CN110819139A - Water-resistant building coating - Google Patents
Water-resistant building coating Download PDFInfo
- Publication number
- CN110819139A CN110819139A CN201911162943.3A CN201911162943A CN110819139A CN 110819139 A CN110819139 A CN 110819139A CN 201911162943 A CN201911162943 A CN 201911162943A CN 110819139 A CN110819139 A CN 110819139A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- color paste
- black color
- building coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a waterproof building coating, which comprises the following components in percentage by weight: 18-25 parts of non-floating aluminum powder slurry; 0.8-1.1 parts of water glass; 6-8 parts of graphite powder; 11-13 parts of hydroxyethyl cellulose; 9-10 parts of linseed oil alkyd resin; 4.5-5 parts of glass fiber; 100 parts of 1.5-1.8% carbon nanotube dispersion liquid; 4-7 parts of an amino resin curing agent; 10-20 parts of black color paste. Compared with the prior art, the waterproof building coating has good waterproof performance and high reliability.
Description
[ technical field ] A method for producing a semiconductor device
The invention belongs to the technical field of building materials, and particularly relates to a waterproof building coating.
[ background of the invention ]
Coatings are one of the most common building materials, and are a general term for liquid or solid materials that can be applied to the surface of an object to form a solid film having protective, decorative or special properties (e.g., insulation, corrosion protection, signs, etc.). The paint comprises paint, water paint, wood lacquer, powder coating and wood wax oil, and is essential for house decoration.
When the building material is dried in water, the building material is easy to crack, and the surface of the building material is scaly to fall off, even poisoned, so that the building material is easy to rework after home decoration, and particularly, the building material is in a place with a damp environment, thereby causing loss of time and economy.
[ summary of the invention ]
The invention aims to provide a waterproof building coating with good waterproofness and high reliability.
In order to solve the technical problems, the invention provides a waterproof building coating which comprises the following components in parts by weight:
18-25 parts of non-floating aluminum powder slurry;
0.8-1.1 parts of water glass;
6-8 parts of graphite powder;
11-13 parts of hydroxyethyl cellulose;
9-10 parts of linseed oil alkyd resin;
4.5-5 parts of glass fiber;
100 parts of 1.5-1.8% carbon nanotube dispersion liquid;
4-7 parts of an amino resin curing agent;
10-20 parts of black color paste.
Preferably, the water-resistant architectural coating comprises the following components in percentage by weight: 20 parts of non-floating aluminum powder slurry, 1.0 part of water glass, 8 parts of graphite powder, 12 parts of hydroxyethyl cellulose, 9 parts of linseed alkyd resin, 4.6 parts of glass fiber, 100 parts of 1.6% carbon nanotube dispersion liquid, 5 parts of amino resin curing agent and 20 parts of black color paste.
Preferably, the carbon black content of the black paste is 15-23%.
Preferably, the carbon black content of the black color paste is 22%.
Compared with the related art, the waterproof building coating has good waterproofness and high reliability.
[ detailed description ] embodiments
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The invention provides a waterproof building coating which comprises the following components in parts by weight: 18-25 parts of non-floating aluminum powder slurry; 0.8-1.1 parts of water glass; 6-8 parts of graphite powder; 11-13 parts of hydroxyethyl cellulose; 9-10 parts of linseed oil alkyd resin; 4.5-5 parts of glass fiber; 100 parts of 1.5-1.8% carbon nanotube dispersion liquid; 4-7 parts of an amino resin curing agent; 10-20 parts of black color paste. The carbon black content of the black color paste is preferably 15% -23%, and the carbon black content of the black color paste is preferably 22%.
Example one
The waterproof building coating comprises the following components in percentage by weight: 20 parts of non-floating aluminum powder slurry, 1.0 part of water glass, 8 parts of graphite powder, 12 parts of hydroxyethyl cellulose, 9 parts of linseed alkyd resin, 4.6 parts of glass fiber, 100 parts of 1.6% carbon nanotube dispersion liquid, 5 parts of amino resin curing agent and 20 parts of black color paste, wherein the carbon black content of the black color paste is 22%.
Example two
25 parts of non-floating aluminum powder slurry; 2.0 parts of water glass; 7 parts of graphite powder; 13 parts of hydroxyethyl cellulose; 9 parts of linseed oil alkyd resin; 4.9 parts of glass fiber; 100 parts of 1.7% carbon nanotube dispersion liquid; 5 parts of an amino resin curing agent; and 15 parts of black color paste. Wherein the carbon black content of the black color paste is 22 percent.
EXAMPLE III
18 parts of non-floating aluminum powder slurry; 0.8 part of water glass; 6 parts of graphite powder; 11 parts of hydroxyethyl cellulose; 9 parts of linseed oil alkyd resin; 4.5 parts of glass fiber; 100 parts of 1.5% carbon nanotube dispersion liquid; 4 parts of an amino resin curing agent; 10 parts of black color paste. Wherein the carbon black content of the black color paste is 22 percent.
Example four
25 parts of non-floating aluminum powder slurry; 1.1 parts of water glass; 8 parts of graphite powder; 13 parts of hydroxyethyl cellulose; 10 parts of linseed oil alkyd resin; 5 parts of glass fiber; 100 parts of 1.8% carbon nanotube dispersion liquid; 7 parts of an amino resin curing agent; and 20 parts of black color paste. Wherein, the carbon black content of the black color paste is preferably 22%.
EXAMPLE five
23 parts of non-floating aluminum powder slurry; 0.9 part of water glass; 7 parts of graphite powder; 12 parts of hydroxyethyl cellulose; 10 parts of linseed oil alkyd resin; 4.8 parts of glass fiber; 100 parts of 1.7% carbon nanotube dispersion liquid; 6 parts of an amino resin curing agent; and 15 parts of black color paste. Wherein, the carbon black content of the black color paste is preferably 22%.
Compared with the related art, the waterproof building coating has good waterproofness and high reliability.
While the foregoing is directed to embodiments of the present invention, it will be understood by those skilled in the art that various changes may be made without departing from the spirit and scope of the invention.
Claims (4)
1. The water-resistant building coating is characterized by comprising the following components in percentage by weight:
18-25 parts of non-floating aluminum powder slurry;
0.8-1.1 parts of water glass;
6-8 parts of graphite powder;
11-13 parts of hydroxyethyl cellulose;
9-10 parts of linseed oil alkyd resin;
4.5-5 parts of glass fiber;
100 parts of 1.5-1.8% carbon nanotube dispersion liquid;
4-7 parts of an amino resin curing agent;
10-20 parts of black color paste.
2. The water-resistant architectural coating according to claim 1, wherein the water-resistant architectural coating comprises the following components in parts by weight: 20 parts of non-floating aluminum powder slurry, 1.0 part of water glass, 8 parts of graphite powder, 12 parts of hydroxyethyl cellulose, 9 parts of linseed alkyd resin, 4.6 parts of glass fiber, 100 parts of 1.6% carbon nanotube dispersion liquid, 5 parts of amino resin curing agent and 20 parts of black color paste.
3. The water-resistant architectural coating according to any one of claims 1 or 2, wherein the carbon black content of the black paste is 15% -23%.
4. The water-resistant architectural coating according to claim 3, wherein the black paste has a carbon black content of 22%.