CN107401061A - A kind of high-grade anti-strike-through dark color shirt lining production technology - Google Patents
A kind of high-grade anti-strike-through dark color shirt lining production technology Download PDFInfo
- Publication number
- CN107401061A CN107401061A CN201710633993.XA CN201710633993A CN107401061A CN 107401061 A CN107401061 A CN 107401061A CN 201710633993 A CN201710633993 A CN 201710633993A CN 107401061 A CN107401061 A CN 107401061A
- Authority
- CN
- China
- Prior art keywords
- drying
- base fabric
- strike
- processing
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-grade anti-strike-through dark color shirt lining production technology, comprise the following steps：A, weave；B, singe；C, processing is padded；D, washing, drying；E, PUR primary coating；F, preliminary drying；G, PUR secondary coating；H, dry, the production technology that uses of the present invention can make shirt lining soft, smooth, while also have the advantages of good peel strength, anti-strike-through.
Description
Technical field
The present invention relates to shirt to serve as a contrast preparing technical field, is specially a kind of high-grade anti-strike-through dark color shirt lining production technology.
Background technology
Shirt is a kind of clothes being loved by consumers.Hot summer, consumer are very big to the demand of shirt, respectively
Apparel brand can release that pattern is changeable, fashionable in style all kinds of shirt products.Wherein, pure cotton shirt fabric using natural cotton fiber as
Raw material, by spinning, weaving and singe, mercerising, the process such as sizing and preshrunk be prepared, due to cotton fiber have it is soft, inhale
The performance such as wet, warming, ventilative, while the consumption concept that consumer recovers one's original simplicity also has been catered to, therefore be that in the market sale is hot
Shirt class product.Dark shirt lining complex manufacturing, efficiency are low in the prior art, and easily strike-through phenomenon occur, influence
Comfortableness.
The content of the invention
It is an object of the invention to provide a kind of high-grade anti-strike-through dark color shirt lining production technology, to solve above-mentioned background skill
The problem of being proposed in art.
To achieve the above object, the present invention provides following technical scheme：A kind of high-grade anti-strike-through dark color shirt lining production work
Skill, comprise the following steps：
A, weave：Using stretch yarn as warp thread and weft yarn, after carrying out hot wet setting processing, it is placed on loom and weaves into base fabric；
B, singe：Processing of singing is carried out to the base fabric that step A is obtained using gas singeing machine, removes the filoplume on its surface；
C, processing is padded：The base fabric that step B is obtained is carried out at an immersing and rolling technique using cold-rolling heap staining technology in staining bath
Reason, base fabric dyeing after clot be stacked in uniform rotation on A cabinet frames, with plastic sheeting encapsulate yardage roll, bank up 4-8h；
D, washing, drying：The base fabric that step C heaps are postponed afterwards uses hot water and cold water wash；Hot water temperature is 60 DEG C -80
DEG C, scavenging period 4-8min；Cold water temperature is 20 DEG C -30 DEG C, scavenging period 10min-15min；Then base fabric is used
Heated-air drying carries out drying and processing；
E, PUR primary coating：Fine powder polyamide hot and polyurethane are carried out by two point painting without powder base slurry system using cylinder
Layer forms hot melt adhesive layer, and the base fabric for then obtaining step D is sent into drying room and carries out primary coating processing；
F, preliminary drying：Drying room preliminary drying temperature is 130 DEG C -150 DEG C, time 3-5min, after preliminary drying terminates, takes out cooling；
G, PUR secondary coating：Pre-baked base fabric is fed again into drying room afterwards and carries out secondary coating；
H, dry：Drying room preliminary drying temperature is 160 DEG C -180 DEG C, time 5-10min, after drying terminates, takes out slow cooling extremely
Room temperature；Obtain shirt lining.
Preferably, in the step B, speed of singing is 50m/min -60m/min, and number of singing is a positive and a negative, flame
Intensity is 5-10mbar.
Preferably, primer layer is used as without powder base slurry using polyurethane in the step E, using polyamide hot as face
Glue-line, the mesh number of the cylinder is CP40, and the aperture of cylinder is 0.4mm, and the thickness of cylinder is 0.2mm.
Preferably, the temperature of heated-air drying is 70 DEG C -80 DEG C in the step D.
Compared with prior art, the beneficial effects of the invention are as follows：The production technology that the present invention uses can make shirt lining soft
Soft, smooth, present invention combination is singed, padded, washing, PUR coating treatment, obtained hand of the shirt lining with soft comfortable
Sense, and its elasticity is high, flexibility is good, and rate of change is small after washing, in addition, using secondary PUR coating treatment, Neng Gouti
Its high peel strength and anti-strike-through effect.
Brief description of the drawings
Fig. 1 is present invention process flow chart.
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other under the premise of creative work is not made
Embodiment, belong to the scope of protection of the invention.
Embodiment one：
Referring to Fig. 1, a kind of high-grade anti-strike-through dark color shirt lining production technology, comprises the following steps：
A, weave：Using stretch yarn as warp thread and weft yarn, after carrying out hot wet setting processing, it is placed on loom and weaves into base fabric；
B, singe：Processing of singing is carried out to the base fabric that step A is obtained using gas singeing machine, removes the filoplume on its surface；
C, processing is padded：The base fabric that step B is obtained is carried out at an immersing and rolling technique using cold-rolling heap staining technology in staining bath
Reason, base fabric dyeing after clot be stacked in uniform rotation on A cabinet frames, with plastic sheeting encapsulate yardage roll, bank up 4h；
D, washing, drying：The base fabric that step C heaps are postponed afterwards uses hot water and cold water wash；Hot water temperature is 60 DEG C, cleaning
Time is 4min；Cold water temperature is 20 DEG C, scavenging period 10min；Base fabric is then subjected to drying and processing using heated-air drying；
E, PUR primary coating：Fine powder polyamide hot and polyurethane are carried out by two point painting without powder base slurry system using cylinder
Layer forms hot melt adhesive layer, and the base fabric for then obtaining step D is sent into drying room and carries out primary coating processing；
F, preliminary drying：Drying room preliminary drying temperature is 130 DEG C, time 3min, after preliminary drying terminates, takes out cooling；
G, PUR secondary coating：Pre-baked base fabric is fed again into drying room afterwards and carries out secondary coating；
H, dry：Drying room preliminary drying temperature is 160 DEG C, time 5min, after drying terminates, takes out slow cooling to room temperature；Produce
Served as a contrast to shirt.
In the present embodiment, in step B, speed of singing is 50m/min, and number of singing is a positive and a negative, and flame intensity is
5mbar。
In the present embodiment, primer layer is used as without powder base slurry using polyurethane in step E, using polyamide hot as face
Glue-line, the mesh number of the cylinder is CP40, and the aperture of cylinder is 0.4mm, and the thickness of cylinder is 0.2mm.
In the present embodiment, the temperature of heated-air drying is 70 DEG C in step D.
Embodiment two：
A kind of high-grade anti-strike-through dark color shirt lining production technology, comprises the following steps：
A, weave：Using stretch yarn as warp thread and weft yarn, after carrying out hot wet setting processing, it is placed on loom and weaves into base fabric；
B, singe：Processing of singing is carried out to the base fabric that step A is obtained using gas singeing machine, removes the filoplume on its surface；
C, processing is padded：The base fabric that step B is obtained is carried out at an immersing and rolling technique using cold-rolling heap staining technology in staining bath
Reason, base fabric dyeing after clot be stacked in uniform rotation on A cabinet frames, with plastic sheeting encapsulate yardage roll, bank up 8h；
D, washing, drying：The base fabric that step C heaps are postponed afterwards uses hot water and cold water wash；Hot water temperature is 80 DEG C, cleaning
Time is 8min；Cold water temperature is 30 DEG C, scavenging period 15min；Base fabric is then subjected to drying and processing using heated-air drying；
E, PUR primary coating：Fine powder polyamide hot and polyurethane are carried out by two point painting without powder base slurry system using cylinder
Layer forms hot melt adhesive layer, and the base fabric for then obtaining step D is sent into drying room and carries out primary coating processing；
F, preliminary drying：Drying room preliminary drying temperature is 150 DEG C, time 5min, after preliminary drying terminates, takes out cooling；
G, PUR secondary coating：Pre-baked base fabric is fed again into drying room afterwards and carries out secondary coating；
H, dry：Drying room preliminary drying temperature is 180 DEG C, time 10min, after drying terminates, takes out slow cooling to room temperature；Produce
Served as a contrast to shirt.
In the present embodiment, in step B, speed of singing is 60m/min, and number of singing is a positive and a negative, and flame intensity is
10mbar。
In the present embodiment, primer layer is used as without powder base slurry using polyurethane in step E, using polyamide hot as face
Glue-line, the mesh number of the cylinder is CP40, and the aperture of cylinder is 0.4mm, and the thickness of cylinder is 0.2mm.
In the present embodiment, the temperature of heated-air drying is 80 DEG C in step D.
Embodiment three：
A kind of high-grade anti-strike-through dark color shirt lining production technology, comprises the following steps：
A, weave：Using stretch yarn as warp thread and weft yarn, after carrying out hot wet setting processing, it is placed on loom and weaves into base fabric；
B, singe：Processing of singing is carried out to the base fabric that step A is obtained using gas singeing machine, removes the filoplume on its surface；
C, processing is padded：The base fabric that step B is obtained is carried out at an immersing and rolling technique using cold-rolling heap staining technology in staining bath
Reason, base fabric dyeing after clot be stacked in uniform rotation on A cabinet frames, with plastic sheeting encapsulate yardage roll, bank up 5h；
D, washing, drying：The base fabric that step C heaps are postponed afterwards uses hot water and cold water wash；Hot water temperature is 65 DEG C, cleaning
Time is 5min；Cold water temperature is 22 DEG C, scavenging period 11min；Base fabric is then subjected to drying and processing using heated-air drying；
E, PUR primary coating：Fine powder polyamide hot and polyurethane are carried out by two point painting without powder base slurry system using cylinder
Layer forms hot melt adhesive layer, and the base fabric for then obtaining step D is sent into drying room and carries out primary coating processing；
F, preliminary drying：Drying room preliminary drying temperature is 135 DEG C, time 4min, after preliminary drying terminates, takes out cooling；
G, PUR secondary coating：Pre-baked base fabric is fed again into drying room afterwards and carries out secondary coating；
H, dry：Drying room preliminary drying temperature is 165 DEG C, time 6min, after drying terminates, takes out slow cooling to room temperature；Produce
Served as a contrast to shirt.
In the present embodiment, in step B, speed of singing is 52m/min, and number of singing is a positive and a negative, and flame intensity is
6mbar。
In the present embodiment, primer layer is used as without powder base slurry using polyurethane in step E, using polyamide hot as face
Glue-line, the mesh number of the cylinder is CP40, and the aperture of cylinder is 0.4mm, and the thickness of cylinder is 0.2mm.
In the present embodiment, the temperature of heated-air drying is 72 DEG C in step D.
Example IV：
A kind of high-grade anti-strike-through dark color shirt lining production technology, comprises the following steps：
A, weave：Using stretch yarn as warp thread and weft yarn, after carrying out hot wet setting processing, it is placed on loom and weaves into base fabric；
B, singe：Processing of singing is carried out to the base fabric that step A is obtained using gas singeing machine, removes the filoplume on its surface；
C, processing is padded：The base fabric that step B is obtained is carried out at an immersing and rolling technique using cold-rolling heap staining technology in staining bath
Reason, base fabric dyeing after clot be stacked in uniform rotation on A cabinet frames, with plastic sheeting encapsulate yardage roll, bank up 7h；
D, washing, drying：The base fabric that step C heaps are postponed afterwards uses hot water and cold water wash；Hot water temperature is 75 DEG C, cleaning
Time is 7min；Cold water temperature is 28 DEG C, scavenging period 14min；Base fabric is then subjected to drying and processing using heated-air drying；
E, PUR primary coating：Fine powder polyamide hot and polyurethane are carried out by two point painting without powder base slurry system using cylinder
Layer forms hot melt adhesive layer, and the base fabric for then obtaining step D is sent into drying room and carries out primary coating processing；
F, preliminary drying：Drying room preliminary drying temperature is 145 DEG C, time 4min, after preliminary drying terminates, takes out cooling；
G, PUR secondary coating：Pre-baked base fabric is fed again into drying room afterwards and carries out secondary coating；
H, dry：Drying room preliminary drying temperature is 175 DEG C, time 9min, after drying terminates, takes out slow cooling to room temperature；Produce
Served as a contrast to shirt.
In the present embodiment, in step B, speed of singing is 58m/min, and number of singing is a positive and a negative, and flame intensity is
9mbar。
In the present embodiment, primer layer is used as without powder base slurry using polyurethane in step E, using polyamide hot as face
Glue-line, the mesh number of the cylinder is CP40, and the aperture of cylinder is 0.4mm, and the thickness of cylinder is 0.2mm.
In the present embodiment, the temperature of heated-air drying is 78 DEG C in step D.
Embodiment five：
A kind of high-grade anti-strike-through dark color shirt lining production technology, comprises the following steps：
A, weave：Using stretch yarn as warp thread and weft yarn, after carrying out hot wet setting processing, it is placed on loom and weaves into base fabric；
B, singe：Processing of singing is carried out to the base fabric that step A is obtained using gas singeing machine, removes the filoplume on its surface；
C, processing is padded：The base fabric that step B is obtained is carried out at an immersing and rolling technique using cold-rolling heap staining technology in staining bath
Reason, base fabric dyeing after clot be stacked in uniform rotation on A cabinet frames, with plastic sheeting encapsulate yardage roll, bank up 5h；
D, washing, drying：The base fabric that step C heaps are postponed afterwards uses hot water and cold water wash；Hot water temperature is 72 DEG C, cleaning
Time is 5min；Cold water temperature is 26 DEG C, scavenging period 11min；Base fabric is then subjected to drying and processing using heated-air drying；
E, PUR primary coating：Fine powder polyamide hot and polyurethane are carried out by two point painting without powder base slurry system using cylinder
Layer forms hot melt adhesive layer, and the base fabric for then obtaining step D is sent into drying room and carries out primary coating processing；
F, preliminary drying：Drying room preliminary drying temperature is 138 DEG C, time 3min, after preliminary drying terminates, takes out cooling；
G, PUR secondary coating：Pre-baked base fabric is fed again into drying room afterwards and carries out secondary coating；
H, dry：Drying room preliminary drying temperature is 172 DEG C, time 9min, after drying terminates, takes out slow cooling to room temperature；Produce
Served as a contrast to shirt.
In the present embodiment, in step B, speed of singing is 54m/min, and number of singing is a positive and a negative, and flame intensity is
7mbar。
In the present embodiment, primer layer is used as without powder base slurry using polyurethane in step E, using polyamide hot as face
Glue-line, the mesh number of the cylinder is CP40, and the aperture of cylinder is 0.4mm, and the thickness of cylinder is 0.2mm.
In the present embodiment, the temperature of heated-air drying is 76 DEG C in step D.
Embodiment six：
A kind of high-grade anti-strike-through dark color shirt lining production technology, comprises the following steps：
A, weave：Using stretch yarn as warp thread and weft yarn, after carrying out hot wet setting processing, it is placed on loom and weaves into base fabric；
B, singe：Processing of singing is carried out to the base fabric that step A is obtained using gas singeing machine, removes the filoplume on its surface；
C, processing is padded：The base fabric that step B is obtained is carried out at an immersing and rolling technique using cold-rolling heap staining technology in staining bath
Reason, base fabric dyeing after clot be stacked in uniform rotation on A cabinet frames, with plastic sheeting encapsulate yardage roll, bank up 6h；
D, washing, drying：The base fabric that step C heaps are postponed afterwards uses hot water and cold water wash；Hot water temperature is 70 DEG C, cleaning
Time is 6min；Cold water temperature is 25 DEG C, scavenging period 12min；Base fabric is then subjected to drying and processing using heated-air drying；
E, PUR primary coating：Fine powder polyamide hot and polyurethane are carried out by two point painting without powder base slurry system using cylinder
Layer forms hot melt adhesive layer, and the base fabric for then obtaining step D is sent into drying room and carries out primary coating processing；
F, preliminary drying：Drying room preliminary drying temperature is 140 DEG C, time 4min, after preliminary drying terminates, takes out cooling；
G, PUR secondary coating：Pre-baked base fabric is fed again into drying room afterwards and carries out secondary coating；
H, dry：Drying room preliminary drying temperature is 170 DEG C, time 7min, after drying terminates, takes out slow cooling to room temperature；Produce
Served as a contrast to shirt.
In the present embodiment, in step B, speed of singing is 55m/min, and number of singing is a positive and a negative, and flame intensity is
8mbar。
In the present embodiment, primer layer is used as without powder base slurry using polyurethane in step E, using polyamide hot as face
Glue-line, the mesh number of the cylinder is CP40, and the aperture of cylinder is 0.4mm, and the thickness of cylinder is 0.2mm.
In the present embodiment, the temperature of heated-air drying is 75 DEG C in step D.
The production technology that the present invention uses can make shirt lining soft, smooth, and the present invention, which combines, to singe, pads, washing, be hot
Melten gel coating treatment, obtained feel of the shirt lining with soft comfortable, and also its elasticity is high, flexibility is good, and become after washing
Rate is small, in addition, using secondary PUR coating treatment, it is possible to increase its peel strength and anti-strike-through effect.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (4)
- A kind of 1. high-grade anti-strike-through dark color shirt lining production technology, it is characterised in that：Comprise the following steps：A, weave：Using stretch yarn as warp thread and weft yarn, after carrying out hot wet setting processing, it is placed on loom and weaves into base fabric；B, singe：Processing of singing is carried out to the base fabric that step A is obtained using gas singeing machine, removes the filoplume on its surface；C, processing is padded：The base fabric that step B is obtained is carried out at an immersing and rolling technique using cold-rolling heap staining technology in staining bath Reason, base fabric dyeing after clot be stacked in uniform rotation on A cabinet frames, with plastic sheeting encapsulate yardage roll, bank up 4-8h；D, washing, drying：The base fabric that step C heaps are postponed afterwards uses hot water and cold water wash；Hot water temperature is 60 DEG C -80 DEG C, scavenging period 4-8min；Cold water temperature is 20 DEG C -30 DEG C, scavenging period 10min-15min；Then base fabric is used Heated-air drying carries out drying and processing；E, PUR primary coating：Fine powder polyamide hot and polyurethane are carried out by two point painting without powder base slurry system using cylinder Layer forms hot melt adhesive layer, and the base fabric for then obtaining step D is sent into drying room and carries out primary coating processing；F, preliminary drying：Drying room preliminary drying temperature is 130 DEG C -150 DEG C, time 3-5min, after preliminary drying terminates, takes out cooling；G, PUR secondary coating：Pre-baked base fabric is fed again into drying room afterwards and carries out secondary coating；H, dry：Drying room preliminary drying temperature is 160 DEG C -180 DEG C, time 5-10min, after drying terminates, takes out slow cooling extremely Room temperature；Obtain shirt lining.
- A kind of 2. high-grade anti-strike-through dark color shirt lining production technology according to claim 1, it is characterised in that：The step In B, speed of singing is 50m/min -60m/min, and number of singing is a positive and a negative, flame intensity 5-10mbar.
- A kind of 3. high-grade anti-strike-through dark color shirt lining production technology according to claim 1, it is characterised in that：The step Primer layer is used as without powder base slurry using polyurethane in E, is as face glue-line, the mesh number of the cylinder using polyamide hot CP40, the aperture of cylinder is 0.4mm, and the thickness of cylinder is 0.2mm.
- A kind of 4. high-grade anti-strike-through dark color shirt lining production technology according to claim 1, it is characterised in that：The step The temperature of heated-air drying is 70 DEG C -80 DEG C in D.