CN111747657A - Preparation method of molybdenum-doped tungsten oxide nanostructure electrochromic film - Google Patents
Preparation method of molybdenum-doped tungsten oxide nanostructure electrochromic film Download PDFInfo
- Publication number
- CN111747657A CN111747657A CN202010444685.4A CN202010444685A CN111747657A CN 111747657 A CN111747657 A CN 111747657A CN 202010444685 A CN202010444685 A CN 202010444685A CN 111747657 A CN111747657 A CN 111747657A
- Authority
- CN
- China
- Prior art keywords
- molybdenum
- tungsten oxide
- doped tungsten
- sol
- oxide nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a molybdenum-doped tungsten oxide nanostructure electrochromic film, which adopts the technical scheme that the method comprises the following steps: dissolving tungstic acid in hydrogen peroxide, heating and stirring in an oil bath until a clear solution is obtained, adding molybdenum oxide, ethylene glycol and deionized water into the clear solution, heating an oil bath, condensing and refluxing to obtain molybdenum-doped tungsten oxide nano sol, centrifuging and washing for later use; dissolving ethyl cellulose in ethanol at room temperature, stirring to obtain clear and transparent sol, adding terpineol and the molybdenum-doped tungsten oxide nano sol prepared in the previous step into the sol, and performing rotary evaporation on an organic solvent to obtain molybdenum-doped tungsten oxide nano slurry; uniformly attaching the molybdenum-doped tungsten oxide nano slurry to an ITO (indium tin oxide) or FTO (fluorine-doped tin oxide) conductive glass substrate by adopting a screen printing or blade coating method, calcining by using a muffle furnace, and naturally cooling to obtain the molybdenum-doped tungsten oxide nano structural electrochromic film.
Description
The application is a divisional application, and the original application name is: a method for preparing a screen printing molybdenum doped tungsten oxide nanostructure electrochromic film is disclosed, and the application number is as follows: 2017102708795, filing date: 20170424.
[ technical field ] A method for producing a semiconductor device
The invention belongs to the field of electrochromism, and particularly relates to a preparation method of a molybdenum-doped tungsten oxide nanostructure electrochromism film.
[ background of the invention ]
A phenomenon that a material exhibits a reversible color change when a voltage is applied to the material is called electrochromism, and electrochromic materials include organic materials and inorganic materials, which are receiving attention due to their good cycle stability, and tungsten oxide is a representative substance among inorganic materials.
At present, magnetron sputtering is mostly adopted for preparing large-area tungsten oxide electrochromic films, but a plurality of problems exist: the cost is expensive and the energy consumption is large. One continuous magnetron sputtering instrument is tens of millions in movement and has large power consumption. And secondly, the tungsten oxide film prepared by magnetron sputtering is too compact, is not beneficial to the insertion and the extraction of lithium ions in the color changing process, and has the problems of overlong response time, poor energy utilization rate and the like. How to prepare the electrochromic film with large area and loose and porous microstructure by a simple and cheap process is a problem to be solved urgently in the engineering process.
[ summary of the invention ]
The invention provides a preparation method of a molybdenum-doped tungsten oxide nanostructure electrochromic film, and the prepared film has a loose and porous structure, is beneficial to embedding and removing electrolyte ions in an electrochromic process, has the advantages of short response time, high color change speed and the like, and is hopeful to be applied and popularized in the electrochromic industrialization process.
The invention is realized by the following technical scheme:
a preparation method of a molybdenum-doped tungsten oxide nanostructure electrochromic film comprises the following steps:
a. dissolving tungstic acid in hydrogen peroxide, heating and stirring in an oil bath until a clear solution is obtained, adding molybdenum oxide, ethylene glycol and deionized water into the clear solution, heating an oil bath, condensing and refluxing to obtain molybdenum-doped tungsten oxide nano sol, centrifuging and washing for later use;
b. at room temperature, dissolving ethyl cellulose in ethanol, stirring to obtain clear and transparent sol, adding terpineol and the molybdenum-doped tungsten oxide nano sol prepared in the step a into the sol, and rotationally evaporating an organic solvent to obtain molybdenum-doped tungsten oxide nano slurry;
c. uniformly attaching the molybdenum-doped tungsten oxide nano slurry to an ITO (indium tin oxide) or FTO (fluorine-doped tin oxide) conductive glass substrate by adopting a screen printing or blade coating method, calcining by using a muffle furnace, and naturally cooling to obtain the molybdenum-doped tungsten oxide nano structural electrochromic film.
Preferably, the initial heating temperature of the oil bath in the step a is 85-95 ℃, the temperature of an oil bath pot after adding molybdenum oxide, ethylene glycol and deionized water is 100-130 ℃, the centrifugation speed is 8000-12000 rpm, the centrifugation time is 15-25 min, and deionized water and ethanol are adopted for washing.
Preferably, in the ethylcellulose sol in the step b, the mass ratio of the ethylcellulose to the ethanol is 1: 8-1: 12. the ethyl cellulose is generally insoluble in water, and the proportion of the ethyl cellulose and the ethanol is selected to be proper, so that the dissolving and volatilization of organic matters can be facilitated, and the porosity of the film is improved.
Preferably, the mass ratio of the molybdenum-doped tungsten oxide, the ethyl cellulose sol and the terpineol in the step b is 1: 4: 5-1: 6: 3. the tungsten oxide nano particles have small size, and after redundant organic matters are volatilized, a main body structure of the porous film is formed.
Preferably, the ITO or FTO conductive glass in the step c is subjected to ultrasonic cleaning treatment and surface activity treatment, wherein the ultrasonic cleaning treatment is to perform ultrasonic treatment on the ITO or FTO conductive glass for 10-15 minutes by using a detergent, deionized water, acetone and ethanol respectively, and dry the ITO or FTO conductive glass in an oven at the temperature of 60-80 ℃. The glass is ultrasonically cleaned by using a mixed solution of a detergent, deionized water, acetone and ethanol, so that foreign matters on the surface are effectively removed, and the glass can be removed by ultrasonic oscillation even though insoluble chemical substances are adsorbed.
Preferably, the surface active treatment is to carry out surface active treatment on the ITO or FTO conductive glass by using a plasma instrument, the working power is 150-250 w, the time is 5-10 min, and the pressure change sequence of oxygen is controlled to be 120Pa, 40Pa, 90Pa and 68Pa during working. The surface of the conductive glass is subjected to surface active treatment, particularly the pressure of oxygen is controlled, the nanoscale material adhesion rate is favorably controlled, and the service life of the electrochromic layer is prolonged.
Preferably, the heat treatment temperature of the muffle furnace in the step c is 350-480 ℃, and the heat preservation time is 1-3 h. The muffle furnace has stable high-temperature condition, is beneficial to the full volatilization of organic matters, and is suitable for the mass production of large-area porous structure films.
Compared with the prior art, the invention has the following advantages:
(1) according to the preparation method of the electrochromic film with the molybdenum-doped tungsten oxide nano structure, the molybdenum-doped tungsten oxide film is adopted for screen printing, the thickness of the film layer can be controlled to be 50-400 nm, the size of tungsten oxide nano particles is small, electron transmission is facilitated, the transmission efficiency is improved, and therefore the color changing efficiency is improved;
(2) according to the preparation method of the electrochromic film with the molybdenum-doped tungsten oxide nanostructure, the molybdenum-doped tungsten oxide nano sol prepared based on a condensation reflux method is a simple and convenient method for preparing a large-area electrochromic layer, after the molybdenum-doped tungsten oxide film is subjected to heat treatment, a loose and porous microstructure is generated due to volatilization of organic matters, so that the ion embedding and ion separation in the color changing process are facilitated, the molybdenum-doped tungsten oxide film is prepared by screen printing, and the key problem encountered in the industrialization of an electrochromic intelligent window is solved;
(2) the preparation method of the electrochromic film with the molybdenum-doped tungsten oxide nanostructure, disclosed by the invention, has the advantages of low process energy consumption and low cost, is beneficial to greatly reducing the production cost of enterprises, and is expected to be popularized in the engineering of electrochromic intelligent windows.
[ description of the drawings ]
FIG. 1 is an electron micrograph of a cross section of a screen printed molybdenum doped tungsten oxide film of example 1;
FIG. 2 is a digital photograph of the assembled device of example 1 before discoloration;
FIG. 3 is a digital photograph of the assembled device of example 1 after discoloration;
FIG. 4 is a graph of the transmittance of the assembled device of example 1;
FIG. 5 is a current-potential diagram of the assembled device in example 2;
fig. 6 is a cyclic voltammogram of the assembled device of example 2.
[ detailed description ] embodiments
The preparation method of the electrochromic film with the molybdenum-doped tungsten oxide nano structure is described by combining specific embodiments
Example 1:
a. dissolving 5g of tungstic acid in 60mL of 30% hydrogen peroxide, heating the solution in an oil bath to 95 ℃, stirring the solution to obtain a clear solution, adding 1.44g of molybdenum oxide, 70mL of ethylene glycol and 70mL of deionized water into the clear solution, heating an oil bath pot to 120 ℃, condensing and refluxing the solution for 10 hours to obtain nano tungsten oxide sol, centrifuging the solution at 10000rpm for 20 minutes, pouring out supernatant, and washing precipitates by using ionized water and ethanol respectively;
b. dissolving ethyl cellulose in ethanol at room temperature, wherein the mass ratio of the ethyl cellulose to the ethanol is 1: stirring to obtain clear and transparent sol, taking 15g of the sol, adding 12g of terpineol and 3g of molybdenum-doped tungsten oxide nano sol, and rotationally evaporating the organic solvent at 90 ℃ to prepare molybdenum-doped tungsten oxide nano slurry;
c. respectively carrying out ultrasonic treatment on ITO or FTO conductive glass for 15 minutes by using a detergent, deionized water, acetone and ethanol, drying the ITO or FTO conductive glass in an oven at the temperature of 70 ℃, carrying out surface active treatment on the ITO or FTO conductive glass by using a plasma instrument at the working power of 200w for 5 minutes, controlling the pressure change sequence of oxygen to be 120Pa, 40Pa, 90Pa and 68Pa during working, taking 1g of the prepared molybdenum-doped tungsten oxide nano slurry, uniformly attaching the molybdenum-doped tungsten oxide nano slurry to the ITO or FTO conductive glass by using a blade coating method, carrying out heat treatment on the ITO or FTO conductive glass by using a muffle furnace, setting the temperature of the muffle furnace to be 450 ℃, keeping the temperature for 2 hours, and naturally cooling to obtain the molybdenum-doped tungsten oxide nano-structure electrochromic film with the thickness of 50 nm.
FIG. 1 is an electron micrograph of a cross section of a screen-printed molybdenum-doped tungsten oxide thin film of example 1;
to further understand the electrochromic properties of the molybdenum-doped tungsten oxide thin film prepared in example 1, the prepared thin film was assembled into a device, and the change in light transmittance of the device was measured using a two-electrode system in combination with an electrochemical workstation and an ultraviolet spectrophotometer, and the results showed that the device turned blue when negative pressure (-3V) was applied to the device; a positive pressure (2V) was applied thereto, and the device was discolored.
Fig. 2 and 3 are front and rear digital photographs of the assembled device in example 1, fig. 2 is a transparent state, fig. 3 is a colored state, fig. 4 is a transmittance diagram of the assembled device in example 1, and the light modulation range is 35%, illustrating that the electrochromic device has good cycle stability.
Example 2:
a. 5g of tungstic acid was dissolved in 60mL of 30% hydrogen peroxide, heated to 95 ℃ in an oil bath and stirred to obtain a clear solution. Adding 1.44g of molybdenum oxide, 70mL of ethylene glycol and 70mL of deionized water into the obtained clear solution, heating the oil bath to 110 ℃, and carrying out condensation reflux for 12 hours to obtain the tungsten oxide nano sol. Then, centrifuging at 10000rpm/min for 20min, and pouring out supernatant; finally, washing the precipitate by respectively adopting ionized water and ethanol;
b. dissolving ethyl cellulose in ethanol at room temperature, wherein the mass ratio of the ethyl cellulose to the ethanol is 1: and 5, stirring to obtain clear and transparent sol. Then, 9g of terpineol and 3g of molybdenum-doped tungsten oxide nano sol are added into 18g of clear ethyl cellulose sol, and the organic solvent is evaporated in a rotating manner at 90 ℃ to prepare molybdenum-doped tungsten oxide nano slurry;
c. respectively carrying out ultrasonic treatment on ITO or FTO conductive glass for 15 minutes by using a detergent, deionized water, acetone and ethanol, and drying by using an oven at the temperature of 70 ℃; performing surface active treatment on ITO or FTO conductive glass by using a plasma instrument, wherein the working power is 200w, the time is 8min, the pressure change sequence of oxygen in working is controlled to be 120Pa, 40Pa, 90Pa and 68Pa, and uniformly attaching 1g of molybdenum-doped tungsten oxide nano slurry prepared in the previous step to the ITO or FTO conductive glass by using a blade coating method. And then carrying out heat treatment on the film by using a muffle furnace, setting the temperature of the muffle furnace at 400 ℃, keeping the temperature for 1h, and naturally cooling to obtain the electrochromic film with the molybdenum-doped tungsten oxide nano structure, wherein the thickness of the obtained film layer is 400 nm.
To further understand the electrochromic properties of the molybdenum-doped tungsten oxide thin film prepared in example 2, the prepared thin film was assembled into a device, and the change in light transmittance of the device was measured using a two-electrode system in combination with an electrochemical workstation and an ultraviolet spectrophotometer, and the results showed that the device turned blue when negative pressure (-3V) was applied to the device; a positive pressure (2V) was applied thereto, and the device was discolored.
FIG. 5 is a current-potential diagram of the assembled device of example 2, with a light modulation range of 35%; fig. 6 is a cyclic voltammogram of the assembled device of example 2, illustrating that the electrochromic device has better capacitance.
The invention relates to a preparation method of a molybdenum-doped tungsten oxide nanostructure electrochromic film, which is a simple and convenient method for preparing a large-area electrochromic layer based on molybdenum-doped tungsten oxide nano sol prepared by a condensation reflux method, wherein after the molybdenum-doped tungsten oxide film is subjected to heat treatment, a loose and porous microstructure is generated due to volatilization of organic matters, so that ions can be embedded and removed in the process of color change, the molybdenum-doped tungsten oxide film is prepared by screen printing, the thickness of the film layer can be controlled to be 50-400 nm, the size of tungsten oxide nano particles is small, the electronic transmission is facilitated, the transmission efficiency is improved, and the color change efficiency is improved.
Claims (1)
1. A preparation method of a molybdenum-doped tungsten oxide nanostructure electrochromic film is characterized by comprising the following steps:
a. dissolving 5g of tungstic acid in 60mL of 30% hydrogen peroxide, heating the solution in an oil bath to 95 ℃, stirring the solution to obtain a clear solution, adding 1.44g of molybdenum oxide, 70mL of ethylene glycol and 70mL of deionized water into the clear solution, heating an oil bath pot to 120 ℃, condensing and refluxing the solution for 10 hours to obtain nano tungsten oxide sol, centrifuging the solution at 10000rpm for 20 minutes, pouring out supernatant, and washing precipitates by using ionized water and ethanol respectively;
b. dissolving ethyl cellulose in ethanol at room temperature, wherein the mass ratio of the ethyl cellulose to the ethanol is 1: stirring to obtain clear and transparent sol, taking 15g of the sol, adding 12g of terpineol and 3g of molybdenum-doped tungsten oxide nano sol, and rotationally evaporating the organic solvent at 90 ℃ to prepare molybdenum-doped tungsten oxide nano slurry;
c. respectively carrying out ultrasonic treatment on ITO or FTO conductive glass for 15 minutes by using a detergent, deionized water, acetone and ethanol, drying the ITO or FTO conductive glass in an oven at the temperature of 70 ℃, carrying out surface activity treatment on the ITO or FTO conductive glass by using a plasma instrument at the working power of 200w for 5 minutes, controlling the pressure change sequence of oxygen to be 120Pa, 40Pa, 90Pa and 68Pa during working, uniformly attaching 1g of prepared molybdenum-doped tungsten oxide nano slurry to the ITO or FTO conductive glass by adopting a blade coating method, carrying out heat treatment on the ITO or FTO conductive glass by using a muffle furnace, setting the temperature of the muffle furnace to be 450 ℃, keeping the temperature for 2 hours, and naturally cooling to obtain the molybdenum-doped tungsten oxide nano structure electrochromic film.