪醇聚氧乙烯醚,
1.8份烷基苯磺酸钠,
2.3份羧甲基纤维素,
1.4份六偏磷酸钠,
0.7份黄柏提取液,
1.2份十二烷基二甲基苄基氯化铵,
2.2份反丁烯二酸,
1.6份对苯二胺,
2.5份磷酸二氢铵,
60份水。
4.根据权利要求1所述的一种保暖纤维面料的制备方法,其特征在于,按重量份计,所述处理液由以下组分组成:
21份常规聚酯纺丝油剂,
2.4份封闭多异氰酸酯,
2.1份乙二醛,
1.6份月桂酰氨乙基硫酸钠,
1.7份油酰氨基酸钠,
2.2份脂肪醇聚氧乙烯醚,
1.8份烷基苯磺酸钠,
2.3份羧甲基纤维素,
1.4份六偏磷酸钠,
0.7份黄柏提取液,
1.2份十二烷基二甲基苄基氯化铵,
2.2份反丁烯二酸,
1.6份对苯二胺,
2.5份磷酸二氢铵,
60份水。