CN111205782A - 一种具有自消毒透明隔离功能的保护膜结构及其加工、涂布方法 - Google Patents
一种具有自消毒透明隔离功能的保护膜结构及其加工、涂布方法 Download PDFInfo
- Publication number
- CN111205782A CN111205782A CN202010126996.6A CN202010126996A CN111205782A CN 111205782 A CN111205782 A CN 111205782A CN 202010126996 A CN202010126996 A CN 202010126996A CN 111205782 A CN111205782 A CN 111205782A
- Authority
- CN
- China
- Prior art keywords
- layer
- self
- film
- protective film
- disinfection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种具有自消毒透明隔离功能的保护膜结构，包括：最下层的粘接层、中间的结构强度层及最上层的自消毒层，所述粘接层是用于将保护膜固定在被贴物表面，结构强度层是使用透明的聚乙烯、聚丙烯、聚酯塑料为原料能使保护膜有一定的力学强度并透明，自消毒层具有杀灭功能且能长期有效杀灭落在其表面通过浮尘、飞沫、接触带来的细菌和病毒；结构强度层为基膜，在粘接层上还贴附有配合使用的离型膜。本发明中间以聚乙烯、聚丙烯、聚酯等原料制成透明的基膜和结构强度层；下面是粘结层，负责贴合被粘物体；上层是自消毒层，负责杀灭细菌和病毒，阻隔污染物黏附到物体上，薄膜表面具有保护作用，沾染上细菌和病毒也会被杀灭，可反复触碰。
Description
技术领域
本发明涉及保护膜结构及加工技术领域，具体为一种具有自消毒透明隔离功能的保护膜结构及其加工、涂布方法。
背景技术
保护膜一般可以看成有三层结构：最下层为粘结层，用途是将保护膜固定在被贴物表面；中间层为结构强度层，用途是保证保护膜有一定的力学强度；最上层为离型层，当薄膜收卷后，这层表面与粘结层接触，展开薄膜时，这两层分离开。离型层起到易撕开作用。有时离型层和结构强度层可以是同层，这种保护膜主要作用是防护被贴物表面。随着社会发展，以及世界各地各种公共卫生事件的发生，大家对环境卫生的要求也越来越高，希望病毒、病菌等传染源能被杀灭和阻断，经常接触的物品能被及时消毒和阻隔。为此，需要设计相应的技术方案给予解决。
发明内容
本发明是通过保护膜膜层的设计，中间以聚乙烯、聚丙烯、聚酯等原料制成透明的基膜和结构强度层；下面是粘结层，负责贴合被粘物体；上层是自消毒层，负责杀灭细菌和病毒；阻隔污染物黏附到物体上，薄膜表面具有保护作用，沾染上细菌和病毒也会被杀灭，可以反复触碰，解决上述背景技术问题，满足实际应用需求。
为实现上述目的，本发明提供如下技术方案：一种具有自消毒透明隔离功能的保护膜结构，从下往上依次包括：最下层的粘接层、中间层的结构强度层以及最上层的自消毒层，所述粘接层是用于将保护膜固定在被贴物表面，所述结构强度层是使用透明的聚乙烯、聚丙烯、聚酯塑料为原料能使保护膜有一定的力学强度并透明，所述自消毒层具有杀灭功能且能长期有效杀灭落在其表面通过浮尘、飞沫、接触带来的细菌和病毒；其中，所述结构强度层为基膜，在所述粘接层上还贴附有配合使用的离型膜。
作为上述技术方案的改进，所述具有自消毒透明隔离功能的保护膜结构的加工方法如下：
S1：底层为粘接层(胶粘层)，选用适合贴附被贴物的材料，如聚苯乙烯-乙烯-加氢丁二烯三段共聚物、聚异丁烯、乙烯-醋酸乙烯共聚物等弹性体和共混复配原料；
S2：中间为结构强度层，选用聚乙烯、聚丙烯、聚酯等材料，保证保护膜的强度和透明；
S3：最上层为自消毒层，原料是塑料和具有杀灭病毒、细菌功能助剂，如使用低加工温度的乙烯-醋酸乙烯共聚物与对温度敏感多聚氨基酸酞菁锌化合物光敏分子共混，聚乙烯、聚丙烯与活性纳米银共混，具有杀菌功能的碱性氨基酸官能团、带长链烷基季铵盐杀菌活性官能团、吡啶类季铵盐官能团接枝聚乙烯；
S4：将上述三层材料流延或吹塑共挤，得到需要的薄膜；其中，如不需要有贴附功能，底层材料选用无黏性材料或将薄膜加工成上下两层都具有自消毒效果或选择薄膜复合的方法，将加工好具有不同性能的薄膜复合起来，以达到应用效果。
作为上述技术方案的改进，所述具有自消毒透明隔离功能的保护膜结构的涂布方法如下：
F1：基膜的选择聚乙烯、聚丙烯、聚酯等透明薄膜以及透明复合膜，基膜底面根据需要涂布胶水，胶水可以选择丙烯酸型、聚氨酯型、硅胶型、橡胶性等各类胶水和热熔胶，根据需要再复合离型膜/纸；
F2：在最上层涂布具有自消毒功能的涂层，涂层由高分子主体，加上具有杀灭病毒、细菌功能的助剂(比如水性/油性丙烯酸型涂料、水性聚氨酯涂料与多聚氨基酸酞菁锌化合物光敏分子溶液配伍，活性纳米银浆料添加丙烯酸型涂料L)；如不需要有贴附功能，可以只涂布一层有自消毒功能的涂层或两面都涂有自消毒功能的涂层。
与现有技术相比，本发明的有益效果是：
本发明是通过保护膜膜层的设计，中间以聚乙烯、聚丙烯、聚酯等原料制成透明的基膜和结构强度层；下面是粘结层，负责贴合被粘物体；上层是自消毒层，负责杀灭细菌和病毒；阻隔污染物黏附到物体上，薄膜表面具有保护作用，沾染上细菌和病毒也会被杀灭，可以反复触碰。
附图说明
图1为本发明所述具有自消毒透明隔离功能的保护膜结构示意图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
在本发明的描述中，需要理解的是，术语“上”、“下”、“前”、“后”、“左”、“右”、“顶”、“底”、“内”、“外”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。
实施例：一种具有自消毒透明隔离功能的保护膜结构，从下往上包括：最下层的粘接层3、中间层的结构强度层2以及最上层的自消毒层1，粘接层3是用于将保护膜固定在被贴物表面，结构强度层2是使用透明的聚乙烯、聚丙烯、聚酯塑料为原料能使保护膜有一定的力学强度并透明，自消毒层1具有杀灭功能且能长期有效杀灭落在其表面通过浮尘、飞沫、接触带来的细菌和病毒；其结构强度层2为基膜，在粘接层3上还贴附有配合使用的离型膜4。
具体地，所述具有自消毒透明隔离功能的保护膜结构的加工方法如下：
S1：底层为粘接层(胶粘层3)，选用适合贴附被贴物的材料，如聚苯乙烯-乙烯-加氢丁二烯三段共聚物、聚异丁烯、乙烯-醋酸乙烯共聚物等弹性体和共混复配原料；
S2：中间为结构强度层2，选用聚乙烯、聚丙烯、聚酯等材料，保证保护膜的强度和透明；
S3：最上层为自消毒层1，原料是塑料和具有杀灭病毒、细菌功能助剂，如使用低加工温度的乙烯-醋酸乙烯共聚物与对温度敏感多聚氨基酸酞菁锌化合物光敏分子共混，聚乙烯、聚丙烯与活性纳米银共混，具有杀菌功能的碱性氨基酸官能团、带长链烷基季铵盐杀菌活性官能团、吡啶类季铵盐官能团接枝聚乙烯；
S4：将上述三层材料流延或吹塑共挤，得到需要的薄膜；其中，如不需要有贴附功能，底层材料选用无黏性材料或将薄膜加工成上下两层都具有自消毒效果或选择薄膜复合的方法，将加工好具有不同性能的薄膜复合起来，以达到应用效果。
更具体地，所述具有自消毒透明隔离功能的保护膜结构的涂布方法如下：
F1：基膜的选择聚乙烯、聚丙烯、聚酯等透明薄膜以及透明复合膜，基膜底面根据需要涂布胶水，胶水可以选择丙烯酸型、聚氨酯型、硅胶型、橡胶性等各类胶水和热熔胶，根据需要再复合离型膜/纸；
F2：在最上层涂布具有自消毒功能的涂层，涂层由高分子主体，加上具有杀灭病毒、细菌功能的助剂(比如水性/油性丙烯酸型涂料、水性聚氨酯涂料与多聚氨基酸酞菁锌化合物光敏分子溶液配伍，活性纳米银浆料添加丙烯酸型涂料L)；如不需要有贴附功能，可以只涂布一层有自消毒功能的涂层或两面都涂有自消毒功能的涂层。
综上所述：本发明是通过保护膜膜层的设计，中间以聚乙烯、聚丙烯、聚酯等原料制成透明的基膜和结构强度层；下面是粘结层，负责贴合被粘物体；上层是自消毒层，负责杀灭细菌和病毒；阻隔污染物黏附到物体上，薄膜表面具有保护作用，沾染上细菌和病毒也会被杀灭，可以反复触碰。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点,对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明；因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内，不应将权利要求中的任何附图标记视为限制所涉及的权利要求。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (3)
1.一种具有自消毒透明隔离功能的保护膜结构，其特征在于：从下往上依次包括：最下层的粘接层(3)、中间层的结构强度层(2)以及最上层的自消毒层(1)，所述粘接层(3)是用于将保护膜固定在被贴物表面，所述结构强度层(2)是使用透明的聚乙烯、聚丙烯、聚酯塑料为原料能使保护膜有一定的力学强度并透明，所述自消毒层(1)具有杀灭功能且能长期有效杀灭落在其表面通过浮尘、飞沫、接触带来的细菌和病毒；其中，所述结构强度层(2)为基膜，在所述粘接层(3)上还贴附有配合使用的离型膜(4)。
2.根据权利要求1所述具有自消毒透明隔离功能的保护膜结构的加工、涂布方法，其特征在于：所述加工方法如下：
S1：底层为粘接层(胶粘层)，选用适合贴附被贴物的材料，如聚苯乙烯-乙烯-加氢丁二烯三段共聚物、聚异丁烯、乙烯-醋酸乙烯共聚物等弹性体和共混复配原料；
S2：中间为结构强度层，选用聚乙烯、聚丙烯、聚酯等材料，保证保护膜的强度和透明；
S3：最上层为自消毒层，原料是塑料和具有杀灭病毒、细菌功能助剂，如使用低加工温度的乙烯-醋酸乙烯共聚物与对温度敏感多聚氨基酸酞菁锌化合物光敏分子共混，聚乙烯、聚丙烯与活性纳米银共混，具有杀菌功能的碱性氨基酸官能团、带长链烷基季铵盐杀菌活性官能团、吡啶类季铵盐官能团接枝聚乙烯；
S4：将上述三层材料流延或吹塑共挤，得到需要的薄膜；其中，如不需要有贴附功能，底层材料选用无黏性材料或将薄膜加工成上下两层都具有自消毒效果或选择薄膜复合的方法，将加工好具有不同性能的薄膜复合起来，以达到应用效果。
3.根据权利要求1所述具有自消毒透明隔离功能的保护膜结构的加工、涂布方法，其特征在于：所述涂布方法如下：
F1：基膜的选择聚乙烯、聚丙烯、聚酯等透明薄膜以及透明复合膜，基膜底面根据需要涂布胶水，胶水可以选择丙烯酸型、聚氨酯型、硅胶型、橡胶性等各类胶水和热熔胶，根据需要再复合离型膜/纸；
F2：在最上层涂布具有自消毒功能的涂层，涂层由高分子主体，加上具有杀灭病毒、细菌功能的助剂(比如水性/油性丙烯酸型涂料、水性聚氨酯涂料与多聚氨基酸酞菁锌化合物光敏分子溶液配伍，活性纳米银浆料添加丙烯酸型涂料L)；如不需要有贴附功能，可以只涂布一层有自消毒功能的涂层或两面都涂有自消毒功能的涂层。