CN1110299A - Organic silicone structure sealant - Google Patents
Organic silicone structure sealant Download PDFInfo
- Publication number
- CN1110299A CN1110299A CN 94112678 CN94112678A CN1110299A CN 1110299 A CN1110299 A CN 1110299A CN 94112678 CN94112678 CN 94112678 CN 94112678 A CN94112678 A CN 94112678A CN 1110299 A CN1110299 A CN 1110299A
- Authority
- CN
- China
- Prior art keywords
- organic
- silicone
- silicate
- aminosilane
- kilograms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a sealant, applicable to structural binding sealing of building crypotmorphic and semicryptomorphic glass curtain wall and marble wall surface. It consists of organic hydroxysilicone, organic methylsilicone, methyl oximidosilane, tin dibutyldilaurate, gas-phase silicon dioxide, silicate and aminosilane, and the above-mentioned materials are reacted at normal temp. to obtain the invented product. It has the advantages of good ageing-resistance, high tensile strength, low-cost and easy to produce, etc..
Description
The present invention relates to a kind of tackiness agent, specifically be used for carrying out structural bonding structure sealant between aluminium alloy extrusions and glass, glass and glass, aluminium alloy extrusions and aluminium alloy extrusions, marble and the concrete etc.
At present, the structure sealant that sell the domestic market is imported product, and domestic still do not have a manufacturer production.The import product have 759 of the SSG4000 of U.S. GE company and DOW CORNING company.The shortcoming of these two kinds of structure glue is owing to add carbon black, and ageing resistance is descended, and tensile strength reduces, and this product cost is than higher in addition.
The object of the present invention is to provide a kind of have good ageing resistance and the structure sealant high-tensile, that cost is low.
Organic silicone structure sealant of the present invention is formed (weight part):
Organic hydroxyl silicone 4-8
Organic methyl silicone 1-4
Methyloxime base silane 0.1-0.6
Dibutyl tin dilaurate 0.005-0.01
Aerosil 0.4-1.2
Silicate 1-5
Aminosilane 0.01-0.09
Preparation method of the present invention stirs above-mentioned raw materials vacuum mixing at normal temperatures 30 minutes, promptly gets the present invention.According to the change of component ratio, can obtain different elastic seal gums.Structure sealant of the present invention is the body of paste that do not trickle.As required, can add different colours, can be black, and perhaps white is perhaps brown.Described silicate is meant Calucium Silicate powder or Magnesium Silicate q-agent.
The present invention is applicable between aluminium alloy extrusions and glass, the aluminium alloy extrusions, between the glass, carry out structural adhering and sealing between marble and the concrete etc., is used for making latent type of Highrise buildings and half latent type glass curtain wall and marble wall.
Advantage of the present invention is:
1, owing to add silicate, improves the ageing resistance of seal gum, can improve the work-ing life of stealth, half stealthy glass curtain wall;
2, owing to all replace carbon black and partly replace aerosil, reduced product cost, can reduce construction costs with silicate.
3, manufacturing process is simple, uses general-purpose equipment, process stabilizing.
Below by embodiment, can do further understanding to the present invention.
Embodiment 1
With 45 kilograms of organic hydroxyl silicone
15 kilograms of organic methyl silicones
3 kilograms of methyloxime base silanes
6 kilograms of aerosils
30 kilograms of Calucium Silicate powder
0.04 kilogram of dibutyl tin dilaurate
0.4 kilogram of aminosilane
Vacuum mixing is at normal temperatures stirred and was promptly got 119.44 kilograms of structure sealants of the present invention in 30 minutes.
Embodiment 2
60 kilograms of organic hydroxyl silicone
30 kilograms of organic methyl silicones
4 kilograms of methyloxime base silanes
9 kilograms of aerosils
35 kilograms of Magnesium Silicate q-agents
0.08 kilogram of dibutyl tin dilaurate
0.7 kilogram of aminosilane
Processing condition are identical with embodiment 1.Make 138.78 kilograms of structure sealants of the present invention.
Embodiment 3
70 kilograms of organic hydroxyl silicone
10 kilograms of organic methyl silicones
3.5 kilograms of methyloxime base silanes
6.5 kilograms of aerosils
40 kilograms of Calucium Silicate powder
0.06 kilogram of dibutyl tin dilaurate
0.6 kilogram of aminosilane
Processing condition are identical with embodiment 1.Make 130.66 kilograms of structure sealants of the present invention.
Embodiment 1,2,3 resulting structures seal gums are carried out performance test and as follows with the SSG4000 and 795 comparative results of GE company by the ASTM standard:
Extreme tensile strength resistance to deterioration
Embodiment 1 314 psi are excellent
Embodiment 2 342 psi are excellent
Embodiment 3 321 psi are excellent
SSG4000 300 psi are good
795 171 psi are good
Claims (2)
1, a kind of to building the organic silicone structure sealant that stealth, half stealthy glass curtain wall and marble wall carry out structural adhering and sealing, it is characterized in that:
A. organic silicone seal gum complete processing is that organic hydroxyl silicone, organic methyl silicone, methyloxime base silane, aerosil, dibutyl tin dilaurate, silicate, aminosilane are mixed stirring at normal temperatures;
B. the contained composition scope of organic silicone seal gum (weight part):
Organic hydroxyl silicone 4-8
Organic methyl silicone 1-4
Methyloxime base silane 0.1-0.6
Aerosil 0.4-1.2
Dibutyl tin dilaurate 0.005-0.01
Silicate 1-5
Aminosilane 0.01-0.07.
2, organic silicone structure sealant according to claim 1 is characterized in that described silicate is Calucium Silicate powder or Magnesium Silicate q-agent.