CN111730932A - Waterproof floor capable of expelling insects and preventing mildew and production process thereof - Google Patents
Waterproof floor capable of expelling insects and preventing mildew and production process thereof Download PDFInfo
- Publication number
- CN111730932A CN111730932A CN202010633669.XA CN202010633669A CN111730932A CN 111730932 A CN111730932 A CN 111730932A CN 202010633669 A CN202010633669 A CN 202010633669A CN 111730932 A CN111730932 A CN 111730932A
- Authority
- CN
- China
- Prior art keywords
- layer
- butt joint
- floor
- waterproof
- mildew
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof floor capable of expelling insects and preventing mildew and a production process thereof, belonging to the technical field of waterproof floors. The insect-expelling and mildew-preventing waterproof floor and the production process thereof have antibacterial and bactericidal performances, the mildew preventive can inhibit growth of mildew and kill the mildew, so that the composite floor is prevented from being corroded by the fungi, good appearance and physical and mechanical properties are kept, the breeding of the mildew is effectively prevented, insects can be effectively expelled through the camphor wood powder and the elm bark powder, insects are effectively prevented, the connection stability of a joint is ensured, the service life is prolonged, the installation and the disassembly are convenient, and the practicability is improved.
Description
Technical Field
The invention relates to the technical field of waterproof floors, in particular to a waterproof floor capable of expelling insects and preventing mildew and a production process thereof.
Background
With the development of the construction industry, various building materials emerge endlessly, and meet various use requirements of people. Among them, the decorative sheet material is important in interior decoration. In the decorative board, the solid wood board has high use performance, is green and environment-friendly, belongs to a superior material, but has the limitation of high manufacturing cost due to less solid wood resources and more complex construction process; at present, the commonly used plates are mostly prepared from fibers, wood residues and the like through processing technologies such as gluing and the like, and in order to meet the use requirements, the properties such as strength, appearance, texture and the like need to be improved. When the prior floor is used, the mildew resistance of the prior floor is poor, so that the floor is easy to mildew when in use, the attractiveness of the floor is further influenced, and the floor is easy to generate insects after being wetted, the floor is damaged, and the use is influenced
Disclosure of Invention
The invention aims to provide the insect-repelling and mildew-preventing waterproof floor and the production process thereof, wherein the waterproof floor has antibacterial and bactericidal properties, the mildew inhibitor can inhibit growth of mildew and kill the mildew, so that the composite floor is prevented from being corroded by fungi, good appearance and physical and mechanical properties are kept, the mildew is effectively prevented from breeding, insects can be effectively repelled by arranging the camphor wood powder and the elm bark powder, the insects are effectively repelled, the connection stability of a joint is ensured, the service life is prolonged, the installation and the disassembly are convenient, and the practicability is improved, so that the problems in the background technology are solved.
In order to achieve the purpose, the invention provides the following technical scheme:
the waterproof floor capable of expelling insects and preventing mildew comprises a floor body, wherein the floor body comprises a base plate, a lower plate layer and an upper plate layer, the base plate is clamped between the lower plate layer and the upper plate layer, the outer side of the floor body is coated with a waterproof layer, the lower plate layer comprises an extrusion layer and a reinforcing layer, the reinforcing layer is connected below the extrusion layer, the upper plate layer comprises a connecting layer, a sound absorption layer and an outer surface layer, the connecting layer is connected with the upper end face of the base plate, the sound absorption layer is arranged above the connecting layer, the outer surface layer is connected above the sound absorption layer, and butt joint devices are arranged on two sides of the base plate;
the butt joint device comprises a butt joint groove, a clamp groove, a butt joint strip and a convex strip, the butt joint groove is formed in one side end of the base plate, the clamp groove is formed in the bottom end of the butt joint groove from top to bottom, the butt joint strip is installed on the other side end of the base plate, and the convex strip is installed above and below one end of the butt joint strip.
Further, the extrusion layer and the connecting layer are respectively connected with the upper end and the lower end of the base plate through coating adhesives, and the base plate, the lower plate layer and the upper plate layer are connected in a pressing mode.
Furthermore, the butt joint strip is inserted and jointed with the butt joint groove, the convex strip is clamped and jointed with the clamp groove, and the two floor bodies are clamped and jointed through the butt joint device.
The invention provides another technical scheme: a production process of a waterproof floor capable of expelling insects and preventing mildew comprises the following steps:
the method comprises the following steps: wood pressing: the connecting surfaces of the lower plate layer and the upper plate layer are both coated with adhesives, and the lower plate layer, the upper plate layer and the base plate are compacted through a press;
step two: surface processing: putting the compacted plate into a drying box for drying, taking out after drying for 7-12 minutes, polishing the surface of the plate by a polishing device, and cutting the plate into a required shape;
step three: processing groove surfaces: cutting a groove on the side end of the cut plate through a grooving machine to obtain a butt joint groove, and milling the groove in the butt joint groove to obtain a clamp groove;
step four: waterproof coating ingredients: selecting and mixing an antibacterial agent, a mildew preventive, a defoaming agent, camphor wood powder, elm bark powder, eucalyptus oil, litsea cubeba oil, sodium diacetate, sodium humate, zinc oxide, magnesium stearate and an adhesive auxiliary agent as raw materials, wherein the antibacterial agent comprises the following components in percentage by weight: 3-15 parts of a mildew preventive: 5-16 parts of defoaming agent: 4-10 parts of camphorwood powder, 4-12 parts of camphorwood powder, 6-11 parts of elm bark powder, 0.5-2 parts of eucalyptus oil, 0.5-2.5 parts of litsea cubeba oil, 0.5-1.5 parts of sodium diacetate, 1-3 parts of sodium humate, 1.5-3.5 parts of zinc oxide, 3-5 parts of magnesium stearate and 10-30 parts of bonding auxiliary agent;
step five: stirring and standing the ingredients: mixing the coating ingredients, stirring and standing to fully react and fuse to obtain the waterproof coating;
step six: coating of a coating: coating waterproof paint on the outer surface of the processed plate for multiple times until the surface coating is uniformly coated, standing for 3-5 minutes, and drying after bubbles are eliminated;
step seven: and (3) drying the coating: placing the plate coated with the waterproof coating into a drying box for drying, and drying at low temperature of 30-40 ℃ for 100-120 minutes;
step eight: assembling the plate materials: the floor board is assembled by inserting the butt joint strips and the convex strips on one floor board body into the butt joint grooves and the clamp grooves on the other floor board body.
Further, aiming at the fourth step, the antibacterial agent is one or two of nano silver and organosilicon quaternary ammonium salt.
Further, aiming at the fourth step, the mildew preventive is one or two of dimethyl fumarate and octahydroxyquinalin copper.
Further, for step four, the defoaming agent is one or two of dialkyl phosphate and fluorinated alkyl phosphate.
Compared with the prior art, the invention has the beneficial effects that:
1. the invention provides a waterproof floor capable of expelling insects and preventing mildew and a production process thereof.A squeezing layer and a connecting layer are respectively connected with the upper end and the lower end of a base plate through coating adhesives, the base plate, a lower plate layer and an upper plate layer are in press fit connection, a waterproof layer is coated on a floor body, an antibacterial agent in the waterproof layer can keep the growth or reproduction of microorganisms below a necessary level within a certain time, has the functions of killing or inhibiting the growth of microorganisms, has the performance of bacteriostasis and sterilization, can inhibit the growth of mildew and kill the mildew, prevents the composite floor from being corroded by fungi, keeps good appearance and physical and mechanical properties, and effectively prevents the growth of the mildew, and can effectively expel insects and effectively prevent insects by arranging camphor wood powder and elm bark powder.
2. According to the waterproof floor capable of expelling insects and preventing mildew and the production process thereof, the butt joint strips are inserted and connected with the butt joint grooves, the convex strips are connected with the clamp groove in a clamping manner, the two floor bodies are in clamping butt joint through the butt joint device, the plurality of floor bodies are assembled through the butt joint device, the connection stability of joints is ensured, the service life is prolonged, the installation and the disassembly are convenient, and the practicability is improved.
Drawings
FIG. 1 is a schematic view of the overall structure of the present invention;
FIG. 2 is a side view of the overall structure of the present invention;
FIG. 3 is a side cross-sectional view of the overall construction of the present invention;
FIG. 4 is an enlarged view taken at A of FIG. 3 according to the present invention;
FIG. 5 is a cross-sectional view of the overall structure of the present invention;
FIG. 6 is a cross-sectional view of the butt-joint structure of the floor body and the butt-joint device of the present invention;
fig. 7 is an overall production flow diagram of the present invention.
In the figure: 1. a floor body; 11. a base layer plate; 12. a lower board layer; 121. extruding the layer; 122. a reinforcement layer; 13. an upper ply; 131. a connecting layer; 132. a sound absorbing layer; 133. an outer skin layer; 2. a docking device; 21. a butt joint groove; 22. a clamp groove; 23. butting strips; 24. a convex strip; 3. and a waterproof layer.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The first embodiment is as follows:
referring to fig. 1-4, a waterproof floor capable of expelling insects and preventing mildew and a manufacturing process thereof, comprising a floor body 1, wherein the floor body 1 comprises a base plate 11, a lower plate layer 12 and an upper plate layer 13, the base plate 11 is sandwiched between the lower plate layer 12 and the upper plate layer 13, the outer side of the floor body 1 is coated with a waterproof layer 3, the lower plate layer 12 comprises an extrusion layer 121 and a reinforcing layer 122, the reinforcing layer 122 is connected below the extrusion layer 121, the upper plate layer 13 comprises a connecting layer 131, a sound-absorbing layer 132 and an outer surface layer 133, the connecting layer 131 is connected with the upper end surface of the base plate 11, the sound-absorbing layer 132 is arranged above the connecting layer 131, the outer surface layer 133 is connected above the sound-absorbing layer 132, butt-joint devices 2 are arranged at two sides of the base plate 11, the extrusion layer 121 and the connecting layer 131 are respectively connected with the upper end and the lower end of the base plate 11 by coating adhesives, and the base plate 11, the lower plate layer 12, the antibacterial agent in the waterproof layer 3 can keep the growth or reproduction of microorganisms below a necessary level within a certain period of time, has the functions of killing or inhibiting the growth of microorganisms, has the antibacterial and bactericidal performance, and the mildew preventive can inhibit the growth of mildew and kill the mildew, so that the composite floor is prevented from being corroded by fungi, good appearance and physical and mechanical properties are kept, the breeding of the mildew is effectively prevented, and the camphor wood powder and the elm bark powder can effectively repel insects and effectively prevent insects.
Referring to fig. 5-6, the butt joint device 2 includes a butt joint groove 21, a clamp groove 22, a butt joint strip 23 and a convex strip 24, the butt joint groove 21 is disposed in one side end of the base plate 11, the clamp groove 22 is disposed at the upper and lower ends of the bottom end of the butt joint groove 21, the butt joint strip 23 is mounted on the other side end of the base plate 11, the convex strip 24 is mounted above and below one end of the butt joint strip 23, the butt joint strip 23 is inserted into the butt joint groove 21, the convex strip 24 is connected with the clamp groove 22 in a clamping manner, the two floor bodies 1 are in clamping butt joint by the butt joint device 2, and the plurality of floor bodies 1 are assembled by the butt joint device 2, so that stable connection of joints is ensured, the service life is prolonged, the.
Referring to fig. 7, in order to better show the process of producing the waterproof floor capable of repelling insects and mildew, the present embodiment provides a production process of the waterproof floor capable of repelling insects and mildew, including the following steps:
the method comprises the following steps: wood pressing: the adhesive is coated on the connecting surface of the lower plate layer 12 and the upper plate layer 13, and the lower plate layer 12, the upper plate layer 13 and the base plate 11 are compacted through a laminating machine;
step two: surface processing: putting the compacted plate into a drying box for drying, taking out after drying for 7-12 minutes, polishing the surface of the plate by a polishing device, and cutting the plate into a required shape;
step three: processing groove surfaces: cutting a groove on the side end of the cut plate through a grooving machine to obtain a butt joint groove 21, and milling the groove in the butt joint groove 21 to obtain a clamp groove 22;
step four: waterproof coating ingredients: selecting and mixing an antibacterial agent, a mildew preventive, a defoaming agent, camphor wood powder, elm bark powder, eucalyptus oil, litsea cubeba oil, sodium diacetate, sodium humate, zinc oxide, magnesium stearate and an adhesive auxiliary agent as raw materials, wherein the antibacterial agent comprises the following components in percentage by weight: 13 parts of a mildew preventive: 15 parts, defoaming agent: 7 parts of camphor wood powder 11 parts, elm bark powder 9 parts, eucalyptus oil 1 part, litsea cubeba oil 2 parts, sodium diacetate 1 part, sodium humate 1 part, zinc oxide 2 parts, magnesium stearate 3.5 parts, bonding auxiliary agent 25 parts, antibacterial agent which is one or two of nano silver and organic silicon quaternary ammonium salt, mildew preventive which is one or two of dimethyl fumarate and octahydroxyquinoline copper, and defoaming agent which is one or two of dialkyl phosphate and fluorinated alkyl phosphate;
step five: stirring and standing the ingredients: mixing the coating ingredients, stirring and standing to fully react and fuse to obtain the waterproof coating;
step six: coating of a coating: coating waterproof paint on the outer surface of the processed plate for multiple times until the surface coating is uniformly coated, standing for 3-5 minutes, and drying after bubbles are eliminated;
step seven: and (3) drying the coating: placing the plate coated with the waterproof coating into a drying box for drying, and drying at low temperature of 30-40 ℃ for 100-120 minutes;
step eight: assembling the plate materials: the assembly is performed by inserting the butt-joint strips 23 and the convex strips 24 of one floor body 1 into the butt-joint grooves 21 and the clip grooves 22 of the other floor body 1.
Example two:
in order to better show the process of the waterproof floor capable of expelling insects and preventing mildew, the embodiment proposes a production process of the waterproof floor capable of expelling insects and preventing mildew, which comprises the following steps:
the method comprises the following steps: wood pressing: the adhesive is coated on the connecting surface of the lower plate layer 12 and the upper plate layer 13, and the lower plate layer 12, the upper plate layer 13 and the base plate 11 are compacted through a laminating machine;
step two: surface processing: putting the compacted plate into a drying box for drying, taking out after drying for 7-12 minutes, polishing the surface of the plate by a polishing device, and cutting the plate into a required shape;
step three: processing groove surfaces: cutting a groove on the side end of the cut plate through a grooving machine to obtain a butt joint groove 21, and milling the groove in the butt joint groove 21 to obtain a clamp groove 22;
step four: waterproof coating ingredients: selecting and mixing an antibacterial agent, a mildew preventive, a defoaming agent, camphor wood powder, elm bark powder, eucalyptus oil, litsea cubeba oil, sodium diacetate, sodium humate, zinc oxide, magnesium stearate and an adhesive auxiliary agent as raw materials, wherein the antibacterial agent comprises the following components in percentage by weight: 5 parts of a mildew preventive: 10 parts, defoaming agent: 6 parts of camphor wood powder, 12 parts of elm bark powder, 1 part of eucalyptus oil, 1.5 parts of litsea cubeba oil, 0.9 part of sodium diacetate, 1.2 parts of sodium humate, 2 parts of zinc oxide, 4 parts of magnesium stearate, 12 parts of bonding auxiliary agent, one or two of nano silver and organic silicon quaternary ammonium salt as an antibacterial agent, one or two of dimethyl fumarate and octahydroxyquinoline copper as a mildew preventive, and one or two of dialkyl phosphate and fluorinated alkyl phosphate as an antifoaming agent;
step five: stirring and standing the ingredients: mixing the coating ingredients, stirring and standing to fully react and fuse to obtain the waterproof coating;
step six: coating of a coating: coating waterproof paint on the outer surface of the processed plate for multiple times until the surface coating is uniformly coated, standing for 3-5 minutes, and drying after bubbles are eliminated;
step seven: and (3) drying the coating: placing the plate coated with the waterproof coating into a drying box for drying, and drying at low temperature of 30-40 ℃ for 100-120 minutes;
step eight: assembling the plate materials: the assembly is performed by inserting the butt-joint strips 23 and the convex strips 24 of one floor body 1 into the butt-joint grooves 21 and the clip grooves 22 of the other floor body 1.
Example three:
in order to better show the process of the waterproof floor capable of expelling insects and preventing mildew, the embodiment proposes a production process of the waterproof floor capable of expelling insects and preventing mildew, which comprises the following steps:
the method comprises the following steps: wood pressing: the adhesive is coated on the connecting surface of the lower plate layer 12 and the upper plate layer 13, and the lower plate layer 12, the upper plate layer 13 and the base plate 11 are compacted through a laminating machine;
step two: surface processing: putting the compacted plate into a drying box for drying, taking out after drying for 7-12 minutes, polishing the surface of the plate by a polishing device, and cutting the plate into a required shape;
step three: processing groove surfaces: cutting a groove on the side end of the cut plate through a grooving machine to obtain a butt joint groove 21, and milling the groove in the butt joint groove 21 to obtain a clamp groove 22;
step four: waterproof coating ingredients: selecting and mixing an antibacterial agent, a mildew preventive, a defoaming agent, camphor wood powder, elm bark powder, eucalyptus oil, litsea cubeba oil, sodium diacetate, sodium humate, zinc oxide, magnesium stearate and an adhesive auxiliary agent as raw materials, wherein the antibacterial agent comprises the following components in percentage by weight: 13 parts of a mildew preventive: 14 parts, defoaming agent: 6 parts of camphor wood powder, 5 parts of elm bark powder, 1 part of eucalyptus oil, 1.5 parts of litsea cubeba oil, 1 part of sodium diacetate, 2 parts of sodium humate, 2 parts of zinc oxide, 4 parts of magnesium stearate, 12 parts of bonding auxiliary agent, one or two of nano silver and organic silicon quaternary ammonium salt as an antibacterial agent, one or two of dimethyl fumarate and octahydroxyquinoline copper as a mildew preventive, and one or two of dialkyl phosphate and fluorinated alkyl phosphate as a defoaming agent;
step five: stirring and standing the ingredients: mixing the coating ingredients, stirring and standing to fully react and fuse to obtain the waterproof coating;
step six: coating of a coating: coating waterproof paint on the outer surface of the processed plate for multiple times until the surface coating is uniformly coated, standing for 3-5 minutes, and drying after bubbles are eliminated;
step seven: and (3) drying the coating: placing the plate coated with the waterproof coating into a drying box for drying, and drying at low temperature of 30-40 ℃ for 100-120 minutes;
step eight: assembling the plate materials: the assembly is performed by inserting the butt-joint strips 23 and the convex strips 24 of one floor body 1 into the butt-joint grooves 21 and the clip grooves 22 of the other floor body 1.
The waterproof floor produced by the production process provided by the embodiment is placed in a test vessel for testing, and the antibacterial performance, the mildew-proof performance, the waterproof performance and the insect-proof performance of the composite floor are graded and evaluated by observing the surface condition of the waterproof floor, and are shown in the following table:
| antibacterial property | Mildew resistance | Insect-proof performance | Water resistance | |
| Example one | 99 points of | 98 minutes | 99 points of | 99 points of |
| Example two | 93 minutes | 94 minutes | 99 points of | 99 points of |
| EXAMPLE III | 98 minutes | 99 points of | 92 point is | 99 points of |
From the above table, the antibacterial property, the mildew resistance and the wear resistance of the waterproof floor produced by the production process provided in the first embodiment can meet the use requirements, the antibacterial property is strong, the mildew resistance is good, the wear resistance is good, and the antibacterial property, the mildew resistance and the insect resistance of the second and third embodiments do not reach the standard.
In summary, the waterproof floor capable of expelling insects and preventing mildew and the production process thereof provided by the invention, the extrusion layer 121 and the connection layer 131 are respectively connected with the upper end and the lower end of the base plate 11 through coating adhesives, the base plate 11, the lower plate layer 12 and the upper plate layer 13 are connected in a pressing way, the waterproof layer 3 is coated on the floor body 1, the antibacterial agent in the waterproof layer 3 can keep the growth or reproduction of microorganisms below a necessary level within a certain time, has the function of killing or inhibiting the growth of microorganisms, has the performance of bacteriostasis and sterilization, the mildew preventive can inhibit the growth of mildew and kill the mildew, prevents the composite floor from being corroded by fungi, keeps good appearance and physical and mechanical properties, effectively prevents the breeding of the mildew, can effectively expel insects and effectively prevent insects by arranging the camphor wood powder and the bark powder, the butt joint strip 23 is connected with the butt joint groove 21 in an inserting manner, and the convex strip 24 is connected with the clamping groove 22 in an inserting manner, and carry out the block butt joint by interfacing apparatus 2 between two floor bodies 1, assemble a plurality of floor bodies 1 through interfacing apparatus 2, guarantee that the junction is connected stably, improve life, and easy to assemble and dismantle, improve practicality.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be able to cover the technical solutions and the inventive concepts of the present invention within the technical scope of the present invention.
Claims (7)
1. The utility model provides a but waterproof floor of expelling parasite anti-mildew which characterized in that: the floor comprises a floor body (1), wherein the floor body (1) comprises a base plate (11), a lower plate layer (12) and an upper plate layer (13), the base plate (11) is clamped between the lower plate layer (12) and the upper plate layer (13), the outer side of the floor body (1) is coated with a waterproof layer (3), the lower plate layer (12) comprises an extrusion layer (121) and a reinforcing layer (122), the reinforcing layer (122) is connected below the extrusion layer (121), the upper plate layer (13) comprises a connecting layer (131), a sound absorption layer (132) and an outer surface layer (133), the connecting layer (131) is connected with the upper end face of the base plate (11), the sound absorption layer (132) is arranged above the connecting layer (131), the outer surface layer (133) is connected above the sound absorption layer (132), and butt joint devices (2) are arranged on two sides of the base plate (11);
butt joint device (2) are including butt joint groove (21), clamp groove (22), butt joint strip (23) and sand grip (24), set up in base plate (11) one side in butt joint groove (21), set up clamp groove (22) from top to bottom butt joint groove (21) bottom, and installation butt joint strip (23) are gone up to base plate (11) opposite side end, and installation sand grip (24) are gone up and down to butt joint strip (23) one end.
2. The insect-repellent, mold-resistant, waterproof floor as claimed in claim 1, wherein: the extrusion layer (121) and the connecting layer (131) are respectively connected with the upper end and the lower end of the base plate (11) through coating adhesives, and the base plate (11), the lower plate layer (12) and the upper plate layer (13) are connected in a pressing mode.
3. The insect-repellent, mold-resistant, waterproof floor as claimed in claim 1, wherein: the butt joint strip (23) is connected with the butt joint groove (21) in an inserting and combining mode, the convex strip (24) is connected with the clamp groove (22) in a clamping mode, and the two floor bodies (1) are in clamping butt joint through the butt joint device (2).
4. A process for producing the insect-repellent and mold-resistant waterproof floor as claimed in claims 1 to 3, wherein: the method comprises the following steps:
the method comprises the following steps: wood pressing: the connecting surfaces of the lower plate layer (12) and the upper plate layer (13) are coated with adhesives, and the lower plate layer (12), the upper plate layer (13) and the base plate (11) are compacted through a laminating machine;
step two: surface processing: putting the compacted plate into a drying box for drying, taking out after drying for 7-12 minutes, polishing the surface of the plate by a polishing device, and cutting the plate into a required shape;
step three: processing groove surfaces: a groove is formed in the cut plate at the side end through a grooving machine to obtain a butt joint groove (21), and a groove is milled in the butt joint groove (21) to obtain a clamp groove (22);
step four: waterproof coating ingredients: selecting and mixing an antibacterial agent, a mildew preventive, a defoaming agent, camphor wood powder, elm bark powder, eucalyptus oil, litsea cubeba oil, sodium diacetate, sodium humate, zinc oxide, magnesium stearate and an adhesive auxiliary agent as raw materials, wherein the antibacterial agent comprises the following components in percentage by weight: 3-15 parts of a mildew preventive: 5-16 parts of defoaming agent: 4-10 parts of camphorwood powder, 4-12 parts of camphorwood powder, 6-11 parts of elm bark powder, 0.5-2 parts of eucalyptus oil, 0.5-2.5 parts of litsea cubeba oil, 0.5-1 part of sodium diacetate, 1-2 parts of sodium humate, 1-2 parts of zinc oxide, 3-5 parts of magnesium stearate and 10-20 parts of bonding auxiliary agent;
step five: stirring and standing the ingredients: mixing the coating ingredients, stirring and standing to fully react and fuse to obtain the waterproof coating;
step six: coating of a coating: coating waterproof paint on the outer surface of the processed plate for multiple times until the surface coating is uniformly coated, standing for 3-5 minutes, and drying after bubbles are eliminated;
step seven: and (3) drying the coating: placing the plate coated with the waterproof coating into a drying box for drying, and drying at low temperature of 30-40 ℃ for 100-120 minutes;
step eight: assembling the plate materials: the floor board is assembled by inserting the butt joint strip (23) and the convex strip (24) on one floor board body (1) into the butt joint groove (21) and the clamp groove (22) on the other floor board body (1).
5. The process for manufacturing a waterproof floor capable of repelling insects and preventing mildew as claimed in claim 4, wherein the process comprises the following steps: aiming at the fourth step, the antibacterial agent is one or two of nano silver and organosilicon quaternary ammonium salt.
6. The process for manufacturing a waterproof floor capable of repelling insects and preventing mildew as claimed in claim 4, wherein the process comprises the following steps: aiming at the fourth step, the mildew preventive is one or two of dimethyl fumarate and octahydroxyquinalin copper.
7. The process for manufacturing a waterproof floor capable of repelling insects and preventing mildew as claimed in claim 4, wherein the process comprises the following steps: and aiming at the fourth step, the defoaming agent is one or two of dialkyl phosphate and fluorinated alkyl phosphate.