CN104213305B - Textile fabric and preparation method thereof on a kind of Novel imitation cotton bed - Google Patents
Textile fabric and preparation method thereof on a kind of Novel imitation cotton bed Download PDFInfo
- Publication number
- CN104213305B CN104213305B CN201410411388.4A CN201410411388A CN104213305B CN 104213305 B CN104213305 B CN 104213305B CN 201410411388 A CN201410411388 A CN 201410411388A CN 104213305 B CN104213305 B CN 104213305B
- Authority
- CN
- China
- Prior art keywords
- fibre
- silk
- carry out
- gou
- textile fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses textile and manufacture method thereof on a kind of Novel imitation cotton bed, its preparation process use terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre form so that fabric has that good deodorization is antibacterial, heat-insulating property, moisture absorbing and sweat releasing performance；Dyeing uses pilling fluffing resistant finishing agent during arranging, and changes the surface character of face liber, effectively enhances the pilling fluffing resistant performance of fabric.
Description
Technical field
The present invention relates to a kind of fabric, belong to field of textile, particularly relate to textile fabric and preparation method thereof on a kind of imitative cotton bed.
Background technology
On traditional bed, textile fabric is single raw material and makes, such as the fabric using single polyester material to be made into, fabric is very, feel is coarse, stiff, the then crease resistance being made into such as the single cotton material used is poor, cloth is shaky, and on terylene bed currently on the market, textile fiber structure is cylindrical, and easy balling-up fluffing, sucting wet air permeability is poor, anti-microbial property is poor.
Summary of the invention
The technical problem existed based on background technology, the present invention proposes textile fabric and manufacture method thereof on a kind of Novel imitation cotton bed.
Technical scheme is as follows:
1, textile fabric on a kind of Novel imitation cotton bed, it is characterized in that, terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre is used to form, terylene height f silk, gou-tree fibre, milk fibre blending silk thread in the percentage by weight of terylene height f silk be 60-75%, the percentage by weight of gou-tree fibre is 10-15%, and the percentage by weight of milk fibre is 15-25%.
Superfine fibre is superfine due to fiber number, greatly reduce the rigidity of silk, the most soft as fabric feeling, fiber finer also increases the layer structure of silk, increase specific surface area and capillary effect, make fibrous inside reflection light finer and smoother in surface distributed, be allowed to the graceful gloss having as real silk, and have good moisture absorption wet dissipation.It is made bedding with superfine fibre, comfortable, attractive in appearance, warming, ventilative, also it is significantly increased in terms of hydrophobicity and soil resistance, utilizes its specific surface area big and soft feature can design different organizational structuries and be allowed to more absorb solar heat energy or the body temperature that faster scatters and disappears plays effect cool in summer and warm in winter.
Broussonetia papyrifera belongs to deciduous tree, has another name called Chu Tao etc., high 10～20m；Bark lead；The close raw pubescence of sprig.Tree crown opens, avette to the most avette；Bark smooths, light grey or taupe, is difficult to split, and Herb contains milk.For strong positive seeds, adaptability extra-heavy, strong stress resistance.Broussonetia papyrifera have fast-growing, adaptive faculty is strong, distribution is wide, easily breeding, heat is high, the period of felling in turn is short feature.In China, distribution is very wide, north from North China, northwest, south to south China, southwestern various places all have.In recent years, numerous domestic scholar has carried out a certain degree of research to the exploitation of Broussonetia papyrifera, and has been achieved for some achievements, tapa contains substantial amounts of good fiber quality, corrosion-resistant, senior speciality paper can be manufactured, be also a kind of fiber that preferably can be suitably used for weaving.Chinese patent CN103123150A discloses the preparation method of a kind of gou-tree fibre, the gou-tree fibre that the method is prepared by the present invention and dacron thread blending, has opened up the new application of gou-tree fibre.
Milk fibre is using Lac Bovis seu Bubali as base stock, through dehydration, defat, separate and a series of chemical treatment technology such as purification is allowed to have linear macromolecule space structure, and then through being blended, the operation such as crosslinking be prepared as spinning solution, finally by wet spinning, solidify, be dried, the mechanical processing tools such as sizing and prepare.As a kind of natural fiber different from the past and the novel animal protein fibre of synthetic fibers, why himself contained protein can finally process fibroblast, owing in milk, protein special construction and character are determined.Milk fibre also has distinctive advantage in terms of wearability, and in terms of inhaling heat release, milk fibre has the microcellular structure of three-dimensional multigap, makes fiber possess characteristic cool in summer and warm in winter；In terms of environmental protection, milk fibre does not contains any carcinogen, and content of formaldehyde is zero；In terms of comfortableness, milk fibre contains several amino acids, it is possible to promoting the metabolism of human body cell, the activated protein in milk also has the function of Glycerin.
Preferably, described superfine denier polyester silk is 150D/288g × 25D/72g, and the weft density of described blended ratio is 230T/210T/190T.
2, the preparation method of textile fabric on a kind of Novel imitation cotton bed, comprises the following steps:
A, weave cotton cloth: using terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre to form, Dobby Weave Design uses satin weave, then through suitable twisting, makes polyster fibre that light is produced diffuse-reflectance phenomenon, uses water-jet loom to make embryo cloth；
B, starching, oil: embryo cloth step A prepared carries out starching and oiling treatment；
C, desizing refining: use low bath raio high-pressure injection overflow machine to carry out desizing refining process, technology preparation and condition as follows: desizing bath pH value 6～7, refining agent: 1～2g/L, NaOH:1～2g/L; bath raio: 1:10～15, temperature: 80～90 DEG C, the time: 5～15min；
D, Alkali reduction: after desizing refining completes, then carry out alkali decrement treatment, treatment conditions are NaOH10～15g/L, temperature: 85～100 DEG C, the time: 20～35min；
E, sizing: after Alkali reduction completes, shape, temperature: 140～160 DEG C, the time: 20～30s；
F, sanding；After sizing terminates, carry out sanding；
G, stamp: use machine of magnetic rod printing machine to carry out stamp
H, rear shaping and drying: carry out rear shaping and drying process after stamp, first carry out clear water and pad, then drying and shaping under the conditions of 140～160 DEG C；
I, arrangement: after drying, use and arranged by pilling fluffing resistant finishing agent, i.e. can get textile fabric on the Novel imitation cotton bed that the present invention proposes after arrangement.
Preferably, the sanding of described step F uses Buddha's warrior attendant rubber that dacron positive and negative longitude and latitude carries out mechanical grinding, forms the fine fleece less than 1mm length；
Preferably, described step I by pilling fluffing resistant finishing agent be pilling fluffing resistant finishing agent be Donghua University research and development AIP pilling fluffing resistant finishing agent, consumption is 1～5g/L；
The invention have benefit that: 1, use 150D/288g × 25D/72g, superfine denier polyester silk that 230T/210T/190T relative density is higher, fiber obvolvent is better than general, considerably increase the water suction area of fiber, better than the water absorption of conventional polyester fabric；2, dacron positive and negative pair warp and weft carries out mechanical grinding, forms the fine fleece less than 1mm length, and textile fiber structure is reeded irregularly shaped for band, has good effect to pilling fluffing resistant；3, good deodorization is antibacterial, heat-insulating property, moisture absorbing and sweat releasing performance to use super fine polyester silk and gou-tree fibre, the mode of blended by milk fibre that fabric is had.
Detailed description of the invention
Embodiment 1:
1, textile fabric on a kind of Novel imitation cotton bed, it is characterized in that, terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre is used to form, terylene height f silk, gou-tree fibre, milk fibre blending silk thread in the percentage by weight of terylene height f silk be 70%, the percentage by weight of gou-tree fibre is 15%, and the percentage by weight of milk fibre is 15%.
2, the preparation method of textile fabric on a kind of Novel imitation cotton bed, comprises the following steps:
A, weave cotton cloth: using terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre to form, Dobby Weave Design uses satin weave, then through suitable twisting, makes polyster fibre that light is produced diffuse-reflectance phenomenon, uses water-jet loom to make embryo cloth；Terylene height f silk specification is 150D/288g × 25D/72g, the weft density of described blended ratio is 210T；
B, starching, oil: embryo cloth step A prepared carries out starching and oiling treatment；
C, desizing refining: use low bath raio high-pressure injection overflow machine to carry out desizing refining process, technology preparation and condition as follows: desizing bath pH value 6, refining agent: 1.5g/L, NaOH:2g/L, bath raio: 1:15, temperature: 90 DEG C, time: 10min；
D, Alkali reduction: after desizing refining completes, then carry out alkali decrement treatment, treatment conditions are NaOH15g/L, temperature: 85 DEG C, time: 30min；
E, sizing: after Alkali reduction completes, shape, temperature: 140 DEG C, time: 20s；
F, sanding；After sizing terminates, carry out sanding；
G, stamp: use machine of magnetic rod printing machine to carry out stamp
H, rear shaping and drying: carry out rear shaping and drying process after stamp, first carry out clear water and pad, then drying and shaping under the conditions of 160 DEG C；
I, arrangement: after drying, use pilling fluffing resistant finishing agent to arrange, i.e. can get textile fabric on the Novel imitation cotton bed that the present invention proposes after arrangement.
Preferably, the sanding of described step F uses Buddha's warrior attendant rubber that dacron positive and negative longitude and latitude carries out mechanical grinding, forms the fine fleece less than 1mm length；
Preferably, described step I by pilling fluffing resistant finishing agent be pilling fluffing resistant finishing agent be Donghua University research and development AIP pilling fluffing resistant finishing agent, consumption is 4g/L；
Embodiment 2:
1, textile fabric on a kind of Novel imitation cotton bed, it is characterized in that, terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre is used to form, terylene height f silk, gou-tree fibre, milk fibre blending silk thread in the percentage by weight of terylene height f silk be 75%, the percentage by weight of gou-tree fibre is 10%, and the percentage by weight of milk fibre is 15%.
2, the preparation method of textile fabric on a kind of Novel imitation cotton bed, comprises the following steps:
A, weave cotton cloth: using terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre to form, Dobby Weave Design uses satin weave, then through suitable twisting, makes polyster fibre that light is produced diffuse-reflectance phenomenon, uses water-jet loom to make embryo cloth；Terylene height f silk specification is 150D/288g × 25D/72g, the weft density of described blended ratio is 190T；
B, starching, oil: embryo cloth step A prepared carries out starching and oiling treatment；
C, desizing refining: use low bath raio high-pressure injection overflow machine to carry out desizing refining process, technology preparation and condition as follows: desizing bath pH value 7, refining agent: 1.5g/L, NaOH:2g/L, bath raio: 1:13, temperature: 90 DEG C, time: 12min；
D, Alkali reduction: after desizing refining completes, then carry out alkali decrement treatment, treatment conditions are NaOH15g/L, temperature: 90 DEG C, time: 35min；
E, sizing: after Alkali reduction completes, shape, temperature: 145 DEG C, time: 25s；
F, sanding；After sizing terminates, carry out sanding；
G, stamp: use machine of magnetic rod printing machine to carry out stamp
H, rear shaping and drying: carry out rear shaping and drying process after stamp, first carry out clear water and pad, then drying and shaping under the conditions of 155 DEG C；
I, arrangement: after drying, use pilling fluffing resistant finishing agent to arrange, i.e. can get textile fabric on the Novel imitation cotton bed that the present invention proposes after arrangement.
Preferably, the sanding of described step F uses Buddha's warrior attendant rubber that dacron positive and negative longitude and latitude carries out mechanical grinding, forms the fine fleece less than 1mm length；
Preferably, described step I by pilling fluffing resistant finishing agent be pilling fluffing resistant finishing agent be Donghua University research and development AIP pilling fluffing resistant finishing agent, consumption is 5g/L；
Embodiment 3:
1, textile fabric on a kind of Novel imitation cotton bed, it is characterized in that, terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre is used to form, terylene height f silk, gou-tree fibre, milk fibre blending silk thread in the percentage by weight of terylene height f silk be 60%, the percentage by weight of gou-tree fibre is 15%, and the percentage by weight of milk fibre is 25%.
2, the preparation method of textile fabric on a kind of Novel imitation cotton bed, comprises the following steps:
A, weave cotton cloth: using terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre to form, Dobby Weave Design uses satin weave, then through suitable twisting, makes polyster fibre that light is produced diffuse-reflectance phenomenon, uses water-jet loom to make embryo cloth；Terylene height f silk specification is 150D/288g × 25D/72g, the weft density of described blended ratio is 2100T；
B, starching, oil: embryo cloth step A prepared carries out starching and oiling treatment；
C, desizing refining: use low bath raio high-pressure injection overflow machine to carry out desizing refining process, technology preparation and condition as follows: desizing bath pH value 6.5, refining agent: 1.5g/L, NaOH:1.5g/L, bath raio: 1:10, temperature: 85 DEG C, time: 8min；
D, Alkali reduction: after desizing refining completes, then carry out alkali decrement treatment, treatment conditions are NaOH12g/L, temperature: 95 DEG C, time: 25min；
E, sizing: after Alkali reduction completes, shape, temperature: 150 DEG C, time: 25s；
F, sanding；After sizing terminates, carry out sanding；
G, stamp: use machine of magnetic rod printing machine to carry out stamp
H, rear shaping and drying: carry out rear shaping and drying process after stamp, first carry out clear water and pad, then drying and shaping under the conditions of 155 DEG C；
I, arrangement: after drying, use pilling fluffing resistant finishing agent to arrange, i.e. can get textile fabric on the Novel imitation cotton bed that the present invention proposes after arrangement.
Preferably, the sanding of described step F uses Buddha's warrior attendant rubber that dacron positive and negative longitude and latitude carries out mechanical grinding, forms the fine fleece less than 1mm length；
Preferably, described step I by pilling fluffing resistant finishing agent be pilling fluffing resistant finishing agent be Donghua University research and development AIP pilling fluffing resistant finishing agent, consumption is 3g/L；
Embodiment 4:
1, textile fabric on a kind of Novel imitation cotton bed, it is characterized in that, terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre is used to form, terylene height f silk, gou-tree fibre, milk fibre blending silk thread in the percentage by weight of terylene height f silk be 60%, the percentage by weight of gou-tree fibre is 20%, and the percentage by weight of milk fibre is 20%.
2, the preparation method of textile fabric on a kind of Novel imitation cotton bed, comprises the following steps:
A, weave cotton cloth: using terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre to form, Dobby Weave Design uses satin weave, then through suitable twisting, makes polyster fibre that light is produced diffuse-reflectance phenomenon, uses water-jet loom to make embryo cloth；Terylene height f silk specification is 150D/288g × 25D/72g, the weft density of described blended ratio is 230T；
B, starching, oil: embryo cloth step A prepared carries out starching and oiling treatment；
C, desizing refining: use low bath raio high-pressure injection overflow machine to carry out desizing refining process, technology preparation and condition as follows: desizing bath pH value 6, refining agent: 1g/L, NaOH:1g/L, bath raio: 1:10, temperature: 80 DEG C, time: 5min；
D, Alkali reduction: after desizing refining completes, then carry out alkali decrement treatment, treatment conditions are NaOH10g/L, temperature: 100 DEG C, time: 20min；
E, sizing: after Alkali reduction completes, shape, temperature: 140 DEG C, time: 20s；
F, sanding；After sizing terminates, carry out sanding；
G, stamp: use machine of magnetic rod printing machine to carry out stamp
H, rear shaping and drying: carry out rear shaping and drying process after stamp, first carry out clear water and pad, then drying and shaping under the conditions of 140 DEG C；
I, arrangement: after drying, use and arranged by pilling fluffing resistant finishing agent, i.e. can get textile fabric on the Novel imitation cotton bed that the present invention proposes after arrangement.
Preferably, the sanding of described step F uses Buddha's warrior attendant rubber that dacron positive and negative longitude and latitude carries out mechanical grinding, forms the fine fleece less than 1mm length；
Preferably, described step I by pilling fluffing resistant finishing agent be pilling fluffing resistant finishing agent be Donghua University research and development AIP pilling fluffing resistant finishing agent, consumption is 1g/L；
Embodiment 5:
1, textile fabric on a kind of Novel imitation cotton bed, it is characterized in that, terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre is used to form, terylene height f silk, gou-tree fibre, milk fibre blending silk thread in the percentage by weight of terylene height f silk be 65%, the percentage by weight of gou-tree fibre is 15%, and the percentage by weight of milk fibre is 20%.
2, the preparation method of textile fabric on a kind of Novel imitation cotton bed, comprises the following steps:
A, weave cotton cloth: using terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre to form, Dobby Weave Design uses satin weave, then through suitable twisting, makes polyster fibre that light is produced diffuse-reflectance phenomenon, uses water-jet loom to make embryo cloth；Terylene height f silk specification is 150D/288g × 25D/72g, the weft density of described blended ratio is 210T；
B, starching, oil: embryo cloth step A prepared carries out starching and oiling treatment；
C, desizing refining: use low bath raio high-pressure injection overflow machine to carry out desizing refining process, technology preparation and condition as follows: desizing bath pH value 6, refining agent: 1.5g/L, NaOH:1g/L, bath raio: 1:10, temperature: 85 DEG C, time: 7min；
D, Alkali reduction: after desizing refining completes, then carry out alkali decrement treatment, treatment conditions are NaOH10g/L, temperature: 95 DEG C, time: 20min；
E, sizing: after Alkali reduction completes, shape, temperature: 140 DEG C, time: 25s；
F, sanding；After sizing terminates, carry out sanding；
G, stamp: use machine of magnetic rod printing machine to carry out stamp
H, rear shaping and drying: carry out rear shaping and drying process after stamp, first carry out clear water and pad, then drying and shaping under the conditions of 140 DEG C；
I, arrangement: after drying, use pilling fluffing resistant finishing agent to arrange, i.e. can get textile fabric on the Novel imitation cotton bed that the present invention proposes after arrangement.
Preferably, the sanding of described step F uses Buddha's warrior attendant rubber that dacron positive and negative longitude and latitude carries out mechanical grinding, forms the fine fleece less than 1mm length；
Preferably, described step I by pilling fluffing resistant finishing agent be pilling fluffing resistant finishing agent be Donghua University research and development AIP pilling fluffing resistant finishing agent, consumption is 1.5g/L；
Embodiment 1-5 is detected:
In upper table, the testing standard of disruptive force is GB/T3923.1-1997 " textile fabric tensile property part 1 disruptive force and the mensuration of elongation at break "
Thermal resistance and the examination criteria of dampness test in upper table are GB/T11048-2008 " thermal resistance and the mensuration of dampness under textile physiological comfort limit "
The examination criteria of the biocidal property in upper table is GB/T20944.3-2008 " the evaluation third portion of antibacterial textile performance: succusion ", uses color fastness to washing testing machine washing methods, test to wash the bacteriostasis rate of fabric after 30 times.
These detection data are just for above-mentioned detection sample.
The above; it is only the present invention preferably detailed description of the invention; but protection scope of the present invention is not limited thereto; any those familiar with the art is in the technical scope that the invention discloses; according to technical scheme and inventive concept equivalent or change in addition thereof, all should contain within protection scope of the present invention.
Claims (2)
1. the preparation method of textile fabric on a Novel imitation cotton bed, it is characterised in that comprise the following steps:
A, weave cotton cloth: using terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre to form, Dobby Weave Design uses satin weave, then through suitable twisting, makes polyster fibre that light is produced diffuse-reflectance phenomenon, uses water-jet loom to make grey cloth；
B, starching, oil: grey cloth step A prepared carries out starching and oiling treatment；
C, desizing refining: use low bath raio high-pressure injection overflow machine to carry out desizing refining process, technology preparation and condition as follows: desizing bath pH value 6～7, refining agent: 1～2g/L, NaOH:1～2g/L; bath raio: 1:10～15, temperature: 80～90 DEG C, the time: 5～15min；
D, Alkali reduction: after desizing refining completes, then carry out alkali decrement treatment, treatment conditions are NaOH 10～15g/L, temperature: 85～100 DEG C, the time: 20～35min；
E, sizing: after Alkali reduction completes, shape, temperature: 140～160 DEG C, the time: 20～30s；
F, sanding；After sizing terminates, carry out sanding；
G, stamp: use machine of magnetic rod printing machine to carry out stamp；
H, rear shaping and drying: carry out rear shaping and drying process after stamp, first carry out clear water and pad, then drying and shaping under the conditions of 140～160 DEG C；
I, arrangement: after drying, use pilling fluffing resistant finishing agent to arrange, i.e. can get textile fabric on Novel imitation cotton bed after arrangement；
Textile fabric on described Novel imitation cotton bed, terylene height f silk, gou-tree fibre, the blending silk thread weaving of milk fibre is used to form, described terylene height f silk, gou-tree fibre, milk fibre blending silk thread in the percentage by weight of terylene height f silk be 60-75%, the percentage by weight of gou-tree fibre is 10-15%, and the percentage by weight of milk fibre is 15-25%.
2. the preparation method of textile fabric on Novel imitation cotton bed as claimed in claim 1, it is characterised in that the pilling fluffing resistant finishing agent of described step I is the AIP pilling fluffing resistant finishing agent of Donghua University's research and development, and consumption is 1～5g/L.