CN110760976A - Comfortable environment-friendly bamboo fiber fabric - Google Patents
Comfortable environment-friendly bamboo fiber fabric Download PDFInfo
- Publication number
- CN110760976A CN110760976A CN201911109869.9A CN201911109869A CN110760976A CN 110760976 A CN110760976 A CN 110760976A CN 201911109869 A CN201911109869 A CN 201911109869A CN 110760976 A CN110760976 A CN 110760976A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- bamboo pulp
- fiber fabric
- comfortable environment
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a comfortable environment-friendly bamboo fiber fabric, which relates to the technical field of clothing fabrics and comprises the following components in parts by weight: the fabric comprises warps and wefts, wherein the warps and the wefts are interwoven, and the fabric is characterized in that the warps adopt polyester filaments, and the wefts adopt bamboo pulp fibers; the bamboo pulp fiber is prepared by wet spinning of a bamboo pulp composite sodium alginate base solution; the fabric prepared by the invention has good hand feeling, and the elasticity of the fabric is greatly improved and the soft and smooth hand feeling is increased by adding the polyester fiber.
Description
Technical Field
The invention belongs to the technical field of clothing fabrics, and particularly relates to a comfortable environment-friendly bamboo fiber fabric.
Background
The garment is made of fabric, and the fabric is used for making the garment. As one of the three elements of the garment, the fabric not only can explain the style and the characteristics of the garment, but also directly controls the expression effects of the color and the shape of the garment. Presents the advantages of high price and perfect self and soft hand feeling.
With the increase of the population at present, the demand of material resources is rapidly rising, the problems of energy crisis, resource crisis and the like are met, bamboo resources in China are very rich, while bamboo is a fast-growing plant and can be continuously felled for use after being cultivated for two to three years, the yield of bamboo is high compared with that of wood, the forming is fast, and the bamboo plant is taken as a monocotyledon angiosperm plant, gramineae, bamboo subfamily and is a perennial plant and is produced in tropical, subtropical and temperate regions.
The bamboo fiber is prepared by the following steps: the bamboo is directly made into natural bamboo fiber by a physical and mechanical method, or the bamboo is made into bamboo pulp by a chemical method, the bamboo pulp is dissolved to be made into bamboo pulp solution, and then the bamboo pulp fiber is made by wet spinning.
However, in the prior art, although the bamboo fiber fabric of application No. 201110296724.1 has natural antibacterial, deodorant and mildewproof effects by using the bamboo fiber, the elasticity is poor and the air permeability is general.
Disclosure of Invention
The invention aims to provide a comfortable environment-friendly bamboo fiber fabric aiming at the existing problems.
The invention is realized by the following technical scheme:
a comfortable environment-friendly bamboo fiber fabric comprises: the fabric comprises warps and wefts, wherein the warps and the wefts are interwoven, the warps adopt polyester filaments, and the wefts adopt bamboo pulp fibers;
the bamboo pulp fiber is prepared by wet spinning of a bamboo pulp composite sodium alginate base solution.
As a further technical scheme, the polyester filament yarn is 200D-250D polyester filament yarn.
As a further technical scheme, the preparation method of the bamboo pulp composite sodium alginate base solution comprises the following steps:
(1) adding clear water with the mass 2 times of that of the bamboo pulp into the bamboo pulp serving as a raw material, and stirring to obtain a bamboo pulp solution;
(2) adding 1.5-2% alkali into the obtained bamboo pulp solution, heating to boil, stirring for 1 hr, and naturally cooling to room temperature to obtain steamed bamboo pulp solution;
(3) adjusting the pH value of the obtained steamed bamboo pulp solution to be neutral, then adding sodium alginate accounting for 3-4% of the mass of the neutral bamboo pulp solution, heating in water bath, and stirring for 1 hour to obtain the bamboo pulp composite sodium alginate base solution.
As a further technical scheme, the content of methyl cellulose in the bamboo pulp in the step (1) is 88.5 percent.
As a further technical scheme, in the step (1), the stirring is carried out at the rotating speed of 1500r/min for 40min at the temperature of 40 ℃.
As a further technical scheme, the alkali in the step (2) is sodium hydroxide.
As a further technical scheme, the pH value of the boiled bamboo pulp solution is adjusted by adopting a hydrochloric acid solution in the step (3).
As a further technical scheme, the mass fraction of the hydrochloric acid solution is 0.1%.
As a further technical scheme, the heating temperature of the water bath in the step (3) is 75-78 ℃.
As a further technical scheme, the warp density of the bamboo fiber fabric is 90-95, and the weft density is 60-70.
Has the beneficial effects that; the fabric prepared by the invention has good hand feeling, the elasticity of the fabric is greatly improved by adding the polyester fiber, the hand feeling is soft and smooth, the fabric prepared by the invention is cool and breathable, the moisture absorption and heat dissipation are fast, and the fabric has obvious inhibition effect on invasion of bacteria, mites and the like by adopting the composite spinning of the polyester fiber and the bamboo pulp fiber prepared by the invention, the strength of the fabric can be increased by blending the synthetic fiber and the bamboo pulp fiber, the three-dimensional layering sense of the fabric is strong, and the unique visual effect and the texture effect can be generated; the bamboo fiber fabric is made of the specially-made bamboo pulp fibers, the cross section of the bamboo fiber fabric is concave-convex deformed, micropores similar to ellipses are distributed on the surface of the bamboo fiber fabric, the bamboo fiber fabric is of a highly hollow structure, the capillary effect is extremely strong, and a large amount of water can be absorbed and evaporated instantly, so that the sweat absorption and sweat release functions of the bamboo fiber fabric are greatly improved, the bamboo fiber fabric can be worn more comfortably, the bamboo fiber fabric can be fluffy and warm when used in winter and spring, redundant hot air and moisture in the body can be discharged, and the comfortable and refreshing wearing feeling is brought to people.
Detailed Description
Example 1
A comfortable environment-friendly bamboo fiber fabric comprises: the fabric comprises warps and wefts, wherein the warps and the wefts are interwoven, the warps adopt polyester filaments, and the wefts adopt bamboo pulp fibers;
the bamboo pulp fiber is prepared by wet spinning of a bamboo pulp composite sodium alginate base solution.
As a further technical scheme, the polyester filament yarn is a 200D polyester filament yarn.
As a further technical scheme, the preparation method of the bamboo pulp composite sodium alginate base solution comprises the following steps:
(1) adding clear water with the mass 2 times of that of the bamboo pulp into the bamboo pulp serving as a raw material, and stirring to obtain a bamboo pulp solution;
(2) adding alkali with the mass of 1.5% into the obtained bamboo pulp solution, heating to boil, stirring for 1 hour, and naturally cooling to room temperature to obtain a steamed bamboo pulp solution;
(3) and adjusting the pH value of the obtained steamed bamboo pulp solution to be neutral, then adding sodium alginate accounting for 3% of the mass of the neutral bamboo pulp solution, heating in a water bath, and stirring for 1 hour to obtain the bamboo pulp composite sodium alginate base solution.
As a further technical scheme, the content of methyl cellulose in the bamboo pulp in the step (1) is 88.5 percent.
As a further technical scheme, in the step (1), the stirring is carried out at the rotating speed of 1500r/min for 40min at the temperature of 40 ℃.
As a further technical scheme, the alkali in the step (2) is sodium hydroxide.
As a further technical scheme, the pH value of the boiled bamboo pulp solution is adjusted by adopting a hydrochloric acid solution in the step (3).
As a further technical scheme, the mass fraction of the hydrochloric acid solution is 0.1%.
As a further technical scheme, the water bath heating temperature in the step (3) is 75 ℃.
As a further technical scheme, the warp density of the bamboo fiber fabric is 90, and the weft density is 60.
Example 2
A comfortable environment-friendly bamboo fiber fabric comprises: the fabric comprises warps and wefts, wherein the warps and the wefts are interwoven, the warps adopt polyester filaments, and the wefts adopt bamboo pulp fibers;
the bamboo pulp fiber is prepared by wet spinning of a bamboo pulp composite sodium alginate base solution.
As a further technical scheme, the polyester filament yarn is a 250D polyester filament yarn.
As a further technical scheme, the preparation method of the bamboo pulp composite sodium alginate base solution comprises the following steps:
(1) adding clear water with the mass 2 times of that of the bamboo pulp into the bamboo pulp serving as a raw material, and stirring to obtain a bamboo pulp solution;
(2) adding alkali with the mass of 2% into the obtained bamboo pulp solution, heating to boil, stirring for 1 hour, and naturally cooling to room temperature to obtain a steamed bamboo pulp solution;
(3) and adjusting the pH value of the obtained steamed bamboo pulp solution to be neutral, then adding sodium alginate accounting for 4% of the mass of the neutral bamboo pulp solution, heating in a water bath, and stirring for 1 hour to obtain the bamboo pulp composite sodium alginate base solution.
As a further technical scheme, the content of methyl cellulose in the bamboo pulp in the step (1) is 88.5 percent.
As a further technical scheme, in the step (1), the stirring is carried out at the rotating speed of 1500r/min for 40min at the temperature of 40 ℃.
As a further technical scheme, the alkali in the step (2) is sodium hydroxide.
As a further technical scheme, the pH value of the boiled bamboo pulp solution is adjusted by adopting a hydrochloric acid solution in the step (3).
As a further technical scheme, the mass fraction of the hydrochloric acid solution is 0.1%.
As a further technical scheme, the water bath heating temperature in the step (3) is 78 ℃.
As a further technical scheme, the warp density of the bamboo fiber fabric is 95, and the weft density is 70.
Example 3
A comfortable environment-friendly bamboo fiber fabric comprises: the fabric comprises warps and wefts, wherein the warps and the wefts are interwoven, the warps adopt polyester filaments, and the wefts adopt bamboo pulp fibers;
the bamboo pulp fiber is prepared by wet spinning of a bamboo pulp composite sodium alginate base solution.
As a further technical scheme, the polyester filament yarn is a 250D polyester filament yarn.
As a further technical scheme, the preparation method of the bamboo pulp composite sodium alginate base solution comprises the following steps:
(1) adding clear water with the mass 2 times of that of the bamboo pulp into the bamboo pulp serving as a raw material, and stirring to obtain a bamboo pulp solution;
(2) adding alkali with the mass of 1.8% into the obtained bamboo pulp solution, heating to boil, stirring for 1 hour, and naturally cooling to room temperature to obtain a steamed bamboo pulp solution;
(3) and adjusting the pH value of the obtained steamed bamboo pulp solution to be neutral, then adding sodium alginate accounting for 3.5% of the mass of the neutral bamboo pulp solution, heating in water bath, and stirring for 1 hour to obtain the bamboo pulp composite sodium alginate base solution.
As a further technical scheme, the content of methyl cellulose in the bamboo pulp in the step (1) is 88.5 percent.
As a further technical scheme, in the step (1), the stirring is carried out at the rotating speed of 1500r/min for 40min at the temperature of 40 ℃.
As a further technical scheme, the alkali in the step (2) is sodium hydroxide.
As a further technical scheme, the pH value of the boiled bamboo pulp solution is adjusted by adopting a hydrochloric acid solution in the step (3).
As a further technical scheme, the mass fraction of the hydrochloric acid solution is 0.1%.
As a further technical scheme, the water bath heating temperature in the step (3) is 76 ℃.
As a further technical scheme, the warp density of the bamboo fiber fabric is 92, and the weft density of the bamboo fiber fabric is 65.
The fabrics prepared in the respective examples were soaked in water for 7 days, and then subjected to an elastic recovery performance test using an electronic fabric strength tester, wherein the elongation rate = (elongation length-original length)/original length × 100%, and the recovery rate = (elongation length-recovery length)/(elongation length-original length) × 100%, and the test results are shown in table 1, and 20 fabrics were taken as an average value:
TABLE 1
| Elongation% radial | Recovery% radial | |
| Example 1 | 22.20 | 76.11 |
| Example 2 | 20.16 | 74.62 |
| Example 3 | 20.52 | 75.34 |
| Control group | 8.63 | 35.67 |
Control group: 201110296724.1A bamboo fiber fabric is made into fabric with the same specification;
table 1 shows that the bamboo fiber fabric prepared by the present invention has excellent elongation and recovery rate.
Air permeability detection
TABLE 2
| Air permeability L.m.S device-1 | |
| Example 1 | 1580 |
| Example 2 | 1490 |
| Example 3 | 1510 |
| Control group | 1220 |
Control group: 201110296724.1A bamboo fiber fabric is made into fabric with the same specification;
as can be seen from Table 2, the air permeability of the bamboo fiber fabric prepared by the invention is greatly improved.
The bamboo pulp fiber monofilament fiber breaking strength prepared in the examples was tested:
the breaking strength of the fiber is tested by using a YG020A type electronic single yarn strength tester, the stretching speed is controlled to be 202mm/min, the ambient temperature is 22 ℃, the humidity is 60%, and the pretension is 0.05 cN/dtex;
TABLE 3
| Fiber breaking strength cN/dtex | |
| Example 1 | 3.09 |
| Example 2 | 3.56 |
| Example 3 | 3.12 |
| Control group | 2.55 |
Control group: 201110296724.1A bamboo fiber monofilament in bamboo fiber fabric, the specification is the same as the embodiment;
as can be seen from Table 3, the single filaments of the bamboo pulp fibers used in the present invention have high breaking strength.
Claims (10)
1. A comfortable environment-friendly bamboo fiber fabric comprises: the fabric comprises warps and wefts, wherein the warps and the wefts are interwoven, and the fabric is characterized in that the warps adopt polyester filaments, and the wefts adopt bamboo pulp fibers;
the bamboo pulp fiber is prepared by wet spinning of a bamboo pulp composite sodium alginate base solution.
2. The comfortable environment-friendly bamboo fiber fabric as claimed in claim 1, wherein the polyester filament is 200D-250D polyester filament.
3. The comfortable environment-friendly bamboo fiber fabric as claimed in claim 2, wherein the preparation method of the bamboo pulp and sodium alginate composite base solution comprises the following steps:
(1) adding clear water with the mass 2 times of that of the bamboo pulp into the bamboo pulp serving as a raw material, and stirring to obtain a bamboo pulp solution;
(2) adding 1.5-2% alkali into the obtained bamboo pulp solution, heating to boil, stirring for 1 hr, and naturally cooling to room temperature to obtain steamed bamboo pulp solution;
(3) adjusting the pH value of the obtained steamed bamboo pulp solution to be neutral, then adding sodium alginate accounting for 3-4% of the mass of the neutral bamboo pulp solution, heating in water bath, and stirring for 1 hour to obtain the bamboo pulp composite sodium alginate base solution.
4. A comfortable environment-friendly bamboo fiber fabric as claimed in claim 3, wherein in step (1), the content of methyl cellulose in the bamboo pulp is 88.5%.
5. A comfortable environment-friendly bamboo fiber fabric as claimed in claim 3, wherein the stirring in step (1) is at 1500r/min for 40min at 40 ℃.
6. A comfortable environment-friendly bamboo fiber fabric as claimed in claim 3, wherein the alkali in step (2) is sodium hydroxide.
7. A comfortable environment-friendly bamboo fiber fabric as claimed in claim 3, wherein the pH of the bamboo pulp cooking solution in step (3) is adjusted by hydrochloric acid solution.
8. The comfortable environment-friendly bamboo fiber fabric as claimed in claim 8, wherein the hydrochloric acid solution is 0.1% by mass.
9. A comfortable environment-friendly bamboo fiber fabric as claimed in claim 3, wherein the water bath heating temperature in step (3) is 75-78 ℃.
10. A comfortable environment-friendly bamboo fiber fabric as claimed in claim 1, wherein the bamboo fiber fabric has a warp density of 90-95 and a weft density of 60-70.