CN110499664A - A kind of facing paper concave and convex technology - Google Patents
A kind of facing paper concave and convex technology Download PDFInfo
- Publication number
- CN110499664A CN110499664A CN201910754210.2A CN201910754210A CN110499664A CN 110499664 A CN110499664 A CN 110499664A CN 201910754210 A CN201910754210 A CN 201910754210A CN 110499664 A CN110499664 A CN 110499664A
- Authority
- CN
- China
- Prior art keywords
- base paper
- decorating base
- concave
- handled
- aqueous ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of facing paper concave and convex technologies, specifically comprise the following steps: step 1, cut the flash of decorating base paper two sides, are handled decorating base paper surface smoothness to decorating base paper surface corrugationless；Step 2, in decorating base paper surface uniform fold Cypres, then carry out drying and processing；Step 3, the color for the aqueous ink at least coating aqueous ink twice on the decorating base paper handled by step 2, and coating every time and glossiness difference；It is added in step 4, hydrotropism's ink and foaming agent and stirs evenly to form foamed slurry, be then coated in foamed slurry by standing, to its solidification on step 3 treated decorating base paper by roller；The decorating base paper handled by step 4 is carried out dipping process by step 5；Step 6 will be dried after traction by the decorating base paper that step 5 is handled, cool down to obtain product.The facing paper that the present invention can prepare image clearly, lines understand, concave-convex effect is good.
Description
Technical field
The present invention relates to the technical fields of facing paper, more particularly, to a kind of facing paper concave and convex technology.
Background technique
With the rapid development of our country's economy, the consumption of timber shows an increasing trend year by year, and timber must as furniture decoration
Indispensable basic material, timber and woodwork demand are continuously increased, therefore cause timber resources increasingly deficient.In order to solve wood
The situation of material shortage, the appearance of wood-based plate solve the problems, such as this, and wood-based plate is increasingly becoming the substitute of some pure wood products, dress
A kind of novel decorative surfacing that paper is also the development with these industries and rises is adornd, sticks to have on wood-based plate and imitate
The facing paper of true wood grain has the ornamental value as timber.
Publication No. is that the Chinese patent of CN106564311A discloses the preparation method of a kind of wood grain heat transfer film or paper, including
Deepen the carving depth of wood grain on cylinder intaglio roller, wood grain includes wood thorn layer and the wooden sarcocyte；Get out stock, ink, scraper
With cylinder intaglio roller, cylinder intaglio roller is mounted on intaglio press；Stock is mounted on intaglio press discharging frame；
The wooden sarcocyte ink is poured into the preceding segment section of intaglio press, pours into wood thorn layer ink in the rear portion color separation section of intaglio press；
Mix up the speed of production of ink viscosity, the box temperature of printing machine and printing machine；Start chromaticity printing；Finished product winding, completes print
Brush.The invention can prepare transfer printing wood grain paper or film with 3D visual effect and protrusion wood grain feel.
Prior art among the above has the following deficiencies: that above-mentioned preparation method is formed by roller gravure with 3D view
Feel effect and protrude the transfer printing wood grain paper or film of wood grain feel, in intaglio process, is easy to cause that printed matter image is apprehensive, lines
It is unclear, concave-convex effect is unobvious, influence the decorative effect of facing paper.
Summary of the invention
The object of the present invention is to provide a kind of facing paper concave and convex technology, image clearly can be prepared, lines understand, concave-convex
The good facing paper of effect.
Above-mentioned technical purpose of the invention has the technical scheme that a kind of facing paper concave and convex technology,
Specifically comprise the following steps:
Step 1, decorating base paper pretreatment: the flash of decorating base paper two sides is cut, to decorating base paper surface smoothness into
Row is handled to decorating base paper surface corrugationless；
Step 2, the processing of decorating base paper top sizing: it in decorating base paper surface uniform fold Cypres, is then dried
Processing；
Step 3, coating aqueous ink: at least coating aqueous ink twice on the decorating base paper handled by step 2, and coating every time
Aqueous ink color and glossiness it is different, the roller that the aqueous ink of different colours correspond to different texture be used to form have it is different
The grain of wood of color；
Step 4, coating foamed slurry: foaming agent is added in hydrotropism's ink and stirs evenly to form foamed slurry, in above-mentioned steps 3
The gap for arbitrarily coating aqueous ink twice at least coats one step foaming slurry, and foamed slurry is coated in decorating base paper by roller
On, it stands, to its solidification；
Step 5, impregnation: the decorating base paper handled by step 4 is subjected to dipping process；
Step 6, foaming: it will be dried after traction by the decorating base paper that step 5 is handled, cool down to obtain product.
By using above-mentioned technical proposal, decorating base paper surface can be improved the strong of body paper surface after sizing is handled
Degree, during reducing coating aqueous ink, the generation of plucking, paper scrap, paper powder, while increasing body paper dimensional stability, prevent paper
That opens is Texturized.The difference of color can be preferably embodied in the aqueous ink of decorating base paper surface coating different colours, so that
The texture of steel roller printing is relatively sharp, forms the grain of wood having levels, and so the grain of wood can be made more true to nature.Use water
Property ink replace traditional oiliness ink, volatile organic gases will not be distributed to atmosphere, reduces the pollution to environment, uses aqueous ink
It is more environmentally-friendly, it will be attached on plate by the facing paper of aqueous ink coating, with the board making furniture, can reduce to human body
Harm.The aqueous ink containing foaming agent is coated on decorating base paper, after drying and processing, foaming agent absorbs heat during the drying process
Amount, expansion become larger, and form protrusion, so that decorating base paper concave-convex surface, has three-dimensional vision.
The further setting of the present invention are as follows: the Cypres in the step 2 are cationic starch.
By using above-mentioned technical proposal, body paper is to consist of fibers, starch and fiber be all by glucose group at,
The two is easy to combine, and in addition fiber surface is negatively charged, and cationic starch is per se with positive electricity, and cation forms sediment under electrostatic force
Powder can preferably be attached to body paper surface.
The further setting of the present invention are as follows: Cypres apply surface in such a way that scraper is glued in the step 2
Jelly is coated in decorating base paper surface.
By using above-mentioned technical proposal, scraper sizing is that enough glues are applied to paper surface, then according to need
It asks angle, pressure for adjusting scraper etc. to remove the glue of excess surface, has by the base paper sheet face that scraper is glued preferable flat
Slip, and glue can be substantially filled in the fiber hole of paper.
The further setting of the present invention are as follows: the foaming agent in the step 4 is blowing agent AC.
By using above-mentioned technical proposal, blowing agent AC gas forming amount is big, and decomposition temperature is adjustable and blowing agent AC decomposes
Gas be mainly nitrogen, the concentration comparable in abscess in the concentration and air of nitrogen is easy to keep abscess is inside and outside to flatten weighing apparatus.
The further setting of the present invention are as follows: foamed slurry is according to mass fraction meter, including 1~3 part of foaming in the step 4
Agent and 97~99 parts of aqueous inks.
The further setting of the present invention are as follows: foamed slurry further includes 2~5 parts of alumina powders in the step 4.
By using above-mentioned technical proposal, alumina powder hardness is big, and alumina powder is added, can be improved facing paper
Wear-resisting property avoids the facing paper for being attached to plate surface because of friction damage.
The further setting of the present invention are as follows: foamed slurry further includes 1~2 part of aluminium-hydroxide powder in the step 4.
By using above-mentioned technical proposal, the ratio of chemical bonding water contained in aluminium hydroxide molecule is up to 34%, this
Kind combines water to keep stablizing in the process of facing paper, starts to decompose when more than 200 DEG C, releases water vapour, plays cold
But, slow down the effect of burn rate.
The further setting of the present invention are as follows: in the step 6 drying temperature be 180~220 DEG C, drying time be 0.5~
3min。
The further setting of the present invention are as follows: hauling speed is 20~25m/min in the step 6.
In conclusion advantageous effects of the invention are as follows:
1. the difference of color can be preferably embodied in the aqueous ink of decorating base paper surface coating different colours, so that steel roller printing
Texture it is relatively sharp, form the grain of wood having levels, so the grain of wood can be made more true to nature.It is replaced using aqueous ink
Traditional oiliness ink, volatile organic gases will not be distributed to atmosphere, the pollution to environment is reduced, uses aqueous ink more ring
It protects, will be attached on plate by the facing paper of aqueous ink coating, with the board making furniture, can reduce the harm to human body.
The aqueous ink containing foaming agent is coated on decorating base paper, after drying and processing, foaming agent absorbs heat during the drying process, swollen
It is swollen to become larger, protrusion is formed, so that decorating base paper concave-convex surface, has three-dimensional vision；
2. Cypres are coated in decorating base paper surface by the way of scraper sizing, scraper sizing is by enough glue
Liquid is applied to paper surface, then adjusts the glue that angle, pressure of scraper etc. removes excess surface according to demand, is applied by scraper
The base paper sheet face of glue has preferable flatness, and glue can be substantially filled in the fiber hole of paper；
3. alumina powder hardness is big, alumina powder is added, can be improved the wear-resisting property of facing paper, avoid being attached to plate table
The facing paper in face is because of friction damage.
Detailed description of the invention
Fig. 1 is facing paper concave and convex technology flow chart.
Specific embodiment
Below with reference to embodiment, invention is further described in detail.
Embodiment 1
A kind of facing paper concave and convex technology, specifically comprises the following steps:
Step 1, decorating base paper pretreatment: the flash of decorating base paper two sides is cut, to decorating base paper surface smoothness into
Row is handled to decorating base paper surface corrugationless；
Step 2, the processing of decorating base paper top sizing: cation is uniformly coated in such a way that scraper is glued on decorating base paper surface
Then starch carries out drying and processing；
Step 3, coating aqueous ink: the water for coating aqueous ink twice on the decorating base paper handled by step 2, and coating twice
Property ink color and glossiness it is different, the roller that the aqueous ink of different colours corresponds to different texture is used to form with different colors
The grain of wood；
Step 4, coating foamed slurry: foaming agent is added in hydrotropism's ink and stirs evenly to form foamed slurry, is coated in step 3
Aqueous ink twice between foamed slurry coated on decorating base paper by roller, stand, to its solidification, foamed slurry presses quality
Number meter includes following component: 1 part of blowing agent AC and 99 parts of aqueous ink；
Step 5, impregnation: the decorating base paper handled by step 4 is subjected to dipping process；
Step 6, foaming: after traction, it will be dried in an oven by the decorating base paper that step 5 is handled, cool down to obtain
Product, wherein hauling speed is 20m/min, and drying temperature is 180 DEG C, drying time 0.5min.
Embodiment 2
A kind of facing paper concave and convex technology, specifically comprises the following steps:
Step 1, decorating base paper pretreatment: the flash of decorating base paper two sides is cut, to decorating base paper surface smoothness into
Row is handled to decorating base paper surface corrugationless；
Step 2, the processing of decorating base paper top sizing: cation is uniformly coated in such a way that scraper is glued on decorating base paper surface
Then starch carries out drying and processing；
Step 3, coating aqueous ink: the water for coating aqueous ink three times on the decorating base paper handled by step 2, and coating three times
Property ink color and glossiness it is different, the roller that the aqueous ink of different colours corresponds to different texture is used to form with different colors
The grain of wood；
Step 4, coating foamed slurry: foaming agent is added in hydrotropism's ink and stirs evenly to form foamed slurry, then in step 3
Foamed slurry is coated on decorating base paper by roller between the preceding aqueous ink twice of coating, is stood, to its solidification, foamed slurry
It according to the mass fraction include following component: 3 parts of blowing agent AC and 97 parts of aqueous ink；
Step 5, impregnation: the decorating base paper handled by step 4 is subjected to dipping process；
Step 6, foaming: after traction, it will be dried in an oven by the decorating base paper that step 5 is handled, cool down to obtain
Product, wherein hauling speed is 25m/min, and drying temperature is 180 DEG C, drying time 3min.
Embodiment 3
A kind of facing paper concave and convex technology, specifically comprises the following steps:
Step 1, decorating base paper pretreatment: the flash of decorating base paper two sides is cut, to decorating base paper surface smoothness into
Row is handled to decorating base paper surface corrugationless；
Step 2, the processing of decorating base paper top sizing: cation is uniformly coated in such a way that scraper is glued on decorating base paper surface
Then starch carries out drying and processing；
Step 3, coating aqueous ink: four aqueous inks, and the water coated every time are coated on the decorating base paper handled by step 2
Property ink color and glossiness it is different, the roller that the aqueous ink of different colours corresponds to different texture is used to form with different colors
The grain of wood；
Step 4, coating foamed slurry: foaming agent is added in hydrotropism's ink and stirs evenly to form foamed slurry, then in step 3
Foamed slurry is coated on decorating base paper by roller between the aqueous ink of third time coating for the second time, is stood, is solidified to it,
Foamed slurry includes following component according to the mass fraction: 2 parts of blowing agent AC, 98 parts of aqueous ink, 2 parts of aluminium oxide and aluminium hydroxide
1 part；
Step 5, impregnation: the decorating base paper handled by step 4 is subjected to dipping process；
Step 6, foaming: after traction, it will be dried in an oven by the decorating base paper that step 5 is handled, cool down to obtain
Product, wherein hauling speed is 25m/min, and drying temperature is 210 DEG C, drying time 2min.
Embodiment 4
A kind of facing paper concave and convex technology, specifically comprises the following steps:
Step 1, decorating base paper pretreatment: the flash of decorating base paper two sides is cut, to decorating base paper surface smoothness into
Row is handled to decorating base paper surface corrugationless；
Step 2, the processing of decorating base paper top sizing: cation is uniformly coated in such a way that scraper is glued on decorating base paper surface
Then starch carries out drying and processing；
Step 3, coating aqueous ink: six aqueous inks, and the water coated every time are coated on the decorating base paper handled by step 2
Property ink color and glossiness it is different, the roller that the aqueous ink of different colours corresponds to different texture is used to form with different colors
The grain of wood；
Step 4, coating foamed slurry: foaming agent is added in hydrotropism's ink and stirs evenly to form foamed slurry, then in step 3
One step foaming slurry is coated on decorating base paper by roller between second of coating aqueous ink and third time coating aqueous ink, then
It is coated on decorating base paper second between the 4th coating aqueous ink and the 5th coating aqueous ink by roller in step 3
Foamed slurry is stood, and to its solidification, foamed slurry includes following component according to the mass fraction: 3 parts of blowing agent AC, aqueous ink 97
Part, 4 parts of aluminium oxide and 2 parts of aluminium hydroxide；
Step 5, impregnation: the decorating base paper handled by step 4 is subjected to dipping process；
Step 6, foaming: after traction, it will be dried in an oven by the decorating base paper that step 5 is handled, cool down to obtain
Product, wherein hauling speed is 23m/min, and drying temperature is 220 DEG C, drying time 2min.
Embodiment 5
A kind of facing paper concave and convex technology, specifically comprises the following steps:
Step 1, decorating base paper pretreatment: the flash of decorating base paper two sides is cut, to decorating base paper surface smoothness into
Row is handled to decorating base paper surface corrugationless；
Step 2, the processing of decorating base paper top sizing: cation is uniformly coated in such a way that scraper is glued on decorating base paper surface
Then starch carries out drying and processing；
Step 3, coating aqueous ink: six aqueous inks, and the water coated every time are coated on the decorating base paper handled by step 2
Property ink color and glossiness it is different, the roller that the aqueous ink of different colours corresponds to different texture is used to form with different colors
The grain of wood；
Step 4, coating foamed slurry: foaming agent is added in hydrotropism's ink and stirs evenly to form foamed slurry, then in step 3
One step foaming slurry is coated on decorating base paper by roller between coating aqueous ink and second of coating aqueous ink for the first time, then
It is coated on decorating base paper second between the 5th coating aqueous ink and the 6th coating aqueous ink by roller in step 3
Foamed slurry is stood, and to its solidification, foamed slurry includes following component according to the mass fraction: 2 parts of blowing agent AC, aqueous ink 98
Part, 5 parts of aluminium oxide and 2 parts of aluminium hydroxide；
Step 5, impregnation: the decorating base paper handled by step 4 is subjected to dipping process；
Step 6, foaming: after traction, it will be dried in an oven by the decorating base paper that step 5 is handled, cool down to obtain
Product, wherein hauling speed is 25m/min, and drying temperature is 200 DEG C, drying time 2min.
Embodiment 6
A kind of facing paper concave and convex technology, the difference with embodiment 5 is in step 6 that drying time is 0.5min, other with implementation
Example 5.
Embodiment 7
A kind of facing paper concave and convex technology, the difference with embodiment 5 are in step 6 that drying time is 1 DEG C, the other the same as in Example 5.
Embodiment 8
A kind of facing paper concave and convex technology, the difference with embodiment 5 are in step 6 that drying time is 3min, other same embodiments
5。
Comparative example 1
A kind of facing paper concave and convex technology, the difference with embodiment 5 are in step 6 that drying temperature is 160 DEG C, other same embodiments
5。
Comparative example 2
A kind of facing paper concave and convex technology, the difference with embodiment 5 are in step 6 that drying temperature is 240 DEG C, other same embodiments
5。
Its foaming height is measured using facing paper prepared by 1~embodiment of embodiment 8 and 1~comparative example of comparative example 2, is used
In the concave-convex effect for illustrating facing paper.
1 facing paper foaming height of table
According to 1~embodiment of embodiment 8, foaming height illustrates that the concave-convex effect of facing paper is good at 80 or more, three-dimensional
Sense is strong；According to 5~embodiment of embodiment 8, at identical temperature, with the extension of drying time, foaming height first increases to be reduced afterwards,
Drying time is short, the shortage of heat that foaming agent absorbs, and cannot foam completely, and time course causes foaming agent absorption heat excessive,
Foaming agent swelling fracture, causes foaming height to reduce.In conjunction with comparative example, 160 DEG C of temperature, temperature is low, the heat that foaming agent absorbs
It is insufficient, it is difficult to foam, temperature is 240 DEG C, and foaming agent then can swelling fracture.
This specific embodiment is only explanation of the invention, not limitation of the present invention, and those skilled in the art exist
It can according to need the modification that not creative contribution is made to the present embodiment after reading this specification, but as long as in the present invention
Scope of the claims in all by the protection of Patent Law.
Claims (9)
1. a kind of facing paper concave and convex technology, it is characterised in that: specifically comprise the following steps:
Step 1, decorating base paper pretreatment: the flash of decorating base paper two sides is cut, to decorating base paper surface smoothness into
Row is handled to decorating base paper surface corrugationless；
Step 2, the processing of decorating base paper top sizing: it in decorating base paper surface uniform fold Cypres, is then dried
Processing；
Step 3, coating aqueous ink: at least coating aqueous ink twice on the decorating base paper handled by step 2, and coating every time
Aqueous ink color and glossiness it is different, the roller that the aqueous ink of different colours correspond to different texture be used to form have it is different
The grain of wood of color；
Step 4, coating foamed slurry: foaming agent is added in hydrotropism's ink and stirs evenly to form foamed slurry, in above-mentioned steps 3
The gap for arbitrarily coating aqueous ink twice at least coats one step foaming slurry, and foamed slurry is coated in decorating base paper by roller
On, it stands, to its solidification；
Step 5, impregnation: the decorating base paper handled by step 4 is subjected to dipping process；
Step 6, foaming: it will be dried after traction by the decorating base paper that step 5 is handled, cool down to obtain product.
2. facing paper concave and convex technology according to claim 1, it is characterised in that: the Cypres in the step 2 are
Cationic starch.
3. facing paper concave and convex technology according to claim 1, it is characterised in that: Cypres pass through in the step 2
Cypres are coated in decorating base paper surface by the mode of scraper sizing.
4. facing paper concave and convex technology according to claim 1, it is characterised in that: the foaming agent in the step 4 is foaming
Agent AC.
5. facing paper concave and convex technology according to claim 1, it is characterised in that: foamed slurry is according to matter in the step 4
Measure number meter, including 1~3 part of foaming agent and 97~99 parts of aqueous inks.
6. facing paper concave and convex technology according to claim 4, it is characterised in that: foamed slurry further includes 2 in the step 4
~5 parts of alumina powders.
7. facing paper concave and convex technology according to claim 4, it is characterised in that: foamed slurry further includes 1 in the step 4
~2 parts of aluminium-hydroxide powders.
8. facing paper concave and convex technology according to claim 1, it is characterised in that: in the step 6 drying temperature be 180~
220 DEG C, drying time is 0.5~3min.
9. facing paper concave and convex technology according to claim 1, it is characterised in that: in the step 6 hauling speed be 20~
25m/min。