CN110466280A - A kind of gilding film and its manufacturing method having flannelette material for surface - Google Patents
A kind of gilding film and its manufacturing method having flannelette material for surface Download PDFInfo
- Publication number
- CN110466280A CN110466280A CN201910709441.1A CN201910709441A CN110466280A CN 110466280 A CN110466280 A CN 110466280A CN 201910709441 A CN201910709441 A CN 201910709441A CN 110466280 A CN110466280 A CN 110466280A
- Authority
- CN
- China
- Prior art keywords
- layer
- adhesive layer
- flannelette
- gilding film
- engaging portion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to gold stamping technical field of membrane, disclose a kind of gilding film for having flannelette material for surface, which is characterized in that basement membrane, release layer, wearing layer, Information Level, electroplated layer, the first adhesive layer, the second adhesive layer including the setting of successively lamination；First adhesive layer and the second adhesive layer are respectively coated on the surface of electroplated layer and flannelette, and first is equipped with engaging portion between adhesive layer and the second adhesive layer, the engaging portion is one of engagement groove or combination protrusion, gilding film in the present invention uses the double-deck bonded structure, enable the gilding film to stablize with this to be attached on flannelette, to efficiently solve the problems, such as that gilding film is caducous；Specifically, wherein one layer of viscose glue guarantees bond area by the way of being coated on flannelette, avoid the occurrence of the phenomenon that bond area reduces, at the same can also when flannelette surface villus stretch in adhesive layer, to improve the stabilization of this layer of viscose glue bonding.
Description
Technical field
The invention belongs to gold stamping technical field of membrane, and in particular to a kind of gilding film and its manufacture for having flannelette material for surface
Method.
Background technique
Pattern or text are transferred to by thermoprint material surface, in commodity by gilding film using the method for being heated and pressurizeed power
Surface forms gorgeous pattern；Common blocking film is mainly by basement membrane, release layer (peeling layer), Information Level, reflecting layer (electroplated layer)
It is formed with five part of adhesive layer；
Wherein basement membrane generally uses the mylar of 16 μ m-thick biaxial tensiones, and main function is that support is attached to finishing coat and just
Continuous action when thermoprint processing；Release layer is mainly coated with by organic siliconresin etc.；The prime cost of Information Level is
Film forming, heat resistance, the transparency suitable synthetic resin and dyestuff, form color and show；Electroplated layer is generally in the information of film
Layer on aluminium film is deposited, thus reflection light change Information Level color, and show metallic luster (such as: yellow is after aluminizing
To be silver color etc. after golden, colourless aluminize)；Adhesive layer is generally meltable thermoplastic resin, and is coated on aluminium layer to realize
Gilding film is in the bonding for being scalded object.
Flannelette, which refers to, is presented plump villous cotton fabric by napping rear surface, and since the presence of villus makes flannelette table
Face exists for the phenomenon that uneven, uneven thickness, according to above-mentioned traditional gilding film hot pressing on flannelette, then will lead to suede
The bond area of cloth and gilding film adhesive layer reduces, and influences adhesion effect of the gilding film on flannelette, so that gilding film be made to be easy
The problem of falling off.
Summary of the invention
The purpose of the present invention is to provide a kind of gilding films and its manufacturing method for having flannelette material for surface, existing to solve
When some gilding films and flannelette bond, since the protrusion of villus causes adhesive layer and flannelette bond area to reduce, to influence to scald
Golden film adheres to the problem of stability.
To achieve the above object, the invention provides the following technical scheme:
1, a kind of gilding film for having flannelette material for surface, which is characterized in that including successively lamination setting basement membrane, release layer,
Wearing layer, Information Level, electroplated layer, the first adhesive layer, the second adhesive layer；First adhesive layer and the second adhesive layer are respectively coated
In the surface of electroplated layer and flannelette, and engaging portion is equipped between the first adhesive layer and the second adhesive layer, the engaging portion is to combine
One of slot or combination protrusion.
Preferably, the engaging portion is made using coining mode, and imprinted on the second adhesive layer.
Preferably, second adhesive layer uses the preferable bonded adhesives of mobility, and its coating thickness is greater than flannelette surface
The thickness of villus.
2, the manufacturing method of above-mentioned gilding film is as follows:
(1) flexible base film is chosen；
(2) release layer is made on basement membrane in the way of nanometer coating；
(3) after release layer is dry, it is coated with wear-resistant paint in release layer surface, so as to form wearing layer；
(4) Information Level is made on the surface of wearing layer by the way of coining or coating；
(5) it aluminizes in information layer surface, and obtains electroplated layer；
(6) in plating layer surface applying hot melt adhesives, the first adhesive layer is obtained；
(7) the second adhesive layer is coated on flannelette surface；
(8) engaging portion is made on the surface of the second adhesive layer in the way of imprinting moulding；
(9) after the second adhesive layer is dry, the connection of the first adhesive layer and the second adhesive layer is carried out in the way of hot pressing, thus
Realize the connection between gilding film and flannelette.
Preferably, the basement membrane is using one of PET, PVB or PC.
Preferably, the Information Level uses one of printed layer, dye coating or stamp and dyestuff binder course.
Compared with the prior art, the present invention has the following beneficial effects:
Gilding film in the present invention uses the double-deck bonded structure, so that the gilding film is stablized with this and is attached on flannelette, thus
Efficiently solve the problems, such as that gilding film is caducous；
Specifically, wherein one layer of viscose glue guarantees bond area by the way of being coated on flannelette, avoids the occurrence of bond area and subtract
Small phenomenon, at the same can also when flannelette surface villus stretch in adhesive layer, thus improve this layer of viscose glue bonding stabilization；
Another layer of viscose glue then increases contact area by way of cooperating with engaging portion, to keep the connection between two layers of viscose glue more steady
It is fixed.
Detailed description of the invention
Fig. 1 is the gold stamping film structure schematic diagram in the embodiment of the present invention one；
Fig. 2 is the making ide schematic diagram in embodiment one；
Fig. 3 is the gold stamping film structure schematic diagram in the embodiment of the present invention two；
Fig. 4 is the making ide schematic diagram in embodiment two；
In figure: 01- basement membrane, 02- release layer, 03- wearing layer, 04- Information Level, 05- electroplated layer, the first adhesive layer of 06-, 07-
Two adhesive layers, a- engagement groove, b- combine protrusion.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
1, refering to fig. 1 and shown in Fig. 3, it is the structural schematic diagram of gilding film:
A kind of gilding film having flannelette material for surface, including successively lamination setting basement membrane 01, release layer 02, wearing layer 03,
Information Level 04, electroplated layer 05, the first adhesive layer 06, the second adhesive layer 07；Wherein the first adhesive layer 06 and the second adhesive layer 07 divide
It is not coated on the surface of electroplated layer 05 and flannelette, and is equipped with engaging portion between the second adhesive layer 07 and the first adhesive layer 06, in conjunction with
Portion is constituted by engagement groove a or in conjunction with protrusion b.
Specifically, the second adhesive layer 07 is completely contacted with flannelette surface, and the villus on flannelette surface is wrapped in viscous
Inside glue, stabilization be bonded between the portion adhesive and flannelette has been effectively ensured；The second adhesive layer 07 is further through engaging portion simultaneously
It is formed and is connected with the first adhesive layer 06, the contact area between the first adhesive layer 06 and the second adhesive layer 07 is increased, to have
Effect ensure that the stabilization being bonded between the part-structure；
To sum up, enable whole gilding film to stablize and be attached to flannelette surface, avoid causing gilding film easily de- because of the influence of villus
The problem of falling.
Further, above-mentioned second adhesive layer 07 is coated with using the preferable bonded adhesives of mobility, and its coating thickness
Greater than the thickness of flannelette surface villus.
2, for the gilding film of above structure, referring to following manufacturing method:
Embodiment one
In the present embodiment, engaging portion is set as engagement groove a, and engagement groove a is imprinted by making ide as shown in Figure 2, whole
Manufacture is as follows:
(1) choose flexible base film 01: basement membrane 01 is using one of PET, PVB or PC；
(2) release layer 02 is made on basement membrane 01 in the way of nanometer coating；
(3) after release layer 02 is dry, it is coated with wear-resistant paint on 02 surface of release layer, so as to form wearing layer 03；
(4) make Information Level 04 on the surface of wearing layer 03 by the way of coining or coating: Information Level 04 using printed layer or
Dye coating or stamp and dyestuff binder course；
(5) it aluminizes on 04 surface of Information Level, and obtains electroplated layer 05；
(6) in 05 surface applying hot melt adhesives of electroplated layer, the first adhesive layer 06 is obtained；
(7) the second adhesive layer 07 is coated on flannelette surface；
(8) engagement groove a is formed in 07 surface imprint of the second adhesive layer using the making ide in Fig. 2；
(9) after the second adhesive layer 07 containing engagement groove a is dry, the hot pressing of the first adhesive layer 06 and the second adhesive layer 07 is carried out
In conjunction with, and complete the connection between gilding film and flannelette.
Specifically, the first adhesive layer 06 generates fusing, part holt melt glue stream under hot pressing function in above-mentioned hot pressing
It moves to the inside of engagement groove a, achievees the effect that increase the first adhesive layer 06 and 07 contact area of the second adhesive layer with this, and first
The contact area that adhesive layer 06 and engagement groove a are ultimately formed is determined by the mobile performance of hot melt adhesive.
Embodiment two
In the present embodiment, engaging portion is set as combining protrusion b, and is imprinted in conjunction with protrusion b by making ide as shown in Figure 4；
Except making ide selected in step (8) is different, remaining manufacturing process is the same as example 1.
Specifically, the first adhesive layer 06 is limited when melting hot pressing by conjunction with protrusion b, to generate flowing and wrap up
In combining around protrusion b, so that complete connection can be formed between the first adhesive layer 06 and combination protrusion b, relative to embodiment one
For, the contact area of formation is more complete, and it is even closer in conjunction with effect, and the mobile performance of whole bonding state and hot melt adhesive
It is unrelated.
In the above two embodiments, specific: in step (7) a metallic, when the second adhesive layer 07 is coated with its viscose glue have compared with
Good mobility, and the gap between villus can be filled automatically using self-flowing effect, to ensure that the second adhesive layer 07 and suede
The complete contact on cloth surface, while but also viscose glue package forms between the second adhesive layer 07 and villus with outside villus
It is adhesively fixed；
In this state the connection of the second adhesive layer 07 and villus can be formed it is certain be auxiliarily fixed, improve the second adhesive layer 07 with
The stability of flannelette bonding；The second adhesive layer 07 is connect by villus gap with flannelette surface simultaneously, and can effectively avoid villus
The problem of the second adhesive layer 07 can be caused to fall off when falling off.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. a kind of gilding film for having flannelette material for surface, which is characterized in that the basement membrane (01), release including the setting of successively lamination
Layer (02), wearing layer (03), Information Level (04), electroplated layer (05), the first adhesive layer (06), the second adhesive layer (07)；
First adhesive layer (06) and the second adhesive layer (07) are respectively coated on the surface of electroplated layer (05) and flannelette, and first
Engaging portion is equipped between adhesive layer (06) and the second adhesive layer (07), the engaging portion is engagement groove (a) or combines in raised (b)
One kind.
2. a kind of gilding film for having flannelette material for surface according to claim 1, it is characterised in that: adopt the engaging portion
It is made with coining mode, and imprinted on the second adhesive layer (07).
3. a kind of gilding film for having flannelette material for surface according to claim 1, it is characterised in that: second bonding
Layer (07) uses the preferable bonded adhesives of mobility.
4. a kind of gilding film for having flannelette material for surface according to claim 3, it is characterised in that: second bonding
The coating thickness of layer (07) is greater than the thickness of flannelette surface villus.
5. the manufacturing method of gilding film described in claim 1, which comprises the following steps:
(1) flexible base film (01) is chosen；
(2) release layer (02) is made on basement membrane (01) in the way of nanometer coating；
(3) after release layer (02) is dry, it is coated with wear-resistant paint on release layer (02) surface, so as to form wearing layer (03)；
(4) Information Level (04) is made on the surface of wearing layer (03) by the way of coining or coating；
(5) it aluminizes on Information Level (04) surface, and obtains electroplated layer (05)；
(6) in electroplated layer (05) surface applying hot melt adhesives, the first adhesive layer (06) is obtained；
(7) the second adhesive layer (07) is coated on flannelette surface；
(8) engaging portion is made on the surface of the second adhesive layer (07) in the way of imprinting moulding；
(9) after the second adhesive layer (07) is dry, the first adhesive layer (06) and the second adhesive layer are carried out in the way of hot pressing
(07) connection, to realize the connection between gilding film and flannelette.
6. a kind of gilding film and its manufacturing method for having flannelette material for surface according to claim 5, it is characterised in that:
The basement membrane (01) is using one of PET, PVB or PC.
7. a kind of gilding film and its manufacturing method for having flannelette material for surface according to claim 5, it is characterised in that:
The Information Level (04) uses one of printed layer, dye coating or stamp and dyestuff binder course.