CN110482974A - 一种低成本外墙专用乳胶漆粉 - Google Patents
一种低成本外墙专用乳胶漆粉 Download PDFInfo
- Publication number
- CN110482974A CN110482974A CN201910822659.8A CN201910822659A CN110482974A CN 110482974 A CN110482974 A CN 110482974A CN 201910822659 A CN201910822659 A CN 201910822659A CN 110482974 A CN110482974 A CN 110482974A
- Authority
- CN
- China
- Prior art keywords
- emulsion paint
- powder
- exterior wall
- brightening agent
- wall special
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种低成本外墙专用乳胶漆粉，属于乳胶漆粉技术领域。原料质量百分比组成为：灰钙粉68‑78%、元明粉5‑8%、乳胶粉5‑10%、增白剂0.2‑0.5%、膨润土0.5‑1%、群青0.1‑0.5%、淀粉醚0.1‑0.5%、高岭土6‑14%。本发明乳胶漆粉可喷涂可涂刷，具有超白细腻加水后不沉淀的优点，耐气候强，耐水性好，耐擦洗效果达到1500次，白度、细度可与乳胶漆相媲美。每平米的成本低于乳胶漆的几倍，甚至十几倍，每平方成本仅需0.5‑0.7元，是一种低成本高效益的产品，且涂刷简单，操作方便，使用范围广，既美化环境，又节省成本，是一种经济实用的新产品，具有使用效益和社会效益。
Description
技术领域
本发明涉及乳胶漆粉技术领域。
背景技术
乳胶漆是乳胶涂料的俗称，诞生于二十世纪七十年代中下期，是一种水分散性涂料，它是以合成树脂乳液为基料，填料经过研磨分散后加入各种助剂精制而成的涂料。乳胶漆具备了与传统墙面涂料不同的众多优点，如易于涂刷、干燥迅速、漆膜耐水、耐擦洗性好等。在我国，人们习惯上把合成树脂乳液作为基料，以水为分散介质，加入颜料、填料和助剂，经一定工艺过程制成的涂料，叫做乳胶漆，也叫乳胶涂料。
现有乳胶漆大多含有有害物质，如有机汞、乙二醇等，涂刷后在通风不良或未完全干燥的情况下入住会对身体造成很大的伤害，少数乳胶漆厂家本着对使用者负责的态度，在原料中不添加有害物质，使用绿色环保助剂，但这样无形中增加了生产成本。除此之外现有乳胶漆还存在众多缺点，比如其流平性和涂膜手感差、耐水、耐擦洗和耐候性差，涂料中部分组分性质活泼，易返粗返稠，不好控制，是涂料行业一大难题，没有很好的解决方法。随着人们环保意识的不断加强，急需一种绿色环保无污染，成本低的乳胶漆。
发明内容
本发明要解决的技术问题是提供一种低成本外墙专用乳胶漆粉，本发明乳胶漆粉是经许多次实验研究取得的一种低成本外墙专用乳胶漆粉，可喷涂可涂刷，具有超白细腻加水后不沉淀的优点，耐气候强，耐水性好，耐擦洗效果达到1500次，白度、细度可与乳胶漆相媲美。每平米的成本低于乳胶漆的几倍，甚至十几倍，每平方成本仅需0.5-0.7元，是一种低成本高效益的产品，且涂刷简单，操作方便，使用范围广，既能美化环境，又能节省成本，是一种经济实用的绿色环保新产品，具有使用效益和社会效益。
为解决上述技术问题，本发明所采取的技术方案是：
外墙专用乳胶漆粉，原料质量百分比组成如下：灰钙粉68-78%、元明粉5-8%、乳胶粉5-10%、增白剂0.2-0.5%、膨润土0.5-1%、群青0.1-0.5%、淀粉醚0.1-0.5%、高岭土 6-14%。
低成本外墙专用乳胶漆粉，原料质量百分比组成可以为：灰钙粉73%、元明粉7%、乳胶粉8%、增白剂0.4%、膨润土0.8%、群青0.4%、淀粉醚0.4%、高岭土 10%。
低成本外墙专用乳胶漆粉，原料质量百分比组成可以为：灰钙粉77%、元明粉5%、乳胶粉9%、增白剂0.2%、膨润土0.5%、群青0.1%、淀粉醚0.2%、高岭土 8%。
低成本外墙专用乳胶漆粉，原料质量百分比组成可以为：灰钙粉68%、元明粉8%、乳胶粉10%、增白剂0.2%、膨润土1%、群青0.3%、淀粉醚0.5%、高岭土 12%。
低成本外墙专用乳胶漆粉，原料质量百分比组成可以为：灰钙粉78%、元明粉6%、乳胶粉7.5%、增白剂0.5%、膨润土1%、群青0.5%、淀粉醚0.5%、高岭土 6%。
低成本外墙专用乳胶漆粉，原料质量百分比组成可以为：灰钙粉68%、元明粉8%、乳胶粉9%、增白剂0.2%、膨润土0.5%、群青0.1%、淀粉醚0.2%、高岭土 14%。
低成本外墙专用乳胶漆粉，原料质量百分比组成可以为：灰钙粉72%、元明粉7%、乳胶粉10%、增白剂0.5%、膨润土0.5%、群青0.5%、淀粉醚0.5%、高岭土 9%。
灰钙粉：又名氢氧化钙、是一种古老的硬性胶凝材料、常用的无机粘结粉体材料，在本申请中主要起到防水、耐水的作用，但其性质活泼，遇空气中的二氧化碳反应生成碳酸钙晶体而产生强度，起到高耐水、高防水的作用。
乳胶粉：它是由聚合物乳液经喷雾干燥加工而成的产品，具有良好的粘合能力，同时具有耐水、耐碱、耐侯、分散性、柔韧性等不同的性能，在本配方中起到粘合、对灰钙粉的分散性和抗裂作用。形成保护胶体，与增白剂混合适用，有增塑增强效果，使胶膜更耐擦洗，更能增加强度。
增白剂：是一种荧光染料也是一种复杂的有机化合物，它的特性是所染物质获得闪闪发光的效应，使眼看到的物质很白，在本配方中，单纯增白剂对灰钙粉是起不到增白效果的，只有添加了乳胶漆粉才能产生增白效应，同时灰钙粉也能增强乳胶粉的增塑性能，增加乳胶粉的强度。灰钙粉与乳胶粉相互关联、相互促进。
膨润土：外观为乳白色粉末、无臭、无味、无毒、吸附性很强，能吸附有色物质，有机物质，具有良好的增稠性，润滑性，成膜性，耐水性及化学稳定性。膨润土在本配方中对粉料悬浮作用，沉降作用，均匀分散在水中。
群青：最古老的和最鲜艳的蓝色颜料，无毒、无害、环保属有机颜料范畴，它用于提白，可消除白色涂料或其它白色颜料中的黄色光，耐碱、耐高温，在大气中对日晒及风雨侵蚀极其稳定，在本配方主要对产品起到增白、增艳的作用，配合增白剂使用效果更为突出，同时可以避免灰钙粉易变黄。
淀粉醚：是一类分子中含有醚键的变性淀粉的总称，也称醚化淀粉，在涂料中具有良好的均涂性和粘度稳定性，还有良好的悬浮稳定性和流动性，此外在本配方中能控制灰钙粉的活泼型，使其不返粗、不沉淀起到稳定作用。
高岭土：又称煅烧高岭土，具有白度高、质软、易分散于水中、良好的可塑性和高的粘接性，优良的绝缘性能、遮盖力高、抗紫外线，在涂料中可替代部分钛白粉，且成本低廉。
总结:本配方各组分缺一不可，多则浪费。本产品为粉剂型，每公斤兑水，粉水质量比为1:2。
增白剂为二苯乙烯型增白剂，为粉剂。
淀粉醚为羟丙基淀粉醚。
低成本外墙专用乳胶漆粉的制备方法为：（1）先将增白剂放入与其等质量的灰钙粉，混合均匀后过120目筛待用；（2）将群青加入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（3）将步骤（1）和步骤（2）制得的粉料及剩余原料放入搅拌机内充分混合搅拌均匀即可。
步骤（1）中首先将粉剂增白剂加入少量灰钙粉中，此做法既可以使增白剂细分化，又可以使增白剂碱性化，更好的溶于水中，起到更好的效果。
步骤（2）中将群青加入少量灰钙粉中，混合均匀后过120目筛待用，此方法使群青更加细分化，使其更加均匀的分散在粉体中。
本发明低成本外墙专用乳胶漆粉检测结果见下表：
以上所检项目符合GBT 9756-2009《合成树脂乳液内墙涂料》、GB 18582-2008《室内装饰装修材料内墙涂料有害物质限量》标准；又符合GB/T 9755-2014《合成树脂乳液外墙涂料》、GB 24408-2009《建筑用外墙涂料中有害物质限量》标准。
采用上述技术方案所产生的有益效果在于：
本发明乳胶漆粉是经许多次实验研究取得的一种低成本外墙专用乳胶漆粉，可喷涂可涂刷，具有超白细腻加水后不沉淀的优点，耐气候强，耐水性好，耐擦洗效果达到1500次，白度、细度可与乳胶漆相媲美。每平米的成本低于乳胶漆的几倍，甚至十几倍，每平方成本仅需0.5-0.7元，是一种低成本高效益的产品，且可喷涂，亦可刷涂，操作方便，使用范围广，既能美化环境，又能节省成本，是一种经济实用的绿色环保新产品，具有使用效益和社会效益。
具体实施方式
实施例1
低成本外墙专用乳胶漆粉，原料质量百分比组成可以为：灰钙粉73%、元明粉7%、乳胶粉8%、增白剂0.4%、膨润土0.8%、群青0.4%、淀粉醚0.4%、高岭土 10%。
制备方法为：（1）将增白剂放入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（2）将群青加入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（3）将步骤（1）和步骤（2）制得的粉料及剩余原料放入搅拌机内充分混合搅拌均匀即可。
实施例2
低成本外墙专用乳胶漆粉，原料质量百分比组成可以为：灰钙粉77%、元明粉5%、乳胶粉9%、增白剂0.2%、膨润土0.5%、群青0.1%、淀粉醚0.2%、高岭土 8%。
制备方法为：（1）将增白剂放入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（2）将群青加入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（3）将步骤（1）和步骤（2）制得的粉料及剩余原料放入搅拌机内充分混合搅拌均匀即可。
实施例3
低成本外墙专用乳胶漆粉，原料质量百分比组成可以为：灰钙粉68%、元明粉8%、乳胶粉10%、增白剂0.2%、膨润土1%、群青0.3%、淀粉醚0.5%、高岭土 12%。
制备方法为：（1）将增白剂放入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（2）将群青加入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（3）将步骤（1）和步骤（2）制得的粉料及剩余原料放入搅拌机内充分混合搅拌均匀即可。
实施例4
低成本外墙专用乳胶漆粉，原料质量百分比组成可以为：灰钙粉78%、元明粉6%、乳胶粉7.5%、增白剂0.5%、膨润土1%、群青0.5%、淀粉醚0.5%、高岭土 6%。
制备方法为：（1）将增白剂放入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（2）将群青加入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（3）将步骤（1）和步骤（2）制得的粉料及剩余原料放入搅拌机内充分混合搅拌均匀即可。
实施例5
低成本外墙专用乳胶漆粉，原料质量百分比组成可以为：灰钙粉68%、元明粉8%、乳胶粉9%、增白剂0.2%、膨润土0.5%、群青0.1%、淀粉醚0.2%、高岭土 14%。
制备方法为：（1）将增白剂放入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（2）将群青加入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（3）将步骤（1）和步骤（2）制得的粉料及剩余原料放入搅拌机内充分混合搅拌均匀即可。
实施例6
低成本外墙专用乳胶漆粉，原料质量百分比组成可以为：灰钙粉72%、元明粉7%、乳胶粉10%、增白剂0.5%、膨润土0.5%、群青0.5%、淀粉醚0.5%、高岭土 9%。
制备方法为：（1）将增白剂放入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（2）将群青加入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（3）将步骤（1）和步骤（2）制得的粉料及剩余原料放入搅拌机内充分混合搅拌均匀即可。
Claims (5)
1.一种低成本外墙专用乳胶漆粉，其特征在于：原料质量百分比组成如下：灰钙粉68-78%、元明粉5-8%、乳胶粉5-10%、增白剂0.2-0.5%、膨润土0.5-1%、群青0.1-0.5%、淀粉醚0.1-0.5%、高岭土 6-14%。
2.根据权利要求1所述的低成本外墙专用乳胶漆粉，其特征在于：原料质量百分比组成如下：灰钙粉73%、元明粉7%、乳胶粉8%、增白剂0.4%、膨润土0.8%、群青0.4%、淀粉醚0.4%、高岭土 10%。
3.根据权利要求1或2所述的低成本外墙专用乳胶漆粉，其特征在于：增白剂为二苯乙烯型增白剂。
4.根据权利要求1或2所述的低成本外墙专用乳胶漆粉，其特征在于：淀粉醚为羟丙基淀粉醚。
5.权利要求1或2所述的低成本外墙专用乳胶漆粉的制备方法，其特征在于：包括以下步骤：（1）将增白剂放入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（2）将群青加入与其等质量的灰钙粉中，混合均匀后过120目筛待用；（3）将步骤（1）和步骤（2）制得的粉料及剩余原料放入搅拌机内充分混合搅拌均匀即可。