CN110699836A - High-density textile fabric and preparation method thereof - Google Patents
High-density textile fabric and preparation method thereof Download PDFInfo
- Publication number
- CN110699836A CN110699836A CN201911103094.4A CN201911103094A CN110699836A CN 110699836 A CN110699836 A CN 110699836A CN 201911103094 A CN201911103094 A CN 201911103094A CN 110699836 A CN110699836 A CN 110699836A
- Authority
- CN
- China
- Prior art keywords
- cotton
- soaking
- fiber
- textile fabric
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-density textile fabric and a preparation method thereof. According to the invention, firstly, primary soaking and secondary soaking are adopted, the cotton fiber and the cotton yarn have higher moisture absorption and sweat releasing functions through the primary soaking, the cotton fiber, the cotton yarn and the silver ion fiber have stronger mite removing functions through the secondary soaking, the generation of mites is avoided, the wearing of a user is influenced, meanwhile, the cotton fiber and the cotton yarn start to be soaked once and soaked twice before spinning, compared with the traditional soaking after spinning, the gap between the cotton fiber and the cotton yarn is larger, the penetration of liquid medicine is facilitated, the soaking efficiency is greatly improved, the soaking effect is improved, and the moisture absorption and sweat releasing functions and the mite removing functions are improved.
Description
Technical Field
The invention relates to the technical field of textile fabric production and processing, in particular to a high-density textile fabric and a preparation method thereof.
Background
The textile fabric is also called textile fabric or knitted fabric, and is divided into two types according to a weaving method, namely weft knitting knitted fabric and warp knitting knitted fabric, wherein the weft knitting knitted fabric is usually formed by taking low-elasticity polyester yarns or special-shaped polyester yarns, nylon yarns, cotton yarns, wool yarns and the like as raw materials and adopting plain stitch, variable plain stitch, rib plain stitch, double rib plain stitch, jacquard weave, terry weave and the like to be knitted on various weft knitting machines.
The traditional textile fabric has less additional functions except for the functions of keeping warm and decorating, and is particularly a knitted fabric applied to the field of underwear production, because underwear is mostly underwear, the density of the underwear is usually higher than that of a common fabric during weaving, but the air permeability of the underwear is poor along with the increase of the density, in order to improve the air permeability, the underwear is usually made of pure cotton fabric, but the pure cotton fabric still needs to be soaked by a moisture absorption and sweat releasing auxiliary agent, so that the better moisture absorption and sweat releasing functions are achieved, but the traditional soaking mode is soaking after weaving, the fabric is formed at the moment, fibers are compact, liquid medicine is inconvenient to permeate, the soaking efficiency is lower, meanwhile, although antibacterial fabric appears at the present stage, the antibacterial fabric has great defects in the aspect of mite removal, and mites are one of the chief causes of damaging the skin, therefore, the manufacturing of the high-density knitted fabric which has good air permeability and is antibacterial and acarid-removing is particularly important.
Disclosure of Invention
The invention aims to solve the defects in the prior art and provides a high-density textile fabric and a preparation method thereof.
In order to achieve the purpose, the invention adopts the following technical scheme: the high-density textile fabric comprises raw material preparation and blending, wherein the raw material preparation is carried out after the raw material preparation is finished, edge sealing is carried out after the blending is finished, thread ends are removed after the edge sealing is finished, and the thread ends are put in storage after the thread ends are removed.
As a further description of the above technical solution:
the raw material preparation comprises the following steps:
(1) preparing materials: preparing 4 parts of cotton fiber, 4 parts of cotton yarn and 2 parts of silver ion fiber, and preparing and storing the cotton fiber, the cotton yarn and the silver ion fiber in a classified manner according to the weight;
(2) manufacturing a moisture absorption and sweat releasing auxiliary agent during material preparation;
(3) putting the cotton fiber and the cotton yarn into a moisture absorption and sweat releasing auxiliary agent for primary soaking;
(4) the mite removing agent is prepared during primary soaking;
(5) taking the once soaked cotton fiber and cotton yarn out of the moisture absorption and sweat releasing auxiliary agent for primary spin-drying;
(6) putting the cotton fibers and the cotton yarns which are subjected to primary spin-drying and the silver ion fibers into a mite removing agent for secondary soaking;
(7) the cotton fiber and the cotton yarn after the secondary soaking and the silver ion fiber are taken out from the mite removing agent for secondary spin-drying;
(8) and drying the twice dried cotton fibers, cotton yarns and silver ion fibers to finish the preparation of the raw materials.
As a further description of the above technical solution:
the moisture absorption and sweat releasing auxiliary agent comprises the following manufacturing processes:
(1) putting a small amount of FERAN ICE-C type moisture absorption and sweat releasing finishing agent into purified water, wherein the proportion is 1: 50-3: 50, preparing a mixed solution;
(2) adding acetic acid into the mixed solution, and adjusting the pH value of the mixed solution to 4.5-5.0;
(3) the mixture was heated to 50-70 ℃.
As a further description of the above technical solution:
the primary soaking time is not less than 20 minutes.
As a further description of the above technical solution:
the preparation process of the mite removing agent is as follows:
(1) adding citronella oil into warm water at a ratio of 1:50, wherein the water temperature is between 45-50 ℃ to prepare a solution;
(2) adding acetic acid into the solution to adjust the pH value of the solution to 4.0-5.0.
As a further description of the above technical solution:
the secondary soaking time is not less than 1 hour.
As a further description of the above technical solution:
the wire density was 2 wires per square meter.
In the invention, firstly, the first soaking and the second soaking are adopted, the first soaking enables the cotton fiber and the cotton yarn to have higher moisture absorption and sweat releasing functions, the second soaking enables the cotton fiber, the cotton yarn and the silver ion fiber to have stronger mite removing functions, the generation of mites is avoided, the wearing of a user is influenced, meanwhile, the first soaking and the second soaking of the cotton fiber and the cotton yarn are started before the spinning, compared with the traditional soaking after the spinning, the gap between the cotton fiber and the cotton yarn is larger, the penetration of liquid medicine is convenient, the soaking efficiency is greatly improved, the soaking effect is improved, the moisture absorption and sweat releasing functions and the mite removing functions are improved, secondly, the metal wire and the silver ion fiber are adopted, the metal wire and the silver ion fiber are blended with the cotton fiber and the cotton yarn, the metal wire can eliminate static electricity, the trouble of a wearer caused by the larger static electricity in winter is avoided, meanwhile, the silver ion fiber has the sterilization and deodorization effects, the device is not easy, the skin of the user is protected, and the wearing is safer.
Drawings
FIG. 1 is a flow chart of a high density textile fabric and method of making the same according to the present invention;
FIG. 2 is a flow chart of the feedstock preparation process of the present invention.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments.
In a first embodiment, referring to fig. 1-2, a high-density textile fabric and a method for manufacturing the same include raw material preparation and blending, where the raw material preparation is followed by blending, the blending is followed by edge sealing, the blending is performed at 300T to ensure textile density, the edge sealing is followed by thread end removal, the thread end removal is followed by warehousing, and for conventional operations, no redundant description is provided here, where the raw material preparation includes the following steps:
(1) preparing materials: 4 parts of cotton fiber, 4 parts of cotton yarn and 2 parts of silver ion fiber are prepared, so that the device is mainly made of cotton materials, is more comfortable to wear, is prepared according to weight and is stored in a classified mode, and is convenient for workers to take;
(2) the moisture absorption and sweat releasing auxiliary agent is manufactured during material preparation, so that the time is saved;
(3) placing the cotton fiber and the cotton yarn into the moisture absorption and sweat releasing auxiliary agent for primary soaking, and stirring while soaking to accelerate the flow of the liquid medicine and prevent the liquid medicine from precipitating;
(4) the mite removing agent is prepared during primary soaking, so that the time is saved, and the working efficiency is improved;
(5) the cotton fiber and the cotton yarn which are soaked for one time are taken out from the moisture absorption and sweat releasing auxiliary agent for one-time spin-drying, so that the moisture absorption and sweat releasing auxiliary agent is prevented from interfering the later-stage medicament to play a role;
(6) the cotton fiber and the cotton yarn which are subjected to primary spin-drying and the silver ion fiber are put into a mite removing agent for secondary soaking, so that effective molecules of the mite removing agent can enter the cotton fiber, the cotton yarn and the silver ion fiber, and the cotton fiber, the cotton yarn and the silver ion fiber have a mite removing function;
(7) the cotton fiber and the cotton yarn after the secondary soaking and the silver ion fiber are taken out from the mite removing agent for secondary spin-drying;
(8) drying the twice spun cotton fibers, cotton yarns and silver ion fibers to shape the product, and finishing the preparation of the raw materials, wherein the moisture absorption and sweat releasing auxiliary agent is prepared in the following manufacturing process:
(1) putting a small amount of FERAN ICE-C type moisture absorption and sweat releasing finishing agent into purified water, wherein the proportion is 1: 50-3: 50, preparing a mixed solution;
(2) adding acetic acid into the mixed solution, and adjusting the pH value of the mixed solution to 4.5-5.0, wherein the mite removing agent is prepared by the following steps:
(1) adding citronella oil into warm water at a ratio of 1:50, wherein the water temperature is between 45-50 ℃ to prepare a solution;
(2) adding acetic acid into the solution to adjust pH to 4.0-5.0, and increasing citronella oil concentration by staff according to actual conditions to ensure mite removing effect
In the second embodiment, referring to fig. 1-2, the first soaking time is not less than 20 minutes to ensure the permeation effect, and the second soaking time is not less than 1 hour, the citronella oil contains a large amount of citronellol and citronellal, which are extracted from natural Chinese herbal medicines, the side effects are low, the drug effect is durable, the density of metal wires is 2 wires per square meter, the wearer can be prevented from feeling foreign body sensation, and the diameter of the metal wires is the same as that of the silver ion fibers.
The working principle is as follows: the secondary soaks makes cotton lun, cotton yarn and silver ion fibre have stronger mite function of removing, avoid breeding the mite, influence the user and dress, and simultaneously, cotton lun and cotton yarn begin once to soak and the secondary soaks before the weaving, soak after weaving for traditional, the clearance is great between cotton lun and the cotton yarn, make things convenient for the liquid medicine infiltration, thereby great improvement soak efficiency, the soaking effect has been promoted, thereby moisture absorption sweat releasing function and mite function have been improved, secondly, wire and silver ion fibre have been adopted, wire and silver ion fibre and cotton lun and cotton yarn blending, the wire can eliminate static, avoid the great vexation that brings for the wearer of static in winter, and simultaneously, silver ion fibre has the deodorant effect of disinfecting, make this device be difficult to breed the bacterium, user's skin has been protected, it is safer to dress.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.
Claims (7)
1. The high-density textile fabric and the preparation method thereof comprise raw material preparation and blending and are characterized in that the raw material preparation is performed with blending, edge sealing is performed after the blending is completed, thread removing is performed after the edge sealing is completed, and the thread removing is performed with warehousing after the thread removing is completed.
2. A high density textile fabric and method of making the same as claimed in claim 1 wherein said raw material preparation is divided into the following steps:
(1) preparing materials: preparing 4 parts of cotton fiber, 4 parts of cotton yarn and 2 parts of silver ion fiber, and preparing and storing the cotton fiber, the cotton yarn and the silver ion fiber in a classified manner according to the weight;
(2) manufacturing a moisture absorption and sweat releasing auxiliary agent during material preparation;
(3) putting the cotton fiber and the cotton yarn into a moisture absorption and sweat releasing auxiliary agent for primary soaking;
(4) the mite removing agent is prepared during primary soaking;
(5) taking the once soaked cotton fiber and cotton yarn out of the moisture absorption and sweat releasing auxiliary agent for primary spin-drying;
(6) putting the cotton fibers and the cotton yarns which are subjected to primary spin-drying and the silver ion fibers into a mite removing agent for secondary soaking;
(7) the cotton fiber and the cotton yarn after the secondary soaking and the silver ion fiber are taken out from the mite removing agent for secondary spin-drying;
(8) and drying the twice dried cotton fibers, cotton yarns and silver ion fibers to finish the preparation of the raw materials.
3. The high-density textile fabric and the preparation method thereof according to claim 2, wherein the moisture-absorbing and sweat-releasing auxiliary agent is prepared by the following steps:
(1) putting a small amount of FERAN ICE-C type moisture absorption and sweat releasing finishing agent into purified water, wherein the proportion is 1: 50-3: 50, preparing a mixed solution;
(2) adding acetic acid into the mixed solution, and adjusting the pH value of the mixed solution to 4.5-5.0;
(3) the mixture was heated to 50-70 ℃.
4. A high density textile fabric and method of making the same as recited in claim 2 wherein said one time soaking time is not less than 20 minutes.
5. The high-density textile fabric and the preparation method thereof according to claim 1, wherein the mite removing agent is prepared by the following steps:
(1) adding citronella oil into warm water at a ratio of 1:50, wherein the water temperature is between 45-50 ℃ to prepare a solution;
(2) adding acetic acid into the solution to adjust the pH value of the solution to 4.0-5.0.
6. A high density textile fabric and method of making the same as in claim 1 wherein said secondary soaking time is not less than 1 hour.
7. A high density textile fabric and method of making same as claimed in claim 1 wherein said density of metal filaments is 2 filaments per square meter.