CN111123638A - Preparation method of high-brightness curtain - Google Patents
Preparation method of high-brightness curtain Download PDFInfo
- Publication number
- CN111123638A CN111123638A CN201911338877.0A CN201911338877A CN111123638A CN 111123638 A CN111123638 A CN 111123638A CN 201911338877 A CN201911338877 A CN 201911338877A CN 111123638 A CN111123638 A CN 111123638A
- Authority
- CN
- China
- Prior art keywords
- layer
- coating
- substrate
- white
- machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The application discloses a preparation method of a high-brightness curtain, which sequentially comprises the following steps: s1, using a PET sheet as a substrate to perform static elimination treatment; s2, transferring the ink layer to the reverse side of the substrate through a precision transfer printing machine; s3, transferring a gold oil layer on the ink layer through a precision transfer printing machine; s4, coating a corona eliminating agent on the front surface of the substrate on a precise screen combined compound machine to form a white corona eliminating agent layer; s5, coating an aging-resistant layer on the white corona-eliminating agent layer on a precise screen combined compound machine; s6 by TiO2Or Al2O3Or SiO2Sputtering to form a barrier layer on the aging resistant layer; s7, coating a protective layer on the barrier layer on a precision screen combined compound machine; s8, sequentially coating white glue and glass beads on the protective layer through a coating bead planting combination machine, heating, curing and shaping to sequentially form a white glue layer and a glass bead layer. The invention obtains a high-brightness curtain with multiple functionalities.
Description
Technical Field
The invention relates to a curtain, in particular to a preparation method of a high-brightness curtain.
Background
At present, the screen used for projection includes white plastic screen, glass bead screen, and metal screen. The white plastic screen is an economic screen, which has the characteristics of curling, diffuse reflection and large view field angle, but the brightness of the screen is not as good as that of a glass bead screen, the glass bead screen overcomes the defects of the white plastic screen, the imaging is clear in daytime, but the glass bead screen has higher requirements on practical environment, the water vapor can not be effectively blocked, the using effect of the glass bead screen is reduced, the power consumption of projection equipment is improved, and the metal screen has the advantages of higher screen surface gain and brightness, but brings inconvenience in the aspects of transportation and installation and is expensive.
Disclosure of Invention
The invention aims to provide a preparation method of a high-brightness curtain, which is used for preparing the high-brightness curtain with multiple functionalities.
In order to achieve the above object, the present invention provides the following technical solutions.
The embodiment of the application discloses a preparation method of a high-brightness curtain, which sequentially comprises the following steps:
s1, using a PET sheet as a substrate to perform static elimination treatment;
s2, transferring the ink layer to the reverse side of the substrate through a precision transfer printing machine;
s3, transferring a gold oil layer on the ink layer through a precision transfer printing machine;
s4, coating a corona eliminating agent on the front surface of the substrate on a precise screen combined compound machine to form a white corona eliminating agent layer;
s5, coating ethylene-tetrafluoroethylene copolymer or fluorinated ethylene propylene copolymer or ethylene chlorotrifluoroethylene copolymer or polyvinylidene fluoride on the white corona eliminating agent layer on a precise screen combined compound machine to form an aging resistant layer;
s6 by TiO2Or Al2O3Or SiO2Sputtering to form a barrier layer on the aging resistant layer;
s7, coating acrylic resin or unsaturated polyester or polyurethane or epoxy resin on the barrier layer on a precision screen combined compound machine to form a protective layer;
s8, sequentially coating white glue and glass beads on the protective layer through a coating bead planting combination machine, heating, curing and shaping to sequentially form a white glue layer and a glass bead layer.
Preferably, in the above method for manufacturing a high brightness curtain, the substrate has a thickness of 0.10 to 0.12 mm.
Preferably, in the above method for producing a high brightness curtain, the thickness of the aging-resistant layer is 30 to 40 μm.
Preferably, in the above method for producing a high brightness curtain, the thickness of the barrier layer is 10 to 15 μm.
Preferably, in the method for preparing the high-brightness curtain, the thickness of the protective layer is 1 to 3 μm.
Preferably, in the method for manufacturing a high brightness curtain, the surface of the gold oil layer is embossed to form a corrugated shape.
Preferably, in the above method for producing a high brightness curtain, the protective layer fills the surface relief and voids of the barrier layer.
Preferably, in the above method for producing a high brightness curtain, the particle size of the glass bead layer beads is less than 0.06 mm.
The invention provides a preparation method of a high-brightness curtain, and the high-brightness curtain with multiple functionalities is obtained.
Detailed Description
Technical solutions in the embodiments of the present invention will be described in detail below, and it is apparent that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments. All other embodiments, which can be obtained by a person skilled in the art without any inventive step based on the embodiments of the present invention, are within the scope of the present invention.
The embodiment of the invention is as follows:
the preparation method of the high-brightness curtain sequentially comprises the following steps:
s1, adopting a PET sheet as a substrate, and performing static elimination treatment, wherein the thickness of the substrate is 0.10-0.12 mm;
s2, transferring the ink layer to the reverse side of the substrate by a precision transfer machine;
s3, transferring a gold oil layer on the ink layer through a precision transfer machine, and carrying out embossing treatment on the surface of the gold oil layer to form a corrugated shape;
s4, coating a corona eliminating agent on the front surface of the substrate on a precise screen combined compound machine to form a white corona eliminating agent layer;
s5 coating ethylene-tetrafluoroethylene copolymer or fluorinated ethylene propylene copolymer or ethylene chlorotrifluoroethylene copolymer or polyvinylidene fluoride on the white corona eliminating agent layer on a precise screen combined compound machine to form an aging-resistant layer, wherein the aging-resistant layer is 30-40 μm thick;
s6 forming a barrier layer on the aging-resistant layer by sputtering TiO2, Al2O3 or SiO2, wherein the thickness of the barrier layer is 10-15 mu m;
s7, coating acrylic resin or unsaturated polyester or polyurethane or epoxy resin on the barrier layer on a precise screen combined compound machine to form a protective layer, wherein the thickness of the protective layer is 1-3 mu m, and the protective layer fills the surface fluctuation and gaps of the barrier layer;
s8, sequentially coating white glue and glass beads on the protective layer through a coating bead-planting combination machine, heating, curing and shaping to sequentially form a white glue layer and a glass bead layer, wherein the particle size of the glass bead layer beads is less than 0.06 mm.
According to the technical scheme, the anti-aging layer can be a fluoride film, the thickness of the fluoride film is 30-40 mu m, the fluoride film is mainly made of materials such as ethylene-tetrafluoroethylene copolymer, fluorinated ethylene propylene copolymer, ethylene chlorotrifluoroethylene copolymer or polyvinylidene fluoride, the anti-aging layer is added, the anti-aging performance of the substrate material can be improved, and the service life of the curtain is prolonged.
The barrier layer is formed by evaporation, sputtering, chemical vapor deposition, etc., and is made of TiO2、Al2O3、SiO2In one of the above, the barrier layer blocks water vapor and the like, and has a function of blocking the external environment.
The protective layer is 1-3 mu m thick and mainly used for filling concave-convex fluctuation and gaps on the surface of the barrier layer so that the surface of the barrier layer is flat and smooth, and the protective layer can be made of acrylic resin, unsaturated polyester, polyurethane, epoxy resin and the like.
The glass microspheres with the glass microsphere layer have high gain, low requirement on environment, moisture resistance, difficulty in generating phenomena of bead falling, yellowing, curved edges and the like, convenient transportation and installation and low cost.
The present embodiments are to be considered as illustrative and not restrictive, and the scope of the patent is to be determined by the appended claims.
Claims (8)
1. A preparation method of a high-brightness curtain is characterized by sequentially comprising the following steps:
s1, using a PET sheet as a substrate to perform static elimination treatment;
s2, transferring the ink layer to the reverse side of the substrate through a precision transfer printing machine;
s3, transferring a gold oil layer on the ink layer through a precision transfer printing machine;
s4, coating a corona eliminating agent on the front surface of the substrate on a precise screen combined compound machine to form a white corona eliminating agent layer;
s5, coating ethylene-tetrafluoroethylene copolymer or fluorinated ethylene propylene copolymer or ethylene chlorotrifluoroethylene copolymer or polyvinylidene fluoride on the white corona eliminating agent layer on a precise screen combined compound machine to form an aging resistant layer;
s6 by TiO2Or Al2O3Or SiO2Sputtering to form a barrier layer on the aging resistant layer;
s7, coating acrylic resin or unsaturated polyester or polyurethane or epoxy resin on the barrier layer on a precision screen combined compound machine to form a protective layer;
s8, sequentially coating white glue and glass beads on the protective layer through a coating bead planting combination machine, heating, curing and shaping to sequentially form a white glue layer and a glass bead layer.
2. The method of claim 1, wherein the substrate has a thickness of 0.10 mm to 0.12 mm.
3. The method of claim 1, wherein the aging-resistant layer has a thickness of 30 to 40 μm.
4. The method of claim 1, wherein the barrier layer has a thickness of 10-15 μm.
5. The method of claim 1, wherein the protective layer has a thickness of 1 to 3 μm.
6. The method of claim 1, wherein the surface of the gold oil layer is embossed to form a corrugated shape.
7. The method of claim 1, wherein the passivation layer fills the surface undulations and voids of the barrier layer.
8. The method of claim 1, wherein the glass bead layer beads have a particle size of less than 0.06 mm.