CN111590704A - Long-acting self-cleaning, deep-maintenance and formaldehyde-release-inhibiting spray for wood products - Google Patents
Long-acting self-cleaning, deep-maintenance and formaldehyde-release-inhibiting spray for wood products Download PDFInfo
- Publication number
- CN111590704A CN111590704A CN202010466942.4A CN202010466942A CN111590704A CN 111590704 A CN111590704 A CN 111590704A CN 202010466942 A CN202010466942 A CN 202010466942A CN 111590704 A CN111590704 A CN 111590704A
- Authority
- CN
- China
- Prior art keywords
- cleaning
- agent
- long
- deep
- spray
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a spray for wooden products with long-acting self-cleaning, deep maintenance and formaldehyde release inhibition, which relates to the technical field of sprays for wooden products and furniture products, in particular to a spray for wooden products with long-acting self-cleaning, deep maintenance and formaldehyde release inhibition, which comprises the following components in percentage by weight: 1-30% of nano inorganic active material, 1-10% of flatting agent, 0.05-5% of anti-settling agent, 5-10% of dust-proof agent, 15-20% of dispersing agent, 1-20% of dry lubricant and the balance of deionized water. The nano inorganic active material arranged in the spray for the long-acting self-cleaning, deep maintenance and formaldehyde release inhibition wooden products has good deep cleaning and maintenance and self-cleaning effects, and the nano inorganic active material can be uniformly mixed with other components in the spray by adding the dispenser; the wood furniture is added with quick and long-acting self-cleaning, so that the wood furniture can be quickly cleaned and protected for a long time, the smoothing agent is added to inhibit the furniture from releasing formaldehyde, and the dustproof agent is added to enable the wood furniture to generate a protective film to isolate dust, so that the long-acting self-cleaning is realized.
Description
Technical Field
The invention relates to the technical field of wood product and furniture product spraying agents, in particular to a long-acting self-cleaning, deep-maintenance and formaldehyde release inhibiting wood product spraying agent.
Background
Along with the improvement of living standard of people, a large amount of woodwork and solid wood furniture enter the life of people, and in the use process, the woodwork and the solid wood furniture are seriously oxidized in surface, dull in color, easy to fall ash, free of self-cleaning function, and excessive in formaldehyde release, so that the quality of life of people is directly influenced. The furniture is dark in color, weakened in texture, seriously damaged and lost original texture under long-term use, so that a user can feel bored.
Generally, a furniture owner consumes a large amount of manpower, material resources and time in the process of maintaining and maintaining furniture, but cannot achieve the long-acting and deep maintenance effect, so that the home owner generates a lifeless mood.
As formaldehyde is involved in the manufacturing process of furniture, the release of the formaldehyde can cause the over-standard concentration of the formaldehyde in a room and seriously affect the health of people.
Disclosure of Invention
Aiming at the defects of the prior art, the invention provides a spray for wooden products with long-acting self-cleaning, deep maintenance and formaldehyde release inhibition, which solves the problems that the furniture proposed in the background art is dark in color, weakened in texture, serious in damage and free of original texture under the long-term use, so that an owner generates boring emotion; a furniture owner consumes a great amount of manpower, material resources and time in the furniture maintenance process, but cannot achieve the long-acting and deep maintenance effect; the formaldehyde is released, so that the concentration of the formaldehyde in a room exceeds the standard, and the health of people is seriously influenced.
In order to achieve the purpose, the invention is realized by the following technical scheme: a spray for wooden products with long-acting self-cleaning, deep maintenance and formaldehyde release inhibition comprises the following components in percentage by weight: 1-30% of nano inorganic active material, 1-10% of flatting agent, 0.05-5% of anti-settling agent, 5-10% of dust-proof agent, 15-20% of dispersing agent, 1-20% of dry lubricant and the balance of deionized water.
Optionally, the nano inorganic active material contains one of modified water-based silicone grease and rare earth up-conversion material.
Optionally, the preparation of the nano inorganic active material comprises the following steps:
s1: dissolving, namely weighing a certain amount of water-based silicone grease, and dissolving the water-based silicone grease in deionized water to prepare a solution A;
s2: stirring, respectively weighing quantitative Zn-STV and ZnO, sequentially placing in a flask, adding deionized water, and fully stirring to dissolve into solution B;
s3: reacting, namely quickly injecting the solution A into the stirred solution B, reacting for 3-5 hours, and obtaining a product C after the reaction is finished;
s4: and (4) centrifugal preparation, namely, centrifugally separating the product C, and fully washing the product C for a plurality of times by using deionized water to obtain the composite inorganic nano material.
Optionally, the particle diameter of the nano inorganic active material is in the range of 20-60 nm.
Optionally, the dispersant comprises one of modified polyether silicon or shin carbonate.
Optionally, the anti-dust agent comprises one of emulsified fatty acid or diethylene glycol butyl ether.
Optionally, the dry lubricant is dimethicone.
Optionally, the dispersant is silica.
Optionally, the flattening agent is modified polyether silicone oil.
Optionally, the preparation of the spray for the wood product with long-acting self-cleaning, deep maintenance and formaldehyde release inhibition comprises the following steps:
s1: weighing 1-30% of nano inorganic active material, 1-10% of flatting agent, 0.05-5% of anti-settling agent, 5-10% of dustproof agent, 15-20% of dispersing agent, 1-20% of dry lubricant and the balance of deionized water according to mass percentage, sequentially placing the components into water, mixing and stirring uniformly;
s2: grinding, pouring the mixed solvent obtained in the step S1 into a dispersion machine for grinding, wherein the grinding temperature is lower than 25 ℃, the rotating speed of a main machine is 1000-1200rmp, and discharging after grinding for 3-5 hours to obtain a spraying agent mother agent A;
s3: mixing, namely uniformly mixing the spray A obtained in the step S2 with a dustproof agent, and stirring at the rotating speed of 800rmp for 3 hours at the temperature of below 25 ℃ to obtain a mother agent B;
s4: emulsifying, namely mixing a smoothing agent, deionized water and the mother liquor B obtained in the step S3, uniformly stirring, and emulsifying for 60 minutes by using a high-shear emulsifying machine;
s5: and (4) preparing, namely filling the product obtained in the step S4 into a bottle with an atomizing nozzle to obtain the furniture spray which is long-acting, self-cleaning, deep in maintenance and capable of inhibiting formaldehyde release.
The invention provides a spray for wooden products with long-acting self-cleaning, deep maintenance and formaldehyde release inhibition, which has the following beneficial effects:
the spray can quickly clean and keep wooden furniture in a long-term manner, plays a role in deep maintenance, can effectively inhibit formaldehyde release, is convenient to use, simple to operate, suitable for household wooden furniture, long in duration after being used, and free of toxicity, harm and side effects, and can be used for simply, lightly and quickly solving the problems of furniture maintenance and cleaning nursing by people;
1. the nano inorganic active material arranged in the spray for the long-acting self-cleaning, deep maintenance and formaldehyde release inhibition wooden products has good deep cleaning and maintenance and self-cleaning effects, and the nano inorganic active material can be uniformly mixed with other components in the spray by adding the dispenser; the wood furniture is added with quick and long-acting self-cleaning, so that the wood furniture can be quickly cleaned and protected for a long time, the smoothing agent is added to inhibit the furniture from releasing formaldehyde, and the dustproof agent is added to enable the wood furniture to generate a protective film to isolate dust, so that the long-acting self-cleaning is realized.
2. The up-conversion material arranged in the spray for the wooden product with the long-acting self-cleaning, deep maintenance and formaldehyde release inhibition functions is a luminescent material which can emit visible light under the excitation of infrared light and convert the infrared light into the visible light, in the prior art, the up-conversion material is mainly doped with a solid compound of rare earth elements, can absorb a plurality of long-wave radiations with low energy by utilizing the metastable state energy level characteristic of the rare earth elements, promotes the infrared light invisible to be changed into the visible light by naked eyes of people, and is mainly applied to the fields of conversion lasers, optical fiber amplifiers, three-dimensional display, defense and the like; the rare earth and the nano silicon oxide originally have excellent dust removal and high permeability; the composite nano material of the nano silicon oxide and the rare earth conversion material has the dust removal effect on wooden furniture, the composite material generated by the nano water-based silicone grease and the rare earth inhibits the release of formaldehyde, and the composite nano material also has the characteristics of high chemical stability and low potential biological toxicity, and is very suitable for being added into a spray.
Detailed Description
In the following, technical solutions in the embodiments of the present invention are clearly and completely described, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments.
Embodiment 1
The invention provides a technical scheme that: a spray for wooden products with long-acting self-cleaning, deep maintenance and formaldehyde release inhibition comprises the following components in percentage by weight: 1-30% of nano inorganic active material, 1-10% of flatting agent, 0.05-5% of anti-settling agent, 5-10% of dust-proof agent, 15-20% of dispersing agent, 1-20% of dry lubricant and the balance of deionized water.
The nano inorganic active material contains one of modified water-based silicone grease and rare earth up-conversion material;
the preparation of the nano inorganic active material comprises the following steps:
s1: dissolving, namely weighing a certain amount of water-based silicone grease, and dissolving the water-based silicone grease in deionized water to prepare a solution A;
s2: stirring, respectively weighing quantitative Zn-STV and ZnO, sequentially placing in a flask, adding deionized water, and fully stirring to dissolve into solution B;
s3: reacting, namely quickly injecting the solution A into the stirred solution B, reacting for 3-5 hours, and obtaining a product C after the reaction is finished;
s4: performing centrifugal preparation, namely performing centrifugal separation on the product C, and fully washing the product C for a plurality of times by using deionized water to obtain a composite inorganic nano material;
the particle diameter range of the nano inorganic active material is 20-60 nm;
60g of dispersant are 30g of silicon dioxide and 30g of dimethyl siloxane;
the dustproof agent is emulsified fatty acid;
the dry lubricant is dimethyl siloxane;
the dispersing agent is silicon dioxide;
the flattening agent is modified polyether silicone oil;
the spray for the wood products with long-acting self-cleaning, deep maintenance and formaldehyde release inhibition is manufactured by the following steps:
s1: weighing, namely weighing 300g of nano inorganic salt active material, 60g of dispersing agent and 640g of deionized water;
s2: grinding, pouring the mixed solvent obtained in the step S1 into a dispersion machine for grinding, wherein the grinding temperature is lower than 25 ℃, the rotating speed of a main machine is 1000-1200rmp, and discharging after grinding for 3 hours to obtain a spraying agent mother agent A;
s3: mixing, namely uniformly mixing 500g of the spray agent A obtained in the step S2 with 20g of the dustproof agent, and stirring at the rotating speed of 800rmp for 3 hours below 25 ℃ to obtain a mother agent B;
s4: emulsifying, namely mixing 247.5g of deionized water with 100g of the mother liquor B obtained in the step S3, uniformly stirring, and emulsifying for 60 minutes by using a high-shear emulsifying machine;
s5: and (4) preparing, namely filling the product obtained in the step S4 into a bottle with an atomizing nozzle to obtain the furniture spray which is long-acting, self-cleaning, deep in maintenance and capable of inhibiting formaldehyde release.
Example II
A spray for wooden products with long-acting self-cleaning, deep maintenance and formaldehyde release inhibition comprises the following components in percentage by weight: 1-30% of nano inorganic active material, 1-10% of flatting agent, 0.05-5% of anti-settling agent, 5-10% of dust-proof agent, 15-20% of dispersing agent, 1-20% of dry lubricant and the balance of deionized water.
The nano inorganic active material contains one of modified water-based silicone grease and rare earth up-conversion material;
the preparation of the nano inorganic active material comprises the following steps:
s1: dissolving, namely weighing a certain amount of water-based silicone grease, and dissolving the water-based silicone grease in deionized water to prepare a solution A;
s2: stirring, respectively weighing quantitative Zn-STV and ZnO, sequentially placing in a flask, adding deionized water, and fully stirring to dissolve into solution B;
s3: reacting, namely quickly injecting the solution A into the stirred solution B, reacting for 3-5 hours, and obtaining a product C after the reaction is finished;
s4: performing centrifugal preparation, namely performing centrifugal separation on the product C, and fully washing the product C for a plurality of times by using deionized water to obtain a composite inorganic nano material;
the particle diameter range of the nano inorganic active material is 20-60 nm;
100g of dispersant are 50g of silica and 50g of dimethylsiloxane;
the dustproof agent is emulsified fatty acid;
the dry lubricant is dimethyl siloxane;
the dispersing agent is silicon dioxide;
the flattening agent is modified polyether silicone oil;
the spray for the wood products with long-acting self-cleaning, deep maintenance and formaldehyde release inhibition is manufactured by the following steps:
s1: weighing 400g of nano inorganic salt active material, 100g of dispersing agent and 850g of deionized water;
s2: grinding, pouring the mixed solvent obtained in the step S1 into a dispersion machine for grinding, wherein the grinding temperature is lower than 25 ℃, the rotating speed of a main machine is 1000-1200rmp, and discharging after grinding for 3 hours to obtain a spraying agent mother agent A;
s3: mixing, namely uniformly mixing 500g of the spray A obtained in the step S2 with 40g of the dustproof agent, and stirring at the rotating speed of 800rmp for 3 hours below 25 ℃ to obtain a mother agent B;
s4: emulsifying, mixing 395g of deionized water with 100g of the mother liquor B obtained in the step S3, stirring uniformly, and emulsifying for 60 minutes by using a high-shear emulsifying machine;
s5: and (4) preparing, namely filling the product obtained in the step S4 into a bottle with an atomizing nozzle to obtain the furniture spray which is long-acting, self-cleaning, deep in maintenance and capable of inhibiting formaldehyde release.
Example three
A spray for wooden products with long-acting self-cleaning, deep maintenance and formaldehyde release inhibition comprises the following components in percentage by weight: 1-30% of nano inorganic active material, 1-10% of flatting agent, 0.05-5% of anti-settling agent, 5-10% of dust-proof agent, 15-20% of dispersing agent, 1-20% of dry lubricant and the balance of deionized water.
The nano inorganic active material contains one of modified water-based silicone grease and rare earth up-conversion material;
the preparation of the nano inorganic active material comprises the following steps:
s1: dissolving, namely weighing a certain amount of water-based silicone grease, and dissolving the water-based silicone grease in deionized water to prepare a solution A;
s2: stirring, respectively weighing quantitative Zn-STV and ZnO, sequentially placing in a flask, adding deionized water, and fully stirring to dissolve into solution B;
s3: reacting, namely quickly injecting the solution A into the stirred solution B, reacting for 3-5 hours, and obtaining a product C after the reaction is finished;
s4: performing centrifugal preparation, namely performing centrifugal separation on the product C, and fully washing the product C for a plurality of times by using deionized water to obtain a composite inorganic nano material;
the particle diameter range of the nano inorganic active material is 20-60 nm;
100g of dispersant are 70g of silica and 70g of dimethylsiloxane;
the dustproof agent is emulsified fatty acid;
the dry lubricant is dimethyl siloxane;
the dispersing agent is silicon dioxide;
the flattening agent is modified polyether silicone oil;
the spray for the wood products with long-acting self-cleaning, deep maintenance and formaldehyde release inhibition is manufactured by the following steps:
s1: weighing 600g of nano inorganic salt active material, 100g of dispersing agent and 963g of deionized water;
s2: grinding, pouring the mixed solvent obtained in the step S1 into a dispersion machine for grinding, wherein the grinding temperature is lower than 25 ℃, the rotating speed of a main machine is 1000-1200rmp, and discharging after grinding for 3 hours to obtain a spraying agent mother agent A;
s3: mixing, namely uniformly mixing 500g of the spray A obtained in the step S2 with 40g of the dustproof agent, and stirring at the rotating speed of 800rmp for 3 hours below 25 ℃ to obtain a mother agent B;
s4: emulsifying, namely mixing 453g of deionized water with 100g of the mother liquor B obtained in the step S3, uniformly stirring, and emulsifying for 60 minutes by using a high-shear emulsifying machine;
s5: and (4) preparing, namely filling the product obtained in the step S4 into a bottle with an atomizing nozzle to obtain the furniture spray which is long-acting, self-cleaning, deep in maintenance and capable of inhibiting formaldehyde release.
The data in the table show that the furniture spray product has good long-acting self-cleaning function, and also has excellent deep maintenance and formaldehyde release inhibition performance.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.
Claims (10)
1. A spray for wooden products with long-acting self-cleaning, deep maintenance and formaldehyde release inhibition is characterized by comprising the following components in percentage by weight: 1-30% of nano inorganic active material, 1-10% of flatting agent, 0.05-5% of anti-settling agent, 5-10% of dust-proof agent, 15-20% of dispersing agent, 1-20% of dry lubricant and the balance of deionized water.
2. The spray for the long-acting self-cleaning, deep maintenance and formaldehyde release inhibition wood product according to claim 1, wherein the nano inorganic active material contains one of modified water-based silicone grease and rare earth up-conversion material.
3. The long-acting self-cleaning, deep-care, formaldehyde-release-inhibiting spray for wood products according to claim 1, wherein: the preparation of the nano inorganic active material comprises the following steps:
s1: dissolving, namely weighing a certain amount of water-based silicone grease, and dissolving the water-based silicone grease in deionized water to prepare a solution A;
s2: stirring, respectively weighing quantitative Zn-STV and ZnO, sequentially placing in a flask, adding deionized water, and fully stirring to dissolve into solution B;
s3: reacting, namely quickly injecting the solution A into the stirred solution B, reacting for 3-5 hours, and obtaining a product C after the reaction is finished;
s4: and (4) centrifugal preparation, namely, centrifugally separating the product C, and fully washing the product C for a plurality of times by using deionized water to obtain the composite inorganic nano material.
4. The long-acting self-cleaning, deep-care, formaldehyde-release-inhibiting spray for wood products according to claim 1, wherein: the particle diameter range of the nano inorganic active material is 20-60 nm.
5. The long-acting self-cleaning, deep-care, formaldehyde-release-inhibiting spray for wood products according to claim 1, wherein: the dispersant contains one of modified polyether silicon or shin carbonate.
6. The long-acting self-cleaning, deep-care, formaldehyde-release-inhibiting spray for wood products according to claim 1, wherein: the dust-proofing agent contains one of emulsified fatty acid or diethylene glycol monobutyl ether.
7. The long-acting self-cleaning, deep-care, formaldehyde-release-inhibiting spray for wood products according to claim 1, wherein: the dry lubricant is dimethyl siloxane.
8. The long-acting self-cleaning, deep-care, formaldehyde-release-inhibiting spray for wood products according to claim 1, wherein: the dispersant is silicon dioxide.
9. The long-acting self-cleaning, deep-care, formaldehyde-release-inhibiting spray for wood products according to claim 1, wherein: the flattening agent is modified polyether silicone oil.
10. The method for producing a long-acting self-cleaning, deep-care, formaldehyde-release-inhibiting spray for wood products according to claim 1, wherein the long-acting self-cleaning, deep-care, formaldehyde-release-inhibiting spray for wood products is produced by the steps of:
s1: weighing 1-30% of nano inorganic active material, 1-10% of flatting agent, 0.05-5% of anti-settling agent, 5-10% of dustproof agent, 15-20% of dispersing agent, 1-20% of dry lubricant and the balance of deionized water according to mass percentage, sequentially placing the components into water, mixing and stirring uniformly;
s2: grinding, pouring the mixed solvent obtained in the step S1 into a dispersion machine for grinding, wherein the grinding temperature is lower than 25 ℃, the rotating speed of a main machine is 1000-1200rmp, and discharging after grinding for 3-5 hours to obtain a spraying agent mother agent A;
s3: mixing, namely uniformly mixing the spray A obtained in the step S2 with a dustproof agent, and stirring at the rotating speed of 800rmp for 3 hours at the temperature of below 25 ℃ to obtain a mother agent B;
s4: emulsifying, namely mixing a smoothing agent, deionized water and the mother liquor B obtained in the step S3, uniformly stirring, and emulsifying for 60 minutes by using a high-shear emulsifying machine;
s5: and (4) preparing, namely filling the product obtained in the step S4 into a bottle with an atomizing nozzle to obtain the furniture spray which is long-acting, self-cleaning, deep in maintenance and capable of inhibiting formaldehyde release.