CN110485164A - A kind of production technology of nice and cool pashm worsted plus material - Google Patents
A kind of production technology of nice and cool pashm worsted plus material Download PDFInfo
- Publication number
- CN110485164A CN110485164A CN201910815994.5A CN201910815994A CN110485164A CN 110485164 A CN110485164 A CN 110485164A CN 201910815994 A CN201910815994 A CN 201910815994A CN 110485164 A CN110485164 A CN 110485164A
- Authority
- CN
- China
- Prior art keywords
- cool
- nice
- pashm
- plus material
- worsted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production technologies of nice and cool pashm worsted plus material, comprising the following steps: S1 configures nice and cool finishing agent, and the Main Components for finishing agent of feeling nice and cool are Waterborne Polyurethane Prepolymer, multicomponent organic acid, the agent of polyalcohol cool feeling, hydramine and water；Pashm worsted plus material is placed in the nice and cool finishing agent of S1 by S2, pads processing, takes out the pashm worsted plus material with liquid；Worsted fabric obtained by S2 is placed at 85~95 DEG C and is dried to drying in advance by S3, then imports at 110~130 DEG C and bake, and obtains nice and cool pashm worsted plus material.Using Waterborne Polyurethane Prepolymer as film forming agent, multicomponent organic acid is added and is crosslinked with cool feeling agent, it is ensured that the persistence of cool feeling reduces fabric xanthochromia degree.
Description
Technical field
The present invention relates to fleece fabrics production technical fields, and in particular to a kind of production work of nice and cool pashm worsted plus material
Skill.
Background technique
Worsted cashmere fabric has the advantages that smooth, frivolous, penetrating, slim and graceful, fine and smooth etc. take.It is original with top cashmere
Material, after combing is spun into combed yarn, is made into fleece fabrics in Seiko.The number of worsted cashmere yarn generally from 28 to
120.Worsted cashmere is very suitable to spring and summer dress, when being used for summer clothes, usually by cashmere fiber and coolmax, outlast
Deng the yarn adjusted with excellent moisture absorption sweat discharging functions or temperature, to improve wearing comfort.
For full pashm worsted plus material, cool feeling agent is applied on fabric by the method for generalling use final finishing.
A kind of finishing fluid is disclosed in CN107523993A, wherein including cool feeling agent and crosslinking agent, further, cool feeling agent is
COOLM6036, crosslinking agent AF3600, but above-mentioned AF series crosslinking agent usually requires to bake to 160 DEG C or more, and above-mentioned bake
Under the conditions of temperature, the strength of cashmere fiber can decline, and different journeys can integrally occur because of the difference of use condition, cashmere fabric
The irreversible xanthochromia of degree.
Therefore, it is necessary to which the nice and cool finishing technique to pashm worsted plus material in the prior art optimizes.
Summary of the invention
It is an object of the invention to overcome defect existing in the prior art, a kind of life of nice and cool pashm worsted plus material is provided
Production. art is added multicomponent organic acid and crosslinks with cool feeling agent, it is ensured that cool feeling using Waterborne Polyurethane Prepolymer as film forming agent
Persistence.
To achieve the above object, the technical solution of the present invention is as follows: a kind of production technology of nice and cool pashm worsted plus material, special
Sign is, comprising the following steps:
S1: configuring nice and cool finishing agent, and the Main Components for finishing agent of feeling nice and cool are Waterborne Polyurethane Prepolymer, multicomponent organic acid, polynary
The agent of alcohol cool feeling, hydramine and water；
S2: pashm worsted plus material is placed in the nice and cool finishing agent of S1, pads processing, takes out the pashm worsted plus material with liquid；
S3: worsted fabric obtained by S2 is placed at 85~95 DEG C and is dried to drying in advance, then imports at 110~130 DEG C and bakes, is obtained nice and cool
Pashm worsted plus material.
Preferred technical solution is that the polyalcohol cool feeling agent is xylitol and/or red sugar alcohol.
Preferred technical solution is the concentration of main component in nice and cool finishing agent are as follows: Waterborne Polyurethane Prepolymer 50~
130g/L, 0.5~4 g/L of multicomponent organic acid, 5~30g/L of polyalcohol cool feeling agent, 0.1~2 g/L of hydramine.
Preferred technical solution is that the organic multicomponent acid is one or both of citric acid, ethanedioic acid and tartaric acid
Above combination.
Preferred technical solution is that hydramine is selected from monoethanolamine, diethanol amine, triethanolamine, diglycolamine, diisopropyl
The combination of one or more of hydramine, N methyldiethanol amine.
Preferred technical solution is that the pick-up of processing is padded in S2 is 60~70%.
The advantages and beneficial effects of the present invention are:
The production technology of the nice and cool pashm worsted plus material using Waterborne Polyurethane Prepolymer as film forming agent, it is multicomponent organic acid, more
The surface group of first alcohol cool feeling agent and hydramine and wool fiber crosslinking, help to improve pashm worsted plus material cool feeling persistence and
Washability；
The preliminary drying and baking temperature of above-mentioned arrangement process are lower, and fabric entirety xanthochromia and influence to fiber strength are smaller.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following embodiment is only used for more
Add and clearly demonstrate technical solution of the present invention, and not intended to limit the protection scope of the present invention.
Embodiment 1
Embodiment 1 feel nice and cool pashm worsted plus material production technology the following steps are included:
S1: configuring nice and cool finishing agent, and the Main Components for finishing agent of feeling nice and cool are Waterborne Polyurethane Prepolymer, multicomponent organic acid, polynary
The agent of alcohol cool feeling, hydramine and water；
S2: pashm worsted plus material is placed in the nice and cool finishing agent of S1, pads processing, takes out the pashm worsted plus material with liquid；
S3: worsted fabric obtained by S2 is placed at 85 DEG C and is dried to drying in advance, then imports at 130 DEG C and bakes, it is spinning to obtain nice and cool cashmere
Fabric.
Polyalcohol cool feeling agent is xylitol.
Embodiment 1 uses the Waterborne Polyurethane Prepolymer of 1000 magnitudes；The concentration of main component in nice and cool finishing agent are as follows: water
Property base polyurethane prepolymer for use as 50g/L, 4 g/L of multicomponent organic acid, polyalcohol cool feeling agent 30g/L, 2 g/L of hydramine.
Organic multicomponent acid is citric acid；Hydramine is monoethanolamine.
The pick-up that processing is padded in S2 is 80%.
Embodiment 2
Embodiment 2 is based on embodiment 1, and difference is:
S3: worsted fabric obtained by S2 is placed at 95 DEG C and is dried to drying in advance, then imports at 110 DEG C and bakes 3min；Polyalcohol cool feeling
Agent is that xylitol and red sugar alcohol 1:1 weight ratio are composed.
The concentration of main component in nice and cool finishing agent are as follows: Waterborne Polyurethane Prepolymer 130g/L, 5 g/L of multicomponent organic acid,
3 g/L of polyalcohol cool feeling agent, 0.1 g/L of hydramine.
Organic multicomponent acid is tartaric acid；Hydramine is diethanol amine.
The pick-up that processing is padded in S2 is 60%.
Embodiment 3
Embodiment 3 is based on embodiment 2, and difference is:
S3: worsted fabric obtained by S2 is placed at 90 DEG C and is dried to drying in advance, then imports at 120 DEG C and bakes；Polyalcohol cool feeling agent is
Red sugar alcohol.
The concentration of main component in nice and cool finishing agent are as follows: Waterborne Polyurethane Prepolymer 80g/L, 2 g/L of multicomponent organic acid, more
First 18 g/L of alcohol cool feeling agent, 1 g/L of hydramine.
Organic multicomponent acid is citric acid；Hydramine is triethanolamine.
The pick-up that processing is padded in S2 is 70%.
Comparative example
Comparative example 1: comparative example 1 is based on embodiment 1 using the world He Te AF3600 disclosed in CN107523993A as crosslinking agent,
The xylitol cool feeling agent of the world He Te AF3600 and 20 g/L in finishing fluid containing 20 g/L, the preliminary drying baking temperature of post-processing
With embodiment 1.
Cool feeling test:
1, there is refrigerant sense compared to the pashm worsted plus material arranged without cool feeling, comparative example 1 and embodiment gained sample, due to
Be cool feeling agent in the finishing fluid of embodiment 1 and comparative example 1 content it is larger, test arrange front and back the temperature difference be -2 DEG C；
2, after cleaning fabric 50 times, the coolness of fabric is still remained, and it is -1.4 DEG C that embodiment 1, which arranges the front and back temperature difference, and is compared
The temperature difference is -0.6 DEG C before and after the arrangement of example 1；
3, compared to the pashm worsted plus material arranged without cool feeling, the fabric of comparative example 1 omits xanthochromia, yellow since baking temperature is low
Change degree is smaller, and embodiment 1 is without xanthochromia.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, several improvements and modifications can also be made, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of production technology of nice and cool pashm worsted plus material, which comprises the following steps:
S1: configuring nice and cool finishing agent, and the Main Components for finishing agent of feeling nice and cool are Waterborne Polyurethane Prepolymer, multicomponent organic acid, polynary
The agent of alcohol cool feeling, hydramine and water；
S2: pashm worsted plus material is placed in the nice and cool finishing agent of S1, pads processing, takes out the pashm worsted plus material with liquid；
S3: worsted fabric obtained by S2 is placed at 85~95 DEG C and is dried to drying in advance, then imports at 110~130 DEG C and bakes, is obtained nice and cool
Pashm worsted plus material.
2. the production technology of nice and cool pashm worsted plus material according to claim 1, which is characterized in that the polyalcohol cool feeling
Agent is xylitol and/or red sugar alcohol.
3. the production technology of nice and cool pashm worsted plus material according to claim 1, which is characterized in that main in nice and cool finishing agent
Want the concentration of component are as follows: 50~130g/L of Waterborne Polyurethane Prepolymer, 0.5~4 g/L of multicomponent organic acid, polyalcohol cool feeling agent 5
~30g/L, 0.1~2 g/L of hydramine.
4. the production technology of nice and cool pashm worsted plus material according to claim 3, which is characterized in that the organic multicomponent acid
For the combination of one or more of citric acid, ethanedioic acid and tartaric acid.
5. the production technology of nice and cool pashm worsted plus material according to claim 1, which is characterized in that hydramine is selected from single second
One or more of hydramine, diethanol amine, triethanolamine, diglycolamine, diisopropanolamine (DIPA), N methyldiethanol amine
Combination.
6. the production technology of nice and cool pashm worsted plus material according to claim 1, which is characterized in that pad processing in S2
Pick-up is 60~70%.