CN111406584B - 一种边坡生态保护和裸露地皮植被保护的方法 - Google Patents
一种边坡生态保护和裸露地皮植被保护的方法 Download PDFInfo
- Publication number
- CN111406584B CN111406584B CN201910016098.2A CN201910016098A CN111406584B CN 111406584 B CN111406584 B CN 111406584B CN 201910016098 A CN201910016098 A CN 201910016098A CN 111406584 B CN111406584 B CN 111406584B
- Authority
- CN
- China
- Prior art keywords
- emulsion
- hydrophobic
- nano
- side slope
- millimeters
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种边坡生态保护和裸露地皮植被保护的方法涉及边坡生态保护和裸露地皮植被保护的方法。主要是为解决目前边坡或裸露的地面很难保水，草籽很难生存的问题而发明的。在边坡表面按照草籽或幼苗的种植办法预先种植并浇水养护。在晴天时或在雨季到来之前数天喷洒纳米超疏水乳液，稀释后用于直接喷洒的纳米超疏水乳液浓度为0.5%—10%，每平方米喷洒1‑5公斤的该稀释乳液，每平方米含有乳液的有效活性物成分为5克至200克。喷洒完毕后，一般春夏季两三天即可形成疏水土层，疏水土层的厚度控制在5毫米至30毫米之间，平均厚度为10‑20毫米。优点是保护边坡防止土壤流失，提高植物的抗旱能力。
Description
技术领域：
本发明涉及一种边坡生态保护和裸露地皮植被保护的方法。
背景技术：
裸露的边坡很容易被雨水冲刷破坏，当种草籽或树苗等植物方法生态保护时，由于雨水的冲刷导致大面积草籽等植物流失，同时旱季时因边坡保水性能差以及土地变硬导致植物成活率很低。
无论是边坡还是裸露的地面，干旱季节裸露的地面很难保水，地面变硬开裂，草籽很难生存，成活率也就很低。
发明内容：
本发明所要解决的技术问题是提供一种可减少边坡水土流失和改善边坡的植物生长环境，能创造出保土保水疏松土壤等有利植物生长环境的边坡生态保护和裸露地皮植被保护的方法。
上述目的是这样实现的：边坡保土保水的方法：
1)在边坡表面按照草籽或幼苗的种植办法预先种植并浇水养护。
2)在晴天时或在雨季到来之前数天喷洒纳米超疏水乳液，根据边坡状况和土的性质，试验得出合适的纳米超疏水乳液喷洒量和合适的浓度，稀释后用于直接喷洒的纳米超疏水乳液浓度为0.5%—10%，每平方米喷洒1-5公斤的该稀释乳液，每平方米含有乳液的有效活性物成分为5克至200克。喷洒完毕后，一般春夏季两三天即可形成疏水土层，疏水土层的厚度控制在5毫米至30毫米之间，平均厚度为10-20毫米。喷洒纳米超疏水乳液后表面土壤无需搅拌无需压实，完全靠乳液的自然渗透形成疏水土层。
所述的纳米超疏水乳液由下列原料制成的：活性物、乳化剂、水；其中活性物占纳米疏水乳液总重量的1—70%，乳化剂占纳米疏水乳液总重量的0.1—10%，水占纳米疏水乳液总重量的98.9—20%；工业生产时活性物的含量可以是从1%至70%的任何溶度；
所述的纳米疏水乳液的活性物为含氢硅氧烷聚合物（又称含氢硅油），纳米疏水乳液的活性物的含氢量为0.1%-1.7%，含氢硅氧烷聚合物的分子式为：
(R)3SiO[RHSiO]nSi(R)3 R = 1-5个碳的烷基；
所述的乳化剂由中性表面活性剂和阴离子表面活性剂组成，两类表面活性剂的混合比例不限；
所述的中性表面活性剂可以是脂肪醇类或醚类或酯类化合物，或者是它们的混合物，混合比例不限；
所述的阴离子表面活性剂为脂肪硫酸盐或脂肪磺酸盐或脂肪酸盐，或者是它们的混合物，混合比例不限；
所述的脂肪醇类可以是：至少含有1个或多个醇羟基（-OH）和含有6-30个直链或支链碳的饱和或不饱和烷烃，也可含有0-3个羧基（-COO-）衍生物。例如月桂醇，硬脂醇和棕榈醇等。
所述的醚类可以是：至少含有1个或多个醚基（C-O-C）和含有至少两个6-30个直链或支链碳的饱和或不饱和烷烃,也可以是聚乙二醇的衍生物，HO[CH2CH2O]n-H(n=100-100000)，例如月桂醇聚醚，平平加-10，聚乙二醇1000，HO[CH2CH2O]1000-H。
所述的酯类化合物可以是：含有6-30个直链或支链碳的饱和或不饱和脂肪酸脂衍生物（-COOC-），也可含有0-5个醇羟基，例如双硬脂酸甘油酯，单硬脂酸甘油酯等。
所述的酯肪酸或其盐可以是：含有6-30个直链或支链碳的饱和或不饱和脂肪酸（-COOH）或其脂肪酸盐（-COOM，M=Na、K、Ca等）或脂肪硫酸盐（ROSO3 -）,或脂肪磺酸盐（RSO3 -），例如油酸，月桂酸钠，月桂基硫酸钠和十二烷基磺酸钠。
所述纳米疏水乳液的制备方法：
将乳化剂按比例溶于50-80℃的热水中，机械搅拌混合物30分钟，直到形成均匀的乳液；当乳液温度降到室温25℃左右时，用少量的10%的盐酸或10%的氢氧化钠溶液调节pH值到7±1；然后用高剪切机在800至2000rpm转速下搅拌该乳液，同时缓慢加入活性物，加完后的混合物继续高速搅拌30分钟直到形成均匀的乳白色浓缩乳液。
本发明的优点是：在雨季时，当雨量不大时，雨水会慢速渗透穿过疏水土层，进入下层土壤。当暴雨来临或上游形成流水时，水量超过疏水层的渗透速度，多余的雨水就会从疏水层表面流走，不会形成泥浆流动现象，从而保护边坡防止土壤流失。
旱季时，因疏水土层就像防水层那样防止或减少下层普通亲水土中的水分向上移动和蒸发，起到了保水的作用，同时，疏水土层不会像普通亲水土那样干旱时形成裂缝，进一步达到了内层土壤保水的作用。内层土壤保水时间增长了，植物的抗旱能力也就随之增强了。
因为疏水土层旱季时不容易形成开裂/裂缝现象并保护内层土壤的水分，这时内层土壤特别是粘土就不易形成硬化现象，这对保护植物的根茎是非常重要的。
裸露的斜坡或类似梯田的非平地地带，都可采用边坡生态保护办法进行生态修复。
利用本方法还可解决夯土墙和泥土房子及各种泥土建筑和设施的防水处理，回填坡面临时性抗冲处理，解决草木恢复前裸露面抗冲处理，解决施工便道后期的直接复垦。
具体实施方式：
边坡保土保水的方法：
（1）在边坡表面按照草籽或幼苗的种植办法预先种植并浇水养护。
（2）在晴天时或在雨季到来之前数天喷洒纳米超疏水乳液，根据边坡状况和土的性质，试验得出合适的纳米超疏水乳液喷洒量和合适的乳液浓度，稀释后用于直接喷洒的纳米超疏水乳液浓度为0.5%—10%，每平方米喷洒1-5公斤的该稀释乳液，每平方米含有乳液的有效活性物成分为5克至200克。喷洒完毕后，一般春夏季两三天即可形成疏水土层，疏水土层的厚度控制在5毫米至30毫米之间，平均厚度为10-20毫米。喷洒纳米超疏水乳液后表面土壤无需搅拌无需压实，完全靠乳液的自然渗透形成疏水土层。
所述的纳米超疏水乳液由下列原料制成的：活性物、乳化剂、水；其中活性物占纳米疏水乳液总重量的1—70%，乳化剂占纳米疏水乳液总重量的0.1—10%，水占纳米疏水乳液总重量的98.9—20%；工业生产时活性物的含量可以是从1%至70%的任何溶度；
所述的纳米疏水乳液的活性物为含氢硅氧烷聚合物（又称含氢硅油），纳米疏水乳液的活性物的含氢量为0.1%-1.7%，含氢硅氧烷聚合物的分子式为：
(R)3SiO[RHSiO]nSi(R)3 R = 1-5个碳的烷基；
所述的乳化剂由中性表面活性剂和阴离子表面活性剂组成，两类表面活性剂的混合比例不限；
所述的中性表面活性剂可以是脂肪醇类或醚类或酯类化合物，或者是它们的混合物，混合比例不限；
所述的阴离子表面活性剂为脂肪硫酸盐或脂肪磺酸盐或脂肪酸盐，或者是它们的混合物，混合比例不限；
所述的脂肪醇类可以是：至少含有1个或多个醇羟基（-OH）和含有6-30个直链或支链碳的饱和或不饱和烷烃，也可含有0-3个羧基（-COO-）衍生物。例如月桂醇，硬脂醇和棕榈醇等。
所述的醚类可以是：至少含有1个或多个醚基（C-O-C）和含有至少两个6-30个直链或支链碳的饱和或不饱和烷烃,也可以是聚乙二醇的衍生物，HO[CH2CH2O]n-H(n=100-100000)，例如月桂醇聚醚，平平加-10，聚乙二醇1000，HO[CH2CH2O]1000-H。
所述的酯类化合物可以是：含有6-30个直链或支链碳的饱和或不饱和脂肪酸脂衍生物（-COOC-），也可含有0-5个醇羟基，例如双硬脂酸甘油酯，单硬脂酸甘油酯等。
所述的酯肪酸或其盐可以是：含有6-30个直链或支链碳的饱和或不饱和脂肪酸（-COOH）或其脂肪酸盐（-COOM，M=Na、K、Ca等）或脂肪硫酸盐（ROSO3 -）,或脂肪磺酸盐（RSO3 -），例如油酸，月桂酸钠，月桂基硫酸钠和十二烷基磺酸钠。
所述纳米疏水乳液的制备方法：
将乳化剂按比例溶于50-80℃的热水中，机械搅拌混合物30分钟，直到形成均匀的乳液；当乳液温度降到室温25℃左右时，用少量的10%的盐酸或10%的氢氧化钠溶液调节pH值到7±1；然后用高剪切机在800至2000rpm转速下搅拌该乳液，同时缓慢加入活性物，加完后的混合物继续高速搅拌30分钟直到形成均匀的乳白色浓缩乳液。
实施例1；
在边坡表面按照草籽或幼苗的种植办法预先种植并浇水养护。在晴天时或在雨季到来之前数天喷洒纳米超疏水乳液，根据边坡状况和土的性质，直接喷洒的纳米超疏水乳液浓度为0.5%，每平方米喷洒1公斤的该稀释乳液，喷洒完后每平方米含有乳液的有效活性物成分为5克。喷洒完毕后，一般春夏季两三天即可形成疏水土层，疏水土层的厚度控制在5毫米至30毫米之间，平均厚度为10-20毫米。喷洒纳米超疏水乳液后表面土壤无需搅拌无需压实，完全靠乳液的自然渗透形成疏水土层。
实施例2；
在边坡表面按照草籽或幼苗的种植办法预先种植并浇水养护。在晴天时或在雨季到来之前数天喷洒纳米超疏水乳液，根据边坡状况和土的性质，试验得出合适的纳米超疏水乳液喷洒量和合适的乳液浓度，稀释后用于直接喷洒的纳米超疏水乳液浓度为7%，每平方米喷洒2.2公斤的该稀释乳液，则每平方米含有乳液的有效活性物成分为150克。喷洒完毕后，一般春夏季两三天即可形成疏水土层，疏水土层的厚度控制在5毫米至30毫米之间，平均厚度为10-20毫米。喷洒纳米超疏水乳液后表面土壤无需搅拌无需压实，完全靠乳液的自然渗透形成疏水土层。
实施例3；
在边坡表面按照草籽或幼苗的种植办法预先种植并浇水养护。在晴天时或在雨季到来之前数天喷洒纳米超疏水乳液，根据边坡状况和土的性质，试验得出合适的纳米超疏水乳液喷洒量和合适的乳液浓度，稀释后用于直接喷洒的纳米超疏水乳液浓度为2%，每平方米喷洒4公斤的该稀释乳液，每平方米含有乳液的有效活性物成分为80克。喷洒完毕后，一般春夏季两三天即可形成疏水土层，疏水土层的厚度控制在5毫米至30毫米之间，平均厚度为10-20毫米。喷洒纳米超疏水乳液后表面土壤无需搅拌无需压实，完全靠乳液的自然渗透形成疏水土层。
实施例4；
在边坡表面按照草籽或幼苗的种植办法预先种植并浇水养护。在晴天时或在雨季到来之前数天喷洒纳米超疏水乳液，根据边坡状况和土的性质，试验得出合适的纳米超疏水乳液喷洒量和合适的乳液浓度，稀释后用于直接喷洒的纳米超疏水乳液浓度为10%，每平方米喷洒2公斤的该稀释乳液，每平方米含有乳液的有效活性物成分为200克。喷洒完毕后，一般春夏季两三天即可形成疏水土层，疏水土层的厚度控制在5毫米至30毫米之间，平均厚度为10-20毫米。喷洒纳米超疏水乳液后表面土壤无需搅拌无需压实，完全靠乳液的自然渗透形成疏水土层。
实施例5；
在边坡表面按照草籽或幼苗的种植办法预先种植并浇水养护。在晴天时或在雨季到来之前数天喷洒纳米超疏水乳液，根据边坡状况和土的性质，试验得出合适的纳米超疏水乳液喷洒量和合适的乳液浓度，稀释后用于直接喷洒的纳米超疏水乳液浓度为1%，每平方米喷洒3公斤的该稀释乳液，每平方米含有乳液的有效活性物成分为30克。喷洒完毕后，一般春夏季两三天即可形成疏水土层，疏水土层的厚度控制在5毫米至30毫米之间，平均厚度为10-20毫米。喷洒纳米超疏水乳液后表面土壤无需搅拌无需压实，完全靠乳液的自然渗透形成疏水土层。
实施例6；
在边坡表面按照草籽或幼苗的种植办法预先种植并浇水养护。在晴天时或在雨季到来之前数天喷洒纳米超疏水乳液，根据边坡状况和土的性质，试验得出合适的纳米超疏水乳液喷洒量和合适的乳液浓度，稀释后用于直接喷洒的纳米超疏水乳液浓度为1%，每平方米喷洒5公斤的该稀释乳液，每平方米含有乳液的有效活性物成分为50克。喷洒完毕后，一般春夏季两三天即可形成疏水土层，疏水土层的厚度控制在5毫米至30毫米之间，平均厚度为10-20毫米。喷洒纳米超疏水乳液后表面土壤无需搅拌无需压实，完全靠乳液的自然渗透形成疏水土层。
Claims (2)
1.一种边坡生态保护和裸露地皮植被保护的方法，其特征是：
(1)在边坡表面按照草籽或幼苗的种植办法预先种植并浇水养护；
(2)在晴天时或在雨季到来之前数天喷洒纳米超疏水乳液，用于直接喷洒的纳米超疏水乳液浓度为0.5％—10％，每平方米喷洒1-5公斤，每平方米含有乳液的有效活性物成分为5克至200克；喷洒完毕后，一般春夏季两三天即可形成疏水土层，疏水土层的厚度控制在5毫米至30毫米之间，平均厚度为10-20毫米；喷洒纳米超疏水乳液后表面土壤无需搅拌无需压实，完全靠乳液的自然渗透形成疏水土层；
所述的纳米超疏水乳液由下列原料制成的：活性物、乳化剂、水；其中活性物占纳米疏水乳液总重量的1—70％，乳化剂占纳米疏水乳液总重量的0.1—10％，水占纳米疏水乳液总重量的98.9—20％；工业生产时活性物的含量为1％至70％的任何溶度；
所述的纳米疏水乳液的活性物为含氢硅氧烷聚合物，纳米疏水乳液的活性物的含氢量为0.1％-1.7％；
含氢硅氧烷聚合物的分子式为：
(R)3SiO[RHSiO]nSi(R)3,R＝含有1-5个碳的烷基。
2.按照权利要求1所述的边坡生态保护和裸露地皮植被保护的方法，其特征是：
所述的乳化剂由中性表面活性剂和阴离子表面活性剂组成，两类表面活性剂的混合比例不限；
所述的阴离子表面活性剂为含有6-30个直链或支链碳的饱和或不饱和脂肪酸或其脂肪酸盐或脂肪硫酸盐或脂肪磺酸盐，或者是它们的混合物，混合比例不限；
所述的中性表面活性剂为脂肪醇类或醚类或酯类化合物，或者是它们的混合物，混合比例不限；
所述的脂肪醇类化合物为含有至少1个醇羟基并含有0-3个羧基，且含有由6-30个直链或支链碳构成的饱和或不饱和烷烃的物质；
所述的醚类化合物为含有至少1个醚键且含有至少两个由6-30个直链或支链碳构成的饱和或不饱和烷烃的物质，或聚乙二醇的衍生物HO[CH2CH2O]n-H，n＝100-100000；
所述的酯类化合物为：含有6-30个直链或支链碳且含有0-5个醇羟基的饱和或不饱和脂肪酸酯或其衍生物；
所述纳米疏水乳液的制备方法：
将乳化剂按比例溶于50-80℃的热水中，机械搅拌混合物30分钟，直到形成均匀的乳液；当乳液温度降到室温25℃左右时，用少量的10％的盐酸或10％的氢氧化钠溶液调节pH值到7±1；然后用高剪切机在800至2000rpm转速下搅拌该乳液，同时缓慢加入活性物，加完后的混合物继续高速搅拌30分钟直到形成均匀的乳白色浓缩乳液。