CN110552244A - White glassine double-silicon release base paper and preparation method thereof - Google Patents
White glassine double-silicon release base paper and preparation method thereof Download PDFInfo
- Publication number
- CN110552244A CN110552244A CN201910711409.7A CN201910711409A CN110552244A CN 110552244 A CN110552244 A CN 110552244A CN 201910711409 A CN201910711409 A CN 201910711409A CN 110552244 A CN110552244 A CN 110552244A
- Authority
- CN
- China
- Prior art keywords
- parts
- base paper
- double
- release base
- glassine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a white glassine double-silicon release base paper and a preparation method thereof, wherein the white glassine double-silicon release base paper comprises, by weight, 40-50 parts of hardwood pulp, 50-60 parts of softwood pulp, 1-2 parts of polyvinyl alcohol, 0.1-0.9 part of a dispersant, 1200 parts of clear water, 0.1-0.2 part of polyester modified dimethylpolysiloxane, 0.1-0.2 part of carboxymethyl cellulose, 1-3 parts of china clay, 0.3-1 part of rosin, 0.01-0.04 part of cellulase and 0.5-1.5 parts of aluminum sulfate, and the polyvinyl alcohol, the dispersant, the polyester modified dimethylpolysiloxane, the carboxymethyl cellulose and the china clay are added on the surface of the white glassine double-silicon release base paper during the preparation process to improve the surface oil resistance of the paper; after the base paper is subjected to double-sided super calendering, the two sides of the base paper are smooth, dense and smooth and bright, and the requirement that the two sides of the paper can be coated with silicon is met.
Description
Technical Field
the invention relates to white glassine double-silicon release base paper and a preparation method thereof.
Background
the glassine paper has the characteristics of high strength, good toughness and good water resistance, so the glassine paper is widely applied to the industries of food, medicine and the like, and can also be used for high-speed automatic labeling of special adhesive tapes, laser anti-counterfeiting labels and the like. The glassine paper is used on one side in the market at present, and in order to enable the glassine paper to meet the requirement of using on two sides, the two sides of the glassine paper are coated in the production process and the two sides of the glassine paper are subjected to supercalendering treatment.
Disclosure of Invention
The invention aims to solve the technical problem of providing the white glassine disilicon release base paper which has the advantages of low production cost, heat resistance, strong tensile resistance, difficult deformation, obvious oil resistance effect and more environment-friendly production process.
In order to solve the problems, the invention is realized by the following technical scheme: the white glassine double-silicon release base paper comprises, by weight, 40-50 parts of hardwood pulp, 50-60 parts of softwood pulp, 1-2 parts of polyvinyl alcohol, 0.1-0.9 part of a dispersant, 1200 parts of clear water, 0.1-0.2 part of polyester modified dimethylpolysiloxane, 0.1-0.2 part of carboxymethyl cellulose, 1-3 parts of china clay, 0.3-1 part of rosin, 0.01-0.04 part of cellulase and 0.5-1.5 parts of aluminum sulfate.
the invention aims to solve another technical problem of providing a preparation method of white glassine double-silicon release base paper,
the invention is realized by the following technical scheme: the preparation process of the white glassine double-silicon release base paper comprises the following steps:
1) Extracting 40-50 parts of hardwood pulp, 50-60 parts of softwood pulp, 1200 parts of clear water and 0.01-0.04 part of cellulose according to the weight part ratio for pulping;
2) 0.5-1.5 parts of aluminum sulfate and 0.3-1 part of rosin are extracted according to the weight part ratio and added into the slurry in the step 1, and a glass rod is used for stirring;
3) Carrying out net part forming treatment on the slurry obtained in the step 2;
4) Squeezing the formed pulp in the step 3;
5) Performing front-stage drying after squeezing in the step 4, and controlling the water content to be 10% after drying;
6) After the drying in the step 4, adding 1 to 2 parts of polyvinyl alcohol, 0.1 to 0.9 part of dispersant, 0.1 to 0.2 part of polyester modified dimethyl polysiloxane, 0.1 to 0.2 part of carboxymethyl cellulose and 1 to 3 parts of china clay for surface sizing treatment;
7) performing post-stage drying after the glue is applied in the step 6, and controlling the moisture to be 15% after the drying;
8) and (4) performing overpressure treatment on the base paper dried in the step (7) to obtain finished base paper.
The white glassine double-silicon release base paper has the beneficial effects that: in the preparation process of the white glassine double-silicon release base paper, polyvinyl alcohol, a dispersant, polyester modified dimethyl polysiloxane, carboxymethyl cellulose and porcelain clay are added to the surface sizing, so that the surface oil resistance of the paper is well improved; after the base paper is subjected to double-sided super calendering, the two sides of the base paper are smooth, dense and smooth and bright, and the requirement that the two sides of the paper can be coated with silicon is met.
Detailed Description
The following examples are intended to illustrate the invention but are not intended to limit the scope of the invention.
Example 1
The white glassine double-silicon release base paper comprises, by weight, 40 parts of hardwood pulp, 50 parts of softwood pulp, 1 part of polyvinyl alcohol, 0.1 part of a dispersing agent, 800 parts of clear water, 0.1 part of polyester modified dimethyl polysiloxane, 0.1 part of carboxymethyl cellulose, 1 part of porcelain clay, 0.3 part of rosin, 0.01 part of cellulase and 0.5 part of aluminum sulfate.
The preparation process of the white glassine double-silicon release base paper comprises the following steps:
1) Extracting 40 parts of hardwood pulp, 50 parts of softwood pulp, 800 parts of clear water and 0.01 part of cellulase according to the weight part ratio for pulping;
2) Extracting 0.5 part of aluminum sulfate and 0.3 part of rosin according to the weight part ratio, adding the aluminum sulfate and the rosin into the slurry obtained in the step 1, and stirring the mixture by using a glass rod;
3) carrying out net part forming treatment on the slurry obtained in the step 2;
4) squeezing the formed pulp in the step 3;
5) Performing front-stage drying after squeezing in the step 4, and controlling the water content to be 10% after drying;
6) After drying in the step 4, adding 1 part of polyvinyl alcohol, 0.1 part of dispersant, 0.1 part of polyester modified dimethyl polysiloxane, 0.1 part of carboxymethyl cellulose and 1 part of china clay for surface sizing treatment;
7) Performing post-stage drying after the glue is applied in the step 6, and controlling the moisture to be 15% after the drying;
8) and (4) performing overpressure treatment on the base paper dried in the step (7) to obtain finished base paper.
Example 2
The difference from the embodiment 1 is that the white glassine disilicide release base paper comprises, by weight, 50 parts of hardwood pulp, 60 parts of softwood pulp, 2 parts of polyvinyl alcohol, 0.9 part of a dispersing agent, 1200 parts of clear water, 0.2 part of polyester modified dimethylpolysiloxane, 0.2 part of carboxymethyl cellulose, 3 parts of china clay, 1 part of rosin, 0.04 part of cellulase and 1.5 parts of aluminum sulfate.
example 3
The difference from the embodiment 1 is that the white glassine disilicide release base paper comprises, by weight, 45 parts of hardwood pulp, 55 parts of softwood pulp, 1 part of polyvinyl alcohol, 0.5 part of a dispersant, 1000 parts of clear water, 0.15 part of polyester modified dimethylpolysiloxane, 0.15 part of carboxymethyl cellulose, 2 parts of china clay, 2 parts of rosin, 0.02 part of cellulase and 1 part of aluminum sulfate.
Example 4
the difference from the embodiment 1 is that the white glassine disilicide release base paper comprises, by weight, 42 parts of hardwood pulp, 51 parts of softwood pulp, 1 part of polyvinyl alcohol, 0.2 part of a dispersant, 855 part of clear water, 0.12 part of polyester modified dimethylpolysiloxane, 0.11 part of carboxymethyl cellulose, 1.3 parts of china clay, 0.6 part of rosin, 0.02 part of cellulase and 0.7 part of aluminum sulfate.
Example 5
The difference from the embodiment 1 is that the white glassine double-silicon release base paper comprises, by weight, 48 parts of hardwood pulp, 57 parts of softwood pulp, 1.8 parts of polyvinyl alcohol, 0.8 part of a dispersing agent, 1123 parts of clear water, 0.17 part of polyester modified dimethylpolysiloxane, 0.18 part of carboxymethyl cellulose, 2.6 parts of china clay, 0.9 part of rosin, 0.03 part of cellulase and 1.3 parts of aluminum sulfate.
example 6
The difference from the embodiment 1 is that the white glassine disilicide release base paper comprises the following components, by weight, 50 parts of hardwood pulp, 50 parts of softwood pulp, 2 parts of polyvinyl alcohol, 0.1 part of a dispersing agent, 1200 parts of clear water, 0.1 part of polyester modified dimethylpolysiloxane, 0.2 part of carboxymethyl cellulose, 1 part of china clay, 1 part of rosin, 0.01 part of cellulase and 1.5 parts of aluminum sulfate.
Example 7
The difference from the embodiment 1 is that the white glassine double-silicon release base paper comprises, by weight, 45 parts of hardwood pulp, 55 parts of softwood pulp, 1.5 parts of polyvinyl alcohol, 0.5 part of a dispersing agent, 900 parts of clear water, 0.15 part of polyester modified dimethyl polysiloxane, 0.15 part of carboxymethyl cellulose, 1.5 parts of china clay, 0.5 part of rosin, 0.025 part of cellulase and 1.5 parts of aluminum sulfate.
The present invention is not limited to the above-mentioned preferred embodiments, and any other products similar or identical to the present invention, which can be obtained by anyone based on the teaching of the present invention, fall within the protection scope of the present invention.
Claims (2)
1. a white glassine double-silicon release base paper and a preparation method thereof are characterized in that: the white glassine disilicide release base paper comprises, by weight, 40-50 parts of hardwood pulp, 50-60 parts of softwood pulp, 1-2 parts of polyvinyl alcohol, 0.1-0.9 part of a dispersing agent, 800 parts of clear water, 0.1-0.2 part of polyester modified dimethyl polysiloxane, 0.1-0.2 part of carboxymethyl cellulose, 1-3 parts of china clay, 0.3-1 part of rosin, 0.01-0.04 part of cellulase and 0.5-1.5 parts of aluminum sulfate.
2. a method for preparing the white glassine double-silicon release base paper of claim 1, which is characterized by comprising the following steps: the method comprises the following steps:
1) Extracting 40-50 parts of hardwood pulp, 50-60 parts of softwood pulp, 1200 parts of clear water and 0.01-0.04 part of cellulose according to the weight part ratio for pulping;
2) 0.5-1.5 parts of aluminum sulfate and 0.3-1 part of rosin are extracted according to the weight part ratio and added into the slurry in the step 1, and a glass rod is used for stirring;
3) carrying out net part forming treatment on the slurry obtained in the step 2;
4) squeezing the formed pulp in the step 3;
5) performing front-stage drying after squeezing in the step 4, and controlling the water content to be 10% after drying;
6) After the drying in the step 4, adding 1 to 2 parts of polyvinyl alcohol, 0.1 to 0.9 part of dispersant, 0.1 to 0.2 part of polyester modified dimethyl polysiloxane, 0.1 to 0.2 part of carboxymethyl cellulose and 1 to 3 parts of china clay for surface sizing treatment;
7) performing post-stage drying after the glue is applied in the step 6, and controlling the moisture to be 15% after the drying;
8) And (4) performing overpressure treatment on the base paper dried in the step (7) to obtain finished base paper.