CN111704832A - Multicolor paint and spraying method thereof - Google Patents
Multicolor paint and spraying method thereof Download PDFInfo
- Publication number
- CN111704832A CN111704832A CN202010579631.9A CN202010579631A CN111704832A CN 111704832 A CN111704832 A CN 111704832A CN 202010579631 A CN202010579631 A CN 202010579631A CN 111704832 A CN111704832 A CN 111704832A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- agent
- multicolor
- spraying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a magic color coating and a spraying method thereof, the magic color coating comprises a black primer, a magic color pearl paint and a bright finish paint, wherein the black primer is prepared by mixing the following raw material components in parts by weight: 55-70 parts of benzene-propylene polymer, 7-12 parts of black slurry, 2-5 parts of wetting agent and 30-45 parts of water; the magic color pearlescent paint comprises the following components in percentage by mass: 40-55% of film-forming material, 3-7% of water-based color paste, 11-18% of auxiliary agent, 35-40% of deionized water and 5-10% of paint solvent oil; the gloss finish paint is prepared by mixing the following raw material components in parts by weight: 60-90 parts of epoxy modified acrylic acid weight ester, 25-45 parts of propylene glycol methyl ether acetate, 60-100 parts of UV monomer, 10-17 parts of photoinitiator, 7-12 parts of aluminum powder, 2-20 parts of dispersant, 0.01-1 part of defoamer, 0.05-0.5 part of flatting agent and 10-15 parts of varnish. The black primer of the multicolor paint has good adhesion performance, the multicolor pearlescent paint has long storage period, wear resistance, scratch resistance, strong adhesion of the bright finish, high heat resistance and yellowing resistance, and the invention also relates to a spraying method of the multicolor paint, which has simple operation.
Description
Technical Field
The invention relates to the field of artware processing, in particular to a magic color coating and a spraying method thereof.
Background
Paint is a broad concept. Including aqueous and oily; the oily paint comprises various single-component and two-component room temperature curing paints, high temperature baking paints, UV light curing paints and the like, and also comprises a PU coating, a powder electrostatic coating and the like. The paint is a material which can be coated on the surface of an object by different construction methods to form a continuous solid film with firm adhesion and certain strength. Since the early coatings mostly use vegetable oil as a main raw material, the coatings are also called as paints. The main components of the coating comprise a film forming substance, an auxiliary agent, a pigment and a solvent, and the coating has three main functions of protecting, decorating and masking the defects of the product and improving the value of the product.
With the rapid development of the coating industry, the application of coating products is more and more important, and the coating products are commonly used on artware, wherein the artware is a product formed by processing raw materials or semi-finished products by hands or machines and is a general term for a group of value artware; the source and the life of the handicraft create higher value than the life. It is a crystal of people's wisdom, fully embodies creativity and artistry of human beings, and is a valuable treasure of human beings. Compared with typical handicraft images, the handicraft images are finely carved according to the material of natural gypsum ores. Because the advantages of bright color, glittering and translucent and fine gypsum and pure texture are fully exerted, the design is novel, the modeling is unique, and the gypsum is elegant in style, antique in color and luster, and can be called as Chinese insulation.
The traditional paint is widely applied in a three-layer paint group, in the existing multicolor paint, the primer mostly has weak adhesion, the multicolor pearlescent paint of the middle layer paint has short storage period, is hard and non-wear-resistant after being dried, is easy to wash by alcohol, detergent and water, and has not obvious effect of presenting different colors at different angles after being combined with the primer, and the finish paint has the same weak adhesion and is easy to yellow, so the improvement on the multicolor paint is necessary.
Disclosure of Invention
The invention aims to provide the magic color coating which has strong adhesive capacity and is not easy to yellow and can present different colors at different angles, and also provides a spraying method of the magic color coating.
In order to solve the above technical problems, the present invention can be implemented by adopting the following technical scheme:
an illusive color coating, the coating comprising a black primer, an illusive color pearlescent paint, and a gloss finish:
the black primer is prepared by mixing the following raw material components in parts by weight: 55-70 parts of benzene-propylene polymer, 7-12 parts of black slurry, 2-5 parts of wetting agent and 30-45 parts of water;
the multicolor pearlescent paint comprises the following components in percentage by mass: 40-55% of film-forming material, 3-7% of water-based color paste, 11-18% of auxiliary agent, 35-40% of deionized water and 5-10% of paint solvent oil;
the gloss finish paint is prepared by mixing the following raw material components in parts by weight: 60-90 parts of epoxy modified acrylic acid weight ester, 25-45 parts of propylene glycol methyl ether acetate, 60-100 parts of UV monomer, 10-17 parts of photoinitiator, 7-12 parts of aluminum powder, 2-20 parts of dispersant, 0.01-1 part of defoamer, 0.05-0.5 part of flatting agent and 10-15 parts of varnish.
The black primer has the advantages of few raw material types, convenient purchase, few production procedures, difficult occurrence of the phenomenon of mutual conflict of physical and chemical properties of the raw materials, low cost of the raw materials and good adhesive force;
the magic color pearlescent paint has the advantages of long storage period, toughness, durability, wear resistance, scratch resistance, alcohol resistance, detergent resistance and water washing resistance after being dried, and can present different colors at different angles;
the bright finish paint has the advantages that the mechanical properties such as adhesive force, heat resistance, yellowing resistance, hardness and the like of the bright finish paint are greatly improved by modifying epoxy modified acrylic acid weighted ester.
Further, the black primer is prepared by mixing the following raw material components in parts by weight: 60-65 parts of benzene-propylene polymer, 8-10 parts of black slurry, 3-4 parts of wetting agent and 34-40 parts of water;
the multicolor pearlescent paint comprises the following components in percentage by mass: 45-50% of film-forming material, 4-6% of water-based color paste, 13-16% of auxiliary agent, 36-39% of deionized water and 7-8% of paint solvent oil;
the auxiliary agent is a dispersant, a film forming auxiliary agent, an antifreezing agent, an antiseptic and mildew-proof agent, a thickening agent, a defoaming agent, a flavoring agent and a thixotropic agent.
The gloss finish paint is prepared by mixing the following raw material components in parts by weight: 70-80 parts of epoxy modified acrylic acid weight ester, 30-40 parts of propylene glycol methyl ether acetate, 65-85 parts of UV monomer, 11-15 parts of photoinitiator, 8-10 parts of aluminum powder, 5-15 parts of dispersant, 0.03-0.07 part of defoamer, 0.1-0.4 part of flatting agent and 12-14 parts of varnish.
Further, the multicolor pearlescent paint as described above:
the auxiliary agent is specifically a dispersing agent, a film forming auxiliary agent, an antifreezing agent, an antiseptic and mildew-proof agent, a thickening agent, a defoaming agent, a flavoring agent and a thixotropic agent.
Further, the gloss finish as described above:
the UV monomer is hydroxypropyl acrylate and tripropylene glycol diacrylate;
the photoinitiator adopts one or more of 2-hydroxy-2-methyl phenyl propane-1-ketone, benzophenone and alpha-hydroxy ketone.
The hydroxypropyl acrylate is a colorless transparent liquid and is used as a functional monomer as a crosslinking monomer of acrylic resin, so that the adhesiveness, weather resistance, impact resistance and gloss of the photocuring film can be improved; the tripropylene glycol diacrylate is colorless or light yellow transparent oily liquid, has the characteristics of low shrinkage and high activity, can be used as an active diluent for UV crosslinking, can be a crosslinking and polymerizing composition, and can endow a photocuring film with better flexibility and stability.
The 2-hydroxy-2-methylphenyl propane-1-ketone is a novel high-efficiency photoinitiator, and has high initiation efficiency, good solubility, low odor and yellowing resistance; benzophenone and alpha-hydroxy ketone are also high-efficiency initiators and have good stability.
Further, the spraying method of the multicolor paint comprises the following steps:
s1, cleaning the blank by using a cleaning agent, and standing for a first time to be dried after cleaning;
s2, spraying black primer, and standing for a second drying time;
s3, polishing, wherein the polishing tool is scouring pad;
s4, spraying colorful pearlescent paint;
and S5, spraying a bright finish paint, and standing for a third drying time.
Further, the cleaning agent is an active diluent, and the active diluent is acetone or methyl ethyl ketone.
Wherein the acetone is colorless transparent liquid, is easily soluble in water and is volatile; the methyl ethyl ketone has excellent solubility and drying characteristics, and has the advantages of higher boiling point, lower vapor pressure and the like.
Further, the first drying time is natural drying for more than 10 min.
Naturally, the first drying time can be carried out in various ways, is not limited to a natural drying way, and can also be carried out for 3min to 5min by carrying out heat curing at the temperature of between 60 and 80 ℃.
Further, the second drying time is more than 4 hours of natural drying.
Similarly, the second drying time can be set in various ways, not limited to natural drying, but also can be set at 60-80 ℃ for 1.5-3 h.
If the black primer generates sagging phenomenon in the process of spraying the black primer, the sagging place is polished after the black primer is dried, and then the black primer is sprayed again.
Further, in step S3, polishing is performed using a scouring pad.
The cleaning cloth can effectively prevent the surface of the black primer from being scratched, the unique structure can effectively dissipate heat, the color change caused by overheating during the polishing of the black primer is prevented, the cleaning cloth also has the characteristics of water resistance, oil resistance and the like, and certainly, if the black primer is polished through during the polishing process, the black primer needs to be repaired.
Further, the third drying time is more than 24 hours of natural drying.
Similarly, the third drying time can also be in various modes, is not limited to a natural drying mode, and can also be thermally cured for 12 to 15 hours at the temperature of between 60 and 80 ℃.
The invention has the beneficial effects that: the processing technology of the magic color handicraft is simple, the blank is cleaned firstly, the black primer is sprayed on the blank after the cleaning is finished, then the black primer is polished, the magic color pearlescent paint is sprayed after the polishing is finished, finally the bright finish paint is sprayed and dried, so that the handicraft is processed, the processing process is simple, and the handicraft can present different colors at different angles by spraying the magic color pearlescent paint on the black primer, so that the visual perception of consumers is improved.
Detailed Description
In order to make the technical solution of the present invention better understood by those skilled in the art, the following detailed description of the product of the present invention is provided with reference to the embodiments.
Example 1
The multicolor paint provided by the embodiment comprises the following components:
the black primer is prepared by mixing the following raw material components in parts by weight: 55 parts of benzene-propylene polymer, 7 parts of black slurry, 2 parts of wetting agent and 30 parts of water;
the magic color pearlescent paint comprises the following components in percentage by mass: 40% of film forming material, 3% of water-based color paste, 11% of dispersing agent, 35% of deionized water and 5% of paint solvent oil;
the gloss finish paint is prepared by mixing the following raw material components in parts by weight: 60 parts of epoxy modified acrylic acid weight ester, 25 parts of propylene glycol methyl ether acetate, 60 parts of hydroxypropyl acrylate, 10 parts of 2-hydroxy-2-methyl phenyl propane-1-ketone, 7 parts of aluminum powder, 2 parts of dispersing agent, 0.01 part of defoaming agent, 0.05 part of flatting agent and 10 parts of varnish.
The spraying method of the multicolor paint comprises the following steps:
s1, cleaning the blank by using an acetone reactive diluent, wherein a cleaning tool adopts a brush to conveniently clean the slot of the blank, and the blank is kept stand for more than 10min after cleaning to naturally dry the blank;
s2, spraying black primer by adopting a spray gun for atomization, standing for more than 4 hours to naturally dry the black primer, if the sagging phenomenon occurs in the spraying of the black primer, polishing the sagging part after the black primer is dried, and spraying the black primer again at the sagging part until the black primer is dried;
s3, polishing the black primer by using scouring pad to improve the smoothness, wherein the black primer cannot be polished through in the polishing process, if the black primer is polished through, the black primer is sprayed on the polished place again, and the black primer is polished again after the black primer is dried;
s4, spraying the multicolor pearlescent paint by adopting spray gun atomization, wherein in the spraying process, the groove seam is required to be sprayed uniformly;
and S5, spraying the bright finish paint by adopting a spray gun for atomization, standing for more than 24 hours, and simultaneously, not generating a sagging phenomenon in the spraying process.
Example 2
The multicolor paint provided by the embodiment comprises the following components:
the black primer is prepared by mixing the following raw material components in parts by weight: 60 parts of benzene-propylene polymer, 8 parts of black slurry, 3 parts of wetting agent and 34 parts of water;
the magic color pearlescent paint comprises the following components in percentage by mass: 45% of film forming material, 4% of water-based color paste, 13% of film forming additive, 36% of deionized water and 7% of paint solvent oil;
the gloss finish paint is prepared by mixing the following raw material components in parts by weight: 70 parts of epoxy modified acrylic acid weight ester, 30 parts of propylene glycol methyl ether acetate, 65 parts of tripropylene glycol diacrylate, 11 parts of benzophenone, 8 parts of aluminum powder, 5 parts of dispersing agent, 0.03 part of defoaming agent, 0.1 part of flatting agent and 12 parts of varnish.
The method of spraying the multicolor paint was the same as in example 1.
Example 3
The black primer is prepared by mixing the following raw material components in parts by weight: 65 parts of benzene-propylene polymer, 10 parts of black slurry, 4 parts of wetting agent and 40 parts of water;
the magic color pearlescent paint comprises the following components in percentage by mass: 50% of film forming material, 6% of water-based color paste, 16% of defoaming agent, 39% of deionized water and 8% of coating solvent oil;
the gloss finish paint is prepared by mixing the following raw material components in parts by weight: 80 parts of epoxy modified acrylic acid weight ester, 40 parts of propylene glycol methyl ether acetate, 85 parts of hydroxypropyl acrylate, 15 parts of benzophenone, 10 parts of aluminum powder, 15 parts of dispersing agent, 0.07 part of defoaming agent, 0.4 part of flatting agent and 14 parts of varnish.
The method of spraying the multicolor paint was the same as in example 1.
Example 4
The black primer is prepared by mixing the following raw material components in parts by weight: 70 parts of benzene-propylene polymer, 12 parts of black slurry, 5 parts of wetting agent and 45 parts of water;
the magic color pearlescent paint comprises the following components in percentage by mass: 55% of film forming material, 7% of water-based color paste, 18% of thixotropic agent, 40% of deionized water and 10% of paint solvent oil;
the gloss finish paint is prepared by mixing the following raw material components in parts by weight: 90 parts of epoxy modified acrylic acid weight ester, 45 parts of propylene glycol methyl ether acetate, 100 parts of tripropylene glycol diacrylate, 17 parts of alpha-hydroxy ketone, 12 parts of aluminum powder, 20 parts of dispersing agent, 1 part of defoaming agent, 0.5 part of flatting agent and 15 parts of varnish.
The method of spraying the multicolor paint was the same as in example 1.
TABLE 1 examples of multicolor coating formulations
As can be seen from Table 1, the black primer of the multicolor paint of the invention has physical and chemical properties which are mutually resisted, and has good adhesive force; the magic color pearlescent paint has long storage period, is hard, tough, durable, wear-resistant, scratch-resistant, alcohol-resistant, detergent-resistant and water-resistant after being dried, and can show different colors at different angles; and the mechanical properties of the finish paint, such as adhesive force, heat resistance, yellowing resistance, hardness and the like, are greatly improved.
Meanwhile, the multicolor paint in the table 1 is sprayed on the artware, so that the artware can present different colors at different angles, different visual senses are brought to consumption, and the artware made of the multicolor paint is resistant to scratching and is not easy to yellow.
The foregoing shows and describes the general principles and features of the present invention, together with the advantages thereof. As will be apparent to those skilled in the art from this disclosure, the present invention may be practiced without these specific details; however, those skilled in the art should appreciate that they can readily use the disclosed conception and specific embodiments as a basis for designing or modifying other structures for carrying out the same purposes of the present invention; meanwhile, any changes, modifications, and evolutions of the equivalent changes of the above embodiments according to the actual techniques of the present invention are still within the protection scope of the technical solution of the present invention.
Claims (10)
1. The colorful coating comprises a black primer, a colorful pearlescent paint and a bright finish paint, and is characterized in that:
the black primer is prepared by mixing the following raw material components in parts by weight: 55-70 parts of benzene-propylene polymer, 7-12 parts of black slurry, 2-5 parts of wetting agent and 30-45 parts of water;
the multicolor pearlescent paint comprises the following components in percentage by mass: 40-55% of film-forming material, 3-7% of water-based color paste, 11-18% of auxiliary agent, 35-40% of deionized water and 5-10% of paint solvent oil;
the gloss finish paint is prepared by mixing the following raw material components in parts by weight: 60-90 parts of epoxy modified acrylic acid weight ester, 25-45 parts of propylene glycol methyl ether acetate, 60-100 parts of UV monomer, 10-17 parts of photoinitiator, 7-12 parts of aluminum powder, 2-20 parts of dispersant, 0.01-1 part of defoamer, 0.05-0.5 part of flatting agent and 10-15 parts of varnish.
2. The multicolor paint according to claim 1, characterized in that:
the black primer is prepared by mixing the following raw material components in parts by weight: 60-65 parts of benzene-propylene polymer, 8-10 parts of black slurry, 3-4 parts of wetting agent and 34-40 parts of water;
the multicolor pearlescent paint comprises the following components in percentage by mass: 45-50% of film-forming material, 4-6% of water-based color paste, 13-16% of auxiliary agent, 36-39% of deionized water and 7-8% of paint solvent oil;
the gloss finish paint is prepared by mixing the following raw material components in parts by weight: 70-80 parts of epoxy modified acrylic acid weight ester, 30-40 parts of propylene glycol methyl ether acetate, 65-85 parts of UV monomer, 11-15 parts of photoinitiator, 8-10 parts of aluminum powder, 5-15 parts of dispersant, 0.03-0.07 part of defoamer, 0.1-0.4 part of flatting agent and 12-14 parts of varnish.
3. The multicolor paint according to any one of claims 1 or 2, characterized in that: the auxiliary agent is specifically a dispersing agent, a film forming auxiliary agent, an antifreezing agent, an antiseptic and mildew-proof agent, a thickening agent, a defoaming agent, a flavoring agent and a thixotropic agent.
4. The multicolor paint according to claim 3, characterized in that: the UV monomer is hydroxypropyl acrylate and tripropylene glycol diacrylate.
5. The multicolor paint according to claim 4, characterized in that: the photoinitiator adopts one or more of 2-hydroxy-2-methyl phenyl propane-1-ketone, benzophenone and alpha-hydroxy ketone.
6. The method for spraying the multicolor paint is characterized by comprising the following steps of:
s1, cleaning the blank by using a cleaning agent, and standing for a first time to be dried after cleaning;
s2, spraying black primer, and standing for a second drying time;
s3, polishing, wherein the polishing tool is scouring pad;
s4, spraying colorful pearlescent paint;
and S5, spraying a bright finish paint, and standing for a third drying time.
7. The method of spraying a multicolor paint according to claim 6, characterized in that: the cleaning agent is an active diluent, and the active diluent is acetone or methyl ethyl ketone.
8. The method of spraying a multicolor paint according to claim 7, characterized in that: and the first drying time is more than 10min of natural drying.
9. The method of spraying a multicolor paint according to claim 8, characterized in that: and the second drying time is more than 4 hours of natural drying.
10. The method of spraying a multicolor paint according to claim 9, characterized in that: and the third drying time is more than 24 hours of natural drying.