CN111701387A - 一种光灸烟盒及其制备方法 - Google Patents
一种光灸烟盒及其制备方法 Download PDFInfo
- Publication number
- CN111701387A CN111701387A CN202010589127.7A CN202010589127A CN111701387A CN 111701387 A CN111701387 A CN 111701387A CN 202010589127 A CN202010589127 A CN 202010589127A CN 111701387 A CN111701387 A CN 111701387A
- Authority
- CN
- China
- Prior art keywords
- powder
- oil
- cigarette case
- liquid
- silica gel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种光灸烟盒及其制备方法,制作所述光灸烟盒的原料包括矿石粉、液态医用硅胶、草本植物油、液态渗透剂和稳定剂;所述矿石粉包括砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉中的一种或多种。本发明的制作方法中将矿石粉和液态医用硅胶共同使用,制得的光灸烟盒疏松多孔可以吸附和净化艾光灸产生的有害物质,用于光灸时火力温和,穿透力强,既能达到刺激穴位、促进局部血液循环的功效,又能有效去除有害物质。本发明提供的方法既利用了传统的中医药理论,又利用了现代制作工艺,制作方法简单,成本少,效果好,并达到调理、保护环境的作用。
Description
技术领域
本发明涉及光灸技术领域,具体涉及一种光灸烟盒及其制备方法。
背景技术
中医艾灸是用艾叶制成的艾灸材料产生的艾热刺激体表穴位或特定部位,通过激发经气的活动来调整人体紊乱的生理生活功能,从而达到防病治病目的的一种中医特色治疗方法。随着艾灸作用机理研究的深入,艾灸局部效应及机制越来越受关注。然而用艾灸调理时,有机物燃烧时产生的烟中含有的尼古丁、焦油、一氧化碳以及刺激性物质对人体可能造成危害,尤其是无法忍受烟味或对烟过敏的人。因此,随着中医艾灸的发展,出现了兼具艾灸和针灸效果的光灸产品。光灸可以给人体组织提供温热刺激和光辐射然而光灸,还能提供电磁作用,能够有效避免烟熏、气味、有害气体和环境污染。
发明内容
本发明的目的是提供一种光灸烟盒,其能够吸收、分解和净化光灸材料产生的有害物质,避免对人体产生危害。
为了实现上述目的,本发明采用了如下的技术方案:
本发明一方面是提供一种光灸烟盒,制作所述光灸烟盒的原料包括矿石粉、液态医用硅胶、草本植物油、液态渗透剂和稳定剂;所述矿石粉包括砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉中的一种或多种。
进一步地,所述光灸烟盒中,所述矿石粉的质量百分含量为3%~6%、液态医用硅胶85%~95%、草本植物油1%~3%、液态渗透剂0.5%~1.2%和稳定剂0.4%~0.6%。
进一步地,所述矿石粉包括砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,且质量比为0.8~1.2:4~6:1.5~2.5:0.8~1.2:1。
进一步地,所述砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉的质量比为1:5:2:1:1。
进一步地,所述草本植物油包括丁香油、郁金香油、薰衣草油、香附子油、山茶籽油、茴香油中的一种或多种。
进一步优选地,所述草本植物油包括丁香油、郁金香油、香附子油,且质量比为0.5:1:1。
进一步地,所述稳定剂为羧甲基纤维素钠或聚维酮。
进一步地,所述液态渗透剂为氮酮。
进一步地,所述液态医用硅胶包括液态硅胶A组分和液态硅胶B组分,且所述液态硅胶A组分和液态硅胶B组分的质量比为1~1.5:1。
本发明又一方面是提供上述的光灸烟盒的制备方法,包括步骤:
(1)按配比称取砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,搅拌均匀后置于阴凉处保存,备用;
(2)取液态医用硅胶、草本植物油、液态渗透剂、稳定剂和步骤(1)所得矿石粉搅拌均匀,得到混合粉末,然后将所述混合粉末注入模具内,送入烘箱在95~105℃下烘干处理1~2h,硫化,冷却后取出,即得所述光灸烟盒。
本发明的有益效果体现在:
1、本发明的光灸烟盒由矿石粉、液态医用硅胶、草本植物油、液态渗透剂和稳定剂制作而成,矿石粉和液态医用硅胶共同作用,光灸烟盒疏松多孔可以吸附和净化光灸材料产生的有害物质;砭石受热后发射出对人体有益的远红外线,对人体有疏通经络、加快血液流动以及活血化瘀、调理气血的作用,且使用时的火力温和,穿透力强,既能达到刺激穴位、促进局部血液循环的功效,又能有效去除有害物质;
2、本发明提供的方法既利用了传统的中医药理论,又利用了现代制作工艺,制作方法简单,成本少,效果好,并达到调理、保护环境的作用。
具体实施方式
下面将对本发明技术方案的实施例进行详细的描述。以下实施例仅用于更加清楚地说明本发明的技术方案,因此只作为示例,而不能以此来限制本发明的保护范围。
需要注意的是,除非另有说明,本申请使用的技术术语或者科学术语应当为本发明所属领域技术人员所理解的通常意义。
下面的实施例中的实验方法,如无特殊说明,均为常规方法。下述实施例中所用的试验材料,如无特殊说明,均为自常规生化试剂商店购买得到。以下实施例中的定量试验,均设置三次重复实验,数据为三次重复实验的平均值或平均值±标准差。
本发明提供了一种光灸烟盒,制作光灸烟盒的原料包括矿石粉的质量百分含量为3%~6%、液态医用硅胶85%~95%、草本植物油1%~3%、液态渗透剂0.5%~1.2%和稳定剂0.4%~0.6%。
具体地,具体地,矿石粉包括砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,且质量比为1:5:2:1:1。具体地,砭石可以为泗滨砭石,泗滨砭石在8000~14000nm光谱区的法向发射率高达0.923。矿石粉在加热的条件下缓慢稳定的发射对人体有益的红外线,加之精油的作用,可以充分发挥光灸烟盒的作用。
具体地,草本植物油包括丁香油、郁金香油、香附子油,且质量比为0.5:1:1。
具体地,液态医用硅胶包括液态硅胶A组分和液态硅胶B组分,且所述液态硅胶A组分和液态硅胶B组分的质量比为1~1.5:1。优选地,液态硅胶A组分和液态硅胶B组分的质量比为50:43。液态硅胶A组分和液态硅胶B组分都是可流动的液体,其中B组分中含金触媒催化剂或其它助剂。在一定温度下,即可硫化成弹性体。其硫化机理是,生胶端基上的乙烯基和交联剂分子上的硅氢键,在含铂化合物的催化下发生加成反映来完成的。液态医用硅胶具有优良的电气性能和化学稳定性、耐水、耐臭氧、耐辐照、耐气候老化、憎水防潮、防震、良好的低压缩变形、低燃烧性;具有生理惰性、无毒、无味、以及硫化速度可以用温度来很顺利控制等优点。本发明的液态医用硅胶可以为现有市场上购买得到的产品。
具体地,液态渗透剂为氮酮。
具体地,稳定剂为羧甲基纤维素钠或聚维酮。
制备上述光灸烟盒的方法包括如下步骤:
(1)按配比称取砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,搅拌均匀后置于阴凉处保存,备用;
(2)取液态医用硅胶、草本植物油、液态渗透剂、稳定剂和步骤(1)所得矿石粉搅拌均匀,得到混合粉末,然后将混合粉末注入模具内,送入烘箱在95~105℃下烘干处理1~2h,硫化,冷却后取出,即得光灸烟盒。
实施例1
本发明提供了一种光灸烟盒,制作光灸烟盒的原料包括如下重量份的组分:矿石粉5份、液态医用级硅胶A 50份、液态医用没硅胶B 43份、丁香油0.5份、郁金香油1份、香附子油1份、液态渗透剂1份和稳定剂0.5份。
具体地,具体地,矿石粉包括砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,质量比为1:5:2:1:1。
具体地,液态渗透剂为氮酮。
具体地,稳定剂为羧甲基纤维素钠。
制备上述光灸烟盒的方法包括如下步骤:
(1)按配比称取砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,搅拌均匀后置于阴凉处保存,备用;
(2)取液态医用硅胶、草本植物油、液态渗透剂、稳定剂和步骤(1)所得矿石粉搅拌均匀,得到混合粉末,然后将混合粉末注入模具内,送入烘箱在100℃下烘干处理1h,硫化,冷却后取出,即得光灸烟盒。
实施例2
本发明提供了一种光灸烟盒,制作光灸烟盒的原料包括如下重量份的组分:矿石粉4份、液态医用级硅胶A 51份、液态医用没硅胶B 44份、丁香油0.4份、郁金香油0.9份、香附子油0.9份、液态渗透剂1.2份和稳定剂0.6份。
具体地,具体地,矿石粉包括砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,质量比为1:5:2:1:1。
具体地,液态渗透剂为氮酮。
具体地,稳定剂为聚维酮。
制备上述光灸烟盒的方法包括如下步骤:
(1)按配比称取砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,搅拌均匀后置于阴凉处保存,备用;
(2)取液态医用硅胶、草本植物油、液态渗透剂、稳定剂和步骤(1)所得矿石粉搅拌均匀,得到混合粉末,然后将混合粉末注入模具内,送入烘箱在95℃下烘干烘干处理2h,硫化,冷却后取出,即得光灸烟盒。
实施例3
本发明提供了一种光灸烟盒,制作光灸烟盒的原料包括如下重量份的组分:矿石粉6份、液态医用级硅胶A 49份、液态医用没硅胶B 41份、丁香油0.4份、郁金香油1份、香附子油1份、液态渗透剂1.2份和稳定剂0.4份。
具体地,具体地,矿石粉包括砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,质量比为1:5:2:1:1。
具体地,液态渗透剂为氮酮。
具体地,稳定剂为羧甲基纤维素钠。
制备上述光灸烟盒的方法包括如下步骤:
(1)按配比称取砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,搅拌均匀后置于阴凉处保存,备用;
(2)取液态医用硅胶、草本植物油、液态渗透剂、稳定剂和步骤(1)所得矿石粉搅拌均匀,得到混合粉末,然后将混合粉末注入模具内,送入烘箱在105℃下烘干烘干处理1h,硫化,冷却后取出,即得光灸烟盒。
对比例1
本对比例提供了一种光灸烟盒,制作光灸烟盒的原料包括如下重量份的组分:矿石粉2份、液态医用级硅胶A 50份、液态医用没硅胶B 43份、丁香油0.5份、郁金香油1份、香附子油1份、液态渗透剂1份和稳定剂0.5份。
具体地,矿石粉包括砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,且质量比为1:5:2:1:1。
具体地,液态渗透剂为氮酮。
具体地,稳定剂为羧甲基纤维素钠。
制备上述光灸烟盒的方法包括如下步骤:
(1)按配比称取砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,搅拌均匀后置于阴凉处保存,备用;
(2)取液态医用硅胶、草本植物油、液态渗透剂、稳定剂和步骤(1)所得矿石粉搅拌均匀,得到混合粉末,然后将混合粉末注入模具内,送入烘箱在100℃下烘干烘干处理1h,硫化,冷却后取出,即得光灸烟盒。
对比例2
本对比例提供了一种光灸烟盒,制作光灸烟盒的原料包括如下重量份的组分:矿石粉5份、液态医用级硅胶A 50份、液态医用没硅胶B 43份、丁香油0.5份、液态渗透剂5份和稳定剂0.5份。
具体地,矿石粉包括砭石粉和稀土粉,质量比为1:5。
具体地,液态渗透剂为氮酮。
具体地,稳定剂为羧甲基纤维素钠。
制备上述光灸烟盒的方法包括如下步骤:
(1)按配比称取砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,搅拌均匀后置于阴凉处保存,备用;
(2)取液态医用硅胶、草本植物油、液态渗透剂、稳定剂和步骤(1)所得矿石粉搅拌均匀,得到混合粉末,然后将混合粉末注入模具内,送入烘箱在100℃下烘干烘干处理1h,硫化,冷却后取出,即得光灸烟盒。
为了验证本发明的光灸烟盒的作用,本发明还进行了体验使用感调查:
施灸者和体验者各80人,男女合计体验160例,平均年龄48岁,最大年龄65岁,最小年龄30岁;体验者使用光灸烟盒进行光灸,一天12时内,每人二次,每次30~40分钟,连续3天,分别将光灸烟盒用于在体验者肩、颈、腰、背的疲劳部位施灸疗;体验完成后,施灸者和体验者互换角色操作。使用感调查共进行3天。
表1光灸烟盒使用感调查结果
总人数 | 有效 | 无效 | 光灸异味 | |
实施例1 | 16 | 15 | 1 | 无 |
实施例2 | 16 | 14 | 2 | 无 |
实施例3 | 16 | 14 | 2 | 无 |
对比例1 | 16 | 10 | 5 | 无 |
对比例2 | 16 | 9 | 6 | 无 |
有效:缓解疲劳、心情舒畅有明显改善效果或疲劳症状消失。
无效:缓解疲劳、心情舒畅没有效果。
光灸异味指光灸过程中产生的烟味或刺激性气味。
最后应说明的是:以上各实施例仅用以说明本发明的技术方案,而非对其限制;尽管参照前述各实施例对本发明进行了详细的说明,本领域的普通技术人员应当理解:其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分或者全部技术特征进行等同替换;而这些修改或者替换,并不使相应技术方案的本质脱离本发明各实施例技术方案的范围,其均应涵盖在本发明的权利要求和说明书的范围当中。
Claims (9)
1.一种光灸烟盒,其特征在于,制作所述光灸烟盒的原料包括矿石粉、液态医用硅胶、草本植物油、液态渗透剂和稳定剂;所述矿石粉包括砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉中的一种或多种。
2.根据权利要求1所述的光灸烟盒,其特征在于,所述光灸烟盒的原料中,所述矿石粉的质量百分含量为3%~6%、液态医用硅胶85%~95%、草本植物油1%~3%、液态渗透剂0.5%~1.2%和稳定剂0.4%~0.6%。
3.根据权利要求1所述的光灸烟盒,其特征在于,所述矿石粉包括砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,且质量比为0.8~1.2:4~6:1.5~2.5:0.8~1.2:1。
4.根据权利要求3所述的光灸烟盒,其特征在于,所述砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉的质量比为1:5:2:1:1。
5.根据权利要求1所述的光灸烟盒,其特征在于,所述草本植物油包括丁香油、郁金香油、薰衣草油、香附子油、山茶籽油、茴香油中的一种或多种。
6.根据权利要求5所述的光灸烟盒,其特征在于,所述草本植物油包括丁香油、郁金香油、香附子油,且质量比为0.5:1:1。
7.根据权利要求1所述的光灸烟盒,其特征在于,所述稳定剂为羧甲基纤维素钠或聚维酮;所述液态渗透剂为氮酮。
8.根据权利要求1所述的光灸烟盒,其特征在于,所述液态医用硅胶包括液态硅胶A组分和液态硅胶B组分,且所述液态硅胶A组分和液态硅胶B组分的质量比为1~1.5:1。
9.权利要求1~8任意一项所述的光灸烟盒的制备方法,其特征在于,包括步骤:
(1)按配比称取砭石粉、稀土粉、纳米陶瓷粉、磁铁矿石粉、纳净石粉,搅拌均匀后置于阴凉处保存,备用;
(2)取液态医用硅胶、草本植物油、液态渗透剂、稳定剂和步骤(1)所得矿石粉搅拌均匀,得到混合粉末,然后将所述混合粉末注入模具内,送入烘箱在95~105℃下烘干处理1~2h,硫化,冷却后取出,即得所述光灸烟盒。