CN111675576A - 玉米抗旱保水型包膜控释剂及其制法 - Google Patents
玉米抗旱保水型包膜控释剂及其制法 Download PDFInfo
- Publication number
- CN111675576A CN111675576A CN202010768585.7A CN202010768585A CN111675576A CN 111675576 A CN111675576 A CN 111675576A CN 202010768585 A CN202010768585 A CN 202010768585A CN 111675576 A CN111675576 A CN 111675576A
- Authority
- CN
- China
- Prior art keywords
- corn
- fertilizer
- water
- weight
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
玉米抗旱保水型包膜控释剂及其制法，包膜层合成的各组分重量份数配比：聚乙烯醇5～10、普通玉米淀粉5～10、丙烯酸树脂吸水剂1、沸石30～40、双氰胺粉、硫酸铜粉、硼砂一种或两种以上0.01～0.11、硫酸锌粉0.01、水38.9～58.9；包膜层厚度重量为包膜颗粒肥料总重量的5％～7％。将保水型原料作为肥料包膜层主要成分，并配合玉米生长所需的有益营养元素铜、铁、锌以及氮素增效剂和环境友好的可生物降解高分子粘结剂包裹玉米专用复合肥为玉米生产提供一种制备工艺简单，保水供肥功能结合的新型玉米专用肥，实现玉米生长期一次施肥，降低玉米生产的劳作成本，提高经济效益，有利于在玉米生产中大规模推广使用。
Description
技术领域
本发明涉及玉米专用肥料制备领域，特别是一种玉米抗旱保水型包膜控释剂及其制法。
背景技术
玉米是高产作物，在世界播种面积和总产量仅次于水稻和小麦居第三位，玉米不仅是粮食作物，又是经济和饲料兼用的作物，是数百种有价值的工业品的重要原料，在国民经济中占极重要的地位。
玉米施肥技术包括基肥、种肥及追肥，追肥分为苗肥、穗肥和粒肥。施肥是玉米产量和品质的保证。但由于玉米价格较低，种植利润太小，施肥次数频繁，农户不愿投入过多劳力去施肥管理；加上玉米种植区多为干旱和半干旱地区，由于供水的影响，使普通玉米专用肥的肥料利用率很低，无法适应玉米生长。因此开发一种价格相对合理，肥料养分缓释性较好，具有保水功能的符合玉米生产的旱田耕作环境的专用控释肥料以适应玉米生产需要。而目前专用肥多以复混造粒为主，肥料养分利用率低，本身不能很好保水，不能很好的满足玉米生长的需要。
发明内容
本发明的目的是采用水肥耦合原理，将保水型原料作为肥料包膜层主要成分，配合玉米生长所需的有益营养元素铜、锌以及氮素增效剂和环境友好的可生物降解高分子粘结剂包裹玉米专用复合肥，为玉米生产提供一种制备工艺简单，保水供肥功能结合的新型玉米专用肥，实现玉米生长期一次施肥，降低玉米生产的劳作成本，提高经济效益，有利于在玉米生产中大规模推广使用。
本发明提供的玉米抗旱保水型包膜控释剂，包括玉米专用颗粒肥料和包膜层，其特征是包膜层投料成分及重量份数比例如下：
聚乙烯醇(PVA)5～10
普通玉米淀粉5～10
丙烯酸树脂吸水剂1
沸石(粒度300～400目)30～40
双氰胺粉、硫酸铜粉、硼砂一种或两种以上0.01～0.11
硫酸锌粉体0.01
水38.9～58.9
包膜层厚度重量为包膜颗粒肥料总重量的5％～7％。
上述的聚乙烯醇PVA分子量为1300～1800。
上述的玉米淀粉为粒级为30～40目的普通玉米淀粉。
上述的膜层成分含有丙烯酸树脂保水剂的吸水倍数100～200，粒度300～400目。
本发明提供的玉米抗旱保水型包膜控释剂制备方法，其特征是：
先进行包膜层合成，将各组分(保水剂除外)按上述重量份数比例投料，在高速搅拌机中搅拌30～40分钟，反应温度80～90℃，搅拌机转速100r/min，在进行包膜作业时，将丙烯酸树脂吸水剂加入搅拌机迅速搅拌后在90～100℃热风作用下包膜；
然后进行包膜，在常用圆盘造粒机上，将包膜液通过气泵雾化后对常用玉米颗粒专用肥料包膜，圆盘转速10r/min，肥料每100kg，喷液速度1L/min，包膜层喷涂厚度重量为包膜颗粒肥料总重量的5％，冷却包装。
本发明和现有技术相比，具有如下优点：
1、利用水肥耦合原理，将保水剂作为包膜层成分，配合肥料养分释放的抑制剂，提高肥料中养分的有效性和水份利用效率，适于旱作生产；
2、工艺简单，设备为常用的反应釜、搅拌器、空气泵，喷枪和圆盘造粒机，生产设备成本低，可直接投入现有肥料厂生产；
3、包膜原料易得，可生物降解，且对环境友好，降解成分有效地改善土壤结构；
具体实施方式
实施例1：
将5kg聚乙烯醇、5kg玉米淀粉、40kg沸石、0.1kg双氰胺粉、0.01kg硫酸铜粉、0.01kg硫酸锌粉与48.9kg水混合，其中双氰胺粉和硫酸铜粉可以使用其中一种，也可以两种同时使用。在高速搅拌机中搅拌30分钟，反应温度90℃，搅拌机转速100r/min。制成包膜液转入与空气泵相连地储液灌中。将玉米专用颗粒复合肥料利用振动筛筛分分级，同一粒度的颗粒一匹次生产；将筛分后的100kg颗粒肥料装入带有加热功能的圆盘造粒机，在60℃条件下预热，旋转刨光肥料表面10分钟；包膜时，将1kg保水剂丙烯酸树脂加入包膜液中快速搅拌，以肥料每100kg，喷液速度1L/min在90℃热风作用下包膜，包膜层喷涂厚度重量为包膜颗粒肥料总重量的5％，冷却包装。
实施例2：
将10kg聚乙烯醇、10kg玉米淀粉、30kg沸石、0.1kg双氰胺粉、0.01kg硫酸铜粉、0.01kg硫酸锌粉与48.9kg水混合，在高速搅拌机中搅拌30分钟，反应温度90℃，搅拌机转速：100r/min。制成包膜液转入与空气泵相连的储液灌中，将玉米专用颗粒复合肥料利用振动筛筛分分级，同一粒度的颗粒一匹次生产；将筛分后的100kg颗粒肥料装入带有加热功能的圆盘造粒机，在60℃条件下预热，旋转刨光肥料表面10分钟；包膜时，将1kg保水剂加入包膜液中快速搅拌，以肥料每100kg，喷液速度1L/min在90℃热风作用下包膜，包膜层喷涂厚度重量为包膜颗粒肥料总重量的5％，冷却包装。
实施例3：
将10kg聚乙烯醇、10kg玉米淀粉、40kg沸石、0.1kg双氰胺粉、0.01kg硫酸铜粉、0.01kg硫酸锌粉与38.9kg水混合，在高速搅拌机中搅拌30分钟，反应温度90℃，搅拌机转速：100r/min。制成包膜液转入与空气泵相连的储液灌中。将玉米专用颗粒复合肥料利用振动筛筛分分级，同一粒度的颗粒一匹次生产；将筛分后的100kg颗粒肥料装入带有加热功能的圆盘造粒机，在60℃条件下预热，旋转刨光肥料表面10分钟；包膜时，将1kg保水剂加入包膜液中快速搅拌，以肥料每100kg，喷液速度1L/min在100℃热风作用下包膜，包膜层喷涂厚度重量为包膜颗粒肥料总重量的5％，冷却包装。
实施例4：
将5kg聚乙烯醇、10kg玉米淀粉、30kg沸石、0.1kg双氰胺粉、0.01kg硫酸铜粉、0.01kg硫酸锌粉、0.01kg硼砂与53.9kg水混合，在高速搅拌机中搅拌30分钟，反应温度90℃，搅拌机转速：100r/min。制成包膜液转入与空气泵相连的储液灌中。将玉米专用颗粒复合肥料利用振动筛筛分分级，同一粒度的颗粒一匹次生产；将筛分后的100kg颗粒肥料装入带有加热功能的圆盘造粒机，在60℃条件下预热，旋转刨光肥料表面10分钟；包膜时，将1kg保水剂加入包膜液中快速搅拌，以肥料每100kg，喷液速度1L/min在100℃热风作用下包膜，包膜层喷涂厚度重量为包膜颗粒肥料总重量的5％，冷却包装。
实施例5：
将7kg聚乙烯醇、9kg玉米淀粉、35kg沸石、0.1kg双氰胺粉、0.01kg硫酸锌粉与53.9kg水混合，在高速搅拌机中搅拌30分钟，反应温度90℃，搅拌机转速：100r/min。制成包膜液转入与空气泵相连的储液灌中。将玉米专用颗粒复合肥料利用振动筛筛分分级，同一粒度的颗粒一匹次生产；将筛分后的100kg颗粒肥料装入带有加热功能的圆盘造粒机，在60℃条件下预热，旋转刨光肥料表面10分钟；包膜时，将1kg保水剂加入包膜液中快速搅拌，以肥料每100kg，喷液速度1L/min在100℃热风作用下包膜，包膜层喷涂厚度重量为包膜颗粒肥料总重量的5％，冷却包装。
使用效果：在山东省种植玉米，两种土壤均为中等肥力。用盆栽和田间试验法验证包膜控释玉米专用肥的应用效果，种植一季后土壤仍有肥料残留。在等养分和等比例条件下，采用包膜和非包膜处理。氮磷钾养分比例为18∶8∶12，或22∶10∶12施肥量按棕壤长期定位肥料试验最佳施肥量氮为8公斤/亩，减10％后为7.2公斤N/亩。采用一次施肥免追肥，用等比例和等量的常规复合肥作对照，使用包膜肥料不论是5％或8％包膜厚度，生长期间两种土壤上均未出现脱肥或后期生长过旺现象，植株生长良好。而对照在抽雄前有明显的养分供应不足，植株较矮，叶色较黄。到成熟期脱肥严重，中下部叶片黄化，变红，出现典型的缺氮症状，产量明显降低。棕壤玉米施用5％包膜和8％包膜复合肥的处理分别比对照增产8.01％～12.58％和14.39％～20.21％。草甸土施用5％包膜肥的增产效果更明显，增产幅度达到18.74％～44.17％。比常规施肥减少肥料用量30％，棕壤玉米产量达到674.98～714.84公斤/亩，草甸土玉米达到621公斤/亩，达到和超过常规施肥产量。
Claims (6)
1.玉米抗旱保水型包膜控释剂，包括玉米专用颗粒肥料和包膜层，其特征是包膜层投料成分及重量份数比例如下：
聚乙烯醇5～10
普通玉米淀粉5～10
丙烯酸树脂吸水剂1
沸石30～40
双氰胺粉、硫酸铜粉、硼砂一种或两种以上0.01～0.11
硫酸锌粉0.01
水38.9～58.9
包膜层厚度重量为包膜颗粒肥料总重量的5％～7％。
2.根据权利要求1所述的玉米抗旱保水型包膜控释剂，其特征在于聚乙烯醇PVA分子量为1300～1800。
3.根据权利要求1所述的玉米抗旱保水型包膜控释剂，其特征在于玉米淀粉为粒级30～40目的普通玉米淀粉。
4.根据权利要求1所述的玉米抗旱保水型包膜控释剂，其特征在于膜层成分含有丙烯酸树脂吸水剂，吸水倍数300～400。
5.根据权利要求1所述的玉米抗旱保水型包膜控释剂，其特征在于沸石粒度为300～400目。
6.玉米抗旱保水型包膜控释剂制法，其特征是：先进行包膜层合成，将各组分按重量份数比例投料，聚乙烯醇5～10、普通玉米淀粉5～10、沸石30～40、双氰胺粉、硫酸铜粉、硼砂一种或两种以上0.01～0.11、硫酸锌粉0.01、水38.9～58.9；
在高速搅拌机中搅拌30～40分钟，反应温度80～90℃，搅拌机转速100r/min，在进行包膜作业时，将重量份数比例为1的丙烯酸树脂吸水剂加入搅拌机迅速搅拌后在90～100℃热风作用下包膜；
在造粒机上，将包膜液通过气泵雾化后对定量常用玉米颗粒专用肥料包膜，圆盘转速10r/min，肥料每100kg，喷液速度1L/min，包膜层喷涂厚度重量为包膜颗粒肥料总重量的5％～7％。