CN110683806A - 一种室内建筑板材 - Google Patents
一种室内建筑板材 Download PDFInfo
- Publication number
- CN110683806A CN110683806A CN201810738835.5A CN201810738835A CN110683806A CN 110683806 A CN110683806 A CN 110683806A CN 201810738835 A CN201810738835 A CN 201810738835A CN 110683806 A CN110683806 A CN 110683806A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- building board
- calcium carbonate
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种室内建筑板材，其由上下两层和中间层组成的复合板，所述中间层为海绵层，所述上下层由以下重量份数组分组成：水泥35‑60份；环氧树脂15‑25份；碳酸钙5‑10份；滑石粉5‑10份；纳米二氧化钛4‑8份；氧化锌2‑7份；氧化锆2‑7份；增稠剂3‑5份；水30‑60份。本发明所制备板材具有优异的隔音性能，能够有效阻隔外界噪音向室内传播，因而能够提高室内装修档次，特别适合商圈建筑室内装修。
Description
技术领域
本发明涉及建筑领域，尤其涉及一种室内建筑板材。
背景技术
目前，室内建筑板材主要研究方向在环保和装饰效果上，而目前室内用建筑板材的隔音性能确并没有研究，且市面上的室内用板材普遍隔音效果较差。
因此，现有技术还有待于改进和发展。
发明内容
鉴于上述现有技术的不足，本发明的目的在于提供一种室内建筑板材，旨在室内建筑板材隔音性能差的问题。
本发明的技术方案如下：
一种室内建筑板材，其中，由上下两层和中间层组成的复合板，所述中间层为海绵层，所述上下层由以下重量份数组分组成：
水泥 35-60份；
环氧树脂 15-25份；
碳酸钙5-10份；
滑石粉5-10份；
纳米二氧化钛4-8份；
氧化锌2-7份；
氧化锆2-7份；
增稠剂3-5份；
水30-60份。
所述的室内建筑板材，其中，所述碳酸钙和滑石粉的添加比例为1:1。
所述的室内建筑板材，其中，所述氧化锌和氧化锆的添加比例为1:1。
所述的室内建筑板材，其中，所述增稠剂由环己烷，烷基乙烯基聚乙二醇醚，聚乙烯醇，聚四氟乙烯，丙烯酰氧乙基三甲基氯化铵中的一种或多种组成。
所述的室内建筑板材，其中，所述上下层由以下重量份数组分组成：
水泥 50份；
环氧树脂 20份；
碳酸钙8份；
滑石粉8份；
纳米二氧化钛6份；
氧化锌5份；
氧化锆5份；
增稠剂4份；
水50份。
有益效果：本发明所制备板材具有优异的隔音性能，能够有效阻隔外界噪音向室内传播，因而能够提高室内装修档次，特别适合商圈建筑室内装修。
具体实施方式
本发明提供一种室内建筑板材，为使本发明的目的、技术方案及效果更加清楚、明确，以下对本发明进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
本发明提供了一种室内建筑板材，其中，由上下两层和中间层组成的复合板，所述中间层为海绵层，所述上下层由以下重量份数组分组成：
水泥 35-60份；
环氧树脂 15-25份；
碳酸钙5-10份；
滑石粉5-10份；
纳米二氧化钛4-8份；
氧化锌2-7份；
氧化锆2-7份；
增稠剂3-5份；
水30-60份。
较佳的是，所述碳酸钙和滑石粉的添加比例为1:1。
进一步的，所述氧化锌和氧化锆的添加比例为1:1。
具体的，所述增稠剂由环己烷，烷基乙烯基聚乙二醇醚，聚乙烯醇，聚四氟乙烯，丙烯酰氧乙基三甲基氯化铵中的一种或多种组成。
优选实施例中所述的室内建筑板材的上下层由以下重量份数组分组成：
水泥 50份；
环氧树脂 20份；
碳酸钙8份；
滑石粉8份；
纳米二氧化钛6份；
氧化锌5份；
氧化锆5份；
增稠剂4份；
水50份。
本发明所制备板材具有优异的隔音性能，能够有效阻隔外界噪音向室内传播，因而能够提高室内装修档次，特别适合商圈建筑室内装修。
应当理解的是，本发明的应用不限于上述的举例，对本领域普通技术人员来说，可以根据上述说明加以改进或变换，所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (5)
1.一种室内建筑板材，其特征在于，由上下两层和中间层组成的复合板，所述中间层为海绵层，所述上下层由以下重量份数组分组成：
水泥 35-60份；
环氧树脂 15-25份；
碳酸钙5-10份；
滑石粉5-10份；
纳米二氧化钛4-8份；
氧化锌2-7份；
氧化锆2-7份；
增稠剂3-5份；
水30-60份。
2.根据权利要求1所述的室内建筑板材，其特征在于，所述碳酸钙和滑石粉的添加比例为1:1。
3.根据权利要求1所述的室内建筑板材，其特征在于，所述氧化锌和氧化锆的添加比例为1:1。
4.根据权利要求1所述的室内建筑板材，其特征在于，所述增稠剂由环己烷，烷基乙烯基聚乙二醇醚，聚乙烯醇，聚四氟乙烯，丙烯酰氧乙基三甲基氯化铵中的一种或多种组成。
5.根据权利要求1所述的室内建筑板材，其特征在于，所述上下层由以下重量份数组分组成：
水泥 50份；
环氧树脂 20份；
碳酸钙8份；
滑石粉8份；
纳米二氧化钛6份；
氧化锌5份；
氧化锆5份；
增稠剂4份；
水50份。