CN111020824A - Manufacturing process of light, thick and warm polar fleece fabric - Google Patents
Manufacturing process of light, thick and warm polar fleece fabric Download PDFInfo
- Publication number
- CN111020824A CN111020824A CN201911189119.7A CN201911189119A CN111020824A CN 111020824 A CN111020824 A CN 111020824A CN 201911189119 A CN201911189119 A CN 201911189119A CN 111020824 A CN111020824 A CN 111020824A
- Authority
- CN
- China
- Prior art keywords
- cloth
- adjusted
- treatment
- fabric
- namely
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing process of a light, thick and warm-keeping polar fleece fabric, which adopts 36S all-cotton combed yarn as the fabric, adopts 75D/36F +300D/288F all-polyester yarn as a bottom material, and makes the yarn into grey cloth in a 30 x 24G1.8mm positive packing machine; pre-treating the grey cloth by shaking, putting the grey cloth into a shaking drum, heating to 80 ℃, shaking for 20 minutes until the front side of the grey cloth presents uniform granules, and then sequentially dyeing the grey cloth, softening the grey cloth, rolling and slitting the grey cloth, performing surface treatment and tentering and setting to obtain a finished product; according to the manufacturing process of the light, thick and warm-keeping polar fleece fabric, 36S all-cotton combed yarn is used as the fabric, 75D/36F +300D/288F full polyester yarn is used as the bottom material, and various processes are adopted for treatment, so that the economic cost is low, the manufactured fabric is light and thick in weight, and good in warm keeping performance, and is suitable for manufacturing various autumn and winter clothes, such as coats, jackets and the like.
Description
Technical Field
The invention relates to the technical field of textile fabric processing, in particular to a manufacturing process of a light, thick and warm polar fleece fabric.
Background
The napped fabric is a cotton fabric with a smooth and fluffy surface after napping, more fluff is generated through a pinhole napping process on the surface of the fabric, and the fabric is strong in stereoscopic impression, high in glossiness and soft and thick to touch. The plain velvet is a flannelette with relatively low hair height, and the flannelette also has cleaning velvet for cleaning, the hair height is high, and the flannelette has high and low grades in weaving and knitting. In terms of production places, the number of manufacturers in the north is small, the production scale of Yishui Hentai and Tianjin Zhongchang in the Shandong is large, the number of manufacturers in Hangzhou and Jiaxing areas in the south is large, a certain scale is formed, and the whole industrial chain is complete.
The existing popular warm-keeping velvet products are used as leisure and household clothes, and have windproof and warm-keeping effects, while the traditional winter clothes fabric is poor in warm-keeping property, long in process duration during dyeing and finishing, low in production efficiency, not thick enough in fabric, and not light enough in quality.
Disclosure of Invention
The invention aims to provide a manufacturing process of a light, thick and warm polar fleece fabric, which aims to solve the problems in the background technology.
The purpose of the invention is realized by the following technical scheme: a manufacturing process of a light, thick and warm polar fleece fabric comprises the following process steps:
step 1: weaving a grey fabric, namely adopting 36S all-cotton combed yarn as a fabric, adopting 75D/36F +300D/288F all-polyester yarn as a bottom material, and making the grey fabric into the grey fabric in a 30 x 24G1.8mm positive wrapping machine, wherein the gram weight of the grey fabric is 130 g;
step 2: carrying out granule shaking treatment, namely carrying out granule shaking pretreatment on the grey cloth treated in the step 1, putting the grey cloth into a granule shaking cylinder, heating to 80 ℃, and carrying out granule shaking for 20 minutes until the front side of the grey cloth presents uniform granules;
and step 3: dyeing grey cloth, namely placing the grey cloth in the step 2 into a dye vat with the dye temperature of 130 ℃ for dyeing, synchronously stirring the dye vat by using a stirrer, preserving heat for 30-45 minutes, naturally cooling the dye in the dye vat to room temperature after the heat preservation is finished, continuously stirring by using the stirrer during the period, and taking out the dyed cloth after the dyeing is finished;
and 4, step 4: performing upper softening treatment, namely putting the dyed cloth in the step 3 into upper softening liquid, wherein the upper softening liquid comprises 2% of silicon softening agent, 1% of smoothing agent and 1% of antistatic agent, continuously stirring by using a stirrer, and heating to 40-50 ℃, wherein the stirring time is 20-30 minutes; the stirring speed of the stirrer is 30-60 revolutions per minute;
and 5: water rolling and slitting, namely preliminarily dewatering the dyed cloth subjected to the softening treatment in the step 4 by using a water mangle, and then performing scutching treatment on the cylindrical polished blank by using a slitting machine;
step 6: surface treatment, namely subjecting the surface of the cloth in the step 5 to napping treatment, carding treatment and shearing treatment in sequence, and measuring the height of fluff to be between 3.5 and 4.5 mm;
and 7: and (4) tentering and setting, namely stretching and setting the cloth processed in the step (6) by using a tentering and setting machine, wherein the tentering and setting temperature is 110 ℃, and the speed is 20m/min, so that a finished product can be obtained.
In the invention, in the napping treatment in the step 6, the surface wool yarn is napped into a pile shape by using a napping machine so as to form a soft pile face.
In the invention, the carding treatment in the step 6 is to place the treated cloth in the step 5 into an automatic carding machine for carding treatment, wherein the revolving drum of the carding machine is adjusted to 75-80 revolutions per minute, the cloth feeding speed is adjusted to 25 meters per minute, the cloth feeding tension is adjusted to 1.03N, the left and right carding brushes are adjusted to 25 meters per minute, the cloth discharging tension is adjusted to 1.035N, the cloth falling tension is adjusted to 1.4N, the carding brushes are obliquely arranged, and the angle between the carding brushes and the cloth feeding surface is 45 degrees.
In the invention, the shearing treatment in the step 6 is to shear the carded cloth in the step 5 by a shearing machine, wherein the shearing direction of the shearing machine is the same as the hair-catching direction, the cloth feeding speed is adjusted to 17.8 m/min, the cloth feeding tension is adjusted to 1.7N, the cloth discharging speed is adjusted to 18.3 m/min, the cloth discharging tension is adjusted to 1.5N, the cloth dropping tension is adjusted to 1.38N, the cloth dropping speed is adjusted to 24.6 m/min, the pressure of a shearing circular knife is adjusted to 8kg, the rotating speed of the shearing circular knife is adjusted to 1100 r/min, the included angle formed by the shearing circular knife and a cloth feeding groove is adjusted to 60-70 degrees, and the distance between the tip of the shearing circular knife and a cloth cover is set to 0.5cm-0.7 cm.
In the invention, 2.5-4.5% of a raising agent is added in the shaping roller of the 7-middle shaping machine, and the raising agent is prepared by mixing 78-88% of organic silicon and 12-22% of silicone oil.
Compared with the prior art, the manufacturing process of the light, thick and warm-keeping polar fleece fabric has the advantages that 36S all-cotton combed yarn is adopted as the fabric and 75D/36F +300D/288F all-polyester yarn is adopted as the bottom material, and various processes are adopted for treatment, so that the economic cost is low, the manufactured fabric is light and thick in weight and good in warm-keeping performance, and is suitable for manufacturing various autumn and winter clothes such as overcoats, jackets and the like.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, rather than all embodiments, and all other embodiments obtained by those skilled in the art without any creative work based on the embodiments of the present invention belong to the protection scope of the present invention.
The invention discloses a manufacturing process of a light, thick and warm polar fleece fabric, which comprises the following process steps:
step 1: weaving a grey fabric, namely adopting 36S all-cotton combed yarn as a fabric, adopting 75D/36F +300D/288F all-polyester yarn as a bottom material, and making the grey fabric into the grey fabric in a 30 x 24G1.8mm positive wrapping machine, wherein the gram weight of the grey fabric is 130 g;
step 2: carrying out granule shaking treatment, namely carrying out granule shaking pretreatment on the grey cloth treated in the step 1, putting the grey cloth into a granule shaking cylinder, heating to 80 ℃, and carrying out granule shaking for 20 minutes until the front side of the grey cloth presents uniform granules;
and step 3: dyeing grey cloth, namely placing the grey cloth in the step 2 into a dye vat with the dye temperature of 130 ℃ for dyeing, synchronously stirring the dye vat by using a stirrer, preserving heat for 30-45 minutes, naturally cooling the dye in the dye vat to room temperature after the heat preservation is finished, continuously stirring by using the stirrer during the period, and taking out the dyed cloth after the dyeing is finished;
and 4, step 4: performing upper softening treatment, namely putting the dyed cloth in the step 3 into upper softening liquid, wherein the upper softening liquid comprises 2% of silicon softening agent, 1% of smoothing agent and 1% of antistatic agent, continuously stirring by using a stirrer, and heating to 40-50 ℃, wherein the stirring time is 20-30 minutes; the stirring speed of the stirrer is 30-60 revolutions per minute;
and 5: water rolling and slitting, namely preliminarily dewatering the dyed cloth subjected to the softening treatment in the step 4 by using a water mangle, and then performing scutching treatment on the cylindrical polished blank by using a slitting machine;
step 6: surface treatment, namely subjecting the surface of the cloth in the step 5 to napping treatment, carding treatment and shearing treatment in sequence, and measuring the height of fluff to be between 3.5 and 4.5 mm;
and 7: and (4) tentering and setting, namely stretching and setting the cloth processed in the step (6) by using a tentering and setting machine, wherein the tentering and setting temperature is 110 ℃, and the speed is 20m/min, so that a finished product can be obtained.
In the invention, in the napping treatment in the step 6, the napping machine is utilized to draw the wool yarns on the surface into a plush shape so as to form a soft suede; the carding treatment in the step 6 is to place the treated cloth in the step 5 into an automatic carding machine for carding treatment, wherein the revolving drum of the carding machine is adjusted to 75-80 revolutions per minute, the cloth feeding speed is adjusted to 25 meters per minute, the cloth feeding tension is adjusted to 1.03N, the left and right carding brushes are adjusted to 25 meters per minute, the cloth discharging tension is adjusted to 1.035N, the cloth falling tension is adjusted to 1.4N, the carding brushes are obliquely arranged, and the carding brushes and the cloth feeding surface form an included angle of 45 degrees; the step 6 is a shearing treatment, namely, the cloth combed in the step 5 is sheared by a shearing machine, wherein the shearing direction of the shearing machine is the same as the hair grabbing direction, the cloth feeding speed is adjusted to 17.8 m/min, the cloth feeding tension is adjusted to 1.7N, the cloth discharging speed is adjusted to 18.3 m/min, the cloth discharging tension is adjusted to 1.5N, the cloth dropping tension is adjusted to 1.38N, the cloth dropping speed is adjusted to 24.6 m/min, the pressure of a shearing circular knife is adjusted to 8kg, the rotating speed of the shearing circular knife is adjusted to 1100 r/min, the included angle formed by the shearing circular knife and a cloth feeding groove is adjusted to 60-70 degrees, and the distance between the tip of the shearing circular knife and a cloth cover is set to 0.5cm-0.7 cm; the raising agent is prepared by mixing 78-88% of organic silicon and 12-22% of silicone oil.
According to the manufacturing process of the light, thick and warm-keeping polar fleece fabric, 36S all-cotton combed yarn is used as the fabric, 75D/36F +300D/288F polyester yarn is used as the bottom material, and various processes are adopted for treatment, so that the economic cost is low, the manufactured fabric is light and thick in weight, good in warm-keeping performance, and suitable for manufacturing various autumn and winter clothes such as overcoat, jacket and the like.
It will be evident to those skilled in the art that the invention is not limited to the details of the foregoing illustrative embodiments, and that the present invention may be embodied in other specific forms without departing from the spirit or essential attributes thereof. The present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description, and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.
Furthermore, it should be understood that although the present description refers to embodiments, not every embodiment may contain only a single embodiment, and such description is for clarity only, and those skilled in the art should integrate the description, and the embodiments may be combined as appropriate to form other embodiments understood by those skilled in the art.
Claims (5)
1. A manufacturing process of a light, thick and warm polar fleece fabric is characterized in that: the method comprises the following process steps:
step 1: weaving a grey fabric, namely adopting 36S all-cotton combed yarn as a fabric, adopting 75D/36F +300D/288F all-polyester yarn as a bottom material, and making the grey fabric into the grey fabric in a 30 x 24G1.8mm positive wrapping machine, wherein the gram weight of the grey fabric is 130 g;
step 2: carrying out granule shaking treatment, namely carrying out granule shaking pretreatment on the grey cloth treated in the step 1, putting the grey cloth into a granule shaking cylinder, heating to 80 ℃, and carrying out granule shaking for 20 minutes until the front side of the grey cloth presents uniform granules;
and step 3: dyeing grey cloth, namely placing the grey cloth in the step 2 into a dye vat with the dye temperature of 130 ℃ for dyeing, synchronously stirring the dye vat by using a stirrer, preserving heat for 30-45 minutes, naturally cooling the dye in the dye vat to room temperature after the heat preservation is finished, continuously stirring by using the stirrer during the period, and taking out the dyed cloth after the dyeing is finished;
and 4, step 4: performing upper softening treatment, namely putting the dyed cloth in the step 3 into upper softening liquid, wherein the upper softening liquid comprises 2% of silicon softening agent, 1% of smoothing agent and 1% of antistatic agent, continuously stirring by using a stirrer, and heating to 40-50 ℃, wherein the stirring time is 20-30 minutes; the stirring speed of the stirrer is 30-60 revolutions per minute;
and 5: water rolling and slitting, namely preliminarily dewatering the dyed cloth subjected to the softening treatment in the step 4 by using a water mangle, and then performing scutching treatment on the cylindrical polished blank by using a slitting machine;
step 6: surface treatment, namely subjecting the surface of the cloth in the step 5 to napping treatment, carding treatment and shearing treatment in sequence, and measuring the height of fluff to be between 3.5 and 4.5 mm;
and 7: and (4) tentering and setting, namely stretching and setting the cloth processed in the step (6) by using a tentering and setting machine, wherein the tentering and setting temperature is 110 ℃, and the speed is 20m/min, so that a finished product can be obtained.
2. The manufacturing process of the light, thick and warm polar fleece fabric according to claim 1, which is characterized in that: and (6) napping treatment, namely napping the wool yarns on the surface into a plush shape by using a napping machine to form a soft suede.
3. The manufacturing process of the light, thick and warm polar fleece fabric according to claim 1, which is characterized in that: and 6, carding in the step 6, namely putting the treated cloth in the step 5 into an automatic carding machine for carding, wherein the revolving drum of the carding machine is adjusted to 75-80 revolutions per minute, the cloth feeding speed is adjusted to 25 m/min, the cloth feeding tension is adjusted to 1.03N, the left and right carding brushes are adjusted to 25 m/min, the cloth discharging tension is adjusted to 1.035N, the cloth falling tension is adjusted to 1.4N, the carding brushes are obliquely arranged, and the carding brushes and the cloth feeding surface form an included angle of 45 degrees.
4. The manufacturing process of the light, thick and warm polar fleece fabric according to claim 1, which is characterized in that: and 6, performing shearing treatment in the step 6, namely shearing the carded cloth in the step 5 by using a shearing machine, wherein the shearing direction of the shearing machine is the same as the hair grabbing direction, the cloth feeding speed is adjusted to 17.8 m/min, the cloth feeding tension is adjusted to 1.7N, the cloth discharging speed is adjusted to 18.3 m/min, the cloth discharging tension is adjusted to 1.5N, the cloth dropping tension is adjusted to 1.38N, the cloth dropping speed is adjusted to 24.6 m/min, the pressure of a shearing circular knife is adjusted to 8kg, the rotating speed of the shearing circular knife is adjusted to 1100 r/min, the included angle formed by the shearing circular knife and a cloth feeding groove is adjusted to 60-70 degrees, and the distance between the tip of the shearing circular knife and a cloth cover is set to 0.5-0.7 cm.
5. The manufacturing process of the light, thick and warm polar fleece fabric according to claim 1, which is characterized in that: and 2.5-4.5% of a raising agent is added in the shaping roller of the 7-middle shaping machine, and the raising agent is prepared by mixing 78-88% of organic silicon and 12-22% of silicone oil.