CN1117477A - Cellulose sulfuric acid ester type concrete additive - Google Patents
Cellulose sulfuric acid ester type concrete additive Download PDFInfo
- Publication number
- CN1117477A CN1117477A CN 95104886 CN95104886A CN1117477A CN 1117477 A CN1117477 A CN 1117477A CN 95104886 CN95104886 CN 95104886 CN 95104886 A CN95104886 A CN 95104886A CN 1117477 A CN1117477 A CN 1117477A
- Authority
- CN
- China
- Prior art keywords
- sulfuric acid
- acid ester
- cement
- cellulose sulfuric
- admixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
It can extremely improve flowability, mechanical strength and other application property of the cement concrete. It contains collulose sulfuric acid ester.
Description
The present invention relates to a kind of new concrete admixture.
In concrete, mix admixture, can improve concrete mechanical strength and improve other performance, make concrete can satisfy of the particular requirement of different engineerings, solve the difficult problem of construction work it.Therefore develop the admixture of excellent performance, become the research topic of domestic and international hot topic.
The concrete admixture that the purpose of this invention is to provide a kind of cellulose sulfuric acid ester type.
Concrete admixture provided by the present invention, wherein the cellulose sulfuric acid ester substitution value is: 0.1--2.0, viscosity: 1.4--500mPa.s (3% aqueous solution, 25 ℃) has three kinds of prescription patterns: (1) cellulose sulfuric acid ester:
R is H or SO
3Na
(2) the metallic salt mixture of cellulose sulfuric acid ester and naphthalene sulfonic acidformaldehyde condensation product, metallic salt is selected sodium salt, calcium salt, mantoquita, molysite and aluminium salt etc. for use.
M is a metal ion
(3) mixture of cellulose sulfuric acid ester and terpolycyantoamino-formaldehyde resin sodium sulfonate.
Cellulose sulfuric acid ester type concrete additive provided by the invention has good application performance to concrete, when it is spiked into time marquis in the cement concrete with certain amount, can improve flowability, mechanical strength and other performance of cement concrete significantly.The result of use of concrete admixture provided by the invention is listed in the table below, for comparing:
| ????CS ????(C％) | ????NFG ????(C％) | ????MS ????(C％) | Flowing degree of net paste of cement (mm) | Cement paste | Sand-cement slurry | ||
| Water cement ratio | Ultimate compression strength (MPa) | Water cement ratio | Ultimate compression strength (MPa) | ||||
| 0.15 | ????0 | ????0 | ????107 | ????0.37 | ????53.7 | ????0.38 | ????39.6 |
| 0.25 | ????0 | ????0 | ????140 | ????0.36 | ????59.6 | ????0.37 | ????41.1 |
| 0.2 | ????0.3 | ????0 | ????203 | ????0.29 | ????79.8 | ????0.33 | ????43.5 |
| 0.2 | ????0 | ????0.3 | ????209 | ????0.28 | ????85.1 | ????0.32 | ????45.9 |
| 0 | ????0 | ????0 | ????66 | ????0.4 | ????41.9 | ????0.44 | ????35.2 |
Wherein C is the cement abbreviation; CS: its substitution value of cellulose sulfuric acid ester is 0.36, viscosity 2.9mPa.s, and NFG: the naphthalene sulfonic acidformaldehyde condensation product sodium salt, its polymerization degree n is about 10, from synthetic sample; MS: terpolycyantoamino-formaldehyde resin sodium sulfonate; Flowing degree of net paste of cement is measured according to method shown in the GB8076-87, and wherein water cement ratio is 0.35.Cement paste and sand-cement slurry ultimate compression strength are measured according to method shown in the GB177-77.Sand meets the specification of quality of stipulating among the GB178-77 in the sand-cement slurry, and the mass ratio of cement and standard sand is 1: 2.5.When being mixed with admixture, select suitable water cement ratio, to keep and clean slurry of the reference cement of not mixing admixture or the identical degree of mobilization of mortar.As can be seen from the table, different three kinds of prescription patterns, though to cement performance have scarcely with, the ultimate compression strength and the flowing property of can add all apparent in view raising of admixture of the present invention certainly cement paste and sand-cement slurry.
Embodiment one
0.25% cellulose sulfuric acid ester (the substitution value: 0.42 of admixture cement amount, viscosity 5.3mPa.s) flowing degree of net paste of cement reaches 115mm, with clean slurry of admixture admixture reference cement not or the identical degree of mobilization of sand-cement slurry under, cement paste ultimate compression strength reaches 60.9MPa, and sand-cement slurry ultimate compression strength reaches 41.4MPa.
Embodiment two
0.35% cellulose sulfuric acid ester (the substitution value 0.36 of admixture cement amount, viscosity: 2.9mPa.s) with naphthalene sulfonic acidformaldehyde condensation product sodium salt mixture, its proportioning is 0.25: 0.1, flowing degree of net paste of cement reaches 140mm, with clean slurry of admixture admixture reference cement not or the identical degree of mobilization of sand-cement slurry under, cement paste ultimate compression strength reaches 74.7MPa, and sand-cement slurry ultimate compression strength reaches 42.1MPa.
Embodiment three
0.35% cellulose sulfuric acid ester (the substitution value: 0.42 of admixture cement amount, viscosity: 5.3mPa.s) with terpolycyantoamino-formaldehyde resin sodium sulfonate mixture, its proportioning is 0.25: 0.1, flowing degree of net paste of cement reaches 126mm, starching under the identical degree of mobilization with admixture admixture reference cement is unclean, cement paste ultimate compression strength reaches 75.1MPa, and sand-cement slurry ultimate compression strength reaches 42.9MPa.
Claims (2)
1, a kind of concrete admixture is characterized in that containing cellulose sulfuric acid ester, its substitution value 0.1--2.0 viscosity 1.4--500mPa.s (3% aqueous solution, 25 ℃)
Three kinds of prescription patterns are arranged:
(1) cellulose sulfuric acid ester, molecular formula
R is H or SO
3Na:
(2) the metal-salt mixture of cellulose sulfuric acid ester and naphthalene sulfonic acidformaldehyde condensation product;
M is a metal ion
(3) mixture of cellulose sulfuric acid ester and terpolycyantoamino-formaldehyde resin sodium sulfonate.
2, according to the admixture described in the claim 1, it is characterized in that second kind of described metal-salt of prescription pattern, wherein metal especially can be sodium, calcium, copper, iron or aluminium.