CN111622431A - 一种保温隔热耐腐蚀的彩砂金属瓦及生产工艺 - Google Patents

一种保温隔热耐腐蚀的彩砂金属瓦及生产工艺 Download PDF

Info

Publication number
CN111622431A
CN111622431A CN202010617879.XA CN202010617879A CN111622431A CN 111622431 A CN111622431 A CN 111622431A CN 202010617879 A CN202010617879 A CN 202010617879A CN 111622431 A CN111622431 A CN 111622431A
Authority
CN
China
Prior art keywords
layer
steel base
base layer
metal tile
acrylic acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010617879.XA
Other languages
English (en)
Inventor
李春贤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hangzhou Fuyang Jiexin Color Steel Co ltd
Original Assignee
Hangzhou Fuyang Jiexin Color Steel Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hangzhou Fuyang Jiexin Color Steel Co ltd filed Critical Hangzhou Fuyang Jiexin Color Steel Co ltd
Priority to CN202010617879.XA priority Critical patent/CN111622431A/zh
Publication of CN111622431A publication Critical patent/CN111622431A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种保温隔热耐腐蚀的彩砂金属瓦及生产工艺，包括钢基层和设在刚基层上的彩石砂粒；其特征还包括设在钢基层上的泡沫层；所述钢基层与泡沫层之间设有第一丙烯酸粘合层；所述泡沫层通过第一丙烯酸粘合层固定在钢基层上。本发明结构简单，能够起到保温、隔热和耐腐蚀的效果，从而来延长金属瓦的使用寿命。

Description

一种保温隔热耐腐蚀的彩砂金属瓦及生产工艺
【技术领域】
本发明涉及一种金属瓦技术领域，具体是指一种保温隔热耐腐蚀的彩砂金属瓦及生产工艺。
【背景技术】
目前，金属瓦已经广泛用于各种建筑屋面封顶的施工中，它具有亲环境性、美观、 耐久性强等特点。它的应用范围也从原来的普通住宅，已经逐步扩大到别墅、公寓、商铺以及大楼的屋面。
若公开号为CN108590044A公开了一种新型彩石金属瓦中记载了一种新型彩石金属瓦，它包括金属钢板，金属钢板表面还涂覆有锌铝合金涂层，锌铝合金涂层表面设有钢板保护膜，钢板保护膜表面设有粘合基层，粘合基层表面喷涂有天然彩砂石层钢板，保护膜与粘合基层之间还设有碱性网格布，解决的技术问题是主要是由于彩砂需要经过涂胶的，直接将涂胶的彩石沙置于瓦楞板基材上，会因为胶液中存在的酸性或碱性物质对基材产生腐蚀的问题，尤其是在常年高温多雨的地区，会增加对基材的腐蚀，从而影响了基材的强度，进而影响了产品的使用寿命；另外，现有的金属彩砂瓦，只因为基材表面彩砂起到美观及便于施工的作用；但是其保温隔热效果较差，尤其是非洲等贫穷地区，人们收入低，且经常断电，买不起空调；导致房屋内的温度持续高温，从而不适于居住，为此提出一种保温隔热耐腐蚀的彩砂金属瓦及生产工艺。
【发明内容】
本发明的目的是为了解决以上问题而提出一种保温隔热耐腐蚀的彩砂金属瓦及生产工艺。
为了达到上述目的，本发明提供了如下技术方案：一种保温隔热耐腐蚀的彩砂金属瓦，包括钢基层和设在刚基层上的彩石砂粒；其特征还包括设在钢基层上的泡沫层；所述钢基层与泡沫层之间设有第一丙烯酸粘合层；所述泡沫层通过第一丙烯酸粘合层固定在钢基层上。
作为优选，所述钢基层上的泡沫层上设有第二丙烯酸粘合层；所述第二丙烯酸粘合层上设有彩石砂粒；所述彩石砂粒上设有丙烯酸上光层。
作为优选，所述钢基层上设有金属钢板、镀铝锌层和油漆层。
作为优选，一种保温隔热耐腐蚀的彩砂金属瓦及生产工艺，具体步骤如下：
第一步：钢基层表面上喷涂上第一丙烯酸粘合层；
第二步：第一丙烯酸粘合层上使用发泡机均匀的喷上泡沫层；
第三步：泡沫层上均匀喷涂上第二丙烯酸粘合层；
第四步：通过喷砂机在第二丙烯酸粘合层上均匀的喷涂彩石砂粒，并进入烘箱烘干；
第五步：经过烘干的金属瓦表面上均匀的喷涂上丙烯酸上光层，然后再次进入烘箱进行烘干；
第六步：再次经过烘干的金属瓦放置到切边机上，通过切边机对金属瓦的外形进行收边，最后进行包装。
作为优选，所述收边机包括支架、安装在支架与产品相适配的下模、支撑柱和安装在支撑柱上的气缸固定板；所述气缸固定板上安装有切边气缸和合模气缸；所述切边气缸上安装有切边块；所述合模气缸上安装有固定块；所述固定块上安装有与产品相适配的上模。
本发明的有益效果：该金属彩砂金属瓦结构简单，能够起到保温、隔热和耐腐蚀的效果，从而来延长金属瓦的使用寿命。
【附图说明】
图1是本发明的结构示意图。
图2是本发明钢基层的结构示意图。
图3是本发明切边机的结构示意图。
图例说明：1钢基层；101镀铝锌层；102油漆层；103金属钢板；2彩石砂粒；3泡沫层；4第一丙烯酸粘合层；5第二丙烯酸粘合层；6丙烯酸上光层；6支架；7下模；8支撑柱；9气缸固定板；10切边气缸；11合模气缸；12切边块；13固定块；14上模。
具体实施方式
下面我们结合附图对本发明所述的一种保温隔热耐腐蚀的彩砂金属瓦及生产工艺做进一步的说明。
结合图1-3所示，本实施例中一种保温隔热耐腐蚀的彩砂金属瓦，包括钢基层1和设在刚基层1上的彩石砂粒2；其特征还包括设在钢基层1上的泡沫层3；所述钢基层1与泡沫层3之间设有第一丙烯酸粘合层4；所述泡沫层3通过第一丙烯酸粘合层4固定在钢基层1上；所述钢基层1上的泡沫层3上设有第二丙烯酸粘合层5；所述第二丙烯酸粘合层5上设有彩石砂粒2；所述彩石砂粒2上设有丙烯酸上光层6；所述钢基层1上设有金属钢板103、镀铝锌层101和油漆层102。
本发明生产工艺如下：
第一步：钢基层1表面上喷涂上第一丙烯酸粘合层4；
第二步：第一丙烯酸粘合层4上使用发泡机均匀的喷上泡沫层3；
第三步：泡沫层3上均匀喷涂上第二丙烯酸粘合层5；
第四步：通过喷砂机在第二丙烯酸粘合层5上均匀的喷涂彩石砂粒2，并进入烘箱烘干；
第五步：经过烘干的金属瓦表面上均匀的喷涂上丙烯酸上光层6，然后再次进入烘箱进行烘干；
第六步：再次经过烘干的金属瓦放置到切边机的下模7上，合模气缸11带动固定块13向下运动，固定块13带动上模14向下运动直至与下模7相配合，然后切边气缸10带动切边块12向下运动，切边块12在向下运动时边切除金属瓦外多余的部分，最后切边气缸10带动切边块12向上运动，合模气缸11带动固定块13和上模14向上运动，进金属瓦从下模7上拿下进行包装存放。
本发明的有益效果，通过在钢基层1上设置泡沫层3，泡沫层3可以对房屋进行保温和隔热的效果，泡沫层3能够有效的阻挡胶液中的酸性物质或碱性物质对钢基层1的腐蚀，不管是常年高温或是多余的地区都能对钢基层1起到保护的作用，从而增加了钢基层1的强度，延长金属瓦的使用寿命，而且泡沫层3还能起到保温隔热的效果，在经常断电或是因收入低买不起空调的地区，泡沫层3能够有效的阻挡太阳直射所产生的热量直接进入屋内，从而可以持续保证屋内的凉爽，方便进行居住；通过在泡沫层3和钢基层1之间设置第一丙烯酸粘合层4，这样可以使泡沫层3更加牢固的固定在钢基层1上，从而延长金属瓦的使用寿命；通过在支架6上安装与产品相适配的下模7和支撑柱8，支撑柱8上安装气缸固定板9，气缸固定板9上安装切边气缸10和合模气缸11，切边气缸10上安装切边12块，合模气缸11上安装固定块13，固定块13上安装与产品相适配的上模14，将金属瓦固定在上模14和下模7之间，并使用切边气缸10带动切边块12将金属瓦多余的部分切除，从而可以用切边气缸10和切边块12来代替人工，节约了时间，提高了生产效率。
上述实施例是对本发明的说明，不是对本发明的限定，任何对本发明简单变换后的方案均属于本发明的保护范围。

Claims (5)

1.一种保温隔热耐腐蚀的彩砂金属瓦，包括钢基层（1）和设在刚基层（1）上的彩石砂粒（2）；其特征还包括设在钢基层（1）上的泡沫层（3）；所述钢基层（1）与泡沫层（3）之间设有第一丙烯酸粘合层（4）；所述泡沫层（3）通过第一丙烯酸粘合层（4）固定在钢基层（1）上。
2.根据权利要求1所述的一种保温隔热耐腐蚀的彩砂金属瓦，其特征在于：所述钢基层（1）上的泡沫层（3）上设有第二丙烯酸粘合层（5）；所述第二丙烯酸粘合层（5）上设有彩石砂粒（2）；所述彩石砂粒（2）上设有丙烯酸上光层（6）。
3.根据权利要求2所述的一种保温隔热耐腐蚀的彩砂金属瓦，其特征在于：所述钢基层（1）上设有金属钢板（103）、镀铝锌层（101）和油漆层（102）。
4.如权利要求1～3所述的一种保温隔热耐腐蚀的彩砂金属瓦及生产工艺，具体步骤如下：
第一步：钢基层（1）表面上喷涂上第一丙烯酸粘合层（4）；
第二步：第一丙烯酸粘合层（4）上使用发泡机均匀的喷上泡沫层（3）；
第三步：泡沫层（3）上均匀喷涂上第二丙烯酸粘合层（5）；
第四步：通过喷砂机在第二丙烯酸粘合层（5）上均匀的喷涂彩石砂粒（2），并进入烘箱烘干；
第五步：经过烘干的金属瓦表面上均匀的喷涂上丙烯酸上光层（6），然后再次进入烘箱进行烘干；
第六步：再次经过烘干的金属瓦放置到收边机上，通过收边机对金属瓦的外形进行收边，最后进行包装。
5.根据权利要求4所述的一种保温隔热耐腐蚀的彩砂金属瓦的生产工艺，其特征在于：所述收边机包括支架（6）、安装在支架（6）上的凹模（7）、支撑柱（8）和安装在支撑柱（8）上的气缸固定板（9）；所述气缸固定板（9）上安装有切边气缸（10）和合模气缸（11）；所述切边气缸（10）上安装有切边块（12）；所述合模气缸（11）上安装有固定块（13）；所述固定块（13）上安装有凸模（14）。
CN202010617879.XA 2020-07-01 2020-07-01 一种保温隔热耐腐蚀的彩砂金属瓦及生产工艺 Pending CN111622431A (zh)