CN110936466A

CN110936466A - Forming device and method for additive manufacturing of inorganic cementing material product

Info

Publication number: CN110936466A
Application number: CN202010078217.XA
Authority: CN
Inventors: 陈勃生; 陈叶
Original assignee: Individual
Current assignee: Individual
Priority date: 2019-03-06
Filing date: 2020-02-03
Publication date: 2020-03-31
Also published as: CN111015895A; CN109732741A

Abstract

The invention discloses a device and a method for additive manufacturing of an inorganic cementing material product. The device is provided with at least two groups of nozzles or nozzle arrays, and is combined with a corresponding method to manufacture inorganic cementing material products and special ceramic products with complex structural shapes and high requirements on dimensional accuracy and surface quality. The permeation-resistant layer forms a separation belt for preventing the permeation of coagulant between the product and the powder material around the product, thereby ensuring better surface quality and higher dimensional precision of the product and preventing the powder material which does not participate in the forming of the product from being polluted.

Description

Forming device and method for additive manufacturing of inorganic cementing material product

Technical Field

The invention relates to the technical field of inorganic cementing material product forming, in particular to a forming device and a forming method for additive manufacturing of an inorganic cementing material product.

Background

The inorganic cementing material product is widely applied to various fields of social production and life. Traditional cements (hydraulic inorganic binders in powder form) and emerging geopolymer products are typical representatives of these.

The common forming method of inorganic gel material products mainly comprises the following steps: a premixed casting method, a direct injection method, a jet vacuum dehydration method, a premixed pressurization method, a premixed extrusion method, a layer-laying method and the like. Wherein: the premixed casting method is mainly suitable for manufacturing small special-shaped products with thicker wall thickness; the direct injection method is mainly suitable for manufacturing products with simple appearance and large area, such as flat plates, corrugated tiles and the like; the jet vacuum dehydration method is mainly suitable for manufacturing products requiring immediate demoulding; premixed pressure processes, mainly suitable for the manufacture of articles with complex surface patterns; the premixed extrusion method is mainly suitable for manufacturing the special-shaped slender product with a complex surface; the layer-laying method is mainly suitable for making products with simple shapes.

The methods described above have in common that: the method comprises the steps of preparing a corresponding model according to the shape of a formed product in advance, pouring mixed inorganic gel slurry into the model in different modes, and removing the model after the slurry is solidified to obtain the product. The method is suitable for manufacturing products with less complex shapes, low requirements on dimensional accuracy (millimeter level) and rough surfaces, such as: large-scale members (structures), well covers, culvert pipes, corrugated tiles, face bricks and the like.

The shape of the inorganic cementing material product cannot be designed to be very complicated under the constraint of the existing molding and demolding technology, thereby greatly limiting the application range of the inorganic cementing material product and being difficult to manufacture fine products of inorganic materials with smooth surfaces and good dimensional precision.

The existing related additive manufacturing technology can manufacture products with relatively complex shapes or structures and relatively high requirements on dimensional accuracy. However, in the case of powder bed printing of inorganic gelling materials, the boundary between the formed product and the inorganic powder material at the periphery thereof is blurred during the forming process due to the penetration of the coagulant into the loose and porous inorganic gelling material, thereby seriously affecting the surface quality and dimensional accuracy of the product.

Disclosure of Invention

The invention aims to solve the problems in the prior art and provide a forming device and a method for additive manufacturing of inorganic cementing material products, which can be used for manufacturing the inorganic cementing material products with complicated shapes or structures, smooth surfaces and high dimensional precision.

In order to solve the technical problem, the invention provides a forming device for additive manufacturing of inorganic gelled material products, which comprises an ultrasonic vibration powder spreading device, a spraying device, a forming cylinder and a lifting platform, wherein the ultrasonic vibration powder spreading device is used for uniformly spreading and compacting inorganic gelled materials on the upper surface of the lifting platform into a plane, the spraying device comprises at least two groups of spray heads or two groups of spray head arrays, one group of spray heads or spray head arrays are used for spraying a permeability inhibitor to the outer edge of the outline of a horizontal section solid area corresponding to the products on the material layer, the other group of spray heads or spray head arrays are used for spraying a coagulant to the horizontal section solid area corresponding to the products on the material layer, and the lifting platform is arranged in the forming cylinder and performs lifting motion along the inner wall surface of the forming cylinder for bearing the spread inorganic gelled materials.

Further, when the ultrasonic vibration powder paving device works, the ultrasonic vibration powder paving device vibrates at the ultrasonic frequency higher than 20 KHz.

Further, the injection frequency f range of the nozzle or nozzle array of the injection device is as follows:

1KHz＜ f ＜20KHz。

further, the viscosity of the liquid sprayed by the spray head or the spray head array for spraying the barrier agent is η in the range of 1CP < η < 150 CP.

The invention also provides a forming method of the forming device for the additive manufacturing of the inorganic cementing material product, which comprises the following steps:

a) spreading and compacting a powdery inorganic cementing material on a plane by an ultrasonic vibration powder spreading device to form a material layer with a specified thickness;

b) a group of spray heads or spray head arrays spray a permeability-blocking agent to the outer edge of the outline of the solid area of the horizontal section corresponding to the product on the material layer;

c) another group of spray heads or spray head arrays spray coagulant to the solid area of the horizontal section corresponding to the product on the material layer;

d) repeating the steps in sequence until the product is formed;

the inorganic gel material and coagulant react to form product layer on the corresponding material layer, the permeation inhibitor prevents the coagulant from reacting with the gel material of the product outside the solid area of the horizontal section and forms a permeation-resistant coating layer on the surface of the product, and after the product is formed, the permeation-resistant coating layer is broken to obtain the required product.

Further, the coagulant is matched with the inorganic gelled material and is composed of one or more of water, water glass, an accelerator and an alkali metal solution.

Further, the inorganic cementing material is cement or geopolymer, and also comprises cement-based composite materials or geopolymer-based composite materials taking the inorganic cementing material as a base material.

Furthermore, the cement-based composite material is formed by mixing a cement base material with a filler or a reinforcing material, and the geopolymer-based composite material is formed by mixing a geopolymer base material with a filler or a reinforcing material.

Further, the filler is one or more of bone meal, stone powder, ceramic powder and organic polymer powder, and the reinforcing material is one or more of carbon fiber, glass fiber and mineral fiber.

Further, the filler has a particle size distribution of D10=30 micrometers, D50=50 micrometers, D90=80 micrometers, and the reinforcement has a length of not more than 120 micrometers, not less than 40 micrometers, and a proportion of not more than 90 micrometers in length of not less than 90 micrometers.

Further, when the cement is high-alumina cement, the filler is one or more of clay mineral, quartz, feldspar or oxide ceramic, nitride ceramic and carbide ceramic powder, and is used for manufacturing refined ceramics.

Furthermore, when the filler is organic high molecular polymer powder, the product is placed in a heating device to be heated to the melting point of the polymer after being formed, and then is slowly cooled to room temperature.

Furthermore, when the inorganic cementing material is high alumina cement, the filler is ceramic powder, and the grain size of the ceramic powder is not more than 20 microns, the formed product is taken as a green piece and put into a sintering furnace, and sintering is carried out according to a ceramic sintering process, so as to obtain a ceramic fine product taking a ceramic phase as a main component. Before the ceramic sintering is started, the green body can be processed with high precision according to the requirement, and the dimensional precision of the green body is improved.

The invention utilizes the characteristic that inorganic gelled material and coagulant are mixed to generate chemical reaction and generate in-situ solidification, and applies the additive manufacturing (3D printing) technical principle of layered manufacturing and superposition forming to the forming of inorganic gelled material products. Compared with the existing traditional inorganic material forming technology and the additive manufacturing inorganic cementing material forming technology, the invention has the beneficial effects that:

1. the method realizes the conversion from digital design to digital direct manufacturing, can better solve the forming problem of inorganic gelled material fine products, and realizes the direct forming of fine products which are difficult to manufacture or even impossible to manufacture in the prior art, have complex shapes, complex inner cavities, hollow-out or nested structures and smooth surfaces, wherein the dimensional precision can reach hundreds of microns or even hundreds of microns or less.

2. The forming device adopted by the invention does not use a laser and a laser galvanometer system, has no strict control requirements in the aspects of temperature field, vacuum degree, atmosphere protection and the like, and has very high price advantage compared with other related 3D printing forming modes, no matter equipment, materials or energy consumption in the product manufacturing process.

3. The arrangement of the permeation-resistant coating layer blocks the path of a coagulant to the periphery of the surface of a formed piece without the permeation of the formed powdery inorganic gelled material, so that on one hand, the surface of the formed piece is not adhered with the peripheral inorganic gelled powder, and the surface of the formed piece is ensured to be smooth; on the other hand, the inorganic gelling material not involved in the forming is also prevented from being contaminated with a coagulant, ensuring the reuse of the raw material.

4. The ultrasonic vibration powder laying device is beneficial to improving the compactness of the powder layer.

5. Adopting high-alumina cement with the alumina content of more than 80 percent as a base material, adding pure alumina as a filling material, and taking a cement product with the high alumina content, which is obtained by cement hydration reaction between a composite material formed by fully mixing the base material and the pure alumina as a blank to manufacture a ceramic product; it is completely different from the existing ceramic production technology: a) taking a uniform mixture of high alumina cement and pure alumina powder as a ceramic raw material, b) taking a curing mechanism as a cement hydration reaction, and c) making a ceramic product blank according to a cement forming process; the beneficial effects are that: because the coagulation of the material is based on in-situ solidification generated by chemical reaction between the inorganic gel material and the coagulant, the influence of occupied removal objects such as moisture, adhesive and the like in the ceramic blank on the size of the ceramic formed piece in the drying and sintering processes can be greatly reduced.

6. After the ceramic blank is generated, the ceramic blank can be processed with high precision as required, the dimensional precision of the green blank is improved, the forward movement of the cold processing of the ceramic product is realized, and the processing cost is effectively reduced.

7. When the filler is organic high molecular polymer powder, a heat treatment process is needed after the product is formed: the formed piece is placed in a heating device to be heated to the melting point of the organic polymer, and then slowly cooled to room temperature. At this time, the organic high molecular polymer powder in the formed piece is heated and melted, and organic polymer grids with reinforcing phase function are formed in the hydration structure of the inorganic gel material around the organic high molecular polymer powder, so that the generation of stress concentration cracks during bearing can be prevented, and the comprehensive mechanical property of the material can be improved.

Drawings

FIG. 1 shows a schematic diagram of the apparatus of the present invention in one embodiment: (1) an ultrasonic vibration powder laying device; (2) forming a workpiece; (3) a spray head or spray head array; (4) a forming cylinder; (5) a lifting platform; (6) an inorganic gelling material;

FIG. 2 shows a process for producing a refined article of geopolymer material;

FIG. 3 shows a process for producing a refined ceramic product.

Detailed Description

The technical solution of the present invention will be clearly and completely described below with reference to the accompanying drawings and specific embodiments. The described embodiments are only specific embodiments of the present application and are not all intended. All other forms of embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present application.

Example one

FIG. 1 shows a schematic drawing of a forming apparatus of the present invention in one embodiment: the forming device comprises an ultrasonic vibration powder spreading device 1, a sprayer or sprayer array 3, a forming cylinder 4 and a lifting table 5, wherein the ultrasonic vibration powder spreading device 1 is used for uniformly spreading and compacting an inorganic gelled material 6 on the upper surface of the lifting table 5 into a plane, the spraying device 3 comprises at least two groups of sprayers or two groups of sprayer arrays, one group of sprayers or sprayer arrays 3 is used for spraying a permeability resistance agent to the outer edge of the outline of a horizontal section solid area corresponding to a product on a material layer, the other group of sprayers or sprayer arrays 3 is used for spraying a coagulant to the horizontal section solid area corresponding to the product on the material layer, and the lifting table 5 is arranged in the forming cylinder 4 and is lifted and lowered along the inner wall surface of the forming cylinder 4 for bearing the spread inorganic gelled material.

Example two

The invention provides an embodiment of a forming method of a forming device for additive manufacturing of an inorganic cementing material product, and the method is used for forming a refined product of a geopolymer material.

Referring to fig. 2, the forming method includes the following steps:

1. dispersing the three-dimensional design pattern of the product to be manufactured into a series of two-dimensional horizontal section patterns, and inputting the two-dimensional horizontal section patterns into a forming device control computer;

2. loading raw materials such as a powdery geopolymer material, a permeability barrier agent (shellac varnish), a coagulant (NaOH solution) and the like into a forming device;

3. an ultrasonic vibration powder spreading mechanism in the forming device spreads and compacts powdery raw materials into a smooth uniform thin layer with the thickness of about 0.1 mm;

4. the impervious agent spray head group in the forming device sprays impervious agent to the outline outer edge of the solid part of the horizontal section corresponding to the specific height of the product to be manufactured on the powder thin layer;

5. a coagulant sprayer group in the forming device sprays coagulant into the area surrounded by the outline, the powder material soaked by the coagulant generates chemical reaction, coagulates in short time and solidifies in situ to form a solid thin layer of a corresponding section on a certain height of the product to be processed;

repeating the

steps

3, 4, 5 and 5 until the forming process of the product is completely finished;

6. taking out the formed workpiece from the forming device;

7. removing the permeation-resistant coating layer on the surface of the formed workpiece, and further processing or other post-treatments are carried out on the surface of the formed workpiece according to the requirements;

8. the manufacturing process is completed.

In the forming process, the inorganic gelled material which is wrapped around the formed product and is not coagulated and is not polluted by coagulant due to the arrangement of the permeation-resisting layer can be reused for manufacturing a new workpiece after being subjected to proper treatment such as screening and the like.

EXAMPLE III

The invention also provides another embodiment of the forming method of the forming device for the additive manufacturing of the inorganic cementing material product, and the forming of the ceramic refined product is realized by the method.

Referring to fig. 3, the method includes the following steps:

2. loading the raw materials of the uniform mixture of the high-alumina cement and the aluminum oxide, a penetration inhibitor (shellac varnish), a water-based coagulant and the like into a forming device;

3. an ultrasonic vibration powder spreading mechanism in the forming device spreads and compacts the powdery raw material into a smooth uniform thin layer with the thickness of about 0.1 mm;

repeating the

steps

3, 4, 5 and 5 until the forming process of the product is completely finished;

6. taking out the formed ceramic blank from the forming device;

7. removing the permeation-resistant coating layer on the surface of the ceramic blank, and further processing or other post-treatment is carried out on the surface of the ceramic blank according to the requirement;

8. placing the ceramic blank in a humid place, and allowing the ceramic blank to be continuously subjected to post-curing to achieve the expected strength;

9. the blank can be processed with high precision according to the requirement, and the size precision of the blank is improved;

10. and (4) placing the ceramic blank reaching the expected strength into a ceramic sintering furnace for sintering, and finally finishing the manufacture of the refined ceramic product.

In the forming process, the uniformly mixed powder material of the high-alumina cement and the aluminum oxide which is wrapped around the formed product and is not coagulated and is not polluted by the coagulant because of the arrangement of the permeation-resisting layer can be used for manufacturing new workpieces after proper treatment such as screening and the like.

The above-mentioned embodiments only express several embodiments of the present invention, and the description thereof is more specific and detailed, but not construed as limiting the scope of the invention. It should be noted that, for a person skilled in the art, several variations and modifications can be made without departing from the inventive concept, which falls within the scope of the present invention. Therefore, the protection scope of the present patent shall be subject to the appended claims.

Claims

1. A forming device for additive manufacturing of inorganic cementing material products is characterized in that the forming device comprises an ultrasonic vibration powder laying device, a spraying device, a forming cylinder and a lifting platform; the ultrasonic vibration powder spreading device is used for uniformly spreading and compacting an inorganic cementing material on the upper surface of the lifting table into a plane; the spraying device comprises at least two groups of spray heads or two groups of spray head arrays, wherein one group of spray heads or spray head arrays are used for spraying the permeability-blocking agent to the outer edge of the outline of the horizontal section solid area corresponding to the product on the material layer, and the other group of spray heads or spray head arrays are used for spraying the coagulant to the horizontal section solid area corresponding to the product on the material layer; the lifting platform is arranged in the forming cylinder, and performs lifting motion along the inner wall surface of the forming cylinder, so as to bear the spreading inorganic cementing material.

2. The forming apparatus according to claim 1, wherein the ultrasonic vibration powder-laying apparatus is operative to vibrate at an ultrasonic frequency higher than 20 KHz; range of injection frequency f of the head or head array of the injection device:

1KHz＜ f ＜20KHz。

3. former according to claim 1 or 2, characterised in that the spray head or array of spray heads for spraying the barrier agent is capable of spraying a liquid having a viscosity η in the range:

1CP＜ η ＜150CP。

4. a method of forming a forming device for additive manufacturing of an inorganic cementitious material product according to any of claims 1 to 3, characterised by comprising the steps of:

d) repeating the steps in sequence until the product is formed;

the inorganic gel material and coagulant react to form product layer on the material layer, the permeation inhibitor prevents the coagulant from reacting with the gel material outside the horizontal section solid area of the product, and forms permeation-resisting coating layer on the surface of the product, and the permeation-resisting coating layer is broken after the product is formed, so that the required product is obtained.

5. The forming method according to claim 4, wherein the coagulant is matched with the inorganic gelling material and consists of one or more of water, water glass, an accelerator and an alkali metal solution.

6. A forming process according to claim 4, wherein the inorganic cementitious material is cement or a geopolymer, also including cement-based or geopolymer-based composites based on inorganic cementitious materials.

7. A forming method according to claim 6, wherein the cement-based composite material is a cement-based matrix mixed filler or reinforcement, and the geopolymer-based composite material is a geopolymer-based matrix mixed filler or reinforcement.

8. The forming method according to claim 7, wherein the filler is one or more of bone meal, stone powder, ceramic powder and organic polymer powder, and the reinforcement is one or more of carbon fiber, glass fiber and mineral fiber.

9. Root of herbaceous plantA forming method according to any one of claims 7 to 8, wherein the filler has a particle size distribution D₁₀=30 μm, D₅₀=50 μm, D₉₀=80 microns, the reinforcement has a length of not more than 120 microns, not less than 40 microns, and a proportion of not less than 90 microns in length.

10. A forming method according to any one of claims 7 to 9, wherein when the cement is high alumina cement, the filler is ceramic powder, and the particle size of the ceramic powder is not more than 20 μm, the formed article is sintered as a green body to obtain a ceramic article having a predominant ceramic phase; when the filler is organic high molecular polymer powder, the product is heated to the melting point of the polymer in a heating device after being formed, and then is slowly cooled to room temperature.