CN111590970B - Real silk wool felting composite folded material and preparation method thereof - Google Patents

Real silk wool felting composite folded material and preparation method thereof Download PDF

Info

Publication number
CN111590970B
CN111590970B CN202010269291.XA CN202010269291A CN111590970B CN 111590970 B CN111590970 B CN 111590970B CN 202010269291 A CN202010269291 A CN 202010269291A CN 111590970 B CN111590970 B CN 111590970B
Authority
CN
China
Prior art keywords
real silk
wool
preparation
felted
winding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202010269291.XA
Other languages
Chinese (zh)
Other versions
CN111590970A (en
Inventor
王丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Institute Fashion Technology
Original Assignee
Beijing Institute Fashion Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Institute Fashion Technology filed Critical Beijing Institute Fashion Technology
Priority to CN202010269291.XA priority Critical patent/CN111590970B/en
Publication of CN111590970A publication Critical patent/CN111590970A/en
Application granted granted Critical
Publication of CN111590970B publication Critical patent/CN111590970B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention provides a real silk wool felting composite folded material and a preparation method thereof, and relates to the technical field of textile clothing and fiber fabrics. The wool tops are arranged into loose sheets, silk fabrics are respectively covered on the upper surface and the lower surface of the obtained loose sheet wool tops, and the felted composite material is obtained through polishing; then, a pressing and pressing mode is adopted to enable the felted composite material to form a wrinkle fabric which is not easy to loosen, and then subsequent steam fixation is carried out, so that wrinkles are firmer, and the preparation method is environment-friendly and green. Meanwhile, the real silk wool felted composite folded material obtained by the preparation method has the texture of real silk, and meanwhile, has rich texture, skin friendliness and air permeability, and is a very competitive personalized product.

Description

Real silk wool felting composite folded material and preparation method thereof
Technical Field
The invention relates to the technical field of textile clothing and fiber fabrics, in particular to a real silk wool felting composite folded material and a preparation method thereof.
Background
The wool fibers are physically kneaded in a damp-heat and alkaline environment, and scales among the fibers are mutually interpenetrated, entangled, felted and felted under the action of mechanical force, so that a wool aggregate is gradually shrunk and compacted, and the special property is called the felting property of the wool. The wool fibers can improve the thickness and the tightness of the fabric through felting, generate neat suede, have beautiful appearance and plump hand feeling, and improve the heat retention property. Although the prior art has combined felting of wool and real silk, the real silk is easy to damage by high-temperature pleating process, so the prior real silk and wool felting material is a flat material without fold texture.
Disclosure of Invention
In view of this, the invention aims to provide a real silk wool felting composite folded material and a preparation method thereof. The invention adopts a pressing mode to form the felt composite material formed by the wool and the real silk fabric into the wrinkle fabric which is not easy to loosen, thereby ensuring the texture of the real silk, and the preparation method is environment-friendly and green.
In order to achieve the above object, the present invention provides the following technical solutions:
the invention provides a preparation method of a real silk wool felted composite folded material, which comprises the following steps:
arranging wool tops into loose sheets, respectively covering real silk fabrics on the upper and lower surfaces of the obtained loose sheet wool tops, and polishing to obtain a felted composite material;
wrapping and winding the felted composite material on a pipe fitting by adopting an engineering line, and then pushing and pressing the felted composite material to one end of the pipe fitting to obtain a corrugated material;
and sequentially dyeing, steam fixation, washing, drying and dismantling the engineering line on the folded material to obtain the real silk wool felted composite folded material.
Preferably, the step of respectively covering the upper surface and the lower surface of the obtained loose flaky wool tops with real silk fabrics comprises the following steps:
the real silk fabric is laid on plastic bubble paper with the same size, and then loose flaky wool tops, the real silk fabric and the plastic gauze with the same size are sequentially laid on the real silk fabric.
Preferably, before polishing, the obtained three-layer material is soaked, and the soaking reagent is soapy water with the pH value of 10-11 and the temperature of 60-80 ℃; and after polishing, removing redundant water in the three layers of polished materials, and removing the plastic bubble paper and the plastic gauze.
Preferably, the winding mode is winding in a mode that the interval of the engineering lines is 1 cm.
Preferably, the pressing is performed once when the winding length of the engineering wire is 8-10 cm.
Preferably, the diameter of the pipe fitting is 10-12 cm.
Preferably, the temperature for the steam fixation is 100-120 ℃, and the time is 40-60 min.
The invention also provides the real silk wool felted composite folded material prepared by the preparation method in the technical scheme.
The invention provides a preparation method of a real silk wool felted composite folded material, which comprises the following steps: arranging wool tops into loose sheets, respectively covering real silk fabrics on the upper and lower surfaces of the obtained loose sheet wool tops, and polishing to obtain a felted composite material; wrapping and winding the felted composite material on a pipe fitting by adopting an engineering line, and then pushing and pressing the felted composite material to one end of the pipe fitting to obtain a corrugated material; and sequentially dyeing, steam fixation, washing, drying and dismantling the engineering line on the folded material to obtain the real silk wool felted composite folded material. According to the invention, the felted composite material formed by the wool and the real silk fabric is formed into the wrinkle fabric which is not easy to loosen in a pushing and pressing mode, and then the wrinkle is firmer through subsequent steam fixation and cooling, and the preparation method is environment-friendly and green.
The invention also provides the real silk wool felted composite folded material obtained by the preparation method in the technical scheme, and the real silk wool felted composite folded material provided by the invention has the texture of real silk, and meanwhile, has rich texture, skin friendliness and air permeability, and is an extremely competitive personalized product.
Drawings
FIG. 1 is a schematic representation of a felted composite according to the present invention wrapped and wound on a pipe;
FIG. 2 is a diagram illustrating the effect of the pleated material obtained by the embodiment of the present invention;
FIG. 3 is a real image of the real silk wool felted composite pleated material obtained in the example.
Detailed Description
The invention provides a preparation method of a real silk wool felted composite folded material, which comprises the following steps:
arranging wool tops into loose sheets, respectively covering real silk fabrics on the upper and lower surfaces of the obtained loose sheet wool tops, and polishing to obtain a felted composite material;
wrapping and winding the felted composite material on a pipe fitting by adopting an engineering line, and then pushing and pressing the felted composite material to one end of the pipe fitting to obtain a corrugated material;
and sequentially dyeing, high-temperature steam fixation, washing, drying and dismantling the engineering line to the folded material to obtain the real silk wool felted composite folded material.
The wool tops are arranged into loose sheets, silk fabrics are respectively covered on the upper surface and the lower surface of the obtained loose sheet wool tops, and the felted composite material is obtained through polishing.
In the invention, the thickness of the loose flaky wool tops is preferably 0.5-2.0 cm, and more preferably 1 cm. The wool top finishing mode is not particularly limited, and wool finishing processes well known to those skilled in the art can be adopted, so long as the wool top is finished into loose sheets.
The invention has no specific requirements on the source or the category of the real silk fabric, and the skilled person can select the real silk fabric according to the actual needs, and in the specific embodiment of the invention, the real silk fabric is preferably 18 mm real silk crepon crenulated fabric.
In the invention, the specific steps of respectively covering the upper surface and the lower surface of the obtained loose flaky wool tops with the real silk fabrics are preferably as follows: the real silk fabric is laid on plastic bubble paper with the same size, and then loose flaky wool tops, the real silk fabric and the plastic gauze with the same size are sequentially laid on the real silk fabric. In the invention, the plastic gauze and the plastic bubble paper have the function of protecting the real silk fabric structure from being damaged in the polishing process.
Before the grinding, the invention preferably further comprises soaking the obtained three-layer material; the soaking reagent is preferably soapy water with the pH value of 10-11 and the temperature of 60-80 ℃.
The invention does not require the polishing mode, equipment and operating parameters of the equipment, and only needs to uniformly drill wool fibers from holes of the real silk fabric. In a particular embodiment of the invention, the sanding machine is preferably a flat plate sander having a power of 180W and an orbital rotation speed (OPM) of 14000.
After polishing, the present invention preferably further comprises removing the plastic blister paper and the plastic gauze after removing excess water from the polished three-layer material. In the invention, the purpose of removing the excessive water in the polished three-layer material is to prevent the three-layer material from dripping water, so that the next operation is convenient. The invention does not specifically limit the removal mode of the plastic blister paper and the plastic gauze.
In the invention, after polishing, the wool fibers are uniformly drilled out of the holes of the real silk fabric, and the wool tops and the two layers of real silk fabrics are not easily separated manually.
After the felted composite material is obtained, the invention adopts an engineering line to wrap and wind the felted composite material on the pipe fitting, and then the felted composite material is pushed and pressed towards one end of the pipe fitting to obtain the corrugated material.
In the present invention, the engineering line is preferably white; the material of the engineering thread is preferably coarse white cotton thread. In the invention, the diameter of the pipe fitting is preferably 10-12 cm, and the material of the pipe fitting is not particularly limited, such as PVC.
The method of wrapping the pipe with the felted composite is not particularly limited, and in a specific embodiment of the present invention, the felted composite is preferably wrapped at 45 ° to the pipe surface of the pipe. In the present invention, the winding is preferably performed in such a manner that the engineering lines are spaced apart by 1 cm. In the present invention, the felted composite is wrapped and wound around a pipe as shown in figure 1.
In the invention, the pushing mode is that once pushing is carried out when the winding length of the engineering wire is 8-10 cm; the present invention is not particularly limited in the way of the pressure release, and the pressure can be pushed to be stationary. .
The invention adopts a pushing mode to prepare folds, thereby ensuring the texture of real silk and enriching the texture of felted composite materials.
After the wrinkle material is obtained, the invention sequentially carries out dyeing, steam fixation, washing, drying and dismantling of the engineering line on the wrinkle material, thus obtaining the real silk wool felted composite wrinkle material.
The dyeing process is not particularly limited in the invention, and a fabric dyeing mode well known to those skilled in the art can be adopted. In a specific embodiment of the present invention, the concentration of the dye for dyeing is preferably 5.0% owf, the temperature of dyeing is preferably 30 ℃, and the time of dyeing is preferably 10 min; the dyeing is preferably carried out under shaking agitation.
After dyeing, the invention preferably further comprises dip fixing the dyed wrinkled material; the method for dip fixation preferably comprises the following steps:
and (3) immersing the dyed PVC pipe with the corrugated material into a sodium carbonate solution with the mass concentration of 8% at the temperature of 55 ℃ for 5 min.
In the invention, the temperature for the steam fixation is preferably 100-120 ℃, more preferably 105 ℃, and the time is preferably 40-60 min, more preferably 40 min. The steam-steaming color fixing temperature is controlled to be 100-120 ℃, protein in the real silk fabric is not damaged, and the texture of the real silk fabric can be ensured.
In the present invention, the washing agent is preferably 95 ℃ soap water and 10 ℃ cold water in this order; the specific process of washing is preferably as follows: the soap water is washed once by using 95 ℃ soap water and then washed three times by using cold water at 10 ℃.
In the present invention, the drying method is preferably natural airing.
The manner of removing the engineering line is not particularly limited.
In the steam fixation process, the outer-layer scales of the wool fibers penetrating through the holes of the real silk fabric in the folded material are opened and contacted with each other, and after cooling, the outer-layer scales are meshed together again, so that the folded shape is supported and fixed.
The invention also provides the real silk wool felted composite folded material obtained by the preparation method of the technical scheme.
The real silk wool felted composite folded material provided by the invention has the texture of real silk, and meanwhile, has rich texture, skin friendliness and air permeability, and is a very competitive personalized product.
The real silk and wool felted composite pleated material and the preparation method thereof provided by the invention are described in detail below with reference to the examples, but they should not be construed as limiting the scope of the invention.
Examples
The real silk fabric is as follows: white 18 mm real silk crepon fabric with the length of 1.5m and the width of 1 m;
the loose flaky wool tops are as follows: arranging 100 white wool tops into flat loose sheets with the length of 1.5m, the width of 1m and the thickness of 1 cm;
Paving a real silk fabric on plastic bubble paper with the same size, and then sequentially paving loose flaky wool tops, the real silk fabric and plastic gauze with the same size on the real silk fabric to obtain three layers of materials; uniformly spraying soapy water with the pH value of 10-11 and the temperature of 80 ℃ on the plastic gauze, and soaking three layers of materials; uniformly pushing the wool fibers on the plastic gauze by using a flat plate type sander with the power of 180W and the orbital rotation speed (OPM)14000, sanding for 25min to uniformly drill the wool fibers from the holes of the real silk fabric, manually separating three layers of materials, and removing 80% of water in the sanded three layers of materials to obtain a felted composite material; folding the felted composite material in the length direction in trisection, and flatly paving for later use;
forming a 45-degree angle between the folded felted composite material and the pipe surface of the pipe fitting, covering the pipe surface of PVC with the diameter of 12cm, continuously winding the pipe surface of the pipe fitting at the interval of 1cm by using white engineering threads (the specific wrapping and winding mode is shown in figure 1), binding the felted composite material on the pipe wall of the PVC, and pushing the felted composite material and the engineering threads downwards until the felted composite material is not moved when the winding length reaches 10cm, so as to extrude wrinkles; the steps are repeated in a circulating mode until all the felted composite materials are wound on the PVC pipe wall, and folds are pushed out of the PVC pipe wall to obtain the folded materials, and the effect graph of the folded materials is shown in figure 2;
Putting the PVC pipe and the corrugated material into a prepared active dye solution, wherein the concentration of the active dye solution is 5.0% owf, the temperature of the active dye solution is 30 ℃, and the PVC pipe and the corrugated material are accelerated for 10min and simultaneously vibrated and stirred;
immersing the dyed PVC pipe with the corrugated material into a sodium carbonate solution with the mass concentration of 8% at the temperature of 55 ℃ for 5 min;
taking out the PVC pipe with the corrugated material after impregnation, and performing steam fixation at 105 ℃ for 40 min;
then soaping once at 95 ℃, and washing 3 times with cold water at 10 ℃;
washing with water and naturally drying;
and removing the white engineering lines on the PVC pipe, and taking down the forming fabric to obtain the real silk and wool felting composite folded material.
The picture of the obtained real silk wool felted composite folded material is shown in figure 3.
The foregoing is only a preferred embodiment of the present invention, and it should be noted that, for those skilled in the art, various modifications and decorations can be made without departing from the principle of the present invention, and these modifications and decorations should also be regarded as the protection scope of the present invention.

Claims (6)

1. A preparation method of a real silk wool felted composite folded material is characterized by comprising the following steps:
arranging wool tops into loose sheets, respectively covering real silk fabrics on the upper and lower surfaces of the obtained loose sheet wool tops, and polishing to obtain a felted composite material;
Wrapping and winding the felted composite material on a pipe fitting by adopting an engineering line, and then pushing and pressing the felted composite material to one end of the pipe fitting to obtain a corrugated material;
sequentially dyeing, steaming and fixing color, washing, drying and removing engineering lines on the folded material to obtain the real silk wool felted composite folded material;
the winding mode is winding in a mode of winding engineering wires at intervals of 1 cm;
the pushing mode is that once pushing is carried out when the winding length of the engineering wire is 8-10 cm.
2. The preparation method of claim 1, wherein the step of covering the silk fabrics on the upper surface and the lower surface of the obtained loose flaky wool tops respectively comprises the following steps:
the real silk fabric is laid on plastic bubble paper with the same size, and then loose flaky wool tops, the real silk fabric and the plastic gauze with the same size are sequentially laid on the real silk fabric.
3. The preparation method of claim 2, further comprising the steps of soaking the obtained three-layer material before polishing, wherein the soaking reagent is soapy water with the pH value of 10-11 and the temperature of 60-80 ℃; and after polishing, removing redundant water in the three layers of polished materials, and removing the plastic bubble paper and the plastic gauze.
4. The method of claim 1, wherein the pipe has a diameter of 10 to 12 cm.
5. The preparation method of claim 1, wherein the temperature of the steam fixation is 100-120 ℃ and the time is 40-60 min.
6. Real silk wool felting composite folded material obtained by the preparation method of any one of claims 1 to 5.
CN202010269291.XA 2020-04-08 2020-04-08 Real silk wool felting composite folded material and preparation method thereof Active CN111590970B (en)