CN110710738A - Bicycle riding suit and preparation method thereof - Google Patents
Bicycle riding suit and preparation method thereof Download PDFInfo
- Publication number
- CN110710738A CN110710738A CN201810459181.2A CN201810459181A CN110710738A CN 110710738 A CN110710738 A CN 110710738A CN 201810459181 A CN201810459181 A CN 201810459181A CN 110710738 A CN110710738 A CN 110710738A
- Authority
- CN
- China
- Prior art keywords
- ironing
- temperature
- suit
- garment
- riding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a preparation method of a bicycle riding suit, which comprises the following specific steps: a) cutting; b) sewing; c) ironing; d) and finishing, inspecting and packaging to obtain a finished product. The invention also discloses the bicycle riding suit prepared by the preparation method. The preparation method is simple and feasible, the riding suit for a wide range of people is prepared by collecting relevant parameters and characteristics of different people, and the neck of the back of the riding suit is provided with the material with special performance, so that the part is more suitable for the principle of ergonomics in the aspect of elasticity, the comfort level of riding personnel is increased, and the cervical vertebra problem of the current white collar class can be relieved and treated.
Description
Technical Field
The invention belongs to the field of bicycle riding clothes, and particularly relates to bicycle riding clothes and a preparation method thereof.
Background
With the improvement of living standard of people, people pay more and more attention to sports and health. The riding sports history is long, a large number of riding athletes and a plurality of riding enthusiasts are cultured, and the requirement for riding clothes is gradually changed from the original simplification requirement to be multifunctional. Most of the current riding clothes are designed according to the characteristics of riding enthusiasts, and special riding clothes are not designed particularly for the riding enthusiasts with cervical vertebra problems, but the riding clothes are not designed in the market at present.
Disclosure of Invention
The purpose of the invention is as follows: in view of the problems of the prior art, a first object of the invention is to provide a method for manufacturing a bicycle riding suit. The second purpose of the invention is to provide a bicycle riding suit.
The technical scheme is as follows: in order to solve the technical problems, the invention provides a preparation method of a bicycle riding suit, which comprises the following specific steps:
a) cutting: respectively cutting the cloth at a certain temperature and humidity according to the requirements of the height, the weight and the style of a rider to obtain various garment pieces;
b) sewing: respectively sewing various types of garment pieces obtained in the step a) to obtain a garment primary finished product, wherein the sewing method comprises one or more of overedges, stretch seams, lock seams and chain seams; the width of the sewn hem is 0.35cm for three threads, 0.5cm for four threads and 0.7cm for five threads;
c) ironing: when the primary finished product of the riding suit is ironed, the temperature of an iron is strictly controlled, the weight with good temperature of the iron is determined according to the type of the grey cloth and the composition of fiber raw materials, and the temperature, the pressure, the time and the steam quantity are controlled;
d) and finishing, inspecting and packaging to obtain a finished product.
Wherein the temperature in the step a) is 20-30 ℃, and the humidity is 30-40%.
The method comprises the following specific steps of c), ironing, namely aligning the sewn garment primary product to stains on the surface by using a PUT pneumatic spraying decontamination gun, wherein the spraying distance is 40 ~ mm, the caliber of a nozzle is 0.6 ~.8 mm, the rated pressure is 0.4 ~.6 Mpa, the spraying amount is 80-110 ml/min, the spraying amplitude is phi 10 ~ phi 40mm, the thread ends and dust on the surface are adhered by using a transparent adhesive tape, ironing is started, the pressure of an iron is 30-50 Mpa, the time is 1 ~ h, the steam amount is 5kw/h, the temperature is 185 ~ ℃ when the whole cotton fabric is ironed, the temperature is 150 ~ ℃ when the polyester fabric is ironed, the temperature is 170-180 ℃ when the whole cotton fabric and the polyester fabric are integrated, and ironing is finished.
Wherein, the different age groups of the step a) comprise four age groups of 20-30 years old, 30-40 years old, 40-50 years old and 50-60 years old, the different heights comprise 150-155 cm, 155-160 cm, 160-165 cm, 165-170 cm, 170-175 cm, 175-180 cm and 180-185 cm, and the different weights comprise 40-45 kg, 45-50 kg, 50-55 kg, 55-60 kg, 60-65 kg, 65-70 kg, 70-75 kg and 75-80 kg.
Wherein, the material of the garment piece in the step a) comprises one or two of all-cotton fabric and polyester fabric.
The size of the cycling clothes prepared by the preparation method is XS, M, L, XL, XXL and XXXL6 types.
Wherein, above-mentioned clothes of riding back the inside adopts the gas permeability material to make, and the outside mesh surface fabric that adopts of back, the back neck adopts the characteristic of material to be: the basis weight is 100 g/m2, the thickness is 0.8mm, the heat insulation heat is 0.7Clo, the rigidity is less than 3, the elastic modulus forward warp is 0.7, the elastic modulus return warp is 0.7, the elastic modulus forward weft is 0.7, the elastic modulus return weft is 0.6, the retardation warp is 0.2, and the retardation weft is 0.2.
Has the advantages that: compared with the prior art, the invention has the following advantages: the preparation method is simple and feasible, the riding suit for a wide range of people is prepared by collecting relevant parameters and characteristics of different people, and the back neck of the riding suit is provided with the material with special performance, so that the part is more suitable for the principle of ergonomics in the aspect of elasticity, the comfort level of a rider is increased, and the cervical vertebra problem of the existing white collar class can be relieved and treated.
Detailed Description
The present invention will be further described with reference to the following examples.
Embodiment 1. a method for preparing a bicycle riding suit, comprising the following steps:
a) cutting: respectively cutting the cloth at a certain temperature and humidity according to the requirements of the height, the weight and the style of a rider to obtain various garment pieces;
b) sewing: respectively sewing various types of garment pieces obtained in the step a) to obtain a garment primary finished product, wherein the sewing method comprises one or more of overedges, stretch seams, lock seams and chain seams; the width of the sewn hem is 0.35cm for three threads, 0.5cm for four threads and 0.7cm for five threads;
c) ironing: when the primary finished product of the riding suit is ironed, the temperature of an iron is strictly controlled, the weight with good temperature of the iron is determined according to the type of the grey cloth and the composition of fiber raw materials, and the temperature, the pressure, the time and the steam quantity are controlled;
d) and finishing, inspecting and packaging to obtain a finished product.
The temperature in step a) was 20 ℃ and the humidity was 30%.
The step c) of ironing comprises the following specific steps: aiming a sewn garment primary finished product at surface stains by using a PUT pneumatic spray decontamination gun, wherein the spray distance is 40mm, the caliber of a nozzle is 0.6mm, the rated pressure is 0.4Mpa, the spray quantity is 80ml/min, the fog amplitude is phi 10mm, thread ends and dust on the surface are stuck off by using a transparent adhesive tape, then ironing is started, the pressure of an iron is 30Mpa, the time is 1h, the steam quantity is 5kw/h, the temperature of an iron is 185 ℃ if the iron is used for ironing all-cotton fabrics, and the temperature of a polyester fabric is 150 ℃; if the fabric is the combination of the all-cotton fabric and the polyester fabric, the temperature is 170-180 ℃; the riding suit is flat.
The different age groups of the step a) comprise four age groups of 20-30 years old, 30-40 years old, 40-50 years old and 50-60 years old, the different heights comprise 150-155 cm, 155-160 cm, 160-165 cm, 165-170 cm, 170-175 cm, 175-180 cm and 180-185 cm, and the different weights comprise 40-45 kg, 45-50 kg, 50-55 kg, 55-60 kg, 60-65 kg, 65-70 kg, 70-75 kg and 75-80 kg.
The material of the garment piece in the step a) comprises all-cotton fabric. The size of the cycling clothes prepared by the preparation method is XS, M, L, XL, XXL and XXXL6 types.
The inside of the back of the riding suit is made of breathable materials, the outside of the back is made of mesh fabrics, and the neck of the back is made of materials with the characteristics that: the basis weight is 100 g/m2, the thickness is 0.8mm, the heat insulation degree is 0.7Clo, the rigidity is within 3, the elastic modulus forward warp is 0.7, the elastic modulus return warp is 0.7, the elastic modulus forward weft is 0.7, the elastic modulus return weft is 0.6, the retardation warp is 0.2, and the retardation weft is 0.2.
Embodiment 2 a method for preparing a bicycle riding suit, comprising the following steps:
a) cutting: respectively cutting the cloth at a certain temperature and humidity according to the requirements of the height, the weight and the style of a rider to obtain various garment pieces;
b) sewing: respectively sewing various types of garment pieces obtained in the step a) to obtain a garment primary finished product, wherein the sewing method comprises one or more of overedges, stretch seams, lock seams and chain seams; the width of the sewn hem is 0.35cm for three threads, 0.5cm for four threads and 0.7cm for five threads;
c) ironing: when the primary finished product of the riding suit is ironed, the temperature of an iron is strictly controlled, the weight with good temperature of the iron is determined according to the type of the grey cloth and the composition of fiber raw materials, and the temperature, the pressure, the time and the steam quantity are controlled;
d) and finishing, inspecting and packaging to obtain a finished product.
The temperature in step a) was 30 ℃ and the humidity was 40%.
The step c) of ironing comprises the following specific steps: aligning the sewed clothing primary finished product to the surface stain by using a PUT pneumatic spray decontamination gun, wherein the spray distance is 80 mm, the caliber of a nozzle is 0.8mm, the rated pressure is 0.6 Mpa, the spray quantity is 110ml/min, the fog amplitude is phi 40mm, sticking off the thread end and dust on the surface by using a transparent adhesive tape, then starting ironing, the pressure of an iron is 50Mpa, the time is 5h, the steam quantity is 5kw/h, the temperature of the whole cotton fabric is 195 ℃ if the whole cotton fabric is ironed, and the temperature of the polyester fabric is 165 ℃ if the whole cotton fabric is ironed; if the fabric is the combination of the all-cotton fabric and the polyester fabric, the temperature is 180 ℃; the riding clothes are ironed.
The different age groups of the step a) comprise four age groups of 20-30 years old, 30-40 years old, 40-50 years old and 50-60 years old, the different heights comprise 150-155 cm, 155-160 cm, 160-165 cm, 165-170 cm, 170-175 cm, 175-180 cm and 180-185 cm, and the different weights comprise 40-45 kg, 45-50 kg, 50-55 kg, 55-60 kg, 60-65 kg, 65-70 kg, 70-75 kg and 75-80 kg.
The material of the garment piece in the step a) comprises all-cotton fabric and polyester fabric.
The size of the cycling clothes prepared by the preparation method is XS, M, L, XL, XXL and XXXL6 types.
The inside of the back of the riding suit is made of breathable materials, the outside of the back is made of mesh fabrics, and the neck of the back is made of materials with the characteristics that: the basis weight is 100 g/m2, the thickness is 0.8mm, the heat insulation degree is 0.7Clo, the rigidity is within 3, the elastic modulus forward warp is 0.7, the elastic modulus return warp is 0.7, the elastic modulus forward weft is 0.7, the elastic modulus return weft is 0.6, the retardation warp is 0.2, and the retardation weft is 0.2.
Example 3: a preparation method of a bicycle riding suit comprises the following specific steps:
a) cutting: respectively cutting the cloth at a certain temperature and humidity according to the requirements of the height, the weight and the style of a rider to obtain various garment pieces;
b) sewing: respectively sewing various types of garment pieces obtained in the step a) to obtain a garment primary finished product, wherein the sewing method comprises one or more of overedges, stretch seams, lock seams and chain seams; the width of the sewn hem is 0.35cm for three threads, 0.5cm for four threads and 0.7cm for five threads;
c) ironing: when the primary finished product of the riding suit is ironed, the temperature of an iron is strictly controlled, the weight with good temperature of the iron is determined according to the type of the grey cloth and the composition of fiber raw materials, and the temperature, the pressure, the time and the steam quantity are controlled;
d) and finishing, inspecting and packaging to obtain a finished product.
The temperature in step a) was 25 ℃ and the humidity was 35%.
The step c) of ironing comprises the following specific steps: aiming a sewn garment primary finished product at surface stains by using a PUT pneumatic spray decontamination gun, wherein the spray distance is 60 mm, the caliber of a nozzle is 0.7mm, the rated pressure is 0.5Mpa, the spray quantity is 95ml/min, the fog amplitude is phi 25 mm, thread ends and dust on the surface are stuck off by using a transparent adhesive tape, then ironing is started, the pressure of an iron is 40Mpa, the time is 3h, the steam quantity is 5kw/h, the temperature of an iron is 190 ℃ if the iron is used for ironing all-cotton fabrics, and the temperature of a polyester fabric is 160 ℃; if the fabric is the combination of all-cotton fabric and polyester fabric, the temperature is 175 ℃; the riding clothes are ironed.
The different age groups of the step a) comprise four age groups of 20-30 years old, 30-40 years old, 40-50 years old and 50-60 years old, the different heights comprise 150-155 cm, 155-160 cm, 160-165 cm, 165-170 cm, 170-175 cm, 175-180 cm and 180-185 cm, and the different weights comprise 40-45 kg, 45-50 kg, 50-55 kg, 55-60 kg, 60-65 kg, 65-70 kg, 70-75 kg and 75-80 kg.
The material of the garment piece in the step a) comprises two of all-cotton fabric and polyester fabric.
The size of the cycling clothes prepared by the preparation method is XS, M, L, XL, XXL and XXXL6 types.
The inside of the back of the riding suit is made of breathable materials, the outside of the back is made of mesh fabrics, and the neck of the back is made of materials with the characteristics that: the basis weight is 100 g/m2, the thickness is 0.8mm, the heat insulation degree is 0.7Clo, the rigidity is within 3, the elastic modulus forward warp is 0.7, the elastic modulus return warp is 0.7, the elastic modulus forward weft is 0.7, the elastic modulus return weft is 0.6, the retardation warp is 0.2, and the retardation weft is 0.2.
The above description is only of the preferred embodiments of the present invention, and it should be noted that: it will be apparent to those skilled in the art that various modifications and adaptations can be made without departing from the principles of the invention and these are intended to be within the scope of the invention.
Claims (7)
1. A preparation method of bicycle riding clothes is characterized by comprising the following specific steps:
a) cutting: respectively cutting the cloth at a certain temperature and humidity according to the requirements of the height, the weight and the style of a rider to obtain various garment pieces;
b) sewing: respectively sewing various types of garment pieces obtained in the step a) to obtain a garment primary finished product, wherein the sewing method comprises one or more of overedges, stretch seams, lock seams and chain seams; the width of the sewn hem is 0.35cm for three threads, 0.5cm for four threads and 0.7cm for five threads;
c) ironing: when the primary finished product of the riding suit is ironed, the temperature of an iron is strictly controlled, the weight with good temperature of the iron is determined according to the type of grey cloth and the composition of fiber raw materials, and the temperature, the pressure, the time and the steam quantity are controlled;
d) and finishing, inspecting and packaging to obtain a finished product.
2. The method for preparing the bicycle riding suit according to claim 1, wherein the temperature in the step a) is 20-30 ℃ and the humidity is 30-40%.
3. The method for preparing the bicycle riding suit according to claim 1, wherein the step c) of ironing specifically comprises the steps of aligning a sewn primary garment product with stains on the surface by a PUT pneumatic spray decontamination gun, wherein the spray distance is 40 ~ mm, the nozzle caliber is 0.6 ~ 0.8mm, the rated pressure is 0.4 ~ 0.6 Mpa, the spray amount is 80-110 ml/min, the fog amplitude is phi 10 ~ phi 40mm, the thread ends and dust on the surface are stuck off by using a transparent adhesive tape, ironing is started, the pressure of an iron is 30-50 Mpa, the time is 1 ~ h, the steam amount is 5kw/h, the ironing temperature is 185 46195 ℃ if the ironing is carried out on a full cotton fabric, the ironing temperature is 150 59165 ℃ if the ironing is carried out on a polyester fabric, and the ironing is carried out after the riding suit is flattened.
4. The method for preparing a cycling suit according to claim 1, wherein the different age groups of step a) include four age groups of 20-30 years old, 30-40 years old, 40-50 years old and 50-60 years old, the different heights include 150-155 cm, 155-160 cm, 160-165 cm, 165-170 cm, 170-175 cm, 175-180 cm and 180-185 cm, and the different weights include 40-45 kg, 45-50 kg, 50-55 kg, 55-60 kg, 60-65 kg, 65-70 kg, 70-75 kg and 75-80 kg.
5. The method for preparing bicycle riding suit according to claim 1, wherein the material of the garment pieces in step a) comprises one or both of all-cotton fabric and polyester fabric.
6. The cycling suit prepared by the preparation method of claim 1, wherein the cycling suit has sizes of XS, M, L, XL, XXL and XXXL6 types.
7. The cycling garment according to claim 6, characterized in that the inside of the back of the cycling garment is made of breathable material, the outside of the back is made of mesh fabric, and the neck of the back is made of material with the following characteristics: the basis weight is 100 g/m2, the thickness is 0.8mm, the heat insulation degree is 0.7Clo, the rigidity is within 3, the elastic modulus forward warp is 0.7, the elastic modulus return warp is 0.7, the elastic modulus forward weft is 0.7, the elastic modulus return weft is 0.6, the retardation warp is 0.2, and the retardation weft is 0.2.