CN111644051A - 一种可高效去除室内甲醛的红松菓净醛棉及其制备的净化器 - Google Patents
一种可高效去除室内甲醛的红松菓净醛棉及其制备的净化器 Download PDFInfo
- Publication number
- CN111644051A CN111644051A CN202010374162.7A CN202010374162A CN111644051A CN 111644051 A CN111644051 A CN 111644051A CN 202010374162 A CN202010374162 A CN 202010374162A CN 111644051 A CN111644051 A CN 111644051A
- Authority
- CN
- China
- Prior art keywords
- fiber layer
- layer
- aldehyde
- cotton
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种可高效去除室内甲醛的红松菓净醛棉及其制备的净化器，所述红松菓净醛棉包括天然纤维层、抗菌纤维层、净化纤维层、表面加强纤维层和压胶层，所述天然纤维层、抗菌纤维层和净化纤维层从上至下依次设置，所述表面加强纤维层设置在上下两侧表面，各个纤维层之间通过压胶层进行边缘粘接，其中抗菌纤维层与净化纤维层之间设置有若干个氧化锰纳米纤维微球，本发明以净化纤维层为主体的红松菓净醛棉配合氧化锰纳米纤维微球可对甲醛进行有效处理，将其去除催化产生二氧化碳和水，活性炭纳米纤维可有效吸附甲醛，配合红松纳米纤维进行催化，氧化锰纳米纤维微球内部形成有空隙，相同体积下相比于活性炭等物质吸附效果更好。
Description
技术领域
本发明涉及红松菓净醛棉技术领域，具体为一种可高效去除室内甲醛的红松菓净醛棉及其制备的净化器。
背景技术
甲醛，无色有刺激性气体，化学式HCHO或CH2O，分子量30.00，又称蚁醛，无色，对人眼、鼻等有刺激作用，气体相对密度1.067（空气=1），液体密度0.815g/cm³（-20℃），熔点-92℃，沸点-19.5℃，易溶于水和乙醇，水溶液的浓度最高可达55%，具有还原性，尤其是在碱性溶液中，还原能力更强，2017年10月27日，世界卫生组织国际癌症研究机构公布的致癌物清单中，将甲醛放在一类致癌物列表中，2019年7月23日，甲醛被列入有毒有害水污染物名录。
甲醛对人体危害极大，红松菓净醛棉的主体为红松纳米纤维可对甲醛进行有效的催化去除。
发明内容
本发明的目的在于提供一种可高效去除室内甲醛的红松菓净醛棉及其制备的净化器，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种可高效去除室内甲醛的红松菓净醛棉，所述红松菓净醛棉包括天然纤维层、抗菌纤维层、净化纤维层、表面加强纤维层和压胶层，所述天然纤维层、抗菌纤维层和净化纤维层从上至下依次设置，所述表面加强纤维层设置在上下两侧表面，各个纤维层之间通过压胶层进行边缘粘接，其中抗菌纤维层与净化纤维层之间设置有若干个氧化锰纳米纤维微球，所述氧化锰纳米纤维微球通过氧化锰纤维膜加捻聚拢成束条，即氧化锰纤维，后经切断后挤压成纤维微球。
优选的，所述天然纤维层通过椰子纤维、竹炭纤维、蚕丝纤维、竹原纤维、剑麻纤维和聚乳酸纤维中的一种或多种组合编织而成。
优选的，所述抗菌纤维层通过二氧化钛纤维和镀银纤维编织而成。
优选的，所述净化纤维层通过红松纳米纤维和活性炭纳米纤维编织而成。
优选的，所述表面加强纤维层为高硅氧纤维层或聚氯乙烯复合材料层。
优选的，所述压胶层包括以重量分数计的氯化聚乙烯橡胶55-80g、丙酮8-16g和石蜡25-35g。
一种可高效去除室内甲醛的红松菓净醛棉制备的净化器，包括壳体，所述壳体的左右两侧端面上分别设置有进气口和排气口，所述进气口和排气口之间通过管道相连通，所述进气口和排气口上设置有防尘网，所述管道上设置有风机和除湿器，所述管道上设置有若干个上下对称分布的净化组件，所述净化组件包括从净醛棉层，所述净醛棉层采用上述任一所述的一种可高效去除室内甲醛的红松菓净醛棉。
优选的，所述净化组件包括盖板，所述盖板上设置有锁扣，所述盖板通过转动座转动安装在管道上，所述盖板内侧壁上固定安装有密封边，所述盖板的内侧壁上设置有对称分布的安装架，所述安装架上设置有插接边，所述插接边的内部插接设置有净醛棉层。
与现有技术相比，本发明的有益效果是：以净化纤维层为主体的红松菓净醛棉配合氧化锰纳米纤维微球可对甲醛进行有效处理，将其去除催化产生二氧化碳和水，净化纤维层由红松纳米纤维和活性炭纳米纤维组成，活性炭纳米纤维可有效吸附甲醛，配合红松纳米纤维进行催化，氧化锰纳米纤维微球内部形成有空隙，相同体积下相比于活性炭等物质吸附效果更好，通过净化器设置，净醛棉层可有效替换安装设置在管道内部，提高催化效果，除湿器可有效去除产生的水分，避免影响后续催化处理。
附图说明
图1为一种可高效去除室内甲醛的红松菓净醛棉及其制备的净化器的结构示意图；
图2为一种可高效去除室内甲醛的红松菓净醛棉及其制备的净化器中净化组件的结构示意图。
图中：1-壳体，2-进气口，3-排气口，4-防尘网，5-管道，6-净化组件，7-风机，8-除湿器，9-盖板，10-锁扣，11-转动座，12-密封边，13-安装架，14-插接边，15-净醛棉层。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一
请参阅图1～2，本发明提供一种技术方案：一种可高效去除室内甲醛的红松菓净醛棉，所述红松菓净醛棉包括天然纤维层、抗菌纤维层、净化纤维层、表面加强纤维层和压胶层，所述天然纤维层、抗菌纤维层和净化纤维层从上至下依次设置，所述表面加强纤维层设置在上下两侧表面，各个纤维层之间通过压胶层进行边缘粘接，其中抗菌纤维层与净化纤维层之间设置有若干个氧化锰纳米纤维微球，所述氧化锰纳米纤维微球通过氧化锰纤维膜加捻聚拢成束条，即氧化锰纤维，后经切断后挤压成纤维微球。
所述天然纤维层通过椰子纤维、竹炭纤维、蚕丝纤维、竹原纤维、剑麻纤维和聚乳酸纤维中的一种或多种组合编织而成。
所述抗菌纤维层通过二氧化钛纤维和镀银纤维编织而成。
所述净化纤维层通过红松纳米纤维和活性炭纳米纤维编织而成。
所述表面加强纤维层为高硅氧纤维层或聚氯乙烯复合材料层。
所述压胶层包括以重量分数计的氯化聚乙烯橡胶55g、丙酮8g和石蜡25g。
一种可高效去除室内甲醛的红松菓净醛棉制备的净化器，包括壳体1，所述壳体1的左右两侧端面上分别设置有进气口2和排气口3，所述进气口2和排气口3之间通过管道5相连通，所述进气口2和排气口3上设置有防尘网4，所述管道5上设置有风机7和除湿器8，所述管道5上设置有若干个上下对称分布的净化组件6，所述净化组件6包括从净醛棉层15，所述净醛棉层15采用上述所述的一种可高效去除室内甲醛的红松菓净醛棉。
所述净化组件6包括盖板9，所述盖板9上设置有锁扣10，所述盖板9通过转动座11转动安装在管道5上，所述盖板9内侧壁上固定安装有密封边12，所述盖板9的内侧壁上设置有对称分布的安装架13，所述安装架13上设置有插接边14，所述插接边14的内部插接设置有净醛棉层15。
实施例二
一种可高效去除室内甲醛的红松菓净醛棉，与实施例一的区别在于，所述压胶层包括以重量分数计的氯化聚乙烯橡胶75g、丙酮12g和石蜡30g。
实施例三
一种可高效去除室内甲醛的红松菓净醛棉，与实施例一的区别在于，所述压胶层包括以重量分数计的氯化聚乙烯橡胶80g、丙酮16g和石蜡35g。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
Claims (8)
1.一种可高效去除室内甲醛的红松菓净醛棉，其特征在于：所述红松菓净醛棉包括天然纤维层、抗菌纤维层、净化纤维层、表面加强纤维层和压胶层，所述天然纤维层、抗菌纤维层和净化纤维层从上至下依次设置，所述表面加强纤维层设置在上下两侧表面，各个纤维层之间通过压胶层进行边缘粘接，其中抗菌纤维层与净化纤维层之间设置有若干个氧化锰纳米纤维微球，所述氧化锰纳米纤维微球通过氧化锰纤维膜加捻聚拢成束条，即氧化锰纤维，后经切断后挤压成纤维微球。
2.根据权利要求1所述的一种可高效去除室内甲醛的红松菓净醛棉，其特征在于：所述天然纤维层通过椰子纤维、竹炭纤维、蚕丝纤维、竹原纤维、剑麻纤维和聚乳酸纤维中的一种或多种组合编织而成。
3.根据权利要求2所述的一种可高效去除室内甲醛的红松菓净醛棉，其特征在于：所述抗菌纤维层通过二氧化钛纤维和镀银纤维编织而成。
4.根据权利要求3所述的一种可高效去除室内甲醛的红松菓净醛棉，其特征在于：所述净化纤维层通过红松纳米纤维和活性炭纳米纤维编织而成。
5.根据权利要求4所述的一种可高效去除室内甲醛的红松菓净醛棉，其特征在于：所述表面加强纤维层为高硅氧纤维层或聚氯乙烯复合材料层。
6.根据权利要求5所述的一种可高效去除室内甲醛的红松菓净醛棉，其特征在于：所述压胶层包括以重量分数计的氯化聚乙烯橡胶55-80g、丙酮8-16g和石蜡25-35g。
7.一种可高效去除室内甲醛的红松菓净醛棉制备的净化器，包括壳体（1），其特征在于：所述壳体（1）的左右两侧端面上分别设置有进气口（2）和排气口（3），所述进气口（2）和排气口（3）之间通过管道（5）相连通，所述进气口（2）和排气口（3）上设置有防尘网（4），所述管道（5）上设置有风机（7）和除湿器（8），所述管道（5）上设置有若干个上下对称分布的净化组件（6），所述净化组件（6）包括从净醛棉层（15），所述净醛棉层（15）采用权利要求1-6任一所述的一种可高效去除室内甲醛的红松菓净醛棉。
8.根据权利要求7所述的一种可高效去除室内甲醛的红松菓净醛棉制备的净化器，其特征在于：所述净化组件（6）包括盖板（9），所述盖板（9）上设置有锁扣（10），所述盖板（9）通过转动座（11）转动安装在管道（5）上，所述盖板（9）内侧壁上固定安装有密封边（12），所述盖板（9）的内侧壁上设置有对称分布的安装架（13），所述安装架（13）上设置有插接边（14），所述插接边（14）的内部插接设置有净醛棉层（15）。