CN110643915A - 一种具有净化功能的热镀专用锌 - Google Patents

一种具有净化功能的热镀专用锌 Download PDF

Info

Publication number
CN110643915A
CN110643915A CN201810675244.8A CN201810675244A CN110643915A CN 110643915 A CN110643915 A CN 110643915A CN 201810675244 A CN201810675244 A CN 201810675244A CN 110643915 A CN110643915 A CN 110643915A
Authority
CN
China
Prior art keywords
zinc
percent
galvanizing
production
purification function
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810675244.8A
Other languages
English (en)
Inventor
梁志强
李海良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cannon Environmental Technology (kunshan) Co Ltd
Original Assignee
Cannon Environmental Technology (kunshan) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cannon Environmental Technology (kunshan) Co Ltd filed Critical Cannon Environmental Technology (kunshan) Co Ltd
Priority to CN201810675244.8A priority Critical patent/CN110643915A/zh
Publication of CN110643915A publication Critical patent/CN110643915A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种具有净化功能的热镀专用锌,是以锌锭为基准,其中添加0.001%~1.00%混合稀土(La‑Ce)、0.001%~2.00%锡(Sn)、0.001%~1.00%铋(Bi)、0.12%镍(Ni)中的至少两种,其余为锌锭所带的固有杂质。本发明锌锭中所添加的金属元素,能够优先与镀锌液中产生的非金属反应而排出,其有益效果在于:1、阻止了非金属与锌的反应,减少了锌耗,提高了流动性,保证了镀锌质量降低了成本。2、解决了非金属杂质净化的问题并实现了不停产净化,提高了生产率。

Description

一种具有净化功能的热镀专用锌
技术领域
本发明涉及钢铁材料表面热镀处理技术领域,尤指一种具有净化功能的热镀专用锌。
背景技术
我国批量热镀锌行业,一直以来生产厂家都是用锌锭融化成锌水(镀锌液),然后将钢铁制件浸入锌水中,通过合金化反应,在钢铁制件表面形成一种铁锌合金层和纯锌层,以达到防腐蚀的目的。但由于生产是连续进行的,随着钢铁件不断地进入锌池镀锌,锌池中锌液中的非金属化合物(如氧化物、硫化物、氯化物、磷化物等等)逐渐增多,造成锌液流动性大大下降和锌耗升高,镀锌质量下降。目前在镀锌生产中,生产十天左右就需要停产进行净化,把铁及其杂质净化排出。这种净化的缺点是:1、只能净化金属产生的杂质,对非金属不起作用;2、需要停产进行,每个月影响生产3天左右,降低了生产率,增加了生产成本。
发明内容
本发明提供了一种具有净化功能的热镀专用锌,能够避免热镀锌过程中非金属与锌反应化合物的生成,减少锌耗,提高镀锌液的流动性,解决了非金属杂质净化的问题。
为达到上述目的,本发明的一种具有净化功能的热镀专用锌,是以锌锭为基准,其中添加0.001%~1.00%混合稀土(La-Ce)、0.001%~2.00%锡(Sn)、0.001%~1.00%铋(Bi)、0.12%镍(Ni)中的至少两种,其余为锌锭所带的固有杂质。
本发明新材料中含有的0.001%~1.00%混合稀土(La-Ce)、0.001%~2.00%锡(Sn)、0.001%~1.00%铋(Bi)、0.12%镍(Ni)的至少两种金属元素,能够优先与镀锌液中产生的非金属反应而排出,其有益效果在于:
1、阻止了非金属与锌的反应,减少了锌耗,提高了流动性,保证了镀锌质量降低了成本。
2、解决了非金属杂质净化的问题并实现了不停产净化,提高了生产率。
具体实施方式
目前批量镀锌厂家生产过程是,将锌锭放在锌池中,加热熔化成锌水(镀锌液),然后将钢铁制件浸入锌水中,使钢铁表面形成一层合金层和纯锌覆盖层。在生产过程中,为了提高产品质量,降低生产成本,生产厂家选择含不同元素的合金调整锌水,如含锰、铝元素的合金等。发明专利(专利号为:103602939A)《一种热度用锌合金及热镀锌方法》,主要解决问题是,复杂成分和结构的钢材表面热度、且产生较多低渣造成锌浪费的技术问题。发明专利(专利号为:101429604B)《一种锌-铝-稀土中间合金及其在热镀锌合金生产中的应用》,这种中间合金成分:Al:3%-5%,RE:6%-10%,余量为Zn。这种中间合金主要是解决生产热镀锌合金时能耗高的问题,在生产热镀锌合金时采用这种中间合金添加铝和稀土,比直接添加铝和稀土能降低能耗。实用新型专利(专利号为:ZL 200720063766.X;和ZL200720063903.X),两项专利均是规定热镀锌合金规格形状的问题。以上四个专利均没有涉及本发明所要解决的问题,没有涉及如何解决镀锌生产中,非金属化合物在锌水中越积越多造成流动性差的问题。
我们通过设计配方、试验等研发工作,从镀锌生产需要的主原料-锌入手,将不同金属元素混合稀土、锡、铋、镍,分别以不同的配比配入金属锌中,具体为将混合稀土(La-Ce)、0.001%~2.00%锡(Sn)、0.001%~1.00%铋(Bi)、0.12%镍(Ni)的至少两种金属元素与金属锌混合,通过特殊工艺冶炼形成镀锌专用锌。该专用锌镀锌生产时替代锌锭直接使用,不需要加任何合金或产品,就可以生产高质量低成本的镀锌产品。
该发明的原理是不同配比的各种元素共同作用,能够优先与镀锌液中产生的非金属反应而排出,在生产的同时起到了净化除杂的作用,使用镀锌液不需要停产净化就可以保持锌水的流动性良好。
上述实施案例,仅例示性说明本发明的原理及其功效,而非用于限制本发明。任何熟悉此技术的人士皆可在不违背本发明的精神及范畴下,对上述实施例进行修饰或改变。因此,举凡所属技术领域中具有通常知识者在未脱离本发明所揭示的精神与技术思想下所完的一切等效修饰或改变,仍应由发明的权利要求所涵盖。

Claims (1)

1.一种具有净化功能的热镀专用锌,其特征在于,以锌锭为基准,其中添加0.001%~1.00%混合稀土(La-Ce)、0.001%~2.00%锡(Sn)、0.001%~1.00%铋(Bi)、0.12%镍(Ni)中的至少两种,其余为锌锭所带的固有杂质。
CN201810675244.8A 2018-06-27 2018-06-27 一种具有净化功能的热镀专用锌 Pending CN110643915A (zh)