CN111139981A - Process for processing and paving modified rubber wooden shingles - Google Patents
Process for processing and paving modified rubber wooden shingles Download PDFInfo
- Publication number
- CN111139981A CN111139981A CN201911372701.7A CN201911372701A CN111139981A CN 111139981 A CN111139981 A CN 111139981A CN 201911372701 A CN201911372701 A CN 201911372701A CN 111139981 A CN111139981 A CN 111139981A
- Authority
- CN
- China
- Prior art keywords
- wood
- ultraviolet
- cloth
- paving
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a process for processing and paving modified rubber wooden shingles, which comprises the following steps: a plurality of wood keels which are distributed at intervals are fixed at the top of the inclined frame; paving a layer of waterproof cloth on the wooden keel; laying a layer of ultraviolet-proof cloth on the waterproof cloth; taking up the shingle body, laying the shingle body on the ultraviolet-proof cloth, and nailing the shingle body by a gun; the invention has the beneficial effects that: when the waterproof cloth is laid on the wood keel and used for a roof, the waterproof effect is favorably improved; when the ultraviolet-proof cloth is used for a roof, the ultraviolet-proof effect after the shingles are paved is increased through the ultraviolet-proof cloth; through the collocation of wooden fossil fragments and rifle nail, help improving the steadiness of shingle installation.
Description
Technical Field
The invention belongs to the technical field of shingle paving, and particularly relates to a process for processing and paving modified rubber wooden shingles.
Background
Shingles are shingles used for roofing from ancient times to modern times, and roof of many buildings are shingles until now.
The advantages of the shingle: the modified rubber wooden shingle can be suitable for use in wet or dry environments; the shingles can resist various adverse weather influences; shingles can bring unique visual enjoyment due to the change in color and texture of wood; the outdoor environment-friendly solar energy collector is properly installed, has a shelf life of 30-50 years in outdoor use, and is certified in engineering test materials institute tests.
In order to further improve the installation stability and the waterproof and ultraviolet-proof performance, a process for processing and paving the modified rubber wooden shingles is provided.
Disclosure of Invention
The invention aims to provide a process for processing and paving modified rubber wooden shingles, which further improves the installation stability and the waterproof and ultraviolet-proof performance.
In order to achieve the purpose, the invention provides the following technical scheme: a process for processing and paving modified rubber wooden shingles comprises the following steps:
the method comprises the following steps: a plurality of wood keels which are distributed at intervals are fixed at the top of the inclined frame;
step two: paving a layer of waterproof cloth on the wooden keel;
step three: laying a layer of ultraviolet-proof cloth on the waterproof cloth;
step four: the shingle body is taken up and laid on the ultraviolet-proof cloth and nailed well by a gun nail.
As a preferred technical solution of the present invention, the shingle body is processed by the following steps:
the first step is as follows: performing double-sided planing on the processed rubber wood product, and correcting burrs of the initial product;
the second step is that: sorting the planed wood, and selecting out wood with serious defects which do not meet the product requirements;
the third step: loading wood into a special modification tank containing a modified liquid, a polymer composition and a mixed composition containing polyalcohol and a crosslinking agent, decompressing for 1 hour, pressurizing for 6 hours to enable the modified liquid to enter wood holes, and emptying for waiting;
the fourth step: drying the modified rubber wood;
the fifth step: and (5) drying, cooling to normal temperature, and cutting into shingles by using a cutting machine.
In the third step, the pressure is reduced for 1 hour and is increased for 6 hours, so that the modification solution enters the wood pores, and the modified solution is emptied for 35-45 min.
As a preferable technical scheme of the invention, in the fourth step, the water content after drying is less than or equal to 8%.
As a preferable technical scheme, the ultraviolet-proof cloth and the waterproof cloth are both of cuboid structures and are matched with each other.
As a preferable technical scheme, the wood keel is of an inverted U-shaped structure.
Compared with the prior art, the invention has the beneficial effects that:
(1) when the waterproof cloth is laid on the wood keel and used for a roof, the waterproof effect is favorably improved;
(2) when the ultraviolet-proof cloth is used for a roof, the ultraviolet-proof effect after the shingles are paved is increased through the ultraviolet-proof cloth;
(3) through the collocation of wooden fossil fragments and rifle nail, help improving the steadiness of shingle installation.
Drawings
FIG. 1 is a schematic structural view of the present invention;
fig. 2 is a schematic view of a wood keel mounting structure of the invention;
FIG. 3 is a schematic view of the laying structure of the waterproof cloth and the ultraviolet-proof cloth of the present invention;
FIG. 4 is a flow chart of the present invention;
in the figure: 1. a first fixing frame; 2. a second fixing frame; 3. a shingle body; 4. wood keel; 5. an inclined frame; 6. anti-ultraviolet cloth; 7. a waterproof cloth.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example 1
Referring to fig. 1, fig. 2, fig. 3 and fig. 4, the present invention provides a technical solution: a process for processing and paving modified rubber wooden shingles comprises the following steps:
the method comprises the following steps: a plurality of wood keels 4 which are distributed at intervals are fixed at the top of the inclined frame 5;
step two: a layer of waterproof cloth 7 is laid on the wood keel 4, and when the waterproof cloth is used for a roof, the waterproof effect is increased;
step three: a layer of ultraviolet-proof cloth 6 is paved on the waterproof cloth 7, the ultraviolet-proof cloth 6 is formed by processing pe, has an ultraviolet-proof effect, and when the ultraviolet-proof cloth is used for a roof, the ultraviolet-proof effect after the shingles are paved is increased through the ultraviolet-proof cloth 6;
step four: the shingle body 3 is taken up and laid on the ultraviolet-proof cloth 6, and the shingle body 3 is firmly installed by nailing with a gun.
The processing steps of the shingle body 3 are as follows:
the first step is as follows: performing double-sided planing on the processed rubber wood product, and correcting burrs of the initial product;
the second step is that: sorting the planed wood, and selecting out wood with serious defects which do not meet the product requirements;
the third step: loading wood into a special modification tank containing a modified liquid, a polymer composition and a mixed composition containing polyalcohol and a crosslinking agent, decompressing for 1 hour, pressurizing for 6 hours to enable the modified liquid to enter wood holes, and emptying for waiting for 35 min;
the fourth step: drying the modified rubber wood, wherein the water content after drying is less than or equal to 8%;
the fifth step: drying, cooling to normal temperature, and cutting into shingles by using a cutting machine; the treated wood has corrosion resistance, insect prevention and flame retardant functions, and the service life of the shingle body 3 is prolonged.
In this embodiment, it is preferred, prevent that ultraviolet cloth 6 and tarpaulin 7 are the cuboid structure, and prevent that ultraviolet cloth 6 and tarpaulin 7 phase-match for prevent that ultraviolet cloth 6 and tarpaulin 7's laminating is inseparabler, better play the effect of anti ultraviolet and rain-proof water.
In this embodiment, preferably, the wooden keel 4 is an inverted U-shaped structure, so that the waterproof cloth 7 and the ultraviolet-proof cloth 6 are laid more smoothly, and the shingle body 3 can be laid conveniently.
Example 2
Referring to fig. 1, fig. 2, fig. 3 and fig. 4, the present invention provides a technical solution: a process for processing and paving modified rubber wooden shingles comprises the following steps:
the method comprises the following steps: a plurality of wood keels 4 which are distributed at intervals are fixed at the top of the inclined frame 5;
step two: a layer of waterproof cloth 7 is laid on the wood keel 4, and when the waterproof cloth is used for a roof, the waterproof effect is increased;
step three: a layer of ultraviolet-proof cloth 6 is paved on the waterproof cloth 7, the ultraviolet-proof cloth 6 is formed by processing pe, has an ultraviolet-proof effect, and when the ultraviolet-proof cloth is used for a roof, the ultraviolet-proof effect after the shingles are paved is increased through the ultraviolet-proof cloth 6;
step four: the shingle body 3 is taken up and laid on the ultraviolet-proof cloth 6, and the shingle body 3 is firmly installed by nailing with a gun.
The processing steps of the shingle body 3 are as follows:
the first step is as follows: performing double-sided planing on the processed rubber wood product, and correcting burrs of the initial product;
the second step is that: sorting the planed wood, and selecting out wood with serious defects which do not meet the product requirements;
the third step: loading wood into a special modification tank containing a modified liquid, a polymer composition and a mixed composition containing polyalcohol and a crosslinking agent, decompressing for 1 hour, pressurizing for 6 hours to enable the modified liquid to enter wood holes, and emptying for 40 min;
the fourth step: drying the modified rubber wood, wherein the water content after drying is less than or equal to 8%;
the fifth step: drying, cooling to normal temperature, and cutting into shingles by using a cutting machine; the treated wood has corrosion resistance, insect prevention and flame retardant functions, and the service life of the shingle body 3 is prolonged.
In this embodiment, it is preferred, prevent that ultraviolet cloth 6 and tarpaulin 7 are the cuboid structure, and prevent that ultraviolet cloth 6 and tarpaulin 7 phase-match for prevent that ultraviolet cloth 6 and tarpaulin 7's laminating is inseparabler, better play the effect of anti ultraviolet and rain-proof water.
In this embodiment, preferably, the wooden keel 4 is an inverted U-shaped structure, so that the waterproof cloth 7 and the ultraviolet-proof cloth 6 are laid more smoothly, and the shingle body 3 can be laid conveniently.
Example 3
Referring to fig. 1, fig. 2, fig. 3 and fig. 4, the present invention provides a technical solution: a process for processing and paving modified rubber wooden shingles comprises the following steps:
the method comprises the following steps: a plurality of wood keels 4 which are distributed at intervals are fixed at the top of the inclined frame 5;
step two: a layer of waterproof cloth 7 is laid on the wood keel 4, and when the waterproof cloth is used for a roof, the waterproof effect is increased;
step three: a layer of ultraviolet-proof cloth 6 is paved on the waterproof cloth 7, the ultraviolet-proof cloth 6 is formed by processing pe, has an ultraviolet-proof effect, and when the ultraviolet-proof cloth is used for a roof, the ultraviolet-proof effect after the shingles are paved is increased through the ultraviolet-proof cloth 6;
step four: the shingle body 3 is taken up and laid on the ultraviolet-proof cloth 6, and the shingle body 3 is firmly installed by nailing with a gun.
The processing steps of the shingle body 3 are as follows:
the first step is as follows: performing double-sided planing on the processed rubber wood product, and correcting burrs of the initial product;
the second step is that: sorting the planed wood, and selecting out wood with serious defects which do not meet the product requirements;
the third step: loading wood into a special modification tank containing a modified liquid, a polymer composition and a mixed composition containing polyalcohol and a crosslinking agent, decompressing for 1 hour, pressurizing for 6 hours to enable the modified liquid to enter wood holes, and emptying for 45 min;
the fourth step: drying the modified rubber wood, wherein the water content after drying is less than or equal to 8%;
the fifth step: drying, cooling to normal temperature, and cutting into shingles by using a cutting machine; the treated wood has corrosion resistance, insect prevention and flame retardant functions, and the service life of the shingle body 3 is prolonged.
In this embodiment, it is preferred, prevent that ultraviolet cloth 6 and tarpaulin 7 are the cuboid structure, and prevent that ultraviolet cloth 6 and tarpaulin 7 phase-match for prevent that ultraviolet cloth 6 and tarpaulin 7's laminating is inseparabler, better play the effect of anti ultraviolet and rain-proof water.
In this embodiment, preferably, the wooden keel 4 is an inverted U-shaped structure, so that the waterproof cloth 7 and the ultraviolet-proof cloth 6 are laid more smoothly, and the shingle body 3 can be laid conveniently.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (6)
1. A process for processing and paving modified rubber wooden shingles is characterized in that: the paving process comprises the following steps:
the method comprises the following steps: a plurality of wood keels (4) which are distributed at intervals are fixed at the top of the inclined frame (5);
step two: a layer of waterproof cloth (7) is laid on the wooden keel (4);
step three: a layer of ultraviolet-proof cloth (6) is laid on the waterproof cloth (7);
step four: the shingle body (3) is taken up and laid on the ultraviolet-proof cloth (6) and is nailed well by a gun nail.
2. The process for processing and paving the modified rubber wooden shingle according to claim 1, wherein the process comprises the following steps: the processing steps of the shingle body (3) are as follows:
the first step is as follows: performing double-sided planing on the processed rubber wood product, and correcting burrs of the initial product;
the second step is that: sorting the planed wood, and selecting out wood with serious defects which do not meet the product requirements;
the third step: loading wood into a special modification tank containing modification solution (a polymer composition, a mixed composition containing polyalcohol and crosslinking agent), reducing pressure for 1 hr, pressurizing for 6 hr to make the modification solution enter wood pores, and emptying;
the fourth step: drying the modified rubber wood;
the fifth step: and (5) drying, cooling to normal temperature, and cutting into shingles by using a cutting machine.
3. The process for processing and paving the modified rubber wooden shingle according to claim 2, wherein the process comprises the following steps: and in the third step, the pressure is reduced for 1 hour and is increased for 6 hours, so that the modification liquid enters the wood holes, and the wood holes are emptied for 35-45 min.
4. The process for processing and paving the modified rubber wooden shingle according to claim 2, wherein the process comprises the following steps: in the fourth step, the water content after drying is less than or equal to 8 percent.
5. The process for processing and paving the modified rubber wooden shingle according to claim 1, wherein the process comprises the following steps: the ultraviolet-proof cloth (6) and the waterproof cloth (7) are both of cuboid structures, and the ultraviolet-proof cloth (6) is matched with the waterproof cloth (7).
6. The process for processing and paving the modified rubber wooden shingle according to claim 1, wherein the process comprises the following steps: the wooden keel (4) is of an inverted U-shaped structure.