CN111016303A - 芳香蕾丝花边面料 - Google Patents
芳香蕾丝花边面料 Download PDFInfo
- Publication number
- CN111016303A CN111016303A CN201911162455.2A CN201911162455A CN111016303A CN 111016303 A CN111016303 A CN 111016303A CN 201911162455 A CN201911162455 A CN 201911162455A CN 111016303 A CN111016303 A CN 111016303A
- Authority
- CN
- China
- Prior art keywords
- aromatic
- lace
- parts
- lace fabric
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种芳香蕾丝花边面料，花边包括底层、纤维层和蕾丝花边，纤维层设于底层之上，并通过粘胶剂粘结，蕾丝花边设于所述纤维层的两侧；纤维层的原料为聚酯纤维：按重量份计，纤维层包括以下组分：聚对苯二甲酸乙二醇酯30～40份；芳香母粒4～8份。本发明的芳香蕾丝花边面料，具有芳香耐久性能；纤维层的原料为聚酯纤维，聚酯纤维通过聚对苯二甲酸乙二醇酯中加入芳香母粒，提高蕾丝花白面料的镇静、杀菌、保健等作用。
Description
技术领域
本发明涉及一种复合花边制备技术领域，特别是涉及一种芳香蕾丝花边面料。
背景技术
现代工业的迅猛发展极大地改变了人类的生活方式和生存环境。当我们享受令人眼花缭乱的工业产品时，也不得不承受日益污染的大气和环境对人类生命健康的威胁。因此回归自然，追求健康已悄然成为都市新时尚。
科学研究证明，许多芳香剂具有镇静、杀菌、保健等作用，而且不同的芳香具有舒缓紧张情绪、解除压力或催人兴奋等作用。日常生活中，很多人都体会到芳香对人的情绪能起到很大的影响。芳香对人的作用已广为人知，例如：
薄荷具有令人头脑灵活，思维清晰的效果。玫瑰味是最受大众欢迎的优雅芳香，可以让人心情开朗，可以平抚情绪，提振心情，舒缓神经紧张和压力。薰衣草具有舒缓镇静，平衡身心的作用，其清爽宜人的花香可安定情绪，赶走焦虑。茉莉优雅迷人的花香能赶走忧郁，增强自信心，调理干燥，安抚神经。
因此市场上出现了具有散发芳香功能的床上用品，但是目前还没有出现一款芳香蕾丝花边面料。
发明内容
针对上述不足之处，本发明的目的在于开发一种芳香蕾丝花边面料，具有面料芳香持久优势。
本发明的技术方案概述如下：
一种芳香蕾丝花边面料，所述花边包括底层、纤维层和蕾丝花边，其中，所述纤维层设于所述底层之上，并通过粘胶剂粘结，所述蕾丝花边设于所述纤维层的两侧；所述纤维层的原料为聚酯纤维；
按重量份计，所述聚酯纤维包括以下组分：
聚对苯二甲酸乙二醇酯 30～40份；
芳香母粒 4～8份。
优选的是，所述的芳香蕾丝花边面料，其中，所述芳香母粒包括：
聚对苯二甲酸乙二醇酯 20～30份；
芳香剂 6～12份；
分散剂 0.5～1份。
优选的是，所述的芳香蕾丝花边面料，其中，所述芳香剂包括15～20wt％蔗糖棕榈酸酯、40～45wt％乙酸芳樟酯、20～40wt％萜-4-醇、15～20wt％亚油酸。
优选的是，所述的芳香蕾丝花边面料，其中，所述分散剂包括30～40wt％油酸酰、20～40wt％棕榈油酸钠、20～30wt％聚山梨酯。
优选的是，所述的芳香蕾丝花边面料，其中，所述芳香母粒还包括0.5～1份的乙酸-3-乙烯酯。
优选的是，所述的芳香蕾丝花边面料，其中，所述芳香母粒还包括2～4份的棕榈酸。
优选的是，所述的芳香蕾丝花边面料，其中，所述芳香母粒还包括0.5～1份的京尼平酸。
优选的是，所述的芳香蕾丝花边面料，其中，所述芳香母粒还包括1～4份的香叶醇和0.2～1份的季戊四醇脂肪酸酯。
优选的是，所述的芳香蕾丝花边面料，其中，所述聚酯纤维的制备方法包括以下步骤：
(1)取聚对苯二甲酸乙二醇酯、芳香剂、分散剂、乙酸-3-乙烯酯、棕榈酸、京尼平酸、香叶醇、季戊四醇脂肪酸酯共混，用螺杆挤压机挤出，切粒，制得芳香母粒，备用；
(2)按权利要求1所述的重量份数取芳香母粒和聚对苯二甲酸乙二醇酯在螺杆挤压机中加热熔融，压缩成熔体，并由其旋转螺杆挤出，然后送入分配管、静态混合器和计量泵，通过喷丝头喷丝、冷却成形、获得聚酯纤维。
优选的是，所述的芳香蕾丝花边面料，其中，所述底层的厚度为300～500微米；所述纤维层的厚度为500～800微米。
本发明的有益效果是：
本发明的芳香蕾丝花边面料，具有芳香耐久性能；纤维层的原料为聚酯纤维，聚酯纤维通过聚对苯二甲酸乙二醇酯中加入芳香母粒，通过加入芳香母粒，提高蕾丝花白面料的镇静、杀菌、保健等作用。
具体实施方式
下面结合实施例对本发明做进一步的详细说明，以令本领域技术人员参照说明书文字能够据以实施。
本案提出一种芳香蕾丝花边面料，花边包括底层、纤维层和蕾丝花边，其中，纤维层设于所述底层之上，并通过粘胶剂粘结，蕾丝花边设于纤维层的两侧；所述纤维层的原料为聚酯纤维；
按重量份计，所述聚酯纤维包括以下组分：
聚对苯二甲酸乙二醇酯 30～40份；
芳香母粒 4～8份。
作为本案又一实施例，其中，芳香母粒包括：
聚对苯二甲酸乙二醇酯 20～30份；
芳香剂 6～12份；
分散剂 0.5～1份。
作为本案又一实施例，其中，芳香剂包括15～20wt％蔗糖棕榈酸酯、40～45wt％乙酸芳樟酯、20～40wt％萜-4-醇、15～20wt％亚油酸。芳香剂具有镇静、杀菌、保健等作用，而且不同的芳香具有舒缓紧张情绪、解除压力或催人兴奋等作用，本案优选的芳香剂为蔗糖棕榈酸酯、乙酸芳樟酯、萜-4-醇、亚油酸。
作为本案又一实施例，其中，分散剂包括30～40wt％油酸酰、20～40wt％棕榈油酸钠、20～30wt％聚山梨酯。分散剂可均一分散那些难于溶解于液体的无机，有机固体及液体颗粒，同时也能防止颗粒的沉降和凝聚，本案优选的分散剂为油酸酰、棕榈油酸钠、聚山梨酯。
作为本案又一实施例，其中，芳香母粒还包括0.5～1份的乙酸-3-乙烯酯。乙酸-3-乙烯酯气味芬芳，自然的芳香经由嗅觉神经进入脑部后，能刺激大脑前叶分泌出内啡汰及脑啡汰两种荷尔蒙，使精神呈现最舒适的状态；能消炎杀菌、可防传染病、防发炎。
作为本案又一实施例，其中，芳香母粒还包括2～4份的棕榈酸。棕榈酸作为乳化剂，改善芳香母粒各组分的混合性能，并提高芳香剂的持久性能。
作为本案又一实施例，其中，芳香母粒还包括0.5～1份的京尼平酸。京尼平酸作为芳香剂，进一步改善花边面料的芳香持久性能。
作为本案又一实施例，其中，芳香母粒还包括1～4份的香叶醇和0.2～1份的季戊四醇脂肪酸酯。季戊四醇脂肪酸酯作为柔软剂，提高花边面料的柔软性能，使得花边面料具有柔软、滑爽、舒适的手感，并进一步提高持久性能。
作为本案又一实施例，其中，聚酯纤维的制备方法包括以下步骤：
(1)取聚对苯二甲酸乙二醇酯、芳香剂、分散剂、乙酸-3-乙烯酯、棕榈酸、京尼平酸、香叶醇、季戊四醇脂肪酸酯共混，用螺杆挤压机挤出，切粒，制得芳香母粒，备用；
(2)按权利要求1所述的重量份数取芳香母粒和聚对苯二甲酸乙二醇酯在螺杆挤压机中加热熔融，压缩成熔体，并由其旋转螺杆挤出，然后送入分配管、静态混合器和计量泵，通过喷丝头喷丝、冷却成形、获得聚酯纤维。
作为本案又一实施例，其中，底层的厚度为300～500微米；所述纤维层的厚度为500～800微米。
下面列出具体的实施例和对比例：
实施例1：
一种芳香蕾丝花边面料，花边包括底层、纤维层和蕾丝花边，纤维层设于底层之上，并通过粘胶剂粘结，蕾丝花边设于纤维层的两侧；底层的厚度为300微米；纤维层的厚度均为500微米；纤维层的原料为聚酯纤维；
按重量份计，聚酯纤维包括以下组分：
聚对苯二甲酸乙二醇酯 30份；
芳香母粒 4份。
芳香母粒包括：
芳香剂包括20wt％蔗糖棕榈酸酯、40wt％乙酸芳樟酯、20wt％萜-4-醇、20wt％亚油酸；分散剂包括30wt％油酸酰、40wt％棕榈油酸钠、30wt％聚山梨酯；
聚酯纤维的制备方法包括以下步骤：
(1)取聚对苯二甲酸乙二醇酯、芳香剂、分散剂、乙酸-3-乙烯酯、棕榈酸、京尼平酸、香叶醇、季戊四醇脂肪酸酯共混，用螺杆挤压机挤出，切粒，制得芳香母粒，备用；
(2)取芳香母粒和聚对苯二甲酸乙二醇酯在螺杆挤压机中加热熔融，压缩成熔体，并由其旋转螺杆挤出，然后送入分配管、静态混合器和计量泵，通过喷丝头喷丝、冷却成形、获得聚酯纤维。
实施例2：
一种芳香蕾丝花边面料，花边包括底层、纤维层和蕾丝花边，纤维层设于所述底层之上，并通过粘胶剂粘结，蕾丝花边设于纤维层的两侧；底层的厚度为400微米；纤维层的厚度均为700微米；纤维层的原料为聚酯纤维；
按重量份计，所述聚酯纤维包括以下组分：
聚对苯二甲酸乙二醇酯 34份；
芳香母粒 6份。
芳香母粒包括：
芳香剂包括15wt％蔗糖棕榈酸酯、45wt％乙酸芳樟酯、20wt％萜-4-醇、20wt％亚油酸；分散剂包括36wt％油酸酰、34wt％棕榈油酸钠、30wt％聚山梨酯。
聚酯纤维的制备方法包括以下步骤：
(1)取聚对苯二甲酸乙二醇酯、芳香剂、分散剂、乙酸-3-乙烯酯、棕榈酸、京尼平酸、香叶醇、季戊四醇脂肪酸酯共混，用螺杆挤压机挤出，切粒，制得芳香母粒，备用；
(2)取芳香母粒和聚对苯二甲酸乙二醇酯在螺杆挤压机中加热熔融，压缩成熔体，并由其旋转螺杆挤出，然后送入分配管、静态混合器和计量泵，通过喷丝头喷丝、冷却成形、获得聚酯纤维。
实施例3：
一种芳香蕾丝花边面料，花边包括底层、纤维层和蕾丝花边，纤维层设于所述底层之上，并通过粘胶剂粘结，蕾丝花边设于所述纤维层的两侧；底层的厚度为500微米；纤维层的厚度均为800微米；纤维层的原料为聚酯纤维；
按重量份计，聚酯纤维包括以下组分：
聚对苯二甲酸乙二醇酯 40份；
芳香母粒 8份；
芳香母粒包括：
芳香剂包括20wt％蔗糖棕榈酸酯、45wt％乙酸芳樟酯、20wt％萜-4-醇、15wt％亚油酸；分散剂包括40wt％油酸酰、40wt％棕榈油酸钠、20wt％聚山梨酯。
聚酯纤维的制备方法包括以下步骤：
(1)取聚对苯二甲酸乙二醇酯、芳香剂、分散剂、乙酸-3-乙烯酯、棕榈酸、京尼平酸、香叶醇、季戊四醇脂肪酸酯共混，用螺杆挤压机挤出，切粒，制得芳香母粒，备用；
(2)取芳香母粒和聚对苯二甲酸乙二醇酯在螺杆挤压机中加热熔融，压缩成熔体，并由其旋转螺杆挤出，然后送入分配管、静态混合器和计量泵，通过喷丝头喷丝、冷却成形、获得聚酯纤维。
对比例1：
一种芳香蕾丝花边面料，花边包括底层、纤维层和蕾丝花边，纤维层设于底层之上，并通过粘胶剂粘结，蕾丝花边设于纤维层的两侧；底层的厚度为300微米；纤维层的厚度均为500微米；纤维层的原料为聚酯纤维；
按重量份计，聚酯纤维包括以下组分：
聚对苯二甲酸乙二醇酯 30份；
芳香母粒 4份。
芳香母粒包括：
芳香剂包括60wt％乙酸芳樟酯、20wt％萜-4-醇、20wt％亚油酸；分散剂包括30wt％油酸酰、40wt％棕榈油酸钠、30wt％聚山梨酯；
聚酯纤维的制备方法包括以下步骤：
(1)取聚对苯二甲酸乙二醇酯、芳香剂、分散剂、乙酸-3-乙烯酯、棕榈酸、京尼平酸、香叶醇、季戊四醇脂肪酸酯共混，用螺杆挤压机挤出，切粒，制得芳香母粒，备用；
(2)取芳香母粒和聚对苯二甲酸乙二醇酯在螺杆挤压机中加热熔融，压缩成熔体，并由其旋转螺杆挤出，然后送入分配管、静态混合器和计量泵，通过喷丝头喷丝、冷却成形、获得聚酯纤维。
对比例2：
一种芳香蕾丝花边面料，花边包括底层、纤维层和蕾丝花边，纤维层设于底层之上，并通过粘胶剂粘结，蕾丝花边设于纤维层的两侧；底层的厚度为300微米；纤维层的厚度均为500微米；纤维层的原料为聚酯纤维；
按重量份计，聚酯纤维包括以下组分：
聚对苯二甲酸乙二醇酯 30份；
芳香母粒 4份。
芳香母粒包括：
芳香剂包括20wt％蔗糖棕榈酸酯、40wt％乙酸芳樟酯、40wt％萜-4-醇、；分散剂包括30wt％油酸酰、40wt％棕榈油酸钠、30wt％聚山梨酯；
聚酯纤维的制备方法包括以下步骤：
(1)取聚对苯二甲酸乙二醇酯、芳香剂、分散剂、乙酸-3-乙烯酯、棕榈酸、京尼平酸、香叶醇、季戊四醇脂肪酸酯共混，用螺杆挤压机挤出，切粒，制得芳香母粒，备用；
(2)取芳香母粒和聚对苯二甲酸乙二醇酯在螺杆挤压机中加热熔融，压缩成熔体，并由其旋转螺杆挤出，然后送入分配管、静态混合器和计量泵，通过喷丝头喷丝、冷却成形、获得聚酯纤维。
对比例3：
一种芳香蕾丝花边面料，花边包括底层、纤维层和蕾丝花边，纤维层设于所述底层之上，并通过粘胶剂粘结，蕾丝花边设于纤维层的两侧；底层的厚度为400微米；纤维层的厚度均为700微米；
按重量份计，所述聚酯纤维包括以下组分：
聚对苯二甲酸乙二醇酯 34份；
芳香母粒 6份。
芳香母粒包括：
芳香剂包括15wt％蔗糖棕榈酸酯、45wt％乙酸芳樟酯、20wt％萜-4-醇、20wt％亚油酸；分散剂包括36wt％油酸酰、64wt％棕榈油酸钠。
聚酯纤维的制备方法包括以下步骤：
(1)取聚对苯二甲酸乙二醇酯、芳香剂、分散剂、乙酸-3-乙烯酯、棕榈酸、京尼平酸、香叶醇、季戊四醇脂肪酸酯共混，用螺杆挤压机挤出，切粒，制得芳香母粒，备用；
(2)取芳香母粒和聚对苯二甲酸乙二醇酯在螺杆挤压机中加热熔融，压缩成熔体，并由其旋转螺杆挤出，然后送入分配管、静态混合器和计量泵，通过喷丝头喷丝、冷却成形、获得聚酯纤维。
对比例4：
一种芳香蕾丝花边面料，花边包括底层、纤维层和蕾丝花边，纤维层设于所述底层之上，并通过粘胶剂粘结，蕾丝花边设于纤维层的两侧；底层的厚度为400微米；纤维层的厚度均为700微米；纤维层的原料为聚酯纤维；
按重量份计，所述聚酯纤维包括以下组分：
聚对苯二甲酸乙二醇酯 34份；
芳香母粒 6份。
芳香母粒包括：
芳香剂包括15wt％蔗糖棕榈酸酯、45wt％乙酸芳樟酯、20wt％萜-4-醇、20wt％亚油酸；分散剂包括36wt％油酸酰、34wt％棕榈油酸钠、30wt％聚山梨酯。
聚酯纤维的制备方法包括以下步骤：
(1)取聚对苯二甲酸乙二醇酯、芳香剂、分散剂、乙酸-3-乙烯酯、棕榈酸、香叶醇、季戊四醇脂肪酸酯共混，用螺杆挤压机挤出，切粒，制得芳香母粒，备用；
(2)取芳香母粒和聚对苯二甲酸乙二醇酯在螺杆挤压机中加热熔融，压缩成熔体，并由其旋转螺杆挤出，然后送入分配管、静态混合器和计量泵，通过喷丝头喷丝、冷却成形、获得聚酯纤维。
对比例5：
一种芳香蕾丝花边面料，花边包括底层、纤维层和蕾丝花边，纤维层设于所述底层之上，并通过粘胶剂粘结，蕾丝花边设于所述纤维层的两侧；底层的厚度为500微米；纤维层的厚度均为800微米；纤维层的原料为聚酯纤维；
按重量份计，聚酯纤维括以下组分：
聚对苯二甲酸乙二醇酯 40份；
芳香母粒 8份。
芳香母粒包括：
芳香剂包括20wt％蔗糖棕榈酸酯、45wt％乙酸芳樟酯、20wt％萜-4-醇、15wt％亚油酸；分散剂包括40wt％油酸酰、40wt％棕榈油酸钠、20wt％聚山梨酯。
聚酯纤维的制备方法包括以下步骤：
(1)取聚对苯二甲酸乙二醇酯、芳香剂、分散剂、乙酸-3-乙烯酯、棕榈酸、京尼平酸、季戊四醇脂肪酸酯共混，用螺杆挤压机挤出，切粒，制得芳香母粒，备用；
(2)取芳香母粒和聚对苯二甲酸乙二醇酯在螺杆挤压机中加热熔融，压缩成熔体，并由其旋转螺杆挤出，然后送入分配管、静态混合器和计量泵，通过喷丝头喷丝、冷却成形、获得聚酯纤维。
对比例6：
一种芳香蕾丝花边面料，花边包括底层、纤维层和蕾丝花边，纤维层设于所述底层之上，并通过粘胶剂粘结，蕾丝花边设于所述纤维层的两侧；底层的厚度为500微米；纤维层的厚度均为800微米；纤维层的原料为聚酯纤维；
按重量份计，聚酯纤维包括以下组分：
聚对苯二甲酸乙二醇酯 40份；
芳香母粒 8份。
芳香母粒包括：
芳香剂包括20wt％蔗糖棕榈酸酯、45wt％乙酸芳樟酯、20wt％萜-4-醇、15wt％亚油酸；分散剂包括40wt％油酸酰、40wt％棕榈油酸钠、20wt％聚山梨酯。
聚酯纤维的制备方法包括以下步骤：
(1)取聚对苯二甲酸乙二醇酯、芳香剂、分散剂、乙酸-3-乙烯酯、棕榈酸、京尼平酸、香叶醇共混，用螺杆挤压机挤出，切粒，制得芳香母粒，备用；
(2)取芳香母粒和聚对苯二甲酸乙二醇酯在螺杆挤压机中加热熔融，压缩成熔体，并由其旋转螺杆挤出，然后送入分配管、静态混合器和计量泵，通过喷丝头喷丝、冷却成形、获得聚酯纤维。
下面列出实施例1～3和对比例1～6的测试结果：
本发明的芳香蕾丝花边面料，实施例1～3与对比例1～6相比，实施例的芳香蕾丝花边面料具有芳香耐久性能。
尽管本发明的实施方案已公开如上，但其并不仅仅限于说明书和实施方式中所列运用，它完全可以被适用于各种适合本发明的领域，对于熟悉本领域的人员而言，可容易地实现另外的修改，因此在不背离权利要求及等同范围所限定的一般概念下，本发明并不限于特定的细节。
Claims (10)
1.一种芳香蕾丝花边面料，所述花边包括底层、纤维层和蕾丝花边，其特征在于，所述纤维层设于所述底层之上，并通过粘胶剂粘结，所述蕾丝花边设于所述纤维层的两侧；所述纤维层的原料为聚酯纤维；
按重量份计，所述聚酯纤维包括以下组分：
聚对苯二甲酸乙二醇酯30～40份；
芳香母粒4～8份。
2.根据权利要求1所述的芳香蕾丝花边面料，其特征在于，所述芳香母粒包括：
聚对苯二甲酸乙二醇酯20～30份；
芳香剂6～12份；
分散剂0.5～1份。
3.根据权利要求2所述的芳香蕾丝花边面料，其特征在于，所述芳香剂包括15～20wt％蔗糖棕榈酸酯、40～45wt％乙酸芳樟酯、20～40wt％萜-4-醇、15～20wt％亚油酸。
4.根据权利要求2所述的芳香蕾丝花边面料，其特征在于，所述分散剂包括30～40wt％油酸酰、20～40wt％棕榈油酸钠、20～30wt％聚山梨酯。
5.根据权利要求2所述的芳香蕾丝花边面料，其特征在于，所述芳香母粒还包括0.5～1份的乙酸-3-乙烯酯。
6.根据权利要求2所述的芳香蕾丝花边面料，其特征在于，所述芳香母粒还包括2～4份的棕榈酸。
7.根据权利要求2所述的芳香蕾丝花边面料，其特征在于，所述芳香母粒还包括0.5～1份的京尼平酸。
8.根据权利要求2所述的芳香蕾丝花边面料，其特征在于，所述芳香母粒还包括1～4份的香叶醇和0.2～1份的季戊四醇脂肪酸酯。
9.根据权利要求1～8任一项所述的芳香蕾丝花边面料，其特征在于，所述聚酯纤维的制备方法包括以下步骤：
(1)取聚对苯二甲酸乙二醇酯、芳香剂、分散剂、乙酸-3-乙烯酯、棕榈酸、京尼平酸、香叶醇、季戊四醇脂肪酸酯共混，用螺杆挤压机挤出，切粒，制得芳香母粒，备用；
(2)按权利要求1所述的重量份数取芳香母粒和聚对苯二甲酸乙二醇酯在螺杆挤压机中加热熔融，压缩成熔体，并由其旋转螺杆挤出，然后送入分配管、静态混合器和计量泵，通过喷丝头喷丝、冷却成形、获得聚酯纤维。
10.根据权利要求1所述的芳香蕾丝花边面料，其特征在于，所述底层的厚度为300～500微米；所述纤维层的厚度为500～800微米。